RESUMEN
Two-dimensional boron materials have recently attracted extensive theoretical interest because of their exceptional structural complexity and remarkable physical and chemical properties. However, such 2D boron monolayers have still not been synthesized. In this report, the synthesis of atomically thin 2D γ-boron films on copper foils is achieved by chemical vapor deposition using a mixture of pure boron and boron oxide powders as the boron source and hydrogen gas as the carrier gas. Strikingly, the optical band gap of the boron film was measured to be around 2.25â eV, which is close to the value (2.07â eV) determined by first-principles calculations, suggesting that the γ-B28 monolayer is a fascinating direct band gap semiconductor. Furthermore, a strong photoluminescence emission band was observed at approximately 626â nm, which is again due to the direct band gap. This study could pave the way for applications of two-dimensional boron materials in electronic and photonic devices.
RESUMEN
ZnO nano-clips with better monodispersion were prepared successfully using zinc acetate hydrate (Zn(OAc)2·nH2O) as Zn source and ethylene glycol (EG) as solvent by a simple solution-based route-polyol process. The effect of solution concentration on the formation of ZnO nano-clips has been investigated deeply. We first prove that the 0.01 M Zn(OAc)2·nH2O can react with EG without added water or alkaline, producing ZnO nano-clips with polycrystalline wurtzite structure at 170 °C. As-synthesized ZnO nano-clips contain a lot of aggregated nanocrystals (~ 5 to 15 nm) with high specific surface area of 88 m2/g. The shapes of ZnO nano-clips basically keep constant with improved crystallinity after annealing at 400-600 °C. The lower solution concentration and slight amount of H2O play a decisive role in ZnO nano-clip formation. When the solution concentration is ≤ 0.0125 M, the complexing and polymerization reactions between Zn(OAc)2·nH2O and EG predominate, mainly elaborating ZnO nano-clips. When the solution concentration is ≥ 0.015 M, the alcoholysis and polycondensation reactions of Zn(OAc)2·nH2O and EG become dominant, leading to ZnO particle formation with spherical and elliptical shapes. The possible growth mechanism based on a competition between complexing and alcoholysis of Zn(OAc)2·nH2O and EG has been proposed.
RESUMEN
The HfO2/TiO2/HfO2 trilayer-structure resistive random access memory (RRAM) devices have been fabricated on Pt- and TiN-coated Si substrates with Pt top electrodes by atomic layer deposition (ALD). The effect of the bottom electrodes of Pt and TiN on the resistive switching properties of trilayer-structure units has been investigated. Both Pt/HfO2/TiO2/HfO2/Pt and Pt/HfO2/TiO2/HfO2/TiN exhibit typical bipolar resistive switching behavior. The dominant conduction mechanisms in low and high resistance states (LRS and HRS) of both memory cells are Ohmic behavior and space-charge-limited current, respectively. It is found that the bottom electrodes of Pt and TiN have great influence on the electroforming polarity preference, ratio of high and low resistance, and dispersion of the operating voltages of trilayer-structure memory cells. Compared to using symmetric Pt top/bottom electrodes, the RRAM cells using asymmetric Pt top/TiN bottom electrodes show smaller negative forming voltage of -3.7 V, relatively narrow distribution of the set/reset voltages and lower ratio of high and low resistances of 102. The electrode-dependent electroforming polarity can be interpreted by considering electrodes' chemical activity with oxygen, the related reactions at anode, and the nonuniform distribution of oxygen vacancy concentration in trilayer-structure of HfO2/TiO2/HfO2 on Pt- and TiN-coated Si. Moreover, for Pt/HfO2/TiO2/HfO2/TiN devices, the TiN electrode as oxygen reservoir plays an important role in reducing forming voltage and improving uniformity of resistive switching parameters.
RESUMEN
N-doped ZnO/g-C3N4 composites have been successfully prepared via a facile and cost-effective sol-gel method. The nanocomposites were systematically characterized by XRD, FE-SEM, HRTEM, FT-IR, XPS, and UV-vis DRS. The results indicated that compared with the pure N-doped ZnO, the absorption edge of binary N-doped ZnO/g-C3N4 shifted to a lower energy with increasing the visible-light absorption and improving the charge separation efficiency, which would enhance its photocatalytic activity. Compared with the pure g-C3N4, ZnO, N-doped ZnO and the composite ZnO/g-C3N4, the as-prepared N-doped ZnO/g-C3N4 exhibits a greatly enhanced photocatalytic degradation of methylene blue and phenol under visible-light irradiation. Meanwhile, N-doped ZnO/g-C3N4 possesses a high stability. Finally, a proposed mechanism for N-doped ZnO/g-C3N4 is also discussed. The improved photocatalysis can be attributed to the synergistic effect between N-doped ZnO and g-C3N4, including the energy band structure and enhanced charge separation efficiency.
RESUMEN
Low-temperature Bi-Nb-O system photocatalysts were prepared by a citrate method using homemade water-soluble niobium precursors. The structures, morphologies, and optical properties of Bi-Nb-O system photocatalysts with different compositions were investigated deeply. All the Bi-Nb-O powders exhibit appreciably much higher photocatalytic efficiency of photo-degradation of methyl violet (MV), especially for Bi-Nb-O photocatalysts sintered at 750 °C (BNO750), only 1.5 h to completely decompose MV, and the obtained first-order rate constant (k) is 1.94/h. A larger degradation rate of Bi-Nb-O photocatalysts sintered at 550 °C (BNO550) can be attributed to the synergistic effect between ß-BiNbO4 and Bi5Nb3O15. Bi5Nb3O15 with small particle size on ß-BiNbO4 surface can effectively short the diffuse length of electron. BNO750 exhibits the best photocatalytic properties under visible-light irradiation, which can be attributed to its better crystallinity and the synergistic effect between ß-BiNbO4 and α-BiNbO4. The small amount of α-BiNbO4 loading on surface of ß-BiNbO4 can effectively improve the electron and hole segregation and migration. Holes are the main active species of Bi-Nb-O system photocatalysts in aqueous solution under visible-light irradiation.
RESUMEN
Low-temperature ß-BiNbO4 powders (denoted as Low-ß) were prepared by citrate and Pechini methods using homemade water-soluble niobium precursors. The addition of ethylene glycol and the resultant polymerization effect on the synthesis and visible-light photocatalytic performance of ß-BiNbO4 powders were fully investigated. The polymerization effect is beneficial to lower the phase formation temperature and obtain smaller particle catalysts. Both methods can synthesize catalysts with excellent performance of visible-light degradation of methyl violet (MV). The Low-ß BiNbO4 powder prepared by citrate method shows better degradation rate of about 1 h to decompose 80 % of MV and also displays good photocatalytic stability. The photodegradation of MV under the visible-light irradiation followed the pseudo-first-order kinetics according to the Langmuir-Hinshelwood model, and the obtained first-order rate constant and half-time are 2.85 × 10(-2) min(-1) and 24.3 min, respectively. The better photocatalytic performance of BiNbO4 powders prepared by citrate method can be attributed to its smaller band gap and better crystallinity.
RESUMEN
A novel photocatalyst of Ta-doped ZnO nanoparticles was prepared by a modified Pechini-type method. The antimicrobial study of Ta-doped ZnO nanoparticles on several bacteria of Gram-positive Bacillus subtilis (B. subtilis) and Staphylococcus aureus (S. aureus) and Gram-negative Escherichia coli (E. coli) and Pseudomonas aeruginosa (P. aeruginosa) were performed using a standard microbial method. The Ta-doping concentration effect on the minimum inhibitory concentration (MIC) of various bacteria under dark ambient has been evaluated. The photocatalytical inactivation of Ta-doped ZnO nanoparticles under visible light irradiation was examined. The MIC results indicate that the incorporation of Ta(5+) ions into ZnO significantly improve the bacteriostasis effect of ZnO nanoparticles on E. coli, S. aureus, and B. subtilis in the absence of light. Compared to MIC results without light irradiation, Ta-doped ZnO and pure ZnO nanoparticles show much stronger bactericidal efficacy on P. aeruginosa, E. coli, and S. aureus under visible light illumination. The possible antimicrobial mechanisms in Ta-doped ZnO systems under visible light and dark conditions were also proposed. Ta-doped ZnO nanoparticles exhibit more effective bactericidal efficacy than pure ZnO in dark ambient, which can be attributed to the synergistic effect of enhanced surface bioactivity and increased electrostatic force due to the incorporation of Ta(5+) ions into ZnO. Based on the antibacterial tests, 5 % Ta-doped ZnO is a more effective antimicrobial agent than pure ZnO.
RESUMEN
A novel photocatalyst ZnTiO(3) powder was prepared by a modified alcoholysis method, using ethylene glycol as reagent/solvent and acetylacetone as stabilizer. A series of analytical techniques were used to characterize the crystallinity, composition, bandgap, morphology, specific surface area and grain size of ZnTiO(3) powders. The relationship between the physicochemical property and the photocatalytic activity was deeply investigated, too. It is found that the photocatalytic activity is dependent on the phase of catalysts. The product of ZnTiO(3) with pure hexagonal-phase calcined at 800 degrees C for 3h exhibits the maximum photocatalytic performance in the photochemical degradation of the azo dye methyl violet under solar light irradiation. The processing parameters such as the concentration of catalysts and the pH value also play an important role in tuning the photocatalytic activity. The optimal concentration and pH value of the pure hexagonal-phase ZnTiO(3) is around 4g/L and 8 in a 10mg/L dye-aqueous solution, respectively.