RESUMEN
An approach has been developed that allows the synthesis of submicron spherical silica particles with a controlled micro-mesoporous structure possessing a large specific surface area (up to 1300 m2g-1). Particle synthesis is carried out by the hydrolysis of a mixture of various organosilanes mostly associated either with CTAB or with each other. A change in the concentration of CTAB in the reaction mixture apparently leads to a change in the formation mechanism of nuclei for the silica particle growth, which allows for varying the diameter of the synthesized particles in the range from 40-450 nm. The effect of the composition of the silica precursor ([3-(methacryloyloxy)propyl]trimethoxysilane, (3-aminopropyl)triethoxysilane and tetraethoxysilane) on the formation process and porosity of the resulting particles is studied. It was shown that by simply varying the ratio of organosilanes in the composition of the precursor, one can control the pore diameter of the particles in a wide range from 0.6-15 nm. The large-pore (up to 15 nm) silica particles are used as a matrix for the spatial distribution of luminescent carbon dots. The incorporation of carbon dots into SiO2particles prevents their aggregation leading to emission quenching after drying, thus allowing us to obtain highly luminescent composite particles. LEDs based on the obtained composite material show bright visible luminescence with spectral characteristics similar to that of a commercial cold white LED.
RESUMEN
Carbon dots (CDs) with an emission in the near infrared spectral region are attractive due to their promising applications in bio-related areas, while their fabrication still remains a challenging task. Herein, we developed a template-assisted method using porous silica microspheres for the formation of CDs with optical transitions in the near infrared. Two organic dyes, Rhodamine 6G and IR1061 with emission in the yellow and near infrared spectral regions, respectively, were used as precursors for CDs. Correlation of morphology and chemical composition with optical properties of obtained CDs revealed the origin of their emission, which is related to the CDs' core optical transitions and dye-derivatives within CDs. By varying annealing temperature, different kinds of optical centers as derivatives of organic dyes are formed in the microsphere's pores. The template-assisted method allows us to synthesize CDs with an emission peaked at 1085 nm and photoluminescence quantum yield of 0.2%, which is the highest value reported so far for CDs emitting at wavelengths longer than 1050 nm.
RESUMEN
Luminescent composites based on entirely non-toxic, environmentally friendly compounds are in high demand for a variety of applications in photonics and optoelectronics. Carbon dots are a recently developed kind of luminescent nanomaterial that is eco-friendly, biocompatible, easy-to-obtain, and inexpensive, with a stable and widely tunable emission. Herein, we introduce luminescent composites based on carbon dots of different chemical compositions and with different functional groups at the surface which were embedded in a nanoporous silicate glass. The structure and optical properties of these composites were comprehensively examined using electron microscopy, Fourier transform infrared transmission, UV-Vis absorption, and steady-state and time-resolved photoluminescence. It is shown that the silicate matrix efficiently preserved, and even enhanced the emission of different kinds of carbon dots tested. The photoluminescence quantum yield of the fabricated nanocomposite materials reached 35-40%, which is comparable to or even exceeds the values for carbon dots in solution.
RESUMEN
Monodisperse carbon nanodots (MCNDs) having an identical composition, structure, shape and size possess identical chemical and physical properties, making them highly promising for various technical and medical applications. Herein, we report a facile and effective route to obtain monodisperse carbon nanodots 3.5 ± 0.9 nm in size by thermal decomposition of organosilane within the pores of monodisperse mesoporous silica particles with subsequent removal of the silica template. Structural studies demonstrated that the MCNDs we synthesized consist of â¼7-10 defective graphene layers that are misoriented with respect to each other and contain various oxygen-containing functional groups. It was demonstrated that, owing to their identical size and chemical composition, the MCNDs are formed via coagulation primary aggregates â¼10-30 nm in size, which are, in turn, combined into secondary porous spherical aggregates â¼100-200 nm in diameter. The processes of coagulation of MCNDs and peptization of their hierarchical aggregates are fully reversible and can be controlled by varying the MCND concentration or the pH value of the hydrosols. Submicrometer spherical aggregates of MCNDs are not disintegrated as the hydrosol is dried. The thus obtained porous spherical aggregates of MCNDs are promising for drug delivery as a self-disassembling container for medicinal preparations.
RESUMEN
In this research, a novel IMAC sorbent with high specificity for chlorine-containing compounds was developed. Ni-functionalized monodisperse spherical mesoporous silica particles of 500±25nm diameter were synthesized and their metal affinity properties were studied with the use of diclofenac as the model substance. The particles were aggregatively stable in the pH range of 3-12. The sorbent demonstrated a high adsorption capacity (0.60±0.06µg of DCF per 1mg of the sorbent) and high adsorption/desorption rate (20 and 5min was enough for the sorbent saturation and desorption of DCF, correspondingly). A mixture of eluents with addition of PFOS providing the almost complete recovery (98%) of diclofenac was first proposed. The monodispersity and the high sedimentation and aggregative stability of the particles provide the formation of a stable hydrosol even under ultrasound treatment which makes the mSiO2/Ni particles suitable for batch chromatography.