Preferential Orientation of Photochromic Gadolinium Oxyhydride Films.

We report preferential orientation control in photochromic gadolinium oxyhydride (GdHO) thin films deposited by a two-step process. Gadolinium hydride (GdH2-x) films were grown by reactive magnetron sputtering, followed by oxidation in air. The preferential orientation, grain size, anion concentrations and photochromic response of the films were strongly dependent on the deposition pressure. The GdHO films showed a preferential orientation along the [100] direction and exhibited photochromism when synthesized at deposition pressures of up to 5.8 Pa. The photochromic contrast was larger than 20% when the films were deposited below 2.8 Pa with a 0.22 H2/Ar flow ratio. We argue that the relation of preferential orientation and the post deposition oxidation since oxygen concentration is known to be a key parameter for photochromism in rare-earth oxyhydride thin films. The experimental observations described above were explained by the decrease of the grain size as a result of the increase of the deposition pressure of the sputtering gas, followed by a higher oxygen incorporation.

A new setup for optical measurements under controlled environment.

We present a new analytical instrument for studying the optical properties of materials in different gaseous environments at room and controlled elevated temperatures. The system consists of a vacuum chamber, which is equipped with temperature and pressure controllers, a heating band, and a residual gas analyzer and is connected to a gas feeding line via a leak valve. Two transparent view ports located around a sample holder allow for optical transmission and pump-probe spectroscopy using an external optical setup. The capabilities of the setup are demonstrated by conducting two experiments. In the first experiment, we study the photodarkening and bleaching kinetics of photochromic oxygen-containing yttrium hydride thin films illuminated in ultra high-vacuum and correlate it with changes in partial pressures inside the vacuum chamber. In the second study, we investigate changes in the optical properties of a 50 nm V film upon hydrogen absorption.