RESUMEN
Sodium niobate (NaNbO3) attracts attention for its great potential in a variety of applications, for instance, due to its unique optical properties. Still, optimization of its synthetic procedures is hard due to the lack of understanding of the formation mechanism under hydrothermal conditions. Through in situ X-ray diffraction, hydrothermal synthesis of NaNbO3 was observed in real time, enabling the investigation of the reaction kinetics and mechanisms with respect to temperature and NaOH concentration and the resulting effect on the product crystallite size and structure. Several intermediate phases were observed, and the relationship between them, depending on temperature, time, and NaOH concentration, was established. The reaction mechanism involved a gradual change of the local structure of the solid Nb2O5 precursor upon suspending it in NaOH solutions. Heating gave a full transformation of the precursor to HNa7Nb6O19·15H2O, which destabilized before new polyoxoniobates appeared, whose structure depended on the NaOH concentration. Following these polyoxoniobates, Na2Nb2O6·H2O formed, which dehydrated at temperatures ≥285 °C, before converting to the final phase, NaNbO3. The total reaction rate increased with decreasing NaOH concentration and increasing temperature. Two distinctly different growth regimes for NaNbO3 were observed, depending on the observed phase evolution, for temperatures below and above ≈285 °C. Below this temperature, the growth of NaNbO3 was independent of the reaction temperature and the NaOH concentration, while for temperatures ≥285 °C, the temperature-dependent crystallite size showed the characteristics of a typical dissolution-precipitation mechanism.
RESUMEN
Material nucleation processes are poorly understood; nevertheless, an atomistic understanding of material formation would aid in the design of material synthesis methods. Here, we apply in situ X-ray total scattering experiments with pair distribution function (PDF) analysis to study the hydrothermal synthesis of wolframite-type MWO4 (M : Mn, Fe, Co, Ni). The data obtained allow the mapping of the material formation pathway in detail. We first show that upon mixing of the aqueous precursors, a crystalline precursor containing [W8O27]6- clusters forms for the MnWO4 synthesis, while amorphous pastes form for the FeWO4, CoWO4 and NiWO4 syntheses. The structure of the amorphous precursors was studied in detail with PDF analysis. Using database structure mining and an automated modelling strategy by applying machine learning, we show that the amorphous precursor structure can be described through polyoxometalate chemistry. A skewed sandwich cluster containing Keggin fragments describes the PDF of the precursor structure well, and the analysis shows that the precursor for FeWO4 is more ordered than that of CoWO4 and NiWO4. Upon heating, the crystalline MnWO4 precursor quickly converts directly to crystalline MnWO4, while the amorphous precursors transform into a disordered intermediate phase before the crystalline tungstates appear. Our data show that the more disordered the precursor is, the longer the reaction time required to form crystalline products, and disorder in the precursor phase appears to be a barrier for crystallization. More generally, we see that polyoxometalate chemistry is useful when describing the initial wet-chemical formation of mixed metal oxides.
RESUMEN
High-entropy materials (HEMs) represent a new class of solid solutions containing at least five different elements. Their compositional diversity makes them promising as platforms for the development of functional materials. We synthesized new HEMs in a mullite-type structure and present five compounds, i.e., Bi2(Al0.25Ga0.25Fe0.25Mn0.25)4O9 and A2Mn4O10 with variations of A = Nd, Sm, Y, Er, Eu, Ce, and Bi, demonstrating the vast accessible composition space. By combining scattering, microscopy, and spectroscopy techniques, we show that our materials are mixed solid solutions. Remarkably, when following their crystallization in situ using X-ray diffraction and X-ray absorption spectroscopy, we find that the HEMs form through a metastable amorphous phase without the formation of any crystalline intermediates. We expect that our synthesis is excellently suited to synthesizing diverse HEMs and therefore will have a significant impact on their future exploration.