The reduction of Pt content in the cathode for proton exchange membrane fuel cells is highly desirable to lower their costs. However, lowering the Pt loading of the cathodic electrode leads to high voltage losses. These voltage losses are known to originate from the mass transport resistance of O2 through the platinum-ionomer interface, the location of the Pt particle with respect to the carbon support and the supports' structures. In this study, we present a new Pt catalyst/support design that substantially reduces local oxygen-related mass transport resistance. The use of chemically modified carbon supports with tailored porosity enabled controlled deposition of Pt nanoparticles on the outer and inner surface of the support particles. This resulted in an unprecedented uniform coverage of the ionomer over the high surface-area carbon supports, especially under dry operating conditions. Consequently, the present catalyst design exhibits previously unachieved fuel cell power densities in addition to high stability under voltage cycling. Thanks to the Coulombic interaction between the ionomer and N groups on the carbon support, homogeneous ionomer distribution and reproducibility during ink manufacturing process is ensured.
RESUMEN
Layered double hydroxides (LDHs) are among the most active and studied catalysts for the oxygen evolution reaction (OER) in alkaline electrolytes. However, previous studies have generally either focused on a small number of LDHs, applied synthetic routes with limited structural control, or used non-intrinsic activity metrics, thus hampering the construction of consistent structure-activity-relations. Herein, by employing new individually developed synthesis strategies with atomic structural control, we obtained a broad series of crystalline α-MA (II)MB (III) LDH and ß-MA (OH)2 electrocatalysts (MA =Ni, Co, and MB =Co, Fe, Mn). We further derived their intrinsic activity through electrochemical active surface area normalization, yielding the trend NiFe LDH > CoFe LDH > Fe-free Co-containing catalysts > Fe-Co-free Ni-based catalysts. Our theoretical reactivity analysis revealed that these intrinsic activity trends originate from the dual-metal-site nature of the reaction centers, which lead to composition-dependent synergies and diverse scaling relationships that may be used to design catalysts with improved performance.
RESUMEN
The direct electrochemical conversion of carbon dioxide (CO2 ) into multi-carbon (C2+ ) products still faces fundamental and technological challenges. While facet-controlled and oxide-derived Cu materials have been touted as promising catalysts, their stability has remained problematic and poorly understood. Herein we uncover changes in the chemical and morphological state of supported and unsupported Cu2 O nanocubes during operation in low-current H-Cells and in high-current gas diffusion electrodes (GDEs) using neutral pH buffer conditions. While unsupported nanocubes achieved a sustained C2+ Faradaic efficiency of around 60 % for 40â h, the dispersion on a carbon support sharply shifted the selectivity pattern towards C1 products. Operando XAS and time-resolved electron microscopy revealed the degradation of the cubic shape and, in the presence of a carbon support, the formation of small Cu-seeds during the surprisingly slow reduction of bulk Cu2 O. The initially (100)-rich facet structure has presumably no controlling role on the catalytic selectivity, whereas the oxide-derived generation of under-coordinated lattice defects, can support the high C2+ product yields.
RESUMEN
A series of Pt/Ni-SiO2/C catalysts with different mass proportions of Ni-SiO2/C (0:100, 30:70, 50:50, 70:30 and 100:0) were prepared and studied towards ethanol electrochemical oxidation in acid medium. The support silica particles were initially synthesized via sol-gel and then modified with NiCl2. The Ni deposited on the silica surface plays a role promoting nucleation sites for the reduction of platinum. Pt was further chemically reduced onto Ni-SiO2 using formic acid and loaded onto carbon Vulcan XC-72 R. The Pt/Ni-SiO2/C catalysts were characterized by X-ray diffraction, Fourier transform infrared spectroscopy, temperature-programmed reduction, X-ray photoelectron spectroscopy, transmission electron microscopy and inductively coupled plasma-optical emission spectroscopy. The physical characterizations reveal the formation of oxide-metal composite and strong interaction between Pt and the Ni-SiO2 composite. The Pt/Ni-SiO2/C catalyst with meso/macroporous structure exhibits higher electrocatalytic activity towards ethanol oxidation and better stability, after 48 h of electrolysis, than a commercial Pt/C catalyst. These improved features could be due to presence of Ni-SiO2 composite that promotes corrosion resistance of the support and prevents the aggregation of Pt nanoparticles and their detachment from the support. The low poisoning of the Pt/Ni-SiO2/C catalyst is probably due to the enhanced oxygen content on the composite surface. The high electrocatalytic activity and enhanced electrochemical stability of the Pt/Ni-SiO2/C catalyst make it promising for further fuel cell applications.
RESUMEN
This 2007 Chemistry Nobel prize update covers scientific advances of the past decade in our understanding of electrocatalytic processes on surfaces of nanoscale shape-controlled polyhedral solids. It is argued that the field of chemical reaction processes on solid surfaces has recently been paying increasing attention to the fundamental understanding of electrified solid-liquid interfaces and toward the operando study of the minute fraction of catalytically active, structurally dynamic non-equilibrium Taylor-type surface sites. Meanwhile, despite mounting evidence of acting as structural proxies in some cases, the concept of catalytic structure sensitivity of well-defined nanoscale solid surfaces continues to be a key organizing principle for the science of shape-controlled nanocrystals and, hence, constitutes a central recurring theme in this review. After addressing key aspects and recent progress in the wet-chemical synthesis of shaped nanocatalysts, three areas of electrocatalytic processes on solid shape-controlled nanocrystals of current scientific priority are discussed in more detail: the oxygen electroreduction on shape-controlled Pt-Ni polyhedra with its technological relevance for low temperature fuel cells, the CO2 electroreduction to hydrocarbons on Cu polyhedra and the puzzling interplay between chemical and structural effects, and the electrocatalytic oxygen evolution reaction from water on shaped transition metal oxides. The review closes with the conclusion that Surface Science and thermal catalysis, honored by Ertl's Nobel prize a decade ago, continue to show major repercussions on the emerging field of Interface Science.
RESUMEN
Ni-Fe oxyhydroxides are the most active known electrocatalysts for the oxygen evolution reaction (OER) in alkaline electrolytes and are therefore of great scientific and technological importance in the context of electrochemical energy conversion. Here we uncover, investigate, and discuss previously unaddressed effects of conductive supports and the electrolyte pH on the Ni-Fe(OOH) catalyst redox behavior and catalytic OER activity, combining in situ UV-vis spectro-electrochemistry, operando electrochemical mass spectrometry (DEMS), and in situ cryo X-ray absorption spectroscopy (XAS). Supports and pH > 13 strongly enhanced the precatalytic voltammetric charge of the Ni-Fe oxyhydroxide redox peak couple, shifted them more cathodically, and caused a 2-3-fold increase in the catalytic OER activity. Analysis of DEMS-based faradaic oxygen efficiency and electrochemical UV-vis traces consistently confirmed our voltammetric observations, evidencing both a more cathodic O2 release and a more cathodic onset of Ni oxidation at higher pH. Using UV-vis, which can monitor the amount of oxidized Ni+3/+4 in situ, confirmed an earlier onset of the redox process at high electrolyte pH and further provided evidence of a smaller fraction of Ni+3/+4 in mixed Ni-Fe centers, confirming the unresolved paradox of a reduced metal redox activity with increasing Fe content. A nonmonotonic super-Nernstian pH dependence of the redox peaks with increasing Fe content-displaying Pourbaix slopes as steep as -120 mV/pH-suggested a two proton-one electron transfer. We explain and discuss the experimental pH effects using refined coupled (PCET) and decoupled proton transfer-electron transfer (PT/ET) schemes involving negatively charged oxygenate ligands generated at Fe centers. Together, we offer new insight into the catalytic reaction dynamics and associated catalyst redox chemistry of the most important class of alkaline OER catalysts.
RESUMEN
Direct ethanol fuel cells are attractive power sources based on a biorenewable, high energy-density fuel. Their efficiency is limited by the lack of active anode materials which catalyze the breaking of the C-C bond coupled to the 12-electron oxidation to CO2 . We report shape-controlled PtNiRh octahedral ethanol oxidation electrocatalysts with excellent activity and previously unachieved low onset potentials as low as 0.1â V vs. RHE, while being highly selective to complete oxidation to CO2 . Our comprehensive characterization and in situ electrochemical ATR studies suggest that the formation of a ternary surface site ensemble around the octahedral Pt3 Ni1 Rhx nanoparticles plays a crucial mechanistic role for this behavior.
RESUMEN
Redox-active support materials can help reduce the noble-metal loading of a solid chemical catalyst while offering electronic catalyst-support interactions beneficial for catalyst durability. This is well known in heterogeneous gas-phase catalysis but much less discussed for electrocatalysis at electrified liquid-solid interfaces. Here, we demonstrate experimental evidence for electronic catalyst-support interactions in electrochemical environments and study their role and contribution to the corrosion stability of catalyst/support couples. Electrochemically oxidized Ir oxide nanoparticles, supported on high surface area carbons and oxides, were selected as model catalyst/support systems for the electrocatalytic oxygen evolution reaction (OER). First, the electronic, chemical, and structural state of the catalyst/support couple was compared using XANES, EXAFS, TEM, and depth-resolved XPS. While carbon-supported oxidized Ir particle showed exclusively the redox state (+4), the Ir/IrOx/ATO system exhibited evidence of metal/metal-oxide support interactions (MMOSI) that stabilized the metal particles on antimony-doped tin oxide (ATO) in sustained lower Ir oxidation states (Ir(3.2+)). At the same time, the growth of higher valent Ir oxide layers that compromise catalyst stability was suppressed. Then the electrochemical stability and the charge-transfer kinetics of the electrocatalysts were evaluated under constant current and constant potential conditions, where the analysis of the metal dissolution confirmed that the ATO support mitigates Ir(z+) dissolution thanks to a stronger MMOSI effect. Our findings raise the possibility that MMOSI effects in electrochemistry-largely neglected in the past-may be more important for a detailed understanding of the durability of oxide-supported nanoparticle OER catalysts than previously thought.
RESUMEN
Multimetallic shape-controlled nanoparticles offer great opportunities to tune the activity, selectivity, and stability of electrocatalytic surface reactions. However, in many cases, our synthetic control over particle size, composition, and shape is limited requiring trial and error. Deeper atomic-scale insight in the particle formation process would enable more rational syntheses. Here we exemplify this using a family of trimetallic PtNiCo nanooctahedra obtained via a low-temperature, surfactant-free solvothermal synthesis. We analyze the competition between Ni and Co precursors under coreduction "one-step" conditions when the Ni reduction rates prevailed. To tune the Co reduction rate and final content, we develop a "two-step" route and track the evolution of the composition and morphology of the particles at the atomic scale. To achieve this, scanning transmission electron microscopy and energy dispersive X-ray elemental mapping techniques are used. We provide evidence of a heterogeneous element distribution caused by element-specific anisotropic growth and create octahedral nanoparticles with tailored atomic composition like Pt1.5M, PtM, and PtM1.5 (M = Ni + Co). These trimetallic electrocatalysts have been tested toward the oxygen reduction reaction (ORR), showing a greatly enhanced mass activity related to commercial Pt/C and less activity loss than binary PtNi and PtCo after 4000 potential cycles.
RESUMEN
Adoption of proton exchange membrane (PEM) water electrolysis technology on a global level will demand a significant reduction of today's iridium loadings in the anode catalyst layers of PEM electrolyzers. However, new catalyst and electrode designs with reduced Ir content have been suffering from limited stability caused by (electro)chemical degradation. This has remained a serious impediment to a wider commercialization of larger-scale PEM electrolysis technology. In this combined DFT computational and experimental study, we investigate a novel family of iridium-niobium mixed metal oxide thin-film catalysts for the oxygen evolution reaction (OER), some of which exhibit greatly enhanced stability, such as minimized voltage degradation and reduced Ir dissolution with respect to the industry benchmark IrOx catalyst. More specifically, we report an unusually durable IrNbOx electrocatalyst with improved catalytic performance compared to an IrOx benchmark catalyst prepared in-house and a commercial benchmark catalyst (Umicore Elyst Ir75 0480) at significantly reduced Ir catalyst cost. Catalyst stability was assessed by conventional and newly developed accelerated degradation tests, and the mechanistic origins were analyzed and are discussed. To achieve this, the IrNbOx mixed metal oxide catalyst and its water splitting kinetics were investigated by a host of techniques such as synchrotron-based NEXAFS analysis and XPS, electrochemistry, and ab initio DFT calculations as well as STEM-EDX cross-sectional analysis. These analyses highlight a number of important structural differences to other recently reported bimetallic OER catalysts in the literature. On the methodological side, we introduce, validate, and utilize a new, nondestructive XRF-based catalyst stability monitoring technique that will benefit future catalyst development. Furthermore, the present study identifies new specific catalysts and experimental strategies for stepwise reducing the Ir demand of PEM water electrolyzers on their long way toward adoption at a larger scale.
RESUMEN
NiFe and CoFe (MFe) layered double hydroxides (LDHs) are among the most active electrocatalysts for the alkaline oxygen evolution reaction (OER). Herein, we combine electrochemical measurements, operando X-ray scattering and absorption spectroscopy, and density functional theory (DFT) calculations to elucidate the catalytically active phase, reaction center and the OER mechanism. We provide the first direct atomic-scale evidence that, under applied anodic potentials, MFe LDHs oxidize from as-prepared α-phases to activated γ-phases. The OER-active γ-phases are characterized by about 8% contraction of the lattice spacing and switching of the intercalated ions. DFT calculations reveal that the OER proceeds via a Mars van Krevelen mechanism. The flexible electronic structure of the surface Fe sites, and their synergy with nearest-neighbor M sites through formation of O-bridged Fe-M reaction centers, stabilize OER intermediates that are unfavorable on pure M-M centers and single Fe sites, fundamentally accounting for the high catalytic activity of MFe LDHs.
RESUMEN
Seawater is an abundant water resource on our planet and its direct electrolysis has the advantage that it would not compete with activities demanding fresh water. Oxygen selectivity is challenging when performing seawater electrolysis owing to competing chloride oxidation reactions. In this work we propose a design criterion based on thermodynamic and kinetic considerations that identifies alkaline conditions as preferable to obtain high selectivity for the oxygen evolution reaction. The criterion states that catalysts sustaining the desired operating current with an overpotential <480â mV in alkaline pH possess the best chance to achieve 100 % oxygen/hydrogen selectivity. NiFe layered double hydroxide is shown to satisfy this criterion at pHâ 13 in seawater-mimicking electrolyte. The catalyst was synthesized by a solvothermal method and the activity, surface redox chemistry, and stability were tested electrochemically in alkaline and near-neutral conditions (borate buffer at pHâ 9.2) and under both fresh seawater conditions. The Tafel slope at low current densities is not influenced by pH or presence of chloride. On the other hand, the addition of chloride ions has an influence in the temporal evolution of the nickel reduction peak and on both the activity and stability at high current densities at pHâ 9.2. Faradaic efficiency close to 100 % under the operating conditions predicted by our design criteria was proven using inâ situ electrochemical mass spectrometry.
Asunto(s)
Hidróxidos/química , Hierro/química , Níquel/química , Agua de Mar/química , Catálisis , Cloruros/química , Electrólisis , Concentración de Iones de HidrógenoRESUMEN
Reducing the noble-metal catalyst content of acid Polymer Electrolyte Membrane (PEM) water electrolyzers without compromising catalytic activity and stability is a goal of fundamental scientific interest and substantial technical importance for cost-effective hydrogen-based energy storage. This study presents nanostructured iridium nanodendrites (Ir-ND) supported on antimony doped tin oxide (ATO) as efficient and stable water splitting catalysts for PEM electrolyzers. The active Ir-ND structures exhibited superior structural and morphological properties, such as particle size and surface area compared to commercial state-of-art Ir catalysts. Supported on tailored corrosion-stable conductive oxides, the Ir-ND catalysts exhibited a more than 2-fold larger kinetic water splitting activity compared with supported Ir nanoparticles, and a more than 8-fold larger catalytic activity than commercial Ir blacks. In single-cell PEM electrolyzer tests, the Ir-ND/ATO outperformed commercial Ir catalysts more than 2-fold at technological current densities of 1.5 A cm-2 at a mere 1.80 V cell voltage, while showing excellent durability under constant current conditions. We conclude that Ir-ND/ATO catalysts have the potential to substantially reduce the required noble metal loading, while maintaining their catalytic performance, both in idealized three-electrode set ups and in the real electrolyzer device environments.
RESUMEN
Water splitting catalysed by earth-abundant materials is pivotal for global-scale production of non-fossil fuels, yet our understanding of the active catalyst structure and reactivity is still insufficient. Here we report on the structurally reversible evolution of crystalline Co3O4 electrocatalysts during oxygen evolution reaction identified using advanced in situ X-ray techniques. At electrode potentials facilitating oxygen evolution, a sub-nanometre shell of the Co3O4 is transformed into an X-ray amorphous CoOx(OH)y which comprises di-µ-oxo-bridged Co(3+/4+) ions. Unlike irreversible amorphizations, here, the formation of the catalytically-active layer is reversed by re-crystallization upon return to non-catalytic electrode conditions. The Co3O4 material thus combines the stability advantages of a controlled, stable crystalline material with high catalytic activity, thanks to the structural flexibility of its active amorphous oxides. We propose that crystalline oxides may be tailored for generating reactive amorphous surface layers at catalytic potentials, just to return to their stable crystalline state under rest conditions.