Positive Synergistic Effect of Adhesives and Resin Cements Containing an Iodonium Salt on Bonding of Fiber Posts.

PURPOSE: To evaluate the push-out bond strength (PBS) of glass-fiber posts (GFP) in different root canal zones (cervical, middle, and apical), bonded with experimental simplified adhesives (ESAs) containing different initiator systems (camphorquinone [CQ] or phenylpropanodione [PPD]) with or without diphenyl iodonium hexafluorophosphate (DPI), in combination with a DPI-containing composite cement. MATERIALS AND METHODS: ESA blends were prepared with bisphenol glycidyl methacrylate (bis-GMA), triethylene glycol dimethacrylate (TEG-DMA), 1,3-glycerol dimethacrylate (GDMA), 2-hydroxyethyl methacrylate (HEMA), and ethanol, then divided into 12 experimental groups (n = 10) according to the initiator systems (CQ, PPD, or CQ + PPD) and the presence or absence of DPI. The roots of 120 extracted bovine incisors were prepared with #5 Largo drills and the GFP were cemented with each ESA and experimental composite cements containing 0.05 mol% of DPI. The push-out bond strength (PBS) test was performed after 24 h of storage. Failure patterns were analyzed under a stereomicroscope. Data were analyzed with split-plot two-way ANOVA and Tukey's test (α = 0.05). RESULTS: PBS was significantly higher for DPI-containing ESAs in all regions evaluated, with the group containing 0.5 CQ + 1 PPD + 0.5 DPI exhibiting the highest PBS. There was no statistically signficant difference among groups without DPI. Most failures were classified as adhesive at the cement-dentin interface. CONCLUSIONS: The combination of an adhesive and a composite cement containing DPI salt can improve GFP bonding to root dentin, even in the apical region.

Influence of ethanol on dentin roughness, surface free energy, and interaction between AH Plus and root dentin.

This study aimed to evaluate the influence of different ethanol concentrations on dentin roughness, surface free energy, and contact angle between AH Plus and the root canal dentin. One hundred human maxillary anterior teeth were split longitudinally and 200 dentin specimens were polished to make the surface flatter and smoother. An acrylic bar was positioned between two dentin specimens and impression material was added to create a block, simulating an instrumented root canal space. Specimens were removed from the mold and cleaned in an ultrasonic bath for 10 min. Thereafter, dentin specimens were divided into four groups (n = 50) according to the drying methods used: a) wet: vacuum only, b) paper points: vacuum + absorbent paper points, c) 70% alcohol: 70% alcohol (1 min) + vacuum + absorbent paper points, and d) 100% alcohol: 100% alcohol (1 min) + vacuum + absorbent paper points. A rugosimeter and a goniometer were used to verify the roughness (Ra) and to measure the surface free energy and the contact angle between the AH Plus sealer and the root canal dentin. ANOVA and Tukey tests (α = 0.05) were used for statistical analysis. The 70% and 100% ethanol groups showed significantly decreased roughness as well as increased surface free energy in the root canal dentin when compared to the wet and paper point groups. In addition, ethanol significantly reduced the contact angle between the AH Plus sealer and the root canal dentin. Ethanol solutions (70% and 100%) provide better wettability of AH Plus sealer on dentin surfaces.

Effect of ethanol-conditioned dentine on sealer penetration into dentinal tubules: a confocal microscopy study

Aim: The aim of this study was to evaluate the effect of ethanol-conditioned dentin on endodontic sealer penetration into dentinal tubules by confocal laser scanning microscopy (CLSM). Methods: Forty human maxillary anterior teeth were instrumented and divided into four groups (n = 10) according to the drying methods: 1) wet: vacuum only, 2) paper points: vacuum + absorbent paper points, (3) 70% ethanol: 70% ethanol (1 min) + vacuum + absorbent paper points, and (4) 100% ethanol: 100% ethanol (1 min) + vacuum + absorbent paper points. All root canals were filled with resin-based endodontic sealer. Four sections from each third (cervical, middle, and apical) were examined by CLSM. Root canal wall perimeter infiltrated by sealer, maximum depth of sealer penetration, percentage of penetrated area, and fluorescence intensity of rhodamine B were measured. Statistical analysis was performed by analysis of variance and Tukey's tests (α = 0.05). Results: No statistical difference was found when percentage of root canal wall coverage infiltrated by sealer were compared. The groups in which ethanol solutions were used presented greater depth of sealer penetration, higher percentage of penetrated area, and higher fluorescence intensity of rhodamine B (p< 0.05) when compared with the wet and paper point groups. Overall, 100% ethanol produced better results than 70% ethanol, except for rhodamine B intensity (cervical third). In addition, the absorbent paper points drying method behaved better than did vacuum only group, except for rhodamine B intensity (apical third). Conclusion: Ethanol-conditioned dentin improved the penetration of resin-based sealer into dentinal tubules, especially at the concentration of 100%

Influence of ethanol on dentin roughness, surface free energy, and interaction between AH Plus and root dentin

Abstract This study aimed to evaluate the influence of different ethanol concentrations on dentin roughness, surface free energy, and contact angle between AH Plus and the root canal dentin. One hundred human maxillary anterior teeth were split longitudinally and 200 dentin specimens were polished to make the surface flatter and smoother. An acrylic bar was positioned between two dentin specimens and impression material was added to create a block, simulating an instrumented root canal space. Specimens were removed from the mold and cleaned in an ultrasonic bath for 10 min. Thereafter, dentin specimens were divided into four groups (n = 50) according to the drying methods used: a) wet: vacuum only, b) paper points: vacuum + absorbent paper points, c) 70% alcohol: 70% alcohol (1 min) + vacuum + absorbent paper points, and d) 100% alcohol: 100% alcohol (1 min) + vacuum + absorbent paper points. A rugosimeter and a goniometer were used to verify the roughness (Ra) and to measure the surface free energy and the contact angle between the AH Plus sealer and the root canal dentin. ANOVA and Tukey tests (α = 0.05) were used for statistical analysis. The 70% and 100% ethanol groups showed significantly decreased roughness as well as increased surface free energy in the root canal dentin when compared to the wet and paper point groups. In addition, ethanol significantly reduced the contact angle between the AH Plus sealer and the root canal dentin. Ethanol solutions (70% and 100%) provide better wettability of AH Plus sealer on dentin surfaces.