RESUMEN
Polyurethanes are one of the most important groups of polymers for numerous sectors of industry. Their production involves using dangerous components (diisocyanates), thus, in the search for safer synthetic routes, alternative methods yielding non-isocyanate polyurethanes (NIPU) have been investigated. In this study, the synthesis of polyhydroxyurethane from cyclic carbonates was performed. A three-factor, three-level Box-Behnken experimental design was constructed and the reaction time, temperature and reagents' molar ratio were the independent variables. The built model revealed that the viscosity was influenced by all three independent factors, while the mechanical properties and glass transition temperature of the PHUs were affected by the reagents' ratios. An experimental verification of the model proved its accuracy as the mechanical strength and glass transition temperature deviated from the modeled values, by 15% and 7%, respectively.
RESUMEN
Poly(lactide) (PLA) films obtained by thermoforming or solution-casting were modified by diffuse coplanar surface barrier discharge plasma (300 W and 60 s). PLA films were used as hot-melt adhesive in joints in oak wood. It was demonstrated that lap shear strength increased from 3.4 to 8.2 MPa, respectively, for the untreated and plasma-treated series. Pull-off tests performed on particleboard for the untreated and treated PLA films showed 100% cohesive failure. Pull-off strength tests on solid oak demonstrated adhesion enhancement from 3.3 MPa with the adhesion failure mode to 6.6 MPa with the cohesion failure mode for untreated and treated PLA. XPS revealed that carbonyl oxygen content increased by two-to-three-fold, which was confirmed in the Fourier-transform infrared spectroscopy experiments of the treated PLA. The water contact angle decreased from 66.4° for the pristine PLA to 49.8° after treatment. Subsequently, the surface free energy increased from 47.9 to 61.05 mJ/m2. Thus, it was clearly proven that discharge air plasma can be an efficient tool to change surface properties and to strengthen adhesive interactions between PLA and woody substrates.
RESUMEN
Hyperbranched polyoxetanes are a relatively new class of polymers. These are branched polyethers that are synthesized from oxetanes-four-member cyclic ethers bearing hydroxymethyl groups-via ring-opening polymerization. Four series of polyoxetanes were synthesized from 3-ethyl-3-(hydroxymethyl)oxetane and 1,1,1-tris(hydroxymethyl)propane as a core molecule. Reagents ratios ranged from 1:5 to 1:50, theoretical molar mass ranged from 714 g/mol to 5942 g/mol, and dispersities ranged from 1.77 to 3.75. The morphology of the macromolecules was investigated by a matrix-assisted laser desorption/ionization time of flight technique. The polyoxetanes' adhesive interactions with polar materials were analyzed and provided results as follows: the work of adhesion was 101-105 mJ/m2, the bond-line tensile shear strengths were 0.39-1.32 MPa, and there was a brittle fracture mode within the polymer. The findings confirmed a good adhesion to polar substrates, but further research on polyoxetane modifications toward a reduction of brittleness is necessary.
RESUMEN
The aim of the study was to evaluate the applicability and performance of polyglycerol- and sucrose-based polyols as components of a simplified formulation of polyurethane adhesives. Colloidal silica was used as a viscosity control and reinforcing agent. The adhesives were examined in terms of reactivity, thermal stability, viscosity, work of adhesion, wetting, surface energy, and bonding strength on wooden substrates. Silica was found to increase gelling time, but markedly improved bonding strength and adhesion with substrates. Bonded solid beech wood samples prepared at 80, 110, and 130 °C showed shear strengths between 7.1 MPa and 9.9 MPa with 100% wood failure. The renewable resource-based polyols were demonstrated to be useful in formulation of polyurethane adhesives for furniture industry-especially with silica as a filler.