RESUMEN
The effects of TiO2 nanotube (TNT) and reduced graphene oxide (rGO) deposition onto titanium, which is widely used in dental implants, on Streptococcus mutans (S. mutans) and preosteoblastic cells were evaluated. TNTs were formed through anodic oxidation on pure titanium, and rGO was deposited using an atmospheric plasma generator. The specimens used were divided into a control group of titanium specimens and three experimental groups: Group N (specimens with TNT formation), Group G (rGO-deposited specimens), and Group NG (specimens under rGO deposition after TNT formation). Adhesion of S. mutans to the surface was assessed after 24 h of culture using a crystal violet assay, while adhesion and proliferation of MC3T3-E1 cells, a mouse preosteoblastic cell line, were evaluated after 24 and 72 h through a water-soluble tetrazolium salt assay. TNT formation and rGO deposition on titanium decreased S. mutans adhesion (p < 0.05) and increased MC3T3-E1 cell adhesion and proliferation (p < 0.0083). In Group NG, S. mutans adhesion was the lowest (p < 0.05), while MC3T3-E1 cell proliferation was the highest (p < 0.0083). In this study, TNT formation and rGO deposition on a pure titanium surface inhibited the adhesion of S. mutans at an early stage and increased the initial adhesion and proliferation of preosteoblastic cells.
Asunto(s)
Grafito , Nanotubos , Streptococcus mutans , Ratones , Animales , Titanio/farmacología , Titanio/química , Propiedades de Superficie , Nanotubos/químicaRESUMEN
Peri-implantitis is an inflammatory disease similar to periodontitis, caused by biofilms formed on the surface of dental implants. This inflammation can spread to bone tissues and result in bone loss. Therefore, it is essential to inhibit the formation of biofilms on the surface of dental implants. Thus, this study examined the inhibition of biofilm formation by treating TiO2 nanotubes with heat and plasma. Commercially pure titanium specimens were anodized to form TiO2 nanotubes. Heat treatment was performed at 400 and 600 °C, and atmospheric pressure plasma was applied using a plasma generator (PGS-200, Expantech, Suwon, Republic of Korea). Contact angles, surface roughness, surface structure, crystal structure, and chemical compositions were measured to analyze the surface properties of the specimens. The inhibition of biofilm formation was assessed using two methods. The results of this study showed that the heat treatment of TiO2 nanotubes at 400 °C inhibited the adhesion of Streptococcus mutans (S. mutans), associated with initial biofilm formation, and that heat treatment of TiO2 nanotubes at 600 °C inhibited the adhesion of Porphyromonas gingivalis (P. gingivalis), which causes peri-implantitis. Applying plasma to the TiO2 nanotubes heat-treated at 600 °C inhibited the adhesion of S. mutans and P. gingivalis.
Asunto(s)
Implantes Dentales , Nanotubos , Periimplantitis , Humanos , Nanotubos/química , Biopelículas , Titanio/química , Propiedades de Superficie , Streptococcus mutansRESUMEN
The alternative antibacterial treatment photothermal therapy (PTT) significantly affects oral microbiota inactivation. In this work, graphene with photothermal properties was coated on a zirconia surface using atmospheric pressure plasma, and then the antibacterial properties against oral bacteria were evaluated. For the graphene oxide coating on the zirconia specimens, an atmospheric pressure plasma generator (PGS-300, Expantech, Suwon, Republic of Korea) was used, and an Ar/CH4 gas mixture was coated on a zirconia specimen at a power of 240 W and a rate of 10 L/min. In the physiological property test, the surface properties were evaluated by measuring the surface shape of the zirconia specimen coated with graphene oxide, as well as the chemical composition and contact angle of the surface. In the biological experiment, the degree of adhesion of Streptococcus mutans (S. mutans) and Porphyromonas gingivalis (P. gingivalis) was determined by crystal violet assay and live/dead staining. All statistical analyzes were performed using SPSS 21.0 (SPSS Inc., Chicago, IL, USA). The group in which the zirconia specimen coated with graphene oxide was irradiated with near-infrared rays demonstrated a significant reduction in the adhesion of S. mutans and P. gingivalis compared with the group not irradiated. The oral microbiota inactivation was reduced by the photothermal effect on the zirconia coated with graphene oxide, exhibiting photothermal properties.
Asunto(s)
Grafito , Grafito/farmacología , Grafito/química , Propiedades de Superficie , Antibacterianos/farmacologíaRESUMEN
Most digitally fabricated removable dentures are currently available in resin only. To overcome this limitation, digitally fabricated dentures were designed by using a general purpose software program rather than a dental computer-aided design (CAD) software program. The functional cusps were made in metal and the denture base in resin with a 3-dimensional (3D) printer. The 2 outputs were combined to complete the metal-containing digitally fabricated dentures. The technique provides new possibilities for making a variety of digital dental prostheses.
Asunto(s)
Dentadura Completa , Impresión Tridimensional , Diseño Asistido por Computadora , Bases para Dentadura , MetalesRESUMEN
The optical properties of zirconia photopolymer suspension for DLP (Digital Light Processing) were evaluated. The light source and intensity were set to 395 nm and 30 mW/cm². Experimental groups were divided into 48, 50, 52, 54, 56 and 58 vol% according to the zirconia volume fraction. The cure depth of all groups was at least 47.35 um when cured for 1 sec, which was higher than layer parameter values of the 3D printer. The geometrical overgrowth showed 28.55% at 48 vol% and 36.94% at 58 vol%. As the volume fraction of zirconia increased, the geometrical overgrowth increased and the cure depth reduced.
RESUMEN
This study evaluated the shear bond strength of zirconia to titanium implant components using silica-based glasses and compared the strength with that of implant components bonded using a commercial resin cement. Forty cylindrical zirconia specimens and forty titanium disks (Grade IV) were divided equally into four groups, depending on the adhesive used: three different types of glasses (group G, group GI, group GIB) and a self-adhesive resin cement (group U200), which was used as a control. The shear bond strength was evaluated using a universal testing machine and failure mode was examined by optical microscope. Data was analyzed using One-way ANOVA with p-value <0.05, which was considered statistically significant. The shear bond strength of the three glass groups was significantly higher than that of group U200 (p<0.05). Failure mode in all groups was a combination of adhesive and cohesive modes. Shear bond strength of zirconia to titanium bonded using glasses was higher than that using self-adhesive resin cement.
RESUMEN
The major failure of dental restorations is caused by dental caries by S. mutans. This study evaluated the effect of nanosized silver ions in feldspathic porcelain on cytotoxicity and antimicrobial activity. The control group was feldspathic porcelain (Noritake EX-3, Kuraray Noritake Dental Inc., Japan) that did not contain Ag (silver). The experimental groups were feldspathic porcelain mixed with colloidal solutions of nanosized silver ions in mixtures of 5% 10%, 20%, 30%. Cell activity assays evaluated with osteoblast hFOB 1.19 cells (human Fetal Osteoblastic cell line, ATCC® CRL- 11372™) and antimicrobial activity test used the streptococcus mutans (S. mutans). According to the observations, the addition of Ag to feldspathic porcelain led to increased cell activity and showed excellent antibacterial performance. Especially, the feldspathic porcelain with 30% nanosized Ag ion appeared to have a significant antimicrobial effect, this allows for the possibility of various clinical applications for such material, including use in dental prosthesis and implants.
RESUMEN
This study evaluated the effect of acid etching on surface characteristics, flexural strength and osteoblast cell response of glass-infiltrated zirconia. Zirconia specimens were divided into six groups: untreated zirconia (Z); glass-infiltrated zirconia (ZG); glass-infiltrated and sandblasted zirconia (ZGS); glass-infiltrated, sandblasted and 5 min acid-etched zirconia (ZGS-E5); glassinfiltrated, sandblasted and 15 min acid-etched zirconia (ZGS-E15); glass-infiltrated, sandblasted and 25 min acid-etched zirconia (ZGS-E25). Surface roughness, biaxial flexural strength and MC3T3-E1 cell proliferation were evaluated. When increasing etching time, surface roughness significantly increased while flexural strength decreased. Cell proliferation rate at day 3 on group ZGS-E15 and ZGS-E25 was significantly higher than that of other groups. Surface roughness and flexural strength of glass-infiltrated zirconia can be controlled by adjusting etching time. Rough surface made by acid etching following glass infiltration significantly enhanced osteoblast cell response. Glass infiltration improved strength of zirconia but severe acid etching slightly reduced strength of zirconia.
RESUMEN
In this study, we examined the effect of ß-tricalcium phosphate (ß-TCP) coating on alkali-treated CP Grade II titanium surface via RF magnetron sputtering on osteoblast like cell (MC3T3-E1) viability and bone formation in rat tibia. The specimens were divided into three groups; commercially pure titanium (control group), alkali-treated titanium with nanofiber structure (NF group) and ß-TCP coating on alkali-treated titanium with nanofiber structure (TNF group). The surface characteristics of specimens were observed under a field emission scanning electron microscope (FE-SEM), and contact angle was measured. The cell viability was assessed in vitro after 1 day, 3 days and 7 days. Implants of 2.0 mm diameter and 5.0 mm length were inserted into the tibia of rats. After 4 wks, the histomorphometric analysis was performed. Group NF and group TNF showed improved hydrophilicity of Ti. Group TNF showed significantly higher cell viability (P < 0.05) after 7 days. The bone to implant contact (BIC) ratio of the control group, NF group, and TNF group were 32.3%, 35.5%, and 63.9%, respectively. The study results suggested that ß-TCP coated alkali-treated titanium surface via RF magnetron sputtering might be effective in implant dentistry due to enhanced hydrophilicity, improved cell response, and better osseointegration.
Asunto(s)
Desarrollo Óseo , Fosfatos de Calcio , Nanofibras , Oseointegración , Titanio , Animales , Materiales Biocompatibles Revestidos , Implantes Dentales , Microscopía Electrónica de Rastreo , Propiedades de SuperficieRESUMEN
The aim of this study was to determine the effect of hydroxyapatite (HA) coating on titanium dioxide (TiO2) nanotube by sol-gel process on viability of osteoblast like cell (MC3T3-E1) and bone formation in rat tibia. Specimens were divided into three groups including commercially pure titanium (control group), TiO2 nanotubes (group N), and HA coated TiO2 nanotubes (group HN). Surface characteristics were determined using field emission scanning electron microscope (FE-SEM; S-4700, Hitachi, Japan) and contact angles were measured. Cell viability was investigated in vitro after 1 day, 3 days, and 7 days of incubation. Implants (2.0 mm in diameter and 5.0 mm in length) were inserted into the tibia of rats. After 4 weeks, histomorphometric analysis was performed. Both N and HN groups showed enhanced hydrophilicity compared to control group. After 7 days of implantation, group HN showed higher cell viability with marginal significance (0.05 < P < 0.1). Bone to implant contact (BIC) ratio in the control group, group N, and group HN were 32.5%, 33.1%, and 43.8%, respectively. Results of this study showed that HA coated TiO2 nanotube using sol-gel process could be used to enhance hydrophilicity and improve osseointegration of dental implant surface.
RESUMEN
The purpose of this study was to evaluate the fitness of zirconia cores according to the amount and treated surface of glass infiltration. A maxillary right central incisor customized abutment was milled to have a 6° slope and a 1 mm deep chamfer margin and was manufactured in an intaglio mold using silicone impression material. Fifty-six stone dies were produced by injecting high strength dental stone into a mold and then zirconia cores were milled with CAD/CAM systems. The control group (Control) used non glass-infiltrated zirconia, and the experiment group was divided by one with the glass and distilled water ratio of 1:300 and the other with the ratio of 1:100. Each group was divided into subgroups by glasstreated surface: external surface infiltration, internal surface infiltration, and both surface infiltration. The zirconia cores sintered after glass infiltration were attached to the stone dies and then cut. Afterwards, the absolute marginal discrepancies and internal gaps of the buccal and lingual sides were measured. The buccal absolute marginal discrepancies and lingual internal gaps were influenced by the glass infiltration amount (p < 0.05); while fitness of zirconia core were not affected by the glasstreated surface (p > 0.05). As a result of the above experiments, the glass-infiltrated zirconia cores showed a clinically acceptable fitness, which is within 120 µm. This means that glass infiltration can be clinically used.
RESUMEN
The aim of this study was to evaluate the antibacterial activity against Porphyromonas gingivalis and osteoblast viability of heat and plasma treatment of TiO2 nanotubes. Specimens were divided into four groups: the Ti (polished titanium), Nano (TiO2 nanotube), NH 300 (heat treated at 300 °C on TiO2 nanotube) and NH 400 (heat treated at 400 °C on TiO2 nanotube) groups. Antibacterial activity and osteoblast viability were evaluated in the four groups according to plasma treatment. Surface adhesion of Porphyromonas gingivalis was evaluated by crystal violet assay. Osteoblast viability was examined by XTT assay. Adhesion of Porphyromonas gingivalis was significantly decreased in the Ti group, Nano group and NH 300 group after plasma treatment (P < 0.05). Osteoblast viability was increased in the NH 400 group in comparison to the Ti group before plasma treatment (P < 0.05). Within the limitations of this study, plasma treatment was found to reduce the adhesion of P. gingivalis but had no influence on osteoblast activation.
Asunto(s)
Antibacterianos , Viabilidad Microbiana/efectos de los fármacos , Nanotubos , Osteoblastos/efectos de los fármacos , Titanio , Animales , Antibacterianos/química , Antibacterianos/farmacología , Antibacterianos/toxicidad , Línea Celular , Supervivencia Celular/efectos de los fármacos , Calor , Ratones , Nanotubos/química , Nanotubos/toxicidad , Gases em Plasma , Porphyromonas gingivalis/efectos de los fármacos , Propiedades de Superficie , Titanio/química , Titanio/farmacología , Titanio/toxicidadRESUMEN
Porphyromonas gingivalis (P. gingivalis) is one of main bacteria that adheres to the surface of dental implants and causes peri-implantitis. The purpose of this study was to observe the surface characteristics of titanium processed with either titanium nitride (TiN) sputter coating or plasma nitriding and to evaluate the subsequent adhesion of P. gingivalis. Specimens were divided into three groups: commercially pure (CP) titanium (control group), TiN sputtercoated titanium (group S), and plasma-nitrided titanium (group P). Surface characteristics such as roughness, morphology, and the formation of a thin TiN film or a nitriding layer were assessed. Adhesion of P. gingivalis in the three groups was determined by means of the crystal violet staining assay, and results were compared with one-way ANOVA, with post hoc comparison using Tukey's test (α = 0.05). Surface roughness values for the control group, group S, and group P were 0.08±0.02 µm, 0.19±0.04 µm, and 0.13±0.02 µm, respectively. In group S, the TiN layer was 1.36±0.1 µm thick, and nitrogen was detected on the surface of the specimens in group P, confirming formation of a nitrided layer. The level of adhesion in group P was significantly higher than that in the control group and in group S (p < 0.05), but there was no significant difference between the control group and group S. Within the limitations of this study, TiN sputter coating did not affect adhesion of P. gingivalis on the titanium surface, whereas adhesion was increased on the plasma-nitrided titanium surface.
RESUMEN
This study was to investigate the various glass thicknesses on the shear bond strength between zirconia and veneering porcelain. The zirconia specimens were classified into 5 groups (n = 12). For the control group, the Y-TZP disk was sintered (G0). For the test group, the presintered zirconia disks were spin coated with different W/P ratio glass compositions. The glass thickness on the zirconia was 1 µm (G1), 4 µm (G4), 10 µm (G10), and 40 µm (G40), respectively. All specimens were build-up veneering porcelain and fired. The shear bond strength (SBS) was tested in a universal testing machine (crosshead speed = 0.5 mm/min). As the thickness of the glass decreased, the shear bond strength increased. The G1 group showed significantly higher than the control group (G0) (P < 0.05). The results suggest that the thickness of glass coating on the zirconia structure needs to be made thin for better bonding strength with veneering porcelain.
RESUMEN
The purpose of this study was to examine the surface characteristics of bioactive glass-infiltrated zirconia specimens that underwent different hydrofluoric acid (HF) etching conditions. Specimens were classified into the following six groups: Zirconia, Zirliner, Porcelain, Bioactive glass A1, Bioactive glass A2, and Bioactive glass A3. Zirliner and porcelain were applied to fully sintered zirconia followed by heat treatment. Bioactive glass was infiltrated into presintered zirconia using a spin coating method followed by complete sintering. All the specimens were acid-etched with 10% or 20% HF, and surface roughness was measured using a profiler. The surface roughness of the zirconia group was not affected by the etching time or the concentration of the acid. The roughness of the three bioactive glass groups (A1, A2, and A3) was slightly increased up until 10 minutes of etching. After 1 hour of etching, the roughness was considerably increased. The infiltrated bioactive glass and acid etching did not affect the adhesion and proliferation of osteoblasts. This study confirmed that surface roughness was affected by the infiltration material, etching time, and acid concentration. For implant surfaces, it is expected that the use of etched bioactive glass-infiltrated zirconia with micro-topographies will be similar to that of machined or sand-blasted/acid-etched (SLA) titanium.
Asunto(s)
Grabado Dental , Vidrio/química , Ácido Fluorhídrico/química , Circonio/química , Ensayo de Materiales , Propiedades de SuperficieRESUMEN
This study investigated the mechanical properties and initial cell response of bioactive glass infiltrated zirconia before and after sandblasting. One hundred zirconia specimens were divided into the following four groups: untreated zirconia (ZR), sandblasted zirconia (ZS), glass infiltrated zirconia (ZG), and sandblasted glass infiltrated zirconia (ZGS). Surface roughness, biaxial flexural strength, hardness and osteoblast cells proliferation were evaluated. ZGS group showed a slight decrease in hardness. However it has improvement in flexural strength (686.2 MPa). After sandblasting, the ZGS group had the highest surface roughness (R a = 1.24 µm) with enhanced osteoblast cells response. Our results indicated that sandblasting method can improve the mechanical properties of bioactive glass infiltrated zirconia with better osteoblast cell response. This new surface is promising for zirconia dental implant application in the future.
Asunto(s)
Materiales Dentales/química , Vidrio/química , Circonio/química , Animales , Línea Celular , Proliferación Celular/efectos de los fármacos , Materiales Dentales/farmacología , Pruebas de Dureza , Ensayo de Materiales , Ratones , Osteoblastos/efectos de los fármacos , Propiedades de Superficie , Circonio/farmacologíaRESUMEN
STATEMENT OF PROBLEM: Although many systems are used to polish zirconia, a comparison of the performance of zirconia and feldspathic porcelain polishing systems is lacking. PURPOSE: The purpose of this in vitro study was to compare the effects of 3 polishing systems on surface roughness, zirconia phase transformation, and durability of the polishing systems when applied to zirconia and feldspathic porcelain. MATERIAL AND METHODS: Three polishing systems were evaluated: Z1, a zirconia polishing system; Z2, a zirconia polishing system, and F1, a feldspathic porcelain polishing system. Three ceramic systems were evaluated: PR and ZM zirconia specimens (diameter 15 mm, height 2 mm; 23 specimens each) and CB feldspathic porcelain specimens of the same size (15 specimens). A rough surface was created on the 3 types of specimens (15 specimens each) to model an occlusal adjustment under the same conditions. Polishing was carried out with the 3 polishing systems for 2 minutes each. Surface roughness was measured with a 3-dimensional (3D) optical profiler. The surface was also observed with a scanning electron microscopy. X-ray diffraction analysis was performed for 8 PR or ZM zirconia specimens polished by using the Z1 and Z2 systems for 8 minutes to evaluate the phase transformation of zirconia before, during, and after polishing. These specimens were compared and analyzed for phase transformation that might have occurred during the polishing of the specimens. After finishing the surface roughness experiment and the phase transformation experiment, the volumes of the polishers were measured with a 3D volume scanner and compared with those before the experiments to evaluate the durability of the polishing system. A statistical analysis of all data was performed using 2-way ANOVA and the Tukey honest significant difference test (α=.05). RESULTS: The 2 zirconia polishing systems (Z1, Z2) created a significantly (P<.001) smoother surface, regardless of the type of specimens used for polishing, than the feldspathic porcelain polishing system (F1). When polishing treatment was carried out on zirconia specimens for 8 minutes, the maximum percentages of monoclinic phase increased by 0.03% in the Z1 system and by 0.09% in the Z2 system. The volume change for the durability evaluation of the polishing system was 13.35 and 29.37% in the Z1 system, 2.05 and 5.92% in the Z2 system, and 3.60 and 4.95% in the F1 system, respectively. CONCLUSIONS: Zirconia polishing systems created a smoother surface on zirconia than the feldspathic porcelain polishing system. No significant changes in the phase transformation of zirconia were found before and after polishing. Each polishing system showed different levels of wear resistance.
Asunto(s)
Pulido Dental/instrumentación , Pulido Dental/métodos , Propiedades de Superficie , Circonio/química , Materiales Dentales , Porcelana Dental/química , Alisadura de la Restauración Dental , Diamante , Humanos , Ensayo de Materiales , Microscopía Electrónica de Rastreo/métodos , Ajuste Oclusal , Difracción de Rayos X/métodosRESUMEN
This study examined the effect of the immobilization of the Gly-Arg-Gly-Asp-Ser (GRGDS) peptide on titanium dioxide (TiO2) nanotube via chemical grafting on osteoblast-like cell (MG-63) viability and differentiation. The specimens were divided into two groups; TiO2 nanotubes and GRGDS-immobilized TiO2 nanotubes. The surface characteristics of GRGDS-immobilized TiO2 nanotubes were observed by using X-ray photoelectron spectroscopy (XPS) and a field emission scanning electron microscope (FE-SEM). The morphology of cells on specimens was observed by FE-SEM after 2 hr and 24 hr. The level of cell viability was investigated via a tetrazolium (XTT) assay after 2 and 4 days. Alkaline phosphatase (ALP) activity was evaluated to measure the cell differentiation after 4 and 7 days. The presence of nitrogen up-regulation or C==O carbons con- firmed that TiO2 nanotubes were immobilized with GRGDS peptides. Cell adhesion was enhanced on the GRGDS-immobilized TiO2 nanotubes compared to TiO2 nanotubes. Furthermore, significantly increased cell spreading and proliferation were observed with the cells grown on GRGDS-immobilized TiO2 nanotubes (P < .05). However, there was no significant difference in ALP activity between GRGDS-immobilized TiO2 nanotubes and TiO2 nanotubes. These results suggest that the GRGDS-immobilized TiO2 nanotubes might be effective in improving the osseointegration of dental implants.
Asunto(s)
Diferenciación Celular/efectos de los fármacos , Nanotubos/química , Oligopéptidos , Osteoblastos/metabolismo , Titanio , Línea Celular Tumoral , Supervivencia Celular/efectos de los fármacos , Humanos , Oligopéptidos/química , Oligopéptidos/farmacología , Osteoblastos/citología , Titanio/química , Titanio/farmacologíaRESUMEN
The aim of this study was to evaluate the response of Streptococcus mutans (S. mutans) via crystal violet staining assay on titanium surface modified by physical vapor deposition/plasma assisted chemical vapor deposition process. Specimens were divided into the following three groups: polished titanium (control group), titanium modified by DC magnetron sputtering (group TiN-Ti), and titanium modified by plasma nitriding (group N-Ti). Surface characteristics of specimens were observed by using nanosurface 3D optical profiler and field emission scanning electron microscope. Group TiN-Ti showed TiN layer of 1.2 microm in thickness. Group N-Ti was identified as plasma nitriding with X-ray photoelectron spectroscopy. Roughness average (Ra) of all specimens had values < or = 0.2 microm (the threshold Ra), which had no effect on bacterial adhesion. No significant difference of S. mutans adhesion was found between the surfaces of control, TiN-Ti, and N-Ti (P > 0.05). Within the process condition of this study, modified titanium surfaces by DC magnetron sputtering and plasma nitriding did not influence the adhesion of S. mutans.
Asunto(s)
Antibacterianos/química , Gases em Plasma/química , Streptococcus mutans/crecimiento & desarrollo , Titanio/química , Propiedades de SuperficieRESUMEN
According to evolving computer-aided design/computer-aided manufacturing (CAD/CAM) technology, ceramic materials such as zirconia can be used to create fixed dental prostheses for partial removable dental prostheses. Since 3D printing technology was introduced a few years ago, dental applications of this technique have gradually increased. This clinical report presents a complete-mouth rehabilitation using 3D printing and the CAD/CAM double-scanning method.