RESUMEN
Highly sensitive multicomponent materials designed for the recognition of hazardous compounds request control over interfacial chemistry. The latter is a key parameter in the construction of the sensing (macro) molecular architectures. In this work, multi-walled carbon nanotubes (CNTs) were deposited on diazonium-modified, flexible indium tin oxide (ITO) electrodes prior to the electropolymerization of pyrrole. This three-step process, including diazonium electroreduction, the deposition of CNTs and electropolymerization, provided adhesively-bonded, polypyrrole-wrapped CNT composite coatings on aminophenyl-modified flexible ITO sheets. The aminophenyl (AP) groups were attached to ITO by electroreduction of the in-situ generated aminobenzenediazonium compound in aqueous, acidic medium. For the first time, polypyrrole (PPy) was electrodeposited in the presence of both benzenesulfonic acid (dopant) and ethylene glycol-bis(2-aminoethylether)-tetraacetic acid (EGTA), which acts as a chelator. The flexible electrodes were characterized by XPS, Raman and scanning electron microscopy (SEM), which provided strong supporting evidence for the wrapping of CNTs by the electrodeposited PPy. Indeed, the CNT average diameter increased from 18 ± 2.6 nm to 27 ± 4.8, 35.6 ± 5.9 and 175 ± 20.1 after 1, 5 and 10 of electropolymerization of pyrrole, respectively. The PPy/CNT/NH2-ITO films generated by this strategy exhibit significantly improved stability and higher conductivity compared to a similar PPy coating without any embedded CNTs, as assessed by from electrochemical impedance spectroscopy measurements. The potentiometric response was linear in the 10-8-3 × 10-7 mol L-1 Pb(II) concentration range, and the detection limit was 2.9 × 10-9 mol L-1 at S/N = 3. The EGTA was found to drastically improve selectivity for Pb(II) over Cu(II). To account for this improvement, the density functional theory (DFT) was employed to calculate the EGTA-metal ion interaction energy, which was found to be -374.6 and -116.4 kJ/mol for Pb(II) and Cu(II), respectively, considering solvation effects. This work demonstrates the power of a subtle combination of diazonium coupling agent, CNTs, chelators and conductive polymers to design high-performance electrochemical sensors for environmental applications.
RESUMEN
4-Benzenethiol-functionalized high-surface-area graphite powder was prepared and decorated with bimetallic Cu100-xRhx nanoparticles (NPs) to serve as electrocatalysts for the reduction of nitrates. In the first step, the HSAG powder was grafted with in-situ-generated diazonium compounds from 4-aminothiophenol (ATP) in an acidic medium using NaNO2 for the diazotization process. The surface composition was tuned using different initial quantities of ATP. The surface XPS-determined S/C atomic ratio was found to increase stepwise with the initial quantity of amine. In a second step, the grafted and untreated HSAG powders were decorated with Cu100-xRhx NPs by a wet chemical method and the elemental composition of the end composites was assessed by EDS-SEM and ICP, whereas TEM and EDS-TEM served to characterize the NP morphology and their composition on the nanometer scale. In all cases, the NP size was invariably found to be â¼1.7 nm but with a size distribution becoming narrower under an increasing grafting rate and the global composition enriched in copper. Voltammetry was performed with a cavity microelectrode to evaluate the electrocatalytic performance of the composites for nitrate reduction. Increasing diazonium grafting led to a progressive reduction of the peak current intensity and a shift of the peak potentials toward cathodic values. The maximum intensity was obtained for 0.005 µmol of diazonium salt per mg of HSAG, with a gain of 40% in comparison to the best untreated sample. This improvement and a change in the voltammogram characteristics after grafting seem to result from modifications of the local composition at the level of NPs that differ from the global composition. This work conclusively shows that diazonium surface modification is important not only in attaching electrocatalytic NPs to carbon supports but also in providing a narrower size distribution of the electrocatalysts together with finely tuned catalytic properties.
RESUMEN
Tetrafluoroborate salts of diazotized Azure A (AA-N2+), Neutral Red (NR-N2+) and Congo Red (CR-N2+) dyes were prepared and reacted with multiwalled carbon nanotubes (MWCNTs) at room temperature, in water without any reducing agent. The as-modified MWCNTs were examined by IRATR, Raman spectroscopy, XPS, TGA, TEM, and cyclic voltammetry. The diazonium band located at â¼2350 cm-1 in the diazotized dye IR spectra vanished after attachment to the nanotubes whereas the Raman D/G peak ratio slightly increased after dye covalent attachment at a high initial diazonium/CNT mass ratio. XPS measurements show the loss of F 1s from the BF4- anion together with a clear change in the high-resolution C 1s region from the modified nanotubes. Thermogravimetric analyses proved substantial mass loadings of the organic grafts leveling off at 40.5, 34.3, and 50.7 wt % for AA, NR, and CR, respectively. High-resolution TEM pictures confirmed the presence of 1.5-7-nm-thick continuous amorphous layers on the nanotubes assigned to the aryl layers from the dyes. Cyclic voltammetry studies in acetonitrile (ACN) confirmed the grafting of the dyes; the latter retain their electrochemical behavior in the grafted state. The experimental results correlate remarkably well with quantum chemical calculations that indicate high binding energies between the dyes and the CNTs accounting for true covalent bonding (140-185 kJ/mol with the CNT-aryl distance <1.6 nm), though attachment by π stacking also contributes to obtaining stable hybrids. Finally, the pH-responsive character of the robust hybrids was demonstrated by a higher degree of protonation of Neutral Red-grafted CNTs at pH 2 compared to that of the neutral aqueous medium. This work demonstrates that diazotized dyes can be employed for the surface modification of MWCNTs in a very simple and efficient manner in water and at room temperature. The hybrids could be employed for many purposes such as optically pH-responsive materials, biosensors, and optothermal composite actuators to name a few.
RESUMEN
The use of enzymatic agents as biological solutions for cleaning ion-exchange membranes fouled by organic compounds during electrodialysis (ED) treatments in the food industry could be an interesting alternative to chemical cleanings implemented at an industrial scale. This paper is focused on testing the cleaning efficiency of three enzyme classes (ß-glucanase, protease, and polyphenol oxidase) chosen for their specific actions on polysaccharides, proteins, and phenolic compounds, respectively, fouled on a homogeneous cation-exchange membrane (referred CMX-Sb) used for tartaric stabilization of red wine by ED in industry. First, enzymatic cleaning tests were performed using each enzyme solution separately with two different concentrations (0.1 and 1.0 g/L) at different incubation temperatures (30, 35, 40, 45, and 50 °C). The evolution of membrane parameters (electrical conductivity, ion-exchange capacity, and contact angle) was determined to estimate the efficiency of the membrane's principal action as well as its side activities. Based on these tests, we determined the optimal operating conditions for optimal recovery of the studied characteristics. Then, cleaning with three successive enzyme solutions or the use of two enzymes simultaneously in an enzyme mixture were tested taking into account the optimal conditions of their enzymatic activity (concentration, temperatures, and pH). This study led to significant results, indicating effective external and internal cleaning by the studied enzymes (a recovery of at least 25% of the electrical conductivity, 14% of the ion-exchange capacity, and 12% of the contact angle), and demonstrated the presence of possible enzyme combinations for the enhancement of the global cleaning efficiency or reducing cleaning durations. These results prove, for the first time, the applicability of enzymatic cleanings to membranes, the inertia of their action towards polymer matrix to the extent that the choice of enzymes is specific to the fouling substrates.