Liquid Exfoliation and Electrochemical Properties of WS2 Nanosheets.

Commercial WS2 powders were exfoliated in sodium dodecyl sulfate solution with a combination of ball-milling and sonication. WS2 nanosheets can be uniformly dispersed in the solution. The layers and thicknesses of WS2 nanosheets could be tailored via changing the ball-milling speed. The effects of the ball-milling speed on crystallinity and morphology of the samples were analyzed. The results show that the layer structure of WS2 nanosheets is destroyed and the crystallinity is decreased with increase of the ball-milling rate. The monolayer WS2 nanosheets at 200 rpm are obtained, which are mesoporous with the specific surface area as 5.419 m2 g-1. The specific capacitance and charge/discharge efficiency of WS2 nanosheets at 200 rpm are better than those of other samples. Its specific capacitance under the scanning rate of 20 mV s-1 and the current density of 0.5 A g-1 are 13.46 F g-1 and 22.50 F g-1, respectively. The charge/discharge curve of WS2 nanosheets at 200 rpm is a symmetrical triangle, which shows rapid charge and slow discharge. It means that WS2 nanosheets at 200 rpm has good electrochemical reversibility. The load transfer resistance and the internal series resistance of this sample are 84.60 Ω and 4.18 Ω, respectively.

Myosin phosphatase target subunit 1 (MYPT1) regulates the contraction and relaxation of vascular smooth muscle and maintains blood pressure.

Myosin light chain phosphatase with its regulatory subunit, myosin phosphatase target subunit 1 (MYPT1) modulates Ca(2+)-dependent phosphorylation of myosin light chain by myosin light chain kinase, which is essential for smooth muscle contraction. The role of MYPT1 in vascular smooth muscle was investigated in adult MYPT1 smooth muscle specific knock-out mice. MYPT1 deletion enhanced phosphorylation of myosin regulatory light chain and contractile force in isolated mesenteric arteries treated with KCl and various vascular agonists. The contractile responses of arteries from knock-out mice to norepinephrine were inhibited by Rho-associated kinase (ROCK) and protein kinase C inhibitors and were associated with inhibition of phosphorylation of the myosin light chain phosphatase inhibitor CPI-17. Additionally, stimulation of the NO/cGMP/protein kinase G (PKG) signaling pathway still resulted in relaxation of MYPT1-deficient mesenteric arteries, indicating phosphorylation of MYPT1 by PKG is not a major contributor to the relaxation response. Thus, MYPT1 enhances myosin light chain phosphatase activity sufficient for blood pressure maintenance. Rho-associated kinase phosphorylation of CPI-17 plays a significant role in enhancing vascular contractile responses, whereas phosphorylation of MYPT1 in the NO/cGMP/PKG signaling module is not necessary for relaxation.

Is CuO Suitable for Improving the Electrochemical Properties of g-C3N4?

G-C3N4 has a bright application prospect as an electrode material of supercapacitors, which makes it a concern. In order to increase the specific capacitance of g-C3N4, we consider to combine it with a metal oxide with high theoretical specific capacitance and utilize the synergistic effect. As a common metal oxide, CuO has the characteristics of high theoretical capacitance, high chemical stability, simple preparation and environmental friendliness. A composite containing CuO nanobelts and graphitic C3N4 (g-C3N4) was successfully synthesized by a chemical precipitation method. Various testing methods were used to explore its composition, microstructure and electrochemical properties to discuss whether CuO is suitable for improving the electrochemical properties of g-C3N4.