Identification and Decomposition of Uranium Oxychloride Phases in Oxygen-Exposed UCl3 Salt Compositions.

Complementary X-ray absorption fine structure (XAFS) spectroscopy and Raman spectroscopy studies were conducted on several UCl3 concentrations in several chloride salt compositions. The samples were 5% UCl3 in LiCl (S1), 5% UCl3 in KCl (S2), 5% UCl3 in LiCl-KCl eutectic (S3), 5% UCl3 in LiCl-KCl eutectic (S4), 50% UCl3 in KCl (S5), and 20% UCl3 in KCl (S6) molar concentrations. Sample S3 had UCl3 sourced from Idaho National Laboratory (INL), and all other samples were UCl3 sourced from TerraPower. The initial compositions were prepared in an inert and oxygen-free atmosphere. XAFS measurements were performed in the atmosphere at a beamline, and Raman spectroscopy was conducted inside a glovebox. Raman spectra were able to confirm initial UCl3. XAFS and later Raman spectra measured, however, did not correctly match the literature and computational spectra for the prepared UCl3 salt. Rather, the data shows some complex uranium oxychloride phases at room temperature that transition into uranium oxides upon heating. Oxygen pollution due to failure of the sealing mechanism can result in oxidation of the UCl3 salts. The oxychlorides present may be both a function of the unknown O2 exposure concentration, depending on the source of the leak and the salt composition. Evidence of this oxychloride claim and its subsequent decomposition is justified in this work.

In Situ Determination of Speciation and Local Structure of NaCl-SrCl2 and LiF-ZrF4 Molten Salts.

Understanding the local environment of the metal atoms in salt melts is important for modeling the properties of melts and predicting their behavior and thus helping enable the development of technologies such as molten salt reactors and solar-thermal power systems and new approaches to recycling rare-earth metals. Toward that end, we have developed an in situ approach for measuring the coordination of metals in molten salt coupling X-ray absorption spectroscopy (XAS) and Raman spectroscopy. Our approach was demonstrated for two salt mixtures (1.9 and 5 mol % SrCl2 in NaCl, 0.8 and 5 mol % ZrF4 in LiF) at up to 1100 °C. Near-edge (X-ray absorption near-edge structure, XANES) and extended X-ray absorption fine structure (EXAFS) spectra were measured. The EXAFS response was modeled using ab initio FEFF calculations. Strontium's first shell is observed to be coordinated with chlorine (Sr2+-Cl-) and zirconium's first shell is coordinated by fluorine (Zr4+-F-), both having coordination numbers that decrease with increasing temperature. Multiple zirconium complexes are believed to be present in the melt, which may interfere and distort the EXAFS spectra and result in an anomalously low zirconium first shell coordination number. The use of boron nitride (BN) powder as a salt diluent for XAFS measurements was found to not interfere with measurements and thus can be used for investigations of such systems.