RESUMEN
We report an X-ray absorption near edge structure (XANES) study of vanadium (V) and nitrogen (N) dopants in anatase TiO2 thin films deposited by radio-frequency magnetron sputtering. Measurements at the Ti K and V K edges were combined with soft X-ray experiments at the Ti L2,3, O K and N K edges. Full potential ab initio spectral simulations of the V, O and N K-edges were carried out for different possible configurations of substitutional and interstitial dopant-related point defects in the anatase structure. The comparison between experiments and simulations demonstrates that V occupies substitutional cationic sites (replacing Ti) irrespective of the film structure and dopant concentration (up to 4.5 at%). On the other hand, N is found both in substitutional anionic sites (replacing O) and as N2 dimers within TiO2 interstices. The dopants' local structures are discussed with reference to the enhanced optical absorption and photocatalytic activity achieved by (co)doping.
RESUMEN
Integrated absorber/electrocatalyst schemes are increasingly adopted in the design of photoelectrodes for photoelectrochemical cells because they can take advantage of separately optimized components. Such schemes also lead to the emergence of novel challenges, among which parasitic light absorption and the nature of the absorber/catalyst junction features prominently. By taking advantage of the versatility of pulsed-laser deposition technique, we fabricated a porous iron(III) oxide nanoparticle-assembled coating that is both transparent to visible light and active as an electrocatalyst for water oxidation. Compared to a compact morphology, the porous catalyst used to functionalize crystalline hematite photoanodes exhibits a superior photoresponse, resulting in a drastic lowering of the photocurrent overpotential (about 200 mV) and a concomitant 5-fold increase in photocurrents at 1.23 V versus reversible hydrogen electrode. Photoelectrochemical impedance spectroscopy indicated a large increase in trapped surface hole capacitance coupled with a decreased charge transfer resistance, consistent with the possible formation of an adaptive junction between the absorber and the porous nanostructured catalyst. The observed effect is among the most prominent reported for the coupling of an electrocatalyst with a thin layer absorber.
RESUMEN
Amorphous iron oxide nanoparticles were synthesized by pulsed-laser deposition (PLD) for functionalization of indium-tin oxide surfaces, resulting in electrodes capable of efficient catalysis in water oxidation. These electrodes, based on earth-abundant and nonhazardous iron metal, are able to sustain high current densities (up to 20 mA/cm2) at reasonably low applied potential (1.64 V at pH 11.8 vs reversible hydrogen electrode) for more than 1 h when employed as anodes for electrochemical water oxidation. The good catalytic performance proves the validity of PLD as a method to prepare nanostructured solid-state materials for catalysis, enabling control over critical properties such as surface coverage and morphology.