RESUMEN
Impact by hailstone, volcanic rock, bird strike, or also dropping tools can cause damage to aircraft materials. For maximum safety, the goal is to increase Charpy impact strength (auc) of a carbon-fiber-reinforced thermoplastic polyphenylene sulfide polymer (CFRTP-PPS) composite for potential application to commercial aircraft parts. The layup was three cross-weave CF plies alternating between four PPS plies, [PPS-CF-PPS-CF-PPS-CF-PPS], designated [PPS]4[CF]3. To strengthen, a new process for CFRP-PPS was employed applying homogeneous low voltage electron beam irradiation (HLEBI) to both sides of PPS plies prior to lamination assembly with untreated CF, followed by hot press under 4.0 MPa at 573 K for 8 min. Experimental results showed a 5 kGy HLEBI dose was at or near optimum, increasing auc at each accumulative probability, Pf. Optical microscopy of 5 kGy sample showed a reduction in main crack width with significantly reduced CF separation and pull-out; while, scanning electron microscopy (SEM) and electron dispersive X-ray (EDS) mapping showed PPS adhering to CF. Electron spin resonance (ESR) of a 5 kGy sample indicated lengthening of PPS chains as evidenced by a reduction in dangling bond peak. It Is assumed that 5 kGy HLEBI creates strong bonds at the interface while strengthening the PPS bulk. A model is proposed to illustrate the possible strengthening mechanism.
RESUMEN
Strong adhesion between recyclable thermoplastic (TP) polymer and carbon fiber (CF) has always been highly sought after. Therefore, for an interlayered CF reinforced TP polypropylene (CFRTPP) composite composed of 3 sized CF plies, alternating between 4 PP sheets, designated [PP]4[CF]3, a process of activating CF plies directly on both sides with homogeneous low energy electron beam irradiation (EBI) under N2 gas, prior to lamination assembly and hot press of 4.0 MPa at 493 K for 3 min was carried out. Experimental results showed EBI dose of 43.2, 129, or 216 kGy significantly raised Charpy impact values, auc at all fracture probabilities, Pf. The 129 kGy dose appeared to be at or near optimum increasing auc 103%, 83%, and 65% at low-, median-, and high-Pf = 0.07, 0.50, and 0.93; while raising statistically lowest impact value, as at Pf = 0 calculated by 3-dimensional Weibull equation about 110%, indicating increased safety and reliability. It is assumed dangling bonds generated by the EBI rapidly form covalent bonds CF:C:O:C:PP and CF:C:C:PP at the interface, along with cross-linking in the PP near the CF. This is by charge transfer from CF to PP.