Individually Dispersed Gold Nanoshell-Bearing Cellulose Nanocrystals with Tailorable Plasmon Resonance.

Cellulose nanocrystals (CNCs) can be attractive templates for the generation of functional inorganic/organic nanoparticles, given their fine sizes, aspect ratios, and sustainable worldwide availability in abundant quantities. Here, we present for the first time a scalable, surfactant-free, tailorable wet chemical process for converting commercially available CNCs into individual aspected gold nanoshell-bearing particles with tunable surface plasmon resonance bands. Using a rational cellulose functionalization approach, stable suspensions of positively charged CNCs have been generated. Continuous, conductive, nanocrystalline gold coatings were then applied to the individual, electrostatically stabilized CNCs via decoration with 1-3 nm diameter gold particles followed by electroless gold deposition. Optical analyses indicated that these core-shell nanoparticles exhibited two surface plasmon absorbance bands, with one located in the visible range (near 550 nm) and the other at near infrared (NIR) wavelengths. The NIR band possessed a peak maximum wavelength that could be tuned over a wide range (1000-1300 nm) by adjusting the gold coating thickness. The bandwidth and wavelength of the peak maximum of the NIR band were also sensitive to the particle size distribution and could be further refined by fractionation using viscosity gradient centrifugation.

Post-sulfonation of cellulose nanofibrils with a one-step reaction to improve dispersibility.

Cellulose nanofibrils (CNF) were sulfonated and the dispersion quality was compared to unfunctionalized and 2,2,6,6-tetramethylpiperdine-1-oxyl radical (TEMPO) post-oxidation treatment of existing CNF (mechanically fibrillated pulp). A post-sulfonation treatment on existing CNF in chlorosulfonic acid and dimethylformamide (DMF) resulted in sulfonated CNF that retained a fibril-like morphology. There was a small decrease in the cellulose crystallinity index for the sulfonated CNF, but this was much lower than the reported regioselective oxidative bisulfite pretreatment method used to make sulfonated CNF. The current approach was extremely quick, and 5min of reaction time was sufficient to result in significant improvements in dispersibility compared to unfunctionalized CNF. The sulfonated CNF and TEMPO oxidized CNF had better dispersibility compared to the unfunctionalized CNF when dispersed in DMF and water, and in many cases the sulfonated CNF had better dispersibility than the TEMPO CNF. It was found that when CNF was dispersed in DMF the TEMPO CNF formed carboxyl dimethylammonium groups, while the sulfonated CNF formed formate groups.