Nanoporous copper (NPC) is the potential affordable surface-enhanced Raman scattering (SERS) substrate in practical use, although restricted by a relatively small enhancement factor. In this report, Cu ion irradiation is applied to effectively increase the enhancement factor of NPC. Two levels of surface roughness in NPC after ion irradiation are proposed to account for the improved SERS effect by careful characterization of microstructures. This study provides a new strategy to acquire a higher Raman enhancement factor in NPC, which perhaps can be extended to other SERS substrate systems.
RESUMEN
In this work, effects of Au ion irradiation on microstructure and surface-enhanced Raman scattering (SERS) performance of nanoporous copper (NPC) were investigated. It is found that the microstructure of NPC could be tailored by the ion irradiation dose, i.e., the pore size decreases while the ligament size significantly coarsens with the increase of the irradiation dose. In addition, the SERS enhancement for rhodamine 6G molecules was improved by Au ions irradiation at an appropriate dose. The underlying mechanism of the increase of SERS enhancement resulted from ion irradiation was discussed. Our findings could provide a new way to tune nanoporosity of nanoporous metals and improve their SERS performance.
RESUMEN
Despite intense research on high entropy films, the mechanism of film growth and the influence of key factors remain incompletely understood. In this study, high entropy films consisting of five elements (FeCoNiCrAl) with columnar and nanometer-scale grains were prepared by magnetron sputtering. The high entropy film growth mechanism, including the formation of the amorphous domain, equiaxial nanocrystalline structure and columnar crystal was clarified by analyzing the microstructure in detail. Besides, the impacts of the important deposition parameters including the substrate temperature, the powder loaded in the target, and the crystal orientation of the substrate on the grain size and morphology, phase structure, crystallinity and elemental uniformity were revealed. The mechanical properties of high entropy films with various microstructure features were investigated by nanoindentation. With the optimized grain size and microstructure, the film deposited at 350 °C using a power of 100 W exhibits the highest hardness of 11.09 GPa. Our findings not only help understanding the mechanisms during the high entropy film deposition, but also provide guidance in manufacturing other novel high entropy films.