RESUMEN
Geopolymers have been proposed as a green alternative to Portland cement with lowered carbon footprints. In this work, a geopolymeric mortar obtained using waste materials is studied. Fly ash, a waste generated by coal combustion, is used as one of the precursors, and waste glass as lightweight aggregates (LWAs) to improve the thermal performance of the mortar. The experimental study investigates the effect of varying the alkali activating solution (AAS) amount on the workability, compressive strength, and thermal conductivity of the mortar. Indeed, AAS represents the most expensive component in geopolymer production and is the highest contributor to the environmental footprint of these materials. This research starts by observing that LWA absorbs part of the activating solution during mixing, suggesting that only a portion of the solution effectively causes the geopolymerization reactions, the remaining part wetting the aggregates. Three mixes were investigated to clarify these aspects: a reference mix with a solution content calibrated to have a plastic consistency and two others with the activating solution reduced by the amount absorbed by aggregates. In these cases, the reduced workability was solved by adding the aggregates in a saturated surface dry state in one mix and free water in the other. The experimental results evidenced that free water addiction in place of a certain amount of the solution may be an efficient way to improve thermal performance without compromising the resistance of the mortar. The maximum compressive strength reached by the mortars was about 10 MPa at 48 days, a value in line with those of repair mortars. Another finding of the experimental research is that UPV was used to follow the curing stages of materials. Indeed, the instrument was sensitive to microstructural changes in the mortars with time. The field of reference of the research is the rehabilitation of existing buildings, as the geopolymeric mortars were designed for thermal and structural retrofitting.
RESUMEN
UPV as non-destructive technique can effectively contribute to the low invasive in situ analysis and diagnosis of masonry elements related to the conservation, rehabilitation and strengthening of the built heritage. The use of non-destructive and non-invasive techniques brings all the times many advantages in diagnostic activities on pre-existing buildings in terms of sustainability; moreover, it is a strong necessity with respect to the conservation constraints when dealing with the historical-architectural heritage. In this work laboratory experiments were carried out to investigate the effectiveness of ultrasonic pulse velocity (UPV) in evaluating physical and mechanical properties of Lecce stone, a soft and porous building limestone. UPV and selected physical-mechanical parameters such as density and uniaxial compressive strength (UCS) were determined. Factors such as anisotropy and water presence that induce variations on the ultrasonic velocity were also assessed. Correlations between the analysed parameters are presented and discussed. The presence of water greatly affected the values of the analysed parameters, leading to a decrease of UPV and to a strong reduction of the compressive strength. A discussion of the role of the water on these results is provided. Regression analysis showed a reliable linear correlation between UPV and compressive strength, which allows a reasonable estimation of the strength of Lecce stone by means of non-destructive testing methods such as the ultrasonic wave velocity. Low correlation between UPV and density was found, suggesting that other factors than density, related to the fabric and composition, also influence the response of the selected stone to the UPV. They have no influence on the UCS, that instead showed to be highly correlated with the packing density.