RESUMEN
The effects of TiO2 nanotube (TNT) and reduced graphene oxide (rGO) deposition onto titanium, which is widely used in dental implants, on Streptococcus mutans (S. mutans) and preosteoblastic cells were evaluated. TNTs were formed through anodic oxidation on pure titanium, and rGO was deposited using an atmospheric plasma generator. The specimens used were divided into a control group of titanium specimens and three experimental groups: Group N (specimens with TNT formation), Group G (rGO-deposited specimens), and Group NG (specimens under rGO deposition after TNT formation). Adhesion of S. mutans to the surface was assessed after 24 h of culture using a crystal violet assay, while adhesion and proliferation of MC3T3-E1 cells, a mouse preosteoblastic cell line, were evaluated after 24 and 72 h through a water-soluble tetrazolium salt assay. TNT formation and rGO deposition on titanium decreased S. mutans adhesion (p < 0.05) and increased MC3T3-E1 cell adhesion and proliferation (p < 0.0083). In Group NG, S. mutans adhesion was the lowest (p < 0.05), while MC3T3-E1 cell proliferation was the highest (p < 0.0083). In this study, TNT formation and rGO deposition on a pure titanium surface inhibited the adhesion of S. mutans at an early stage and increased the initial adhesion and proliferation of preosteoblastic cells.
Asunto(s)
Grafito , Nanotubos , Streptococcus mutans , Ratones , Animales , Titanio/farmacología , Titanio/química , Propiedades de Superficie , Nanotubos/químicaRESUMEN
Peri-implantitis is an inflammatory disease similar to periodontitis, caused by biofilms formed on the surface of dental implants. This inflammation can spread to bone tissues and result in bone loss. Therefore, it is essential to inhibit the formation of biofilms on the surface of dental implants. Thus, this study examined the inhibition of biofilm formation by treating TiO2 nanotubes with heat and plasma. Commercially pure titanium specimens were anodized to form TiO2 nanotubes. Heat treatment was performed at 400 and 600 °C, and atmospheric pressure plasma was applied using a plasma generator (PGS-200, Expantech, Suwon, Republic of Korea). Contact angles, surface roughness, surface structure, crystal structure, and chemical compositions were measured to analyze the surface properties of the specimens. The inhibition of biofilm formation was assessed using two methods. The results of this study showed that the heat treatment of TiO2 nanotubes at 400 °C inhibited the adhesion of Streptococcus mutans (S. mutans), associated with initial biofilm formation, and that heat treatment of TiO2 nanotubes at 600 °C inhibited the adhesion of Porphyromonas gingivalis (P. gingivalis), which causes peri-implantitis. Applying plasma to the TiO2 nanotubes heat-treated at 600 °C inhibited the adhesion of S. mutans and P. gingivalis.
Asunto(s)
Implantes Dentales , Nanotubos , Periimplantitis , Humanos , Nanotubos/química , Biopelículas , Titanio/química , Propiedades de Superficie , Streptococcus mutansRESUMEN
The alternative antibacterial treatment photothermal therapy (PTT) significantly affects oral microbiota inactivation. In this work, graphene with photothermal properties was coated on a zirconia surface using atmospheric pressure plasma, and then the antibacterial properties against oral bacteria were evaluated. For the graphene oxide coating on the zirconia specimens, an atmospheric pressure plasma generator (PGS-300, Expantech, Suwon, Republic of Korea) was used, and an Ar/CH4 gas mixture was coated on a zirconia specimen at a power of 240 W and a rate of 10 L/min. In the physiological property test, the surface properties were evaluated by measuring the surface shape of the zirconia specimen coated with graphene oxide, as well as the chemical composition and contact angle of the surface. In the biological experiment, the degree of adhesion of Streptococcus mutans (S. mutans) and Porphyromonas gingivalis (P. gingivalis) was determined by crystal violet assay and live/dead staining. All statistical analyzes were performed using SPSS 21.0 (SPSS Inc., Chicago, IL, USA). The group in which the zirconia specimen coated with graphene oxide was irradiated with near-infrared rays demonstrated a significant reduction in the adhesion of S. mutans and P. gingivalis compared with the group not irradiated. The oral microbiota inactivation was reduced by the photothermal effect on the zirconia coated with graphene oxide, exhibiting photothermal properties.
Asunto(s)
Grafito , Grafito/farmacología , Grafito/química , Propiedades de Superficie , Antibacterianos/farmacologíaRESUMEN
The aim of this study was to evaluate the antibacterial activity against Streptococcus mutans and fibroblast viability of zirconia coated with glass ceramic powder containing Ag and F nanoparticles. Specimens were divided into eight groups depending on the glass ceramic powders: 5, 10, 15, 20 wt% of NaF and Ag, respectively. Adhesion of Streptococcus mutans on glass-coated zirconia surface was evaluated by antimicrobial test. Fibroblast viability was examined by WST-8 assay. In result, the bacterial activity was reduced by 11.8%, 15.4% in Ag 10 wt% and 20 wt% groups. When 5~15 wt% of NaF was added, bacterial counts decreased to 4.2~65.4%, and when 20 wt% of NaF was added, the number of bacteria increased by 29.4%. Regardless of Ag and NaF content, all zirconia specimens showed cell viability above 70%. Within the limitations of this study, zirconia coated with glass ceramics powder containing Ag and NaF was found to reduce the adhesion of Streptococcus mutans but had no influence on osteoblast activation.
Asunto(s)
Nanopartículas , Plata , Antibacterianos/farmacología , Supervivencia Celular , Cerámica/farmacología , Fibroblastos , Ensayo de Materiales , Plata/farmacología , Propiedades de Superficie , Circonio/farmacologíaRESUMEN
In this study, we examined the effect of ß-tricalcium phosphate (ß-TCP) coating on alkali-treated CP Grade II titanium surface via RF magnetron sputtering on osteoblast like cell (MC3T3-E1) viability and bone formation in rat tibia. The specimens were divided into three groups; commercially pure titanium (control group), alkali-treated titanium with nanofiber structure (NF group) and ß-TCP coating on alkali-treated titanium with nanofiber structure (TNF group). The surface characteristics of specimens were observed under a field emission scanning electron microscope (FE-SEM), and contact angle was measured. The cell viability was assessed in vitro after 1 day, 3 days and 7 days. Implants of 2.0 mm diameter and 5.0 mm length were inserted into the tibia of rats. After 4 wks, the histomorphometric analysis was performed. Group NF and group TNF showed improved hydrophilicity of Ti. Group TNF showed significantly higher cell viability (P < 0.05) after 7 days. The bone to implant contact (BIC) ratio of the control group, NF group, and TNF group were 32.3%, 35.5%, and 63.9%, respectively. The study results suggested that ß-TCP coated alkali-treated titanium surface via RF magnetron sputtering might be effective in implant dentistry due to enhanced hydrophilicity, improved cell response, and better osseointegration.
Asunto(s)
Desarrollo Óseo , Fosfatos de Calcio , Nanofibras , Oseointegración , Titanio , Animales , Materiales Biocompatibles Revestidos , Implantes Dentales , Microscopía Electrónica de Rastreo , Propiedades de SuperficieRESUMEN
The aim of this study was to determine the effect of hydroxyapatite (HA) coating on titanium dioxide (TiO2) nanotube by sol-gel process on viability of osteoblast like cell (MC3T3-E1) and bone formation in rat tibia. Specimens were divided into three groups including commercially pure titanium (control group), TiO2 nanotubes (group N), and HA coated TiO2 nanotubes (group HN). Surface characteristics were determined using field emission scanning electron microscope (FE-SEM; S-4700, Hitachi, Japan) and contact angles were measured. Cell viability was investigated in vitro after 1 day, 3 days, and 7 days of incubation. Implants (2.0 mm in diameter and 5.0 mm in length) were inserted into the tibia of rats. After 4 weeks, histomorphometric analysis was performed. Both N and HN groups showed enhanced hydrophilicity compared to control group. After 7 days of implantation, group HN showed higher cell viability with marginal significance (0.05 < P < 0.1). Bone to implant contact (BIC) ratio in the control group, group N, and group HN were 32.5%, 33.1%, and 43.8%, respectively. Results of this study showed that HA coated TiO2 nanotube using sol-gel process could be used to enhance hydrophilicity and improve osseointegration of dental implant surface.
RESUMEN
The aim of this study was to evaluate the antibacterial activity against Porphyromonas gingivalis and osteoblast viability of heat and plasma treatment of TiO2 nanotubes. Specimens were divided into four groups: the Ti (polished titanium), Nano (TiO2 nanotube), NH 300 (heat treated at 300 °C on TiO2 nanotube) and NH 400 (heat treated at 400 °C on TiO2 nanotube) groups. Antibacterial activity and osteoblast viability were evaluated in the four groups according to plasma treatment. Surface adhesion of Porphyromonas gingivalis was evaluated by crystal violet assay. Osteoblast viability was examined by XTT assay. Adhesion of Porphyromonas gingivalis was significantly decreased in the Ti group, Nano group and NH 300 group after plasma treatment (P < 0.05). Osteoblast viability was increased in the NH 400 group in comparison to the Ti group before plasma treatment (P < 0.05). Within the limitations of this study, plasma treatment was found to reduce the adhesion of P. gingivalis but had no influence on osteoblast activation.
Asunto(s)
Antibacterianos , Viabilidad Microbiana/efectos de los fármacos , Nanotubos , Osteoblastos/efectos de los fármacos , Titanio , Animales , Antibacterianos/química , Antibacterianos/farmacología , Antibacterianos/toxicidad , Línea Celular , Supervivencia Celular/efectos de los fármacos , Calor , Ratones , Nanotubos/química , Nanotubos/toxicidad , Gases em Plasma , Porphyromonas gingivalis/efectos de los fármacos , Propiedades de Superficie , Titanio/química , Titanio/farmacología , Titanio/toxicidadRESUMEN
Porphyromonas gingivalis (P. gingivalis) is one of main bacteria that adheres to the surface of dental implants and causes peri-implantitis. The purpose of this study was to observe the surface characteristics of titanium processed with either titanium nitride (TiN) sputter coating or plasma nitriding and to evaluate the subsequent adhesion of P. gingivalis. Specimens were divided into three groups: commercially pure (CP) titanium (control group), TiN sputtercoated titanium (group S), and plasma-nitrided titanium (group P). Surface characteristics such as roughness, morphology, and the formation of a thin TiN film or a nitriding layer were assessed. Adhesion of P. gingivalis in the three groups was determined by means of the crystal violet staining assay, and results were compared with one-way ANOVA, with post hoc comparison using Tukey's test (α = 0.05). Surface roughness values for the control group, group S, and group P were 0.08±0.02 µm, 0.19±0.04 µm, and 0.13±0.02 µm, respectively. In group S, the TiN layer was 1.36±0.1 µm thick, and nitrogen was detected on the surface of the specimens in group P, confirming formation of a nitrided layer. The level of adhesion in group P was significantly higher than that in the control group and in group S (p < 0.05), but there was no significant difference between the control group and group S. Within the limitations of this study, TiN sputter coating did not affect adhesion of P. gingivalis on the titanium surface, whereas adhesion was increased on the plasma-nitrided titanium surface.
RESUMEN
This study was to investigate the various glass thicknesses on the shear bond strength between zirconia and veneering porcelain. The zirconia specimens were classified into 5 groups (n = 12). For the control group, the Y-TZP disk was sintered (G0). For the test group, the presintered zirconia disks were spin coated with different W/P ratio glass compositions. The glass thickness on the zirconia was 1 µm (G1), 4 µm (G4), 10 µm (G10), and 40 µm (G40), respectively. All specimens were build-up veneering porcelain and fired. The shear bond strength (SBS) was tested in a universal testing machine (crosshead speed = 0.5 mm/min). As the thickness of the glass decreased, the shear bond strength increased. The G1 group showed significantly higher than the control group (G0) (P < 0.05). The results suggest that the thickness of glass coating on the zirconia structure needs to be made thin for better bonding strength with veneering porcelain.
RESUMEN
The purpose of this study was to examine the surface characteristics of bioactive glass-infiltrated zirconia specimens that underwent different hydrofluoric acid (HF) etching conditions. Specimens were classified into the following six groups: Zirconia, Zirliner, Porcelain, Bioactive glass A1, Bioactive glass A2, and Bioactive glass A3. Zirliner and porcelain were applied to fully sintered zirconia followed by heat treatment. Bioactive glass was infiltrated into presintered zirconia using a spin coating method followed by complete sintering. All the specimens were acid-etched with 10% or 20% HF, and surface roughness was measured using a profiler. The surface roughness of the zirconia group was not affected by the etching time or the concentration of the acid. The roughness of the three bioactive glass groups (A1, A2, and A3) was slightly increased up until 10 minutes of etching. After 1 hour of etching, the roughness was considerably increased. The infiltrated bioactive glass and acid etching did not affect the adhesion and proliferation of osteoblasts. This study confirmed that surface roughness was affected by the infiltration material, etching time, and acid concentration. For implant surfaces, it is expected that the use of etched bioactive glass-infiltrated zirconia with micro-topographies will be similar to that of machined or sand-blasted/acid-etched (SLA) titanium.
Asunto(s)
Grabado Dental , Vidrio/química , Ácido Fluorhídrico/química , Circonio/química , Ensayo de Materiales , Propiedades de SuperficieRESUMEN
This study examined the effect of the immobilization of the Gly-Arg-Gly-Asp-Ser (GRGDS) peptide on titanium dioxide (TiO2) nanotube via chemical grafting on osteoblast-like cell (MG-63) viability and differentiation. The specimens were divided into two groups; TiO2 nanotubes and GRGDS-immobilized TiO2 nanotubes. The surface characteristics of GRGDS-immobilized TiO2 nanotubes were observed by using X-ray photoelectron spectroscopy (XPS) and a field emission scanning electron microscope (FE-SEM). The morphology of cells on specimens was observed by FE-SEM after 2 hr and 24 hr. The level of cell viability was investigated via a tetrazolium (XTT) assay after 2 and 4 days. Alkaline phosphatase (ALP) activity was evaluated to measure the cell differentiation after 4 and 7 days. The presence of nitrogen up-regulation or C==O carbons con- firmed that TiO2 nanotubes were immobilized with GRGDS peptides. Cell adhesion was enhanced on the GRGDS-immobilized TiO2 nanotubes compared to TiO2 nanotubes. Furthermore, significantly increased cell spreading and proliferation were observed with the cells grown on GRGDS-immobilized TiO2 nanotubes (P < .05). However, there was no significant difference in ALP activity between GRGDS-immobilized TiO2 nanotubes and TiO2 nanotubes. These results suggest that the GRGDS-immobilized TiO2 nanotubes might be effective in improving the osseointegration of dental implants.
Asunto(s)
Diferenciación Celular/efectos de los fármacos , Nanotubos/química , Oligopéptidos , Osteoblastos/metabolismo , Titanio , Línea Celular Tumoral , Supervivencia Celular/efectos de los fármacos , Humanos , Oligopéptidos/química , Oligopéptidos/farmacología , Osteoblastos/citología , Titanio/química , Titanio/farmacologíaRESUMEN
The aim of this study was to evaluate the response of Streptococcus mutans (S. mutans) via crystal violet staining assay on titanium surface modified by physical vapor deposition/plasma assisted chemical vapor deposition process. Specimens were divided into the following three groups: polished titanium (control group), titanium modified by DC magnetron sputtering (group TiN-Ti), and titanium modified by plasma nitriding (group N-Ti). Surface characteristics of specimens were observed by using nanosurface 3D optical profiler and field emission scanning electron microscope. Group TiN-Ti showed TiN layer of 1.2 microm in thickness. Group N-Ti was identified as plasma nitriding with X-ray photoelectron spectroscopy. Roughness average (Ra) of all specimens had values < or = 0.2 microm (the threshold Ra), which had no effect on bacterial adhesion. No significant difference of S. mutans adhesion was found between the surfaces of control, TiN-Ti, and N-Ti (P > 0.05). Within the process condition of this study, modified titanium surfaces by DC magnetron sputtering and plasma nitriding did not influence the adhesion of S. mutans.
Asunto(s)
Antibacterianos/química , Gases em Plasma/química , Streptococcus mutans/crecimiento & desarrollo , Titanio/química , Propiedades de SuperficieRESUMEN
This study compared the removal torque between injection molded zirconia implants and titanium implants with resorbable blast media (RBM) surfaces in beagle humeri. Fifteen screw-shaped implants were classified into 3 groups; titanium implant with RBM surface (Group RT), injection molded zirconia implant (Group Zr) and injection molded zirconia implant with sand-blasted surface (Group ZrS). Implants were inserted into beagle humeri. After 12 weeks, removal torque values were measured. The Zr group has a slightly higher removal torque value than the RT and ZrS groups but there were no significant differences among groups. Zirconia implants shows a similar removal torque to RBM titanium implants. This in vivo study showed injection molded zirconia implants could be an alternative to RBM titanium implants in terms of removal torque.
Asunto(s)
Materiales Biocompatibles/química , Implantes Dentales , Remoción de Dispositivos , Circonio/química , Animales , Perros , Húmero/cirugía , Modelos Biológicos , Diseño de Prótesis , Propiedades de Superficie , Titanio/químicaRESUMEN
Purpose: Atomic layer deposition (ALD) is a method that can deposit zirconia uniformly on an atomic basis. The effect of deposited zirconia on titanium implants using ALD was evaluated in vivo. Methods: Machined titanium implants (MTIs) were used as the Control. MTIs treated by sandblasting with large grit and acid etching (SA) and MTIs deposited with zirconia using ALD are referred to as Groups S and Z, respectively. Twelve implants were prepared for each group. Six rabbits were used as experimental animals. To evaluate the osteogenesis and osteocyte aspects around the implants, radiological and histological analyses were performed. The bone-to-implant contact (BIC) ratio was measured and statistically analyzed to evaluate the osseointegration capabilities. Results: In the micro-CT analysis, more radiopaque bone tissues were observed around the implants in Groups S and Z. Histological observation found that Groups S and Z had more and denser mature bone tissues around the implants in the cortical bone area. Many new and mature bone tissues were also observed in the medullary cavity area. For the BIC ratio, Groups S and Z were significantly higher than the Control in the cortical bone area (P < 0.017), but there was no significant difference between Groups S and Z. Conclusion: MTIs deposited with zirconia using ALD (Group Z) radiologically and histologically showed more mature bone formation and activated osteocytes compared with MTIs (Control). Group Z also had a significantly higher BIC ratio than the Control. Within the limitations of this study, depositing zirconia on the surface of MTIs using ALD can improve osseointegration in vivo.
Asunto(s)
Oseointegración , Titanio , Circonio , Animales , Circonio/química , Circonio/farmacología , Conejos , Titanio/química , Titanio/farmacología , Oseointegración/efectos de los fármacos , Propiedades de Superficie , Microtomografía por Rayos X , Materiales Biocompatibles Revestidos/química , Materiales Biocompatibles Revestidos/farmacología , Interfase Hueso-Implante , Osteogénesis/efectos de los fármacos , Implantes Dentales , Prótesis e ImplantesRESUMEN
Purpose: This study aimed to confirm the synergy effect of these two materials by evaluating osteoblast and antibacterial activity by applying a double-layered hydroxyapatite(HA) zirconium oxide(ZrO2) coating to titanium. Methods: The specimens used in this study were divided into four groups: a control group (polished titanium; group T) and three experimental groups: Group TH (RF magnetron sputtered HA deposited titanium), Group Z (ZrO2 ALD deposited titanium), and Group ZH (RF magnetron sputtered HA and ZrO2 ALD deposited titanium). The adhesion of Streptococcus mutans (S.mutans) to the surface was assessed using a crystal violet assay. The adhesion, proliferation, and differentiation of MC3T3-E1 cells, a mouse osteoblastic cell line, were assessed through a WST-8 assay and ALP assay. Results: Group Z showed a decrease in the adhesion of S. mutans (p < 0.05) and an improvement in osteoblastic viability (p < 0.0083). Group TH and ZH showed a decrease in adhesion of S. mutans (p < 0.05) and an increase in osteoblastic cell proliferation and cell differentiation (p < 0.0083). Group ZH exhibited the highest antibacterial and osteoblastic differentiation. Conclusion: In conclusion double-layered HA and ZrO2 deposited on titanium were shown to be more effective in inhibiting the adhesion of S. mutans, which induced biofilm formation, and increasing osteoblastic differentiation involved in osseointegration by the synergistic effect of the two materials.
Asunto(s)
Adhesión Bacteriana , Diferenciación Celular , Proliferación Celular , Materiales Biocompatibles Revestidos , Durapatita , Osteoblastos , Streptococcus mutans , Propiedades de Superficie , Titanio , Circonio , Circonio/química , Circonio/farmacología , Titanio/química , Titanio/farmacología , Streptococcus mutans/efectos de los fármacos , Animales , Ratones , Durapatita/química , Durapatita/farmacología , Osteoblastos/efectos de los fármacos , Osteoblastos/citología , Proliferación Celular/efectos de los fármacos , Diferenciación Celular/efectos de los fármacos , Adhesión Bacteriana/efectos de los fármacos , Materiales Biocompatibles Revestidos/química , Materiales Biocompatibles Revestidos/farmacología , Línea Celular , Antibacterianos/farmacología , Antibacterianos/química , Adhesión Celular/efectos de los fármacos , Supervivencia Celular/efectos de los fármacosRESUMEN
This study examined the bone response to titanium dioxide nanotube modified implants. A total of 24 implants were placed in the femur of 4 beagles. Before placement, screw-shaped implants were classified into 3 groups; machined surface (group M), titanium dioxide nanotube modification of the machined surface (group MN) and titanium dioxide nanotube modification of the RBM surface (group RN). The texture morphology was observed via scanning electron microscopy. Animals were euthanized after 4 and 12 weeks of submerged healing and the histologic and histomorphometric analyses were performed. Groups MN and RN showed a significantly higher percentage of mineralized bone than that in group M (p < 0.05). The results of this in vivo study constitute significant evidence that the presence of the titanium dioxide nanotubes enhance osseointegration of implants.
Asunto(s)
Desarrollo Óseo , Nanotubos , Prótesis e Implantes , Titanio/farmacología , Animales , Perros , Microscopía Electrónica de RastreoRESUMEN
Plasma treatment on a zirconia surface prevents bacterial contamination and maintains osteoblast activity. To assess the degree of adhesion of Porphyromonas gingivalis on a zirconia surface after non-thermal plasma (NTP) treatment, specimens were treated with plasma for 60, 300, and 600 s, after which P. gingivalis was inoculated onto the surface and incubated for 48 h. To assess osteoblast activity after NTP treatment, osteoblasts (MC3T3-E1) were dispensed onto the specimens contaminated with P. gingivalis immediately after NTP for 60 and 120 s, followed by incubation for 48, 72, and 96 h. P. gingivalis was cultured after 60 s of NTP treatment of zirconia. The NTP and control groups showed no significant difference (p = 0.91), but adhesion was significantly increased following NTP treatment for 300 s or longer (300, 600 s groups) (p < 0.05). After NTP treatment of P. gingivalis-contaminated zirconia, osteoblast activity significantly increased at 72 and 96 h (I60 and I120 s group) in the groups treated with plasma (p < 0.017). Application of NTP to dental zirconia implants for 60 s not only inhibits the proliferation of P. gingivalis, which causes peri-implantitis but also increases osseointegration on zirconia surfaces contaminated with P. gingivalis.
RESUMEN
PURPOSE: The study was intended to create a uniform zirconia layer even on the surface of complex structures via atomic layer deposition (ALD). The impact of crystalline zirconia deposited by ALD on bacterial adhesion and osteoblast viability was assessed via surface treatment of dental implants. METHODS: Amorphous zirconia was deposited using an atomic layer deposition reactor (Atomic Classic, CN1, Hwaseong, Korea) on titanium discs. Heating the samples at 400°C resulted in crystallization. Samples were divided into three groups: the control group, the group carrying amorphous ALD-zirconia (Z group), and the heat-treated group following zirconia ALD deposition (ZH group).The surface of each sample was analyzed, followed by the assessment of adhesion of Streptococcus mutans and Porphyromonas gingivalis, and viability and differentiation of MC3T3-E1 cells. RESULTS: The adhesion of S. mutans and P. gingivalis was significantly reduced in the Z and ZH groups compared with the control group (P < 0.05). The viability of MC3T3-E1 cells was significantly increased in the ZH group compared with the control group (P < 0.001), while no significant differences were observed in the Z group (P > 0.05). Differentiation of MC3T3-E1 cells showed a marginally significant increase in the ZH group compared with the control group (P < 0.1), while no significant differences were found in the Z group (P > 0.1). CONCLUSION: Compared with the pure titanium group, the groups that were coated with zirconia via ALD showed a decreased adhesion of S. mutans during the early stages of biofilm formation and P. gingivalis adhesion inducing peri-implantitis, and an increase in MC3T3-E1 cell viability and differentiation. The findings indicate the possibility of treating the implant surface to reduce peri-implantitis and improve osseointegration.
Asunto(s)
Adhesión Bacteriana , Osteoblastos/citología , Titanio/farmacología , Circonio/química , Animales , Adhesión Bacteriana/efectos de los fármacos , Diferenciación Celular/efectos de los fármacos , Línea Celular , Supervivencia Celular/efectos de los fármacos , Humanos , Ratones , Microscopía de Fuerza Atómica , Osteoblastos/efectos de los fármacos , Osteoblastos/metabolismo , Osteoblastos/ultraestructura , Espectroscopía de Fotoelectrones , Espectrometría por Rayos X , Propiedades de Superficie , Difracción de Rayos XRESUMEN
OBJECTIVE: To determine the effects of graphene oxide (GO) deposition (on a zirconia surface) on bacterial adhesion and osteoblast activation. METHODS: An atmospheric pressure plasma generator (PGS-300) was used to coat Ar/CH4 mixed gas onto zirconia specimens (15-mm diameter × 2.5-mm thick disks) at a rate of 10 L/min and 240 V. Zirconia specimens were divided into two groups: uncoated (control; Zr) group and GO-coated (Zr-GO) group. Surface characteristics and element structures of each specimen were evaluated by field emission scanning electron microscope (FE-SEM), X-ray photoelectron spectroscopy (XPS), Raman spectroscopy, and contact angle. Additionally, crystal violet staining was performed to assess the adhesion of Streptococcus mutans. WST-8 and ALP (Alkaline phosphatase) assays were conducted to evaluate MC3T3-E1 osteoblast adhesion, proliferation, and differentiation. Statistical analysis was calculated by the Mann-Whitney U-test. RESULTS: FE-SEM and Raman spectroscopy demonstrated effective GO deposition on the zirconia surface in Zr-GO. The attachment and biofilm formation of S. mutans was significantly reduced in Zr-GO compared with that of Zr (P < 0.05). While no significant differences in cell attachment of MC3T3-1 were observed, both proliferation and differentiation were increased in Zr-GO as compared with that of Zr (P < 0.05). SIGNIFICANCE: GO-coated zirconia inhibited the attachment of S. mutans and stimulated proliferation and differentiation of osteoblasts. Therefore, GO-coated zirconia can prevent peri-implantitis by inhibiting bacterial adhesion. Moreover, its osteogenic ability can increase bone adhesion and success rate of implants.
Asunto(s)
Antiinfecciosos , Implantes Dentales , Proliferación Celular , Grafito , Osteoblastos , Osteogénesis , Propiedades de Superficie , Titanio , CirconioRESUMEN
Since carbon dots (CDs) exhibit excellent biocompatibility, low cytotoxicity, near-infrared (NIR) absorbance, and superior photostability, many types of CDs are considered as powerful candidates for photothermal therapy (PTT) applications. However, the development of a desirable CD is still difficult due to insufficient photothermal conversion, thus resulting in the use of high laser power densities at a high dose of CDs for the PTT effect. Herein, bioinspired sulfur-doped CDs (S-CDs) with strong NIR absorbance were prepared from Camellia japonica flowers via a facile hydrothermal method for enhancing the photothermal conversion efficiency. The as-prepared S-CDs exhibited various advantages including cost-effective preparation, good water-solubility, high biocompatibility, intense NIR absorption, and excellent photothermal effect with robust photostability. Most importantly, the optimal low dose of S-CDs (45 µg mL-1) successfully led to efficient PTT performance with a high photothermal conversion efficiency (55.4%) under moderate laser power (808 nm, 1.1 W cm-2) for safe and effective cancer therapy.