RESUMEN
Antibacterial coatings on biomedical instruments are of great interest because they can suppress bacterial colonization on these instruments. In this study, antibacterial polymeric thin coatings were deposited on teflon substrates using atmospheric pressure plasma polymerization from a propane-butane mixture. The plasma polymerization was performed by means of surface dielectric barrier discharge burning in nitrogen at atmospheric pressure. The chemical composition of plasma polymerized propane-butane films was studied by energy-dispersive X-ray spectroscopy (EDX) and FTIR. The film surface properties were studied by SEM and by surface energy measurement. The EDX analysis showed that the films consisted of carbon, nitrogen and oxygen from ambient air. The FTIR analysis confirmed, in particular, the presence of alkyl, nitrile, acetylene, imide and amine groups. The deposited films were hydrophilic with a water contact angle in the range of 13-23°. The thin film deposited samples were highly active against both S. aureus and E. coli strains in general. On the other hand, the films were cytocompatible, reaching more than 80% of the cell viability threshold compared to reference polystyrene tissue.
Asunto(s)
Propano , Staphylococcus aureus , Escherichia coli , Nitrógeno , Presión Atmosférica , Antibacterianos/farmacología , ButanosRESUMEN
Poly(2-oxazoline) is a promising new class of polymeric materials due to their antibiofouling properties and good biocompatibility. Poly(2-oxazoline) coatings can be deposited on different substrates via plasma polymerization, which can be more advantageous than other coating methods. The aim of this study is to deposit poly(2-oxazoline) coatings using a surface dielectric barrier discharge burning in nitrogen at atmospheric pressure using 2-methyl-2-oxazoline and 2-ethyl-2-oxazoline vapours as monomers and compare the film properties. For the comparison, the antibacterial and cytocompatibility tests were peformed according to ISO norms. The antibacterial tests showed that all the deposited films were highly active against Staphylococcus aureus and Escherichia coli bacteria. The chemical composition of the films was studied using FTIR and XPS, and the film surface's properties were studied using AFM and surface energy measurement. The cytocompatibility tests showed good cytocompatibility of all the deposited films. However, the films deposited from 2-methyl-2-oxazoline exhibit better cytocompatibility. This difference can be explained by the different chemical compositions and surface morphologies of the films deposited from different monomers.
Asunto(s)
Antibacterianos , Oxazoles , Polimerizacion , Oxazoles/farmacología , Oxazoles/química , Antibacterianos/farmacología , Escherichia coliRESUMEN
In this study, furcellaran (FUR) obtained from Furcellaria lumbricalis was firstly employed for sulfation via various methods, including SO3-pyridine (SO3âPy) complex in different aprotic solvents, chlorosulfonic acid and sulfuric acid with a "coupling" reagent N,N'-Dicyclohexylcarbodiimide. Structural characterization through FT-IR, GPC, XPS and elemental analyses confirmed the successful synthesis of 6-O-sulfated FUR derivates characterized by varying degrees of sulfation (DS) ranging from 0.15 to 0.91 and molecular weight (Mw) spanning from12.5 kDa to 2.7 kDa. In vitro clotting assays, partial thromboplastin time (aPTT), thrombin time (TT), and prothrombin time (PT) underscored the essential role of sulfate esters in conferring anticoagulant activity whereas FUR prepared via chlorosulfonic acid with DS of 0.91 reached 311.4 s in aPPT showing almost 4-fold higher anticoagulant activity than native FUR at the concentration 2 mg/mL. MTT test showed all tested samples decreased cell viability in a dose dependent manner while all of them are non-cytotoxic up to the concentration of 0.1 mg/mL. Furthermore, sulfated derivates deposited onto polyethylene terephthalate surface presented substantial decrease in platelet adhesion, as well as absence of the most activated platelet stages. These findings support the pivotal role of O-6 FUR sulfates in enhancing hemocompatibility and provide valuable insights for a comparative assessment of effective sulfating approaches.
Asunto(s)
Alginatos , Anticoagulantes , Coagulación Sanguínea , Gomas de Plantas , Ácidos Sulfónicos , Anticoagulantes/farmacología , Espectroscopía Infrarroja por Transformada de Fourier , Tiempo de Tromboplastina Parcial , Sulfatos/químicaRESUMEN
Polyoxazoline thin coatings were deposited on glass substrates using atmospheric pressure plasma polymerization from 2-ethyl-2-oxazoline vapours. The plasma polymerization was performed in dielectric barrier discharge burning in nitrogen at atmospheric pressure. The thin films stable in aqueous environments were obtained at the deposition with increased substrate temperature, which was changed from 20 ∘C to 150 ∘C. The thin film deposited samples were highly active against both S. aureus and E. coli strains in general. The chemical composition of polyoxazoline films was studied by FTIR and XPS, the mechanical properties of films were studied by depth sensing indentation technique and by scratch tests. The film surface properties were studied by AFM and by surface energy measurement. After tuning the deposition parameters (i.e., monomer flow rate and substrate temperature), stable films, which resist bacterial biofilm formation and have cell-repellent properties, were achieved. Such antibiofouling polyoxazoline thin films can have many potential biomedical applications.
RESUMEN
Polyoxazolines are a new promising class of polymers for biomedical applications. Antibiofouling polyoxazoline coatings can suppress bacterial colonization of medical devices, which can cause infections to patients. However, the creation of oxazoline-based films using conventional methods is difficult. This study presents a new way to produce plasma polymerized oxazoline-based films with antibiofouling properties and good biocompatibility. The films were created via plasma deposition from 2-methyl-2-oxazoline vapors in nitrogen atmospheric pressure dielectric barrier discharge. Diverse film properties were achieved by increasing the substrate temperature at the deposition. The physical and chemical properties of plasma polymerized polyoxazoline films were studied by SEM, EDX, FTIR, AFM, depth-sensing indentation technique, and surface energy measurement. After tuning of the deposition parameters, films with a capacity to resist bacterial biofilm formation were achieved. Deposited films also promote cell viability.