This study aims to increase the pozzolanic reactivity of metakaolin (MK) in Portland cement (PC) blends by adding additional calcium hydroxide (CH_add) to the initial mixture. Cement paste samples were prepared with PC, MK and water with a water-to-binder ratio of 0.6. Cement replacement ratios were chosen from 5 to 40 wt.% MK. For higher replacement ratios, i.e., 20, 30 and 40 wt.% MK, CH_add was included in the mixture. CH_add-to-MK ratios of 0.1, 0.25 and 0.5 were investigated. Thermogravimetric analysis (TGA) was carried out to study the pozzolanic reactivity after 1, 7, 28 and 56 days of hydration. A modified mass balance approach was used to normalize thermogravimetric data and to calculate the calcium hydroxide (CH) consumption of samples with CH_add. Results showed that, without CH_add, a replacement ratio of 30 wt.% or higher results in the complete consumption of CH after 28 days at the latest. In these samples, the pozzolanic reaction of MK turned out to be restricted by the amount of CH available from the cement hydration. The increased amount of CH in the samples with CH_add resulted in an enhanced pozzolanic reaction of MK as confirmed by CH consumption measurements from TGA.
RESUMEN
The reactivity of supplementary cementitious materials (SCMs) is a key issue in the sustainability of cement-based materials. In this study, the effect of drying with isopropanol and acetone as well as the interpretation of thermogravimetric data on the results of an R3 test for evaluation of the SCM pozzolanic reaction were investigated. R3 samples consisting of calcium hydroxide, potassium hydroxide, potassium sulphate, water, and SCM were prepared. Besides silica fume, three different types of calcined clays were investigated as SCMs. These were a relatively pure metakaolin, a quartz-rich metakaolin, and a mixed calcined clay, where the amount of other types of clays was two times higher than the kaolinite content. Thermogravimetric analysis (TGA) was carried out on seven-day-old samples dried with isopropanol and acetone to stop the reaction processes. Additional calorimetric measurement of the R3 samples was carried out for evaluation of the reaction kinetics. Results show that drying with isopropanol is more suitable for analysis of R3 samples compared to acetone. The use of acetone results in increased carbonation and TGA mass losses until 40 (isothermal drying for 30 min) and 105 °C (ramp heating), indicating that parts of the acetone remain in the sample, causing problems in the interpretation of TGA data. A mass balance approach was proposed to calculate calcium hydroxide consumption from TGA data, while also considering the amount of carbonates in the sample and TGA data corrections of original SCMs. With this approach, an improvement of the linear correlation of TGA results and heat release from calorimetric measurement was achieved.