On the extraction of MoO x photothermally active nanoparticles by gel filtration from a byproduct of few-layer MoS2 exfoliation.

Gel filtration is a versatile technique employed for biological molecules and nanoparticles, offering their reproducible classification based on size and shape. Colloidal nanoparticles are of significant interest in biomedical applications due to a large number of solution-based bioconjugation procedures. Nevertheless, the inherent polydispersity of the nanoparticles produced by various techniques necessitates the employment of high yield separation and purification techniques. Here we demonstrate the employment of gel filtration on non-stoichiometric plasmonic MoO x nanoparticles, prepared by an oxidation process during liquid-phase exfoliation of few-layer MoS2 nanosheets. This resulted in the separation of two types of MoO x particles, in the form of two different chromatographic fractions. They showed different sizes, morphological and optical properties. The fraction containing smaller particles with diameters of 1-4 nm, exhibited an increased absorbance peak in the near IR region and responded with a significant temperature increase to laser irradiation at the wavelength close to the maximal absorption. The fraction with the larger particles from 3 up to 10 nm, showed weak photoluminescence and a preferred orientation upon the deposition on a planar substrate. However, it had no absorbance in the near IR compared to the former fraction. According to our knowledge, this is the first time that the gel filtration was applied to the separation of molybdenum oxide nanomaterials. This step ensured the isolation of plasmonic MoO x nanoparticles suitable for further bioconjugation and target photothermal treatment.

Tailored Langmuir-Schaefer Deposition of Few-Layer MoS2 Nanosheet Films for Electronic Applications.

Few-layer MoS2 films stay at the forefront of current research of two-dimensional materials. At present, continuous MoS2 films are prepared by chemical vapor deposition (CVD) techniques. Herein, we present a cost-effective fabrication of the large-area spatially uniform films of few-layer MoS2 flakes using a modified Langmuir-Schaefer technique. The compression of the liquid-phase exfoliated MoS2 flakes on the water subphase was used to form a continuous layer, which was subsequently transferred onto a submerged substrate by removing the subphase. After vacuum annealing, the electrical sheet resistance dropped to a level of 10 kΩ/sq, being highly competitive with that of CVD-deposited MoS2 nanosheet films. In addition, a consistent fabrication protocol of the large-area conductive MoS2 films was established. The morphology and electrical properties predetermine these films to advanced detecting, sensing, and catalytic applications. A large number of experimental techniques were used to characterize the exfoliated few-layer MoS2 flakes and to elucidate the formation of the few-layer MoS2 Langmuir film.

Tailoring the interparticle distance in Langmuir nanoparticle films.

The ability to control the interparticle distance in self-assembled arrays of nanoparticles plays an important role in a large number of applications, which require tunable electronic and photonic properties. Importantly, practical applications in real devices rely on arrays satisfying more stringent requirements of lateral homogeneity controlled over a large scale. Herein, the interparticle distance in ordered nanoparticle assemblies was controlled by varying the nanoparticle effective size via the molecular chemical nature and chain length of the ligand. Iron oxide nanoparticles (IONPs) were functionalized by three types of ligands, namely (i) a mixture of oleic acid/oleylamine (OA/OAm), (ii) poly(n-butyl acrylate) (PBA) and (iii) polystyrene (PS), while two different molar masses of PBA and PS were used. The polymeric ligands with narrow dispersity and bearing phosphonic chain-end groups were prepared by atom transfer radical polymerization. Functionalization of the IONPs with polymeric ligands was achieved using a ligand exchange method. Both the hydrodynamic diameter and size distribution of the nanoparticles in colloidal solution were determined by dynamic light scattering (DLS). The mean interparticle distances in Langmuir-Schaefer monolayers prepared on solid substrates were assessed by means of the pair correlation function calculated from the atomic force microscopy (AFM) images. Furthermore, the lateral ordering, homogeneity, and interparticle distances averaged over a mesoscopic scale of the ordered monolayers were studied by the grazing-incidence small-angle X-ray scattering (GISAXS) technique. We demonstrate that the (nanoparticle) centre-to-centre distance in the ordered assemblies constituted by the IONPs with the core diameter of about 6 nm can be varied from 7.6 to about 12 nm with the resulting interparticle gap change by a factor of about 4.

Evolution of Defects, Morphology, and Strain during FAMAPbI3 Perovskite Vacuum Deposition: Insights from In Situ Photoluminescence and X-ray Scattering.

At present, the power conversion efficiency of single-junction perovskite-based solar cells reaches over 26%. The further efficiency increase of perovskite-based optoelectronic devices is limited mainly by defects, causing the nonradiative recombination of charge carriers. To improve efficiency and ensure reproducible fabrication of high-quality layers, it is crucial to understand the perovskite nucleation and growth mechanism along with associated process control to reduce the defect density. In this study, we investigate the growth kinetics of a promising narrow bandgap perovskite, formamidinium methylammonium lead iodide (FAMAPbI3), for high-performance single-junction solar cells. The temporal evolution of structural and optoelectronic properties during FAMAPbI3 vacuum codeposition was inspected in real time by grazing-incidence wide-angle X-ray scattering and photoluminescence. Such a combination of analytical techniques unravels the evolution of intrinsic defect density and layer morphology correlated with lattice strain from the early stages of the perovskite deposition.

SERS Performance of Ti3C2Tx MXene-Based Substrates Correlates with Surface Morphology.

The surface-enhanced Raman scattering (SERS) properties of low-dimensional semiconducting MXene nanoflakes have been investigated over the last decade. Despite this fact, the relationship between the surface characteristics and SERSing performance of a MXene layer has yet to be comprehensively investigated and elucidated. This work shows the importance of surface morphology on the overall SERS effect by studying few-layer Ti3C2Tx MXene-based SERS substrates fabricated by vacuum-assisted filtration (VAF) and spray coating on filter paper. The VAF deposition results in a dense MXene layer suitable for SERS with high spot-to-spot and substrate-to-substrate reproducibility, with a significant limit of detection (LoD) of 20 nM for Rhodamine B analyte. The spray-coated MXenes film revealed lower uniformity, with a LoD of 50 nM for drop-casted analytes. Moreover, we concluded that the distribution of the analyte deposited onto the MXene layer is affected by the presence of MXene aggregates created during the deposition of the MXene layer. Accumulation of the analyte molecules in the vicinity of MXene aggregates was observed for drop-casted deposition of the analyte, which affects the resulting SERS enhancement. Ti3C2Tx MXene layers deposited on filter paper by VAF offer great potential as a cost-effective, easy-to-manufacture, yet robust, platform for sensing applications.

Wettability of MXene films.

HYPOTHESIS: One of the highlighted properties of Ti3C2Tx MXene compared to other 2D nanomaterials is its hydrophilicity. However, the broad range of static contact angles of Ti3C2Tx reported in the literature is misleading. To elucidate the experimental values of the static contact angles and get reproducible contact angle data, it is wiser to perform the advancing and receding contact angle measurements on smooth and compact Ti3C2Tx layers and focus on deep understanding of the physical basis behind the wettability, which is provided by contact angle hysteresis. EXPERIMENTS: Measurements of the advancing and receding contact angle on mono-, bi, and trilayer Ti3C2Tx on two different substrates were performed. As substrates, UV-ozone treated silicon wafer and silicon wafer functionalized by (3-aminopropyl)triethoxysilane, were used. FINDINGS: The values of the advancing contact angle on Ti3C2Tx on both substrates were proved to be independent of the number of Ti3C2Tx layers, demonstrating a negligible effect of the background substrate wettability. In addition, a giant contact angle hysteresis (44-52 °) was observed on very smooth surface, most likely as a result of chemical heterogeneity arising from the diversity of surface terminal groups (F, O, and OH). The findings reported in this study provide a comprehensive understanding of the wettability of MXene.

Nanofriction Properties of Mono- and Double-Layer Ti3C2Tx MXenes.

Unique structure and ability to control the surface termination groups of MXenes make these materials extremely promising for solid lubrication applications. Due to the challenging delamination process, the tribological properties of two-dimensional MXenes particles have been mostly investigated as additive components in the solvents working in the macrosystem, while the understanding of the nanotribological properties of mono- and few-layer MXenes is still limited. Here, we investigate the nanotribological properties of mono- and double-layer Ti3C2Tx MXenes deposited by the Langmuir-Schaefer technique on SiO2/Si substrates. The friction of all of the samples demonstrated superior lubrication properties with respect to SiO2 substrate, while the friction force of the monolayers was found to be slightly higher compared to double- and three-layer flakes, which demonstrated similar friction. The coefficient of friction was estimated to be 0.087 ± 0.002 and 0.082 ± 0.003 for mono- and double-layer flakes, respectively. The viscous regime was suggested as the dominant friction mechanism at high scanning velocities, while the meniscus forces affected by contamination of the MXenes surface were proposed to control the friction at low sliding velocities.

A wide-angle X-ray scattering laboratory setup for tracking phase changes of thin films in a chemical vapor deposition chamber.

The few-layer transition metal dichalcogenides (TMD) are an attractive class of materials due to their unique and tunable electronic, optical, and chemical properties, controlled by the layer number, crystal orientation, grain size, and morphology. One of the most commonly used methods for synthesizing the few-layer TMD materials is the chemical vapor deposition (CVD) technique. Therefore, it is crucial to develop in situ inspection techniques to observe the growth of the few-layer TMD materials directly in the CVD chamber environment. We demonstrate such an in situ observation on the growth of the vertically aligned few-layer MoS2 in a one-zone CVD chamber using a laboratory table-top grazing-incidence wide-angle X-ray scattering (GIWAXS) setup. The advantages of using a microfocus X-ray source with focusing Montel optics and a single-photon counting 2D X-ray detector are discussed. Due to the position-sensitive 2D X-ray detector, the orientation of MoS2 layers can be easily distinguished. The performance of the GIWAXS setup is further improved by suppressing the background scattering using a guarding slit, an appropriately placed beamstop, and He gas in the CVD reactor. The layer growth can be monitored by tracking the width of the MoS2 diffraction peak in real time. The temporal evolution of the crystallization kinetics can be satisfactorily described by the Avrami model, employing the normalized diffraction peak area. In this way, the activation energy of the particular chemical reaction occurring in the CVD chamber can be determined.