RESUMEN
Recently, various calcium silicate-based sealers have been introduced for use in root canal filling. The MTA Fillapex is one of these sealers, but some of its physicochemical properties are not in accordance with the ISO requirements. Objective: The aim of this study was to evaluate the flowability, pH level and calcium release of pure MTA Fillapex (MTAF) or containing 5% (MTAF5) or 10% (MTAF10) calcium hydroxide (CH), in weight, in comparison with AH Plus sealer. Material and Methods: The flowability test was performed according to the ISO 6876:2001 requirements. For the pH level and calcium ion release analyses, the sealers were placed individually (n=10) in plastic tubes and immersed in deionized water. After 24 hours, 7 and 14 days, the water in which each specimen had been immersed was evaluated to determine the pH level changes and calcium released. Flowability, pH level and calcium release data were analyzed statistically by the ANOVA test (α=5%). Results: In relation to flowability: MTAF>AH Plus>MTAF5>MTAF10. In relation to the pH level, for 24 h: MTAF5=MTAF10=MTAF>AH Plus; for 7 and 14 days: MTAF5=MTAF10>MTAF>AH Plus. For the calcium release, for all periods: MTAF>MTAF5=MTAF10>AH Plus. Conclusions: The addition of 5% CH to the MTA Fillapex (in weight) is an alternative to reduce the high flowability presented by the sealer, without interfering in its alkalization potential. .
Asunto(s)
Compuestos de Aluminio/química , Compuestos de Calcio/química , Hidróxido de Calcio/química , Calcio/química , Resinas Epoxi/química , Óxidos/química , Materiales de Obturación del Conducto Radicular/química , Silicatos/química , Análisis de Varianza , Combinación de Medicamentos , Ensayo de Materiales , Valores de Referencia , Factores de Tiempo , Viscosidad , Agua/químicaRESUMEN
Objetivo: O objetivo do estudo foi avaliar a efetividade da guta-percha e Resilon no preenchimento de canais laterais nos terços cervical, médio e apical radicular quando utilizada a técnica termomecânica. Material e Método: Canais radiculares de dentes artificiais foram preparados utilizando um método padrão. Canais laterais foram confeccionados utilizando broca com 0,3 mm de diâmetro nos três terços radiculares. Os canais radiculares foram obturados pela técnica híbrida de Tagger utilizando-se o compactador de McSpadden. Foi avaliado o preenchimento dos canais laterais pelos seguintes materiais: cones de guta-percha Dentsply, guta-percha Endopoint e Resilon. A avaliação foi realizada por meio da análise de radiografias digitalizadas usando o programa Image Tool. A porcentagem da área preenchida pela área total de cada canal lateral foi determinada. Os dados foram submetidos à análise de variância (ANOVA) e teste de Tukey com nível de significância de 5%. Resultado: O Resilon mostrou melhor efetividade como material de preenchimento. Na comparação entre os terços, o Resilon foi mais efetivo no terço apical que no cervical (p < 0,05). Conclusão: O Resilon foi o material mais efetivo para o preenchimento dos canais laterais quando utilizada a técnica termoplástica.
Objective: The aim of this study was to evaluate the effectiveness of gutta-percha and Resilon in filling lateral root canals in cervical, middle, and apical third using a thermomechanical technique. Material and Method: Root canals of artificial teeth were prepared using a standard preparation. The lateral canals were fabricated using a 0.3-mm-diameter bur at 3 parts of each root. By using Tagger's hybrid technique with a McSpadden thermomechanical compactor, the root canal was filled using the following filling materials: Dentsply gutta-percha, Endopoint gutta-percha, and Resilon cones. The root canal fillings were evaluated using digitized radiographs and the Image Tool software. The percentage of filled area of each lateral canal was determined. The data were subjected to analysis of variance (ANOVA) and Tukey tests at a 5% significance level. Result: Resilon showed better effectiveness as a filling material. When the three thirds were compared, Resilon was more effective in the apical third than in the cervical third (p < 0.05). Conclusion: Resilon is an effective filling material for lateral root canals using a thermomechanical technique.
Asunto(s)
Materiales de Obturación del Conducto Radicular , Obturación del Conducto Radicular , Diente Artificial , Análisis de Varianza , Radiografía Dental Digital , Cavidad Pulpar , GutaperchaRESUMEN
Lesões endo-perio são lesões inflamatórias que acometem, em diversos graus, tanto os tecidos periodontais como a polpa dental. O objetivo deste artigo é mostrar, através de uma revisão da literatura, a importância da classificação das lesões endo-perio, assim como o diagnóstico dessas lesões. A partir dos trabalhos revisados, conclui-se que as lesões endo-perio apresentam uma etiologia variada, sendo de fundamental importância o conhecimento do profissional quanto às causas e seu correto diagnóstico. Assim, para o sucesso e a resolução das lesões endo-perio, uma avaliação clínica e radiográfica eficaz determinará a correta classificação e, consequentemente, a melhor forma de tratamento.
Endo-periodontal lesions are inflammatory conditions that affect the periodontal tissues and the dental pulp. The aim of this article is to show the importance of the classification and the diagnosis of the endo-perio lesions. From the studies reviewed, it is concluded that endo-perio lesions present a varied etiology, being of fundamental importance the knowledge of the professional as to its causative factors and its correct diagnosis. Thus, for the success and resolution of endo-perio lesions an effective clinical and radiographic evaluation will determine the correct classification and consequently the best form of treatment.
Asunto(s)
Humanos , Masculino , Femenino , Cavidad Pulpar/diagnóstico por imagen , Cavidad Pulpar/lesiones , Enfermedades de la Pulpa Dental/clasificación , Enfermedades de la Pulpa Dental/diagnóstico , Pulpa Dental/lesiones , Enfermedades PeriodontalesRESUMEN
Objetivo: O objetivo deste estudo foi avaliar a ação do salicilato de metila na dissolução de Resilon e guta-percha. Material e método: Dez discos de Resilon, guta-percha (Alpha) e guta-percha (ProTaper) foram preparados (10 mm de diâmetro × 1 mm de espessura) e mantidos a 37 °C por 48 horas. Cada amostra foi pesada em uma balança de precisão, determinando a massa inicial. Os espécimes foram imersos em salicilato de metila ou xilol (controle) por 5 minutos, lavados em água por 30 minutos, secos e, posteriormente, pesados em intervalos de 24 horas, até a estabilização da massa (massa final). A capacidade solvente foi expressa pela diferença entre a massa final e a inicial. Os dados foram submetidos à análise de variância e teste de Tukey, com nível de significância de 5%. Resultado: Os resultados mostraram que o salicilato de metila foi mais efetivo sobre o Resilon do que sobre a guta-percha (p <0,05). A capacidade solvente do salicilato de metila foi semelhante à do xilol sobre o Resilon (p >0,05). O xilol mostrou melhor atuação sobre a guta-percha em comparação ao salicilato de metila (p < 0,05). Conclusão: Concluiu-se que o salicilato de metila não apresenta atuação solvente sobre guta-percha, sendo eficaz na dissolução do Resilon. O salicilato de metila demonstra ser alternativa ao uso do xilol durante o retratamento endodôntico de dentes obturados com Resilon.
Objective: The aim of this study was to evaluate the action of methyl salicylate in dissolving Resilon and gutta-percha. Material and method: Ten discs of Resilon, Alpha gutta-percha and ProTaper gutta-percha were prepared (10 mm diameter × 1 mm thick) and kept at 37 °C for 48 hours. Each sample was weighed in a balance of accuracy determining the initial mass. The specimens were immersed in methyl salicylate or xylene (control) for 5 minutes, rinsed in water for 30 minutes, dried and subsequently weighed in 24 hours intervals until the stabilization of weight (final mass). The solvent capacity was expressed by the difference between the final and initial mass. The data were analyzed by using ANOVA and Tukey test with significance level of 5%. Result: The results showed that the methyl salicylate was more effective on Resilon than on gutta-percha (p < 0.05). Methyl salicylate and xylene had similar solvent action on Resilon (p > 0.05). The xylene showed better performance on gutta-percha than methyl salicylate (p < 0.05). Conclusion: It was concluded that methyl salicylate did not show solvent action on gutta-percha, however it showed effectiveness in dissolution of Resilon. Thus methyl salicylate can be a possible alternative to the use of xylene during endodontic retreatment of teeth obturated with Resilon.
Asunto(s)
Materiales de Obturación del Conducto Radicular , Xilenos , Endodoncia , Disolución , GutaperchaRESUMEN
The aim of this study was to evaluate the effectiveness of gutta-percha and Resilon in filling lateral root canals by using the Obtura II system. Root canals of artificial teeth were prepared using a standard protocol, and lateral canals were made in three thirds of the root canal. The root canals were filled with either Obtura gutta-percha (OB), Endo-points flow gutta-percha (ED), or Resilon (RE) by using the Obtura II system. The fillings were evaluated using digitized radiographs and analyzed by using Image Tool software. Outlines of the total areas of the lateral canals and the filled areas were used to determine the percentage of filling in each lateral canal. Data were analyzed with the Kruskal-Wallis and Dunn tests at a 5 percent significance level. RE and ED showed better results than OB did in the three thirds of the root canals. When the root canal thirds were compared, OB and RE were more effective in the cervical third than in the apical third (p < 0.05). In conclusion, Resilon and EndoFlow gutta-percha were effective in filling lateral canals by using the Obtura II system.
Asunto(s)
Cavidad Pulpar/anatomía & histología , Gutapercha/uso terapéutico , Materiales de Obturación del Conducto Radicular/uso terapéutico , Obturación del Conducto Radicular/métodos , Gutapercha/química , Procesamiento de Imagen Asistido por Computador , Ensayo de Materiales , Materiales de Obturación del Conducto Radicular/química , Obturación del Conducto Radicular/instrumentación , Estadísticas no ParamétricasRESUMEN
Objetivo: O objetivo deste trabalho foi verificar se a irrigação final com EDTA a 17 por cento, isoladamente ou seguidado digluconato de clorexidina a 2 por cento, interfere no vedamento apical de sobreobturações endodônticas em função dos cimentos Sealer 26® ou Sealapex®. Métodos: Quarenta incisivos inferiores extraídos, com umúnico canal, tiveram seus condutos radiculares preparados biomecanicamente, a 2,0 mm aquém do ápice radicular, com o sistema ProTaper®, finalizado com o instrumento F3. A irrigação foi executada com 1,0 mL de NaOCl a 2,5 por cento a cada troca de calibre de instrumento e, ao final, com 5,0 mL de soro fisiológico. Concluída a instrumentação, o canal cementário foipadronizado com uma lima K 25 até que sua guia de penetração aparecesse na abertura foraminal. A partir deste momento, os dentes foram subdivididos em dois grupos de vinte espécimes cada, em função do método de irrigação final utilizado: I irrigação com EDTAa 17 por cento por 3min e II idêntico protocolo, porém após a aspiração do EDTA a 17 por cento, novamente irrigado com o digluconato de clorexidina a 2 por cento, também mantido intracanal, por 3min. Cada grupo foi novamente subdivido em dois subgrupos (dez dentes cada), conforme o cimento empregado (Sealer 26® ou Sealapex®), e obturado pela técnica do cone único, com o cone F1 (ProTaper®, Universal Obturação), de tal forma que este ultrapassasse 2,0 mm além do ápice radicular. Imediatamente após, os dentes foram imersos em RhodamineB® por 72h, sob vácuo, e após o desgaste das raízes no sentido vestibulolingual, as infiltrações demarcadas foram medidas com o programa Image Tool®. Resultadose Conclusão: As magnitudes das infiltrações assemelharam-se entre si (p > 0,05), à exceção do próprio grupodo cimento Sealapex®, pois o uso final com a clorexidina reduziu a infiltração apical (p < 0,05)
Asunto(s)
Cementos Dentales , Clorhexidina , Obturación del Conducto RadicularRESUMEN
Objetivo: Este estudo avaliou o pH do hidróxido de cálcio (Calen®) associado ou não com clorexidina 0,4 por cento e,quando associado à clorexidina, acrescido de 10 por cento ou 20 por cento de racealfatocoferol, em diversos períodos de tempo. Métodos: Quarenta tubos de dentina de 20 mm, devidamente padronizados, foram confeccionados a partir de raízes de dentes anteriores bovinos. Na sequência,uma perfuração foi realizada na face distal das raízes, a 7 mm da linha cervical radicular, com a broca carbide1/2. Após a total impermeabilização da raiz, exceto no local da perfuração, os canais radiculares foram preenchidoscom uma das seguintes associações: Grupo I Calen®; Grupo II Calen® com clorexidina a 0,4 por cento; Grupo III Calen® com clorexidina a 0,4 por cento acrescida com 20 por cento (em peso) de composto de racealfatocoferol;Grupo IV Calen® com clorexidina a 0,4 por cento acrescida com 10 por cento (em peso) de composto de racealfatocoferol. Após o vedamento da porção cervical, as raízes foram imersas em água MiliQ e o pH, avaliado em 24h, 7, 14, 21, 28 e 45 dias. Resultados e Conclusão: Em todos os períodos testados o pH do hidróxido de cálcio (Calen ®) assemelhou ao pH do hidróxido de cálcio (Calen®) associado com clorexidina 0,4 por cento e 10 por cento de racealfatocoferol (p > 0,05). Associação de 20 por cento de racealfatocoferol sempre obteve menor pH que a associação com 10 por cento (p < 0,05). O pH da associação com clorexidina foi semelhante ao hidróxido de cálcio puro (Calen®) somente após o 14o dia(p > 0,05). Porém, no 45o dia essa diferença voltou a ser significativa (p < 0,05)
Asunto(s)
Endodoncia , Hidróxido de Calcio , alfa-TocoferolRESUMEN
Introdução e objetivo: Buscou-se quantificar, indiretamente, a liberaçãode oxigênio após a reação química intracoronária, por deslocamentoaxial de fluido em capilares de vidro, adaptados em coroas dentárias.Material e métodos: Coroas bovinas foram acessadas, e foi executadoo tampão cervical e posicionado um capilar de vidro na face externavestibular, contendo um veículo oleoso. Na sequência, foram preparadasquatro associações de clareadores e colocadas em seu interior: G1? perborato de sódio e peróxido de hidrogênio a 3%; G2 ? perborato de sódio e água; G3 ? associação de percarbonato de sódio e peróxidode hidrogênio a 3%; G4 ? associação de percarbonato de sódio eágua destilada. Após serem mantidas por 24 horas, quantificou-se odeslocamento axial do fluido, interpretado como liberação de oxigêniopela reação química. Resultados: Os resultados mostraram umatendência das associações com o peróxido de hidrogênio em promovermaior liberação de oxigênio. Entretanto não houve diferença entre operborato de sódio e o percarbonato de sódio (p > 0,05). Conclusão:Os grupos experimentais não demonstraram diferenças entre si duranteas 24 horas de reação química.
Objective: To indirectly quantify the release of oxygen after intracoronarychemical reaction, by axial displacement of fluid in glass capillariesarranged in dental crowns. Material and methods: Bovine crownswere accessed, the cervical plug was executed and a glass capillarywas placed in the vestibular external face, containing an oily vehicle.Following that, four associations of bleaching were prepared and placedin its interior: G1 ? sodium perborate and hydrogen peroxide 3%; G2? sodium perborate and water, G3 ? sodium percarbonate and hydrogenperoxide 3%; G4 ? sodium percarbonate and distilled water. After beingkept for 24 hours, the axial displacement of the fluid was quantifiedand interpreted as the release of oxygen by the chemical reaction.Results: The results showed a trend of the associations with hydrogenperoxide to promote the release of more oxygen. However, there wasno difference between sodium perborate and sodium percarbonate(p > 0.05). Conclusion: The experimental groups showed no differencesbetween them during the 24 hours of chemical reaction.
RESUMEN
Introdução: O cimento Sealer 26® contém resina epóxi associada aohidróxido de cálcio, apresentando menor radiopacidade que algunscimentos endodônticos. Com o intuito de melhorar essa propriedade,tem-se agregado iodofórmio ao pó do cimento. Entretanto, aoexecutar tal procedimento, desconhecem-se as possíveis alteraçõesnas propriedades físicas e químicas do material. Objetivo: Avaliar acapacidade de selamento marginal apical, a solubilidade e o pH doSealer 26® puro ou acrescido de iodofórmio em diversas proporções.Material e métodos: Foram manipuladas e submetidas ao teste desolubilidade três associações experimentais de Sealer 26®, puroou acrescido de iodofórmio. Paralelamente, as combinações foraminseridas em tubos de polietileno e imersas em água destilada, e opH das soluções foi avaliado nos períodos de 24 horas e 7 dias. Emseguida, 40 raízes de incisivos inferiores extraídos, subdivididosem quatro grupos de dez espécimes cada, foram retrobturados comuma das misturas anteriormente descritas. Imergiram-se as raízesem Rhodamine B, sob vácuo, por 72 horas. Concluída a imersão,os espécimes foram desgastados longitudinalmente, os fragmentosradiculares fotografados, as imagens digitalizadas e a infiltração apicalmedida pelo programa Image Tool. Os dados obtidos foram submetidosa análise estatística, com nível de significância de 5%. Resultados:Os testes de infiltração e solubilidade não demonstraram diferençasentre os grupos experimentais (p > 0,05). A análise do pH apresentoudiferença apenas no período de 24 horas entre o grupo do Sealer 26®puro e o grupo com 1,1 g de iodofórmio (p < 0,05). Conclusão: Aadição de iodofórmio ao Sealer 26®, nas proporções descritas, nãoalterou as propriedades de selamento marginal apical, a solubilidadenem o pH do cimento original
Introduction: Sealer 26® cement contains bisphenol epoxy resinassociated with calcium hydroxide, presenting smaller radiopacity thanother endodontic cements. Aiming to improve this property, iodoformhas been added in its composition. However, this addition?s possiblechanges in physical and chemical properties still need to be studied.Objective: To evaluate the apical sealing ability, solubility, and pH ofSealer 26® alone or with iodoform, at several proportions. Material andmethods: Three experimental mixtures of Sealer 26®, alone or withiodoform, were prepared and subjected to solubility test. Additionally,these combinations were inserted into polyethylene tubes and immersedin distilled water, and, their pH was evaluated after 24-h and 7-dayperiods. Subsequently, forty roots of extracted lower incisors subdividedinto four groups of 10 specimens each, were retrograde filled with oneof the previously described mixtures and gutta-percha points. The rootswere immersed in Rhodamine B, under vacuum, for 72 hours. Afterthis period, the specimens were longitudinally sectioned, root fragmentsphotographed, these images scanned, and apical infiltration measuredby Image tool software. The obtained data were subjected to statisticalanalysis, at a significance level of 5%. Results: Marginal leakage andsolubility tests did not show any difference among the experimentalgroups (p > 0.05). pH analysis was only statistically different at 24-h period and between Sealer 26® alone and 1.1g iodoform group(p < 0.05). Conclusion: The presence of iodoform in Sealer 26®, at theused proportions, did not alter the solubility, apical marginal leakageand pH properties of the original cement.
RESUMEN
Introdução: o objetivo do presente trabalho foi comparar o tempo gasto para o preparo de canais simulados, bem como os desvios em graus proporcionados pelos sistemas rotatórios Twisted File e Endowave. Métodos: foram empregados 30 blocos de acrílico com canais simulados e curvatura de 30°, que foram divididos em dois grupos: grupo 1 Sistema Twisted File; grupo 2 Sistema Endowave. Durante o preparo foi empregado o motor X-Smart com1,4N/cm de torque e 250rpm de velocidade. Os blocos foram radiografados antes e após o preparo. As radiografias foram digitalizadas e analisadas pelo ângulo formado antese após o preparo por meio do programa Image Tools.Foram analisados o tempo de preparo, o número de instrumentos deformados e fraturados, e o desvio. Resultados:os resultados mostraram que o Endowave preparou os canais simulados significativamente mais rápido (p<0,05) e fraturou menos que o sistema Twisted File. Quanto ao desvio apical, ambos desviaram significativamente (p<0,05)mais na parede interna, não havendo diferença significativa(p>0,05) entre ambos. Conclusão: concluiu-se que o Endowave preparou os canais simulados de forma mais rápida que o Twisted File e com menor índice de fratura
Asunto(s)
Instrumentos Dentales , Cavidad Pulpar , Endodoncia/métodos , Preparación del Conducto Radicular/métodos , Tratamiento del Conducto Radicular/métodosRESUMEN
O objetivo deste estudo foi avaliar a capacidade de preenchimento de canais laterais simulados pela guta-percha e Resilon, empregando diferentes técnicas termoplastificadoras de obturação: Condensação Vertical Aquecida (CVA), Compactação Termomecânica (CT) e Sistema Obtura II (SO). Foram utilizados 135 dentes humanos unirradiculados extraídos. Após preparo biomecânico, foram confeccionados seis canais laterais simulados em suas raízes, de acordo com a técnica proposta por Venturi et al. (2005). O diâmetro desses canais foi correspondente aos instrumentos # 08 e 10, sendo estabelecidos a 2, 5 e 8 mm do comprimento de trabalho (CT). Os espécimes foram divididos em 9 grupos (n=15), sendo: Grupo I (CVA + guta-percha Dentsply), Grupo II (CVA + Resilon), Grupo III (CVA + gutapercha Odous), Grupo IV (CT + guta-percha Dentsply), Grupo V (CT + Resilon), Grupo VI (CT + guta-percha Odous), Grupo VII (SO + gutapercha Obtura Flow 150), Grupo VIII (SO + Resilon) e Grupo IX (SO + guta-percha Odous Flow). Após a realização das obturações, os espécimes foram analisados pelos métodos radiográfico e diafanização, em função do percentual de preenchimento nos canais laterais, nos três terços. Os resultados foram submetidos ao teste de Kruskal-Wallis, com 5% de nível de significância, de acordo com avaliações específicas intragrupos: CVA (Grupos I, II e III), CTH (Grupos IV, V e VI), SO (Grupos VII, VIII e IX) e Resilon (Grupos II, V e VIII). As avaliações CVA e CTH mostraram que o Resilon apresentou maior capacidade de preenchimento nas duas análises, em relação aos demais materiais, nos terços apical e médio (p<0,05). Quanto à avaliação SO, todos os materiais apresentaram boa capacidade de preenchimento dos canais laterais em todos os terços, com exceção do terço cervical onde o Resilon foi melhor pela análise radiográfica (extensão e área) e nos terços cervical e médio pela análise de diafanização (extensão), em relação à guta-percha Obtura Flow 150 (p<0,05). Já a avaliação dos grupos Resilon mostrou que não houve diferença entre as três técnicas utilizadas, que apresentaram elevados percentuais de preenchimento dos canais laterais. Diante dos resultados obtidos podemos concluir que o Resilon representa alternativa para utilização como material obturador sólido, nas três técnicas termoplastificadoras avaliadas
The aim of this study was to evaluate the ability of guttapercha and Resilon to fill simulated canals using different thermoplastic obturation techniques: Warm Vertical Compaction (CVA), Thermomechanical Compaction (CTE) and Obtura II System (SO). It was used 135 extracted human teeth uniradicular. After biomechanical preparation, six simulated lateral canals were prepared in the roots, according to the technique proposed by Venturi et al. (2005). The diameter of these canals was equivalent to # 08 and 10 instruments and are set at 2, 5 and 8 mm to working length (WL). The specimens were divided into nine groups (n=15), as follow: Group I (CVA + gutta-percha Denstply), Group II (CVA + Resilon), Group III (CVA + gutta-percha Odous), Group IV (CTE + gutta-percha Dentsply), Group V (CTE + Resilon), Group VI (CTE + gutta-percha Odous), Group VII (SO + gutta-percha Obtura Flow 150), Group VIII (SO + Resilon) and Group IX (SO + gutta-percha Odous Flow). After the obturation, the samples were analyzed by radiographic and clearing methods, according to percentage of filling the lateral canals, in the three thirds. The result were submitted to the Kruskal-Wallis test at 5% significance level, according to specific intra-group evaluations: CVA (Groups I, II and III), CTH (Groups IV, V and VI), SO (Groups VII, VIII and IX) and Resilon (Groups II, V and VIII). CVA and CTH assessments showed that the Resilon has great ability to fill lateral canals in the two tests, compared to the other materials, in the apical and middle thirds (p < 0.05). As for SO evaluation, all materials showed good filling capacity of the lateral canals in all thirds, except in the cervical third where Resilon was better by radiographic analysis (extension and area) and in the cervical and middle thirds for clearing analysis (extension), in relation to gutta-percha Obtura Flow 150 (p < 0.05). The assessment of Resilon groups showed no difference among the three techniques, which show high percentage of filling lateral canals. Based on these results it was concluded that Resilon is suitable alternative to be used as a solid filling material in the evaluated techniques
Asunto(s)
Estadísticas no Paramétricas , Gutapercha , Materiales de Obturación del Conducto Radicular , Obturación del Conducto RadicularRESUMEN
Objetivo: o objetivo desse estudo in vivo foi avaliar a influência da infiltração coronária no reparo apical de dentes de cães que receberam curativo de demora com hidróxido de cálcio e foram mantidos, ou não, em contato com o meio bucal. Métodos: após o preparo biomecânico e preenchimento com pasta de hidróxido de cálcio, 26 canais foram divididos aleatoriamente em dois grupos experimentais (Grupo 1 = selamento coronário com material restaurador temporário; Grupo 2 = não selados). Os animais foram sacrificados após 7 dias e os espécimes foram preparados para análise histológica.Resultados: em ambos os grupos, os resultados foram semelhantes, células inflamatórias não estavam presentes no tecido apical ou no cemento. Além disso, observou-se necrose na superfície do terço coronário do coto pulpar em contato com o hidróxido de cálcio, e microrganismos foram observados apenas em contato com resíduos que estavam presentes na câmara pulpar dos espécimes sem selamento, mas não no canal radicular. Conclusão: concluiu-se que o hidróxido de cálcio utilizado como curativo impediu a contaminação do canal radicular e manteve seu mecanismo de ação nos tecidos apicais, mesmo sem selamento coronário, por um período de 7 dias
Asunto(s)
Hidróxido de Calcio , Filtración Dental , Endodoncia/métodos , Factores de TiempoRESUMEN
Foi propósito deste trabalho observar o processo de reparo de dentes de cães após obturação dos canais com dois cimentos diferentes, fazendo ou não a patência apical. Após uma sobreinstrumentação, os canais receberam um curativo de uma solução de corticosteróide-antibiótico por 7 dias, com o objetivo de obter invaginação de tecido conjuntivo para dentro dos canais. Após esse período, esse tecido foi totalmente removido em metade dos casos (grupos com patência apical) e preservados no restante dos casos (grupos sem patência apical). Os canais foram obturados pela técnica da condensação lateral empregando um cimento a base de hidróxido de cálcio (Sealer Plus) ou um cimento de Grossman (Fill Canal). Os animais foram sacrificados por overdose anestésica 60 dias após o tratamento endodôntico e as peças anatômicas foram obtidas e preparadas para análise histológica. Os dados obtidos foram analisados com base em diversos parâmetros histomorfológicos. Os resultados foram melhores nos grupos sem patência apical (p=0,01) do que nos grupos com patência. Dentre os cimentos estudados, os melhores resultados foram observados com o cimento Sealer Plus (p=0,01). Em conclusão, tanto a patência apical (presença ou ausência) quanto o tipo de material obturador de canal influíram no processo de reparo apical de dentes de cães com polpas vitais após tratamento endodôntico. O emprego de um cimento a base de hidróxido de cálcio em dentes sem patência apical promoveu os melhores resultados, dentre as condições experimentais propostas.
Asunto(s)
Animales , Perros , Materiales de Obturación del Conducto Radicular/farmacología , Obturación del Conducto Radicular/métodos , Ápice del Diente/fisiología , Análisis de Varianza , Sulfato de Bario/farmacología , Bismuto/farmacología , Boratos/farmacología , Hidróxido de Calcio/farmacología , Combinación de Medicamentos , Cemento Dental/efectos de los fármacos , Pulpa Dental/fisiología , Eugenol/farmacología , Ligamento Periodontal/efectos de los fármacos , Resinas Sintéticas/farmacología , Estadísticas no Paramétricas , Cicatrización de Heridas/efectos de los fármacos , Óxido de Zinc/farmacologíaRESUMEN
O objetivo do presente trabalho foi analisar a influência do emprego de tampão de MTA na melhora do selamento em obturações endodônticas. Vinte e seis dentes uniradiculados que foram abertos, realizou-se a ondontometria e efetuou-se a instrumentação, padronizando-se o forame até a lima tipo K#30, e então, confeccionou-se o batente apical com Lima tipo K #50, procedendose os escalonamento até a lima tipo K #80. Durante todo preparo empregou-se o hipoclorito de sódio a 1% e ao final EDTA por 3 minutos e irrigação final com solução fisiológica. Após a instrumentação, os dentes foram impermeabilizados e divididos em dois grupos. No grupo 1 realizou-se um tampão de 3mm de MTA e após 24 horas realizou-se a obturação. O grupo 2 efetuou-se a obturação foi feita sem emprego de tampão. O cimento empregado para a obturação foi o AH Plus.Finalizada as obturações, as coroas foram seladas e os dentes imersos em Rhodamina a 1% durante 72 horas. Concluído esse período, os dentes foram removidos do corante, lavados, raspados e seccionados no sentido vestíbulo lingual. A hemisecção foi digitalizada conjuntamente com um régua e a infiltração mensurada no Image Tools 3.1. Os resultados mostraram que a média de infiltração no grupo com tampão foi de1,69mm, enquanto que no grupo 2 foi de 1,41mm. No confronto estatístico pelo teste de Mann Whitney, não houve diferença significante. Concluiu-se que o tampão de MTA não melhorou a capacidade seladora in vitro de obturações endodônticas.
The objective of this present work was to analyze MTAs influence in the sealing improvement of endodontic obturations. Twenty-six unirooted teeth were open, it was done an ondometry and it was done the instrumentation, standardizing the pit up to the file K#30, and then, it was made the apical surfline with file K#50, proceeding to the staggering up to file K#80. During all the preparation sodium hypochlorite was applied at 1% and at the EDTAs end for three minutes and a final irrigation with physiologic solution. After the instrumentation the teeth were waterproofed and divided in two groups. In the group one it was done the 3mm MTA and subsequently to twentyfour hours the obturation was done. The group two the obturation was done without MTA. The cement used was AH Plus. When the obturations were finished, the crowns were sealed and the teeth were immersed in Rhodamine at 1% for seventy-two hours. Once that period was concluded, the teeth were removed from the dyeing, washed, rubbed out and sectioned to the direction of the tongue hall. The hemi-section was digitalized altogether with a rule and measured infiltration in the computer program Image Tools version 3.1. The results showed the the average infiltraton at the MTA group was 1,69mm, and in the group two was 1,41mm. at the statistic confrontation by Mann Whitneys test, there was any meaningful difference. It was concluded that MTA didnt improve the sealing capacity of endodontic obturations in the in vitro test.
Asunto(s)
Cemento de Óxido de Zinc-Eugenol/química , Filtración Dental/diagnóstico , Obturación del Conducto Radicular , Ápice del Diente , Estadísticas no ParamétricasRESUMEN
O presente trabalho teve como objetivo analisar a influencia do preparo cervical com dois instrumentos diferentes na determinação do diâmetro anatômico em incisivos inferiores. E Foram empregados 20 incisivos inferiores, que foram abertos e com um instrumento 10 penetrouse até a abertura foraminal para determinação do comprimento real do dente, numerando-se de 1 a 20 e anotando-se os comprimento e subtraindo-se 1mm obteve-se o comprimento real de trabalho (CRT). Posteriormente, foi estipulado o diâmetro anatômico. Após determinar o diâmetro de cada dente, os mesmos foram divididos em dois grupos de 10, sendo que no grupo 1 realizou-se o preparo cervical com La Axxess 35/06 enquanto que no grupo 2 empregou-se o CP Drill para preparo cervical utilizando-se o 30/18 em baixa rotação penetrando-se 4 mm a menos do comprimento de trabalho. Após o preparo cervical, determinou-se novamente o diâmetro anatômico. Os resultados mostraram que para o grupo 1 a média de diâmetro antes do preparo foi de 0,16mm e após foi de 0,26mm, enquanto que para o grupo 2 a média antes foi de 0,18mm e após 0,27mm. Na comparação pelo teste T-pareado houve diferença significante entre o diâmetro antes e após para ambos os grupos. Na comparação da diferença do diâmetro entre os dois instrumentos empregados o preparo cervical, não houve diferença significante. Concluiu-se que o preparo cervical interfere significantemente na determinação do diâmetro anatômico e o tipo de instrumento empregado no preparo apresentam resultados similares.
The objective of this paper was evaluate the influence of cervical preflaring with two instruments at the values of anatomic diameter. Twenty teeth were open and with a file 06 was determined the canal lenght and 1mm of the ápices was stipulated the working lenght. The teeth were numbered and the anatomical diameter was determined. After the teeth were divided into two groups in function the isntrument used at cervical preflaring: group 1: La Axxess; group 2: CP Drill. Afterly the cervical preflaring the anatomic diameter was newly measured. The results showed that the diameter before cervical preflaring was 0,16mm to La Axxess group and 0,18mm to CP drill group. The values after preflaring was 0,26mm to La Axxess group and 0,27mm to CP Drill group. There were significante differences (P<0,05) at the comparison of the diameter before and after cervical preflaring. There wasnt significant differences at the comparisons between the two groups. I was concluded that the cervical preflaring influenced sgnificantly at the anatomic diameter determination. The kind of instruments didnt interfere at anatomic diameter.