Characterization of a Novel TiF4 Inclusion Complex and in vitro Evaluation of Its Effect on Inhibiting Enamel Demineralization.

INTRODUCTION: Titanium tetrafluoride (TiF4) is an anticariogenic agent with high remineralizing potential. However, the acidic pH of TiF4 solution can limit its clinical application. The present study aimed to prepare and characterize a new TiF4-dendrimer inclusion complex and evaluate its ability to inhibit enamel demineralization under pH cycling conditions. METHODS: PEG-citrate dendrimer and TiF4-dendrimer inclusion complex were synthesized and their molecular structures were evaluated using Fourier-transform Infrared Spectroscopy (FTIR), Hydrogen Nuclear Magnetic Resonance (HNMR), and Liquid Chromatography-Mass Spectrometry (LC-MS) tests. Forty-eight enamel samples were prepared and randomly divided into four groups: distilled water (negative control), TiF4 solution (T), dendrimer solution (D), and TiF4-dendrimer solution (TD). The microhardness of the samples was measured initially. Next, the samples underwent pH cycling, were exposed to the solutions, the microhardness was measured again, and microhardness loss was calculated. EDX analysis was performed on the surface and cross-sectional segments of the samples. RESULTS: The microhardness loss was significantly higher in control (-65.1 ± 6.0) compared to other groups. No significant difference was observed between T (-47.9 ± 5.6) and D (-41.7 ± 12.0) and also D and TD (-40.5 ± 9.4) in this regard. Microhardness loss was significantly higher in T compared to TD group. The TD samples showed similar fluoride and titanium content in both surface and subsurface regions, while the T group had higher concentrations in the surface region. Moreover, the TD solution had a higher pH of 3.4 compared to the T solution's pH of 1.1. CONCLUSION: No significant difference was observed between the efficacy of TiF4-dendrimer and TiF4 solution in inhibiting demineralization while TiF4-dendrimer solution had the added advantage of having a higher pH.

Enamel Caries Lesion Depth Obtained by Optical Coherence Tomography and Transverse Microradiography: A Comparative Study.

INTRODUCTION: Visual imaging of subsurface caries lesions is of vital interest in dentistry, which can be obtained by invasive radiography technique as well as by available non-destructive imaging approaches. Thus, as a first step toward the development of a new innovative approach, Spectral-domain optical coherence tomography (SD-OCT) was applied to detect the lesion depth in comparison to the established reference technique (transverse microradiography [TMR]). METHODS: Bovine enamel specimens were demineralized for 5 days, following previous studies. For OCT, the resulting artificial lesions were scanned three-dimensionally (SD-OCT) and semi-automated measured (CarLQuant). For TMR, specimens were sectioned and the lesion depth was manually determined (Inspektor Research System). RESULTS: The range of lesion depth detected with OCT was 24.0-174.0 µm (mouth rinse study), 18.0-178.0 µm (toothpastes study) and with TMR 59.2-198.0 µm (mouth rinse study), 33.2-133.4 µm (toothpastes study). We found a strong correlation between both methods in terms of lesion depth (Spearman rankwith outlierp < 0.001, Rho = 0.75, Spearman rankwithout outlierp = 0.001, Rho = 0.79). The two methods produce similar results (Passing-Bablok regression, 1.16). As deeper is the lesion, the smallest is the difference between both methods as indicated by Bland-Altman-plots. CONCLUSION: Especially in the case of deep lesions, the values obtained by both methods are in agreement, and OCT can potentially substitute TMR to detect and assess lesion depth with the benefit of being non-destructive.

Acquired Pellicle and Biofilm Engineering by Rinsing with Hemoglobin Solution.

INTRODUCTION: The identification of acid-resistant proteins, including hemoglobin (Hb), within the acquired enamel pellicle (AEP) led to the proposition of the "acquired pellicle engineering" concept, which involves the modification of the AEP by incorporating specific proteins, presenting a novel strategy to prevent dental demineralization. OBJECTIVE: Combining in vivo and in vitro proof-of-concept protocols, we sought to reveal the impact of AEP engineering with Hb protein on the biofilm microbiome and enamel demineralization. METHODS: In the in vivo studies, 10 volunteers, in 2 independent experiments, rinsed (10 mL,1 min) with deionized water-negative control or 1.0 mg/mL Hb. The AEP and biofilm formed along 2 or 3 h, respectively, were collected. AEP was analyzed by quantitative shotgun-label-free proteomics and biofilm by 16S-rRNA next-generation sequencing (NGS). In in vitro study, a microcosm biofilm protocol was employed. Seventy-two bovine enamel specimens were treated with (1) phosphate-buffered solution (PBS), (2) 0.12% chlorhexidine, (3) 500 ppm NaF, (4) 1.0 mg/mL Hb, (5) 2.0 mg/mL Hb, and (6) 4.0 mg/mL Hb. The biofilm was cultivated for 5 days. Resazurin, colony forming units (CFU), and transversal microradiography were performed. RESULTS: Proteomics and NGS analysis revealed that Hb increased proteins with antioxidant, antimicrobial, acid-resistance, hydroxyapatite-affinity, calcium-binding properties and showed a reduction in oral pathogenic bacteria. In vitro experiments demonstrated that the lowest Hb concentration was the most effective in reducing bacterial activity, CFU, and enamel demineralization compared to PBS. CONCLUSION: These findings suggest that Hb could be incorporated into anticaries dental products to modify the oral microbiome and control caries, highlighting its potential for AEP and biofilm microbiome engineering.

Influence of the orthodontic bonding procedure on biofilm formation.

INTRODUCTION: In orthodontics, white spot lesions are a persistent and widespread problem caused by the demineralization of buccal tooth surfaces around bonded brackets. The remaining adhesive around the brackets leads to surface roughness, which might contribute to demineralization. The present in vitro study aimed to compare a conventional and a modern adhesive system (APC Flash-Free technology) for orthodontic brackets with regard to the adhesion of Streptococcus sobrinus, a leading caries pathogen. METHODS: This in vitro study included 20 premolar teeth and compared 10 APC Flash-Free adhesive-coated ceramic brackets (FF)with 10 conventionally bonded (CB) ceramic clarity brackets. Specimens were incubated in an S. sobrinus suspension for 3 h. To evaluate the bacterial formation, samples were analysed with a scanning electron microscope (SEM). Imaging software was used to quantify and statistically compare percentage values of colonization (PVC) in both groups' adhesion and transition areas. RESULTS: We found a significant difference in biofilm formation between the groups for the adhesive and transition areas. PVC in the adhesive area was approximately 10.3-fold greater for the CB group compared with the FF group (median: 3.2 vs 0.31; P < 0.0001). For the transition area, median PVC was approximately 2.4-fold greater for the CB group compared with the FF group (median: 53.17 vs 22.11; P < 0.01). CONCLUSIONS: There was a significantly lower level of S. sobrinus formation around the FF bracket system than there was surrounding the conventionally bonded group. This study suggests that the FF adhesive bracket system can help reduce the occurrence of bacterial growth around orthodontic brackets.

Clinical and ex-vivo effect of LASERs on prevention of early-enamel caries: systematic review & meta-analyses.

To investigate the in vivo and in situ effect of different types of lasers in prevention of enamel demineralization in high caries risk cases (around orthodontic brackets, around restoration and in caries susceptible pits and fissures). PubMed was searched using the following keyword sequence; (Laser therapy OR laser irradiation OR laser application) AND (enamel caries prevention OR enamel demineralization OR enamel remineralization OR early enamel caries OR early-enamel caries OR enamel resistance OR enamel decalcification OR white spot lesions WSLs OR incipient lesion OR enamel decay OR enamel Dissolution OR enamel microhardness) AND (clinical trial OR Randomized clinical trial OR In situ study). The latest literature search was ended by "30 January 2023". PubMed was used as a primary data base for study selection. Scopus, EBSCO, and Google scholar are checked in our study after results of systematic search on PubMed. Only duplicates were found. Two meta-analyses were carried out. The first, clinical meta-analysis on incidence of white spot lesions (WSLs) following CO2 laser irradiation of enamel. The second meta-analysis on ex-vivo/in situ effect of CO2 laser on microhardness of enamel. In each meta-analysis three studies were included. Risk of bias was assessed. The search identified eight studies (four ex-vivo and four clinical trials). Regarding the clinical meta-analysis, the overall standardized mean difference was 0.21 [ 95% confidence interval (CI): 0.15-0.30, p < 0.00001]. This indicates that the incidence of new WSLs in patients who received low power CO2 laser treatment was highly significantly lower than placebo groups. The heterogeneity was considerable (I2 = 71%). In the second meta-analysis, the overall standardized mean difference was 49.55 [ 95% confidence interval (CI): 37.74, 61.37, p < 0.00001]. This indicates that microhardness of enamel receiving low power (0.4-5 W) CO2 laser irradiation is highly significantly lower than control untreated enamel. The heterogeneity was substantial (I2 = 48%). Within the limitations of this study, Low level laser therapy concept with CO2 laser seems to be effective in preventing enamel caries.Prospero registration number: CRD42023437379.

Acquired enamel pellicle and biofilm engineering with a combination of acid-resistant proteins (CaneCPI-5, StN15, and Hemoglobin) for enhanced protection against dental caries - in vivo and in vitro investigations.

OBJECTIVE: This study was designed in two-legs. In the in vivo, we explored the potential of a rinse solution containing a combination (Comb) of 0.1 mg/mL CaneCPI-5 (sugarcane-derive cystatin), 1.88 × 10- 5M StN15 (statherin-derived peptide) and 1.0 mg/mL hemoglobin (Hb) to change the protein profile of the acquired enamel pellicle(AEP) and the microbiome of the enamel biofilm. The in vitro, was designed to reveal the effects of Comb on the viability and bacterial composition of the microcosm biofilm, as well as on enamel demineralization. MATERIALS AND METHODS: In vivo study, 10 participants rinsed (10mL,1 min) with either deionized water (H2O-control) or Comb. AEP and biofilm were collected after 2 and 3 h, respectively, after rinsing. AEP samples underwent proteomics analysis, while biofilm microbiome was assessed via 16 S-rRNA Next Generation Sequencing(NGS). In vitro study, a microcosm biofilm protocol was employed. Ninety-six enamel specimens were treated with: 1)Phosphate-Buffered Solution-PBS(negative-control), 2)0.12%Chlorhexidine, 3)500ppmNaF and 4)Comb. Resazurin, colony-forming-units(CFU) and Transversal Microradiography(TMR) were performed. RESULTS: The proteomic results revealed higher quantity of proteins in the Comb compared to control associated with immune system response and oral microbial adhesion. Microbiome showed a significant increase in bacteria linked to a healthy microbiota, in the Comb group. In the in vitro study, Comb group was only efficient in reducing mineral-loss and lesion-depth compared to the PBS. CONCLUSIONS: The AEP modification altered the subsequent layers, affecting the initial process of bacterial adhesion of pathogenic and commensal bacteria, as well as enamel demineralization. CLINICAL RELEVANCE: Comb group shows promise in shaping oral health by potentially introducing innovative approaches to prevent enamel demineralization and deter tooth decay.

Pomegranate extract in polyphosphate-fluoride mouthwash reduces enamel demineralization.

OBJECTIVES: To evaluate the anti-demineralizing effect of a mouthwash comprising pomegranate peel extract (PPE 3%), sodium trimetaphosphate (TMP 0.3%), and fluoride (F 225 ppm) in an in situ study, and to assess its irritation potential in an ex vivo study. METHODS: This double-blind crossover study was conducted in four phases with 7 days each. Twelve volunteers used palatal appliances containing enamel blocks, which were subjected to cariogenic challenges. The ETF formulation (PPE + TMP + F, pH 7.0), TF formulation (TMP + F, pH 7.0), deionized water (W, pH 7.0), and essential oil commercial mouthwash (CM, 220 ppm F, pH 4.3) were dropped onto the enamel twice daily. The percentage of surface hardness loss, integrated loss of subsurface hardness, calcium, phosphorus, and fluoride in enamel and biofilms were determined. In addition, alkali-soluble extracellular polysaccharide concentrations were analyzed in the biofilms. The irritation potential was evaluated using the hen's egg chorioallantoic membrane test through the vascular effect produced during 300-s of exposure. RESULTS: ETF was the most efficacious in preventing demineralization. It also showed the highest concentrations of calcium and phosphorus in the enamel and in the biofilm, as well as the lowest amount of extracellular polysaccharides in the biofilm. In the eggs, ETF produced light reddening, whereas CM led to hyperemia and hemorrhage. CONCLUSIONS: The addition of PPE to formulations containing TMP and F increased its anti-demineralizing property, and this formulation presented a lower irritation potential than the CM. CLINICAL RELEVANCE: ETF can be a promising alternative alcohol-free mouthwash in patients at high risk of caries.

In-vitro and in-vivo comparative studies of treatment effects on enamel demineralization during orthodontic therapy: implications for clinical early-intervention strategy.

OBJECTIVES: This study aimed to investigate if CPP-ACP / infiltrating resin was superior in treating enamel demineralization during orthodontic therapy compared with fluoride varnish, in order to provide early-intervention implications for dental professionals. MATERIALS AND METHODS: In the in-vitro study, premolars were grouped into four: remineralization with fluoride varnish / CPP-ACP, sealing with infiltrating resin, and negative control. Experimental demineralization of enamel surfaces was analyzed using techniques of QLF, SEM, EDS and micro-hardness testing. An in-vivo intervention study was conducted on patients randomly assigned into three groups. At the baseline and every-3-month follow-up, QLF parameters were compared temporally and parallelly to yield potential implications for promotion in clinical practice. RESULTS: The in-vitro study performed on 48 experimental tooth surfaces demonstrated that sealing with infiltrating resin reduced enamel surface porosity and increased surface micro-hardness significantly. In the in-vivo intervention study on 163 tooth surfaces, it was suggested that for those who meet the criteria of -10 < ΔF < -6 and - 1000 < ΔQ < -20 at the baseline, all these treatment methods could achieve acceptable outcomes; with the rising of absolute values of ΔF and ΔQ, sealing with infiltrating resin showed more evident advantages. CONCLUSION: For enamel demineralization during orthodontic therapy, all the treatment methods involved in this study showed acceptable effectiveness but had respective characteristics in treatment effects. QLF parameters could be used as indicators for clinical early-intervention strategy with regards to this clinical issue. CLINICAL RELEVANCE: With QLF parameters, clinical early-intervention strategy for enamel demineralization during orthodontic therapy could be optimized.

Microbial shift of oral biofilm associated with remineralization of root dentin lesions.

PURPOSE: To examine the relationship between remineralization of incipient root dentin lesions and the presence of polymicrobial biofilms, as well as examine changes in microbial composition. METHODS: Bovine root dentin disks used as specimens for biofilm formation, were cultured using saliva from a single donor. Amsterdam Active Attachment biofilm model was used to grow biofilms. The culture medium was McBain 2005 with 0.2% sucrose and 0.4 ppm F as sodium fluoride. After cultivation for 48 hours to achieve demineralization, a control group (n=10) was obtained and the other specimens were further cultured for 336 hours in two types of remineralization culture medium, with sucrose (S+) and without sucrose (S-), through continuous anaerobic incubation (10% CO2,10% H2, 80% N2). Then half of the specimens cultured in the S- medium were transferred to the S+ medium for an additional 48 hours resulting in three experimental groups S(+) (n=10), S(-) (n=10), and S(-)de (n=10), respectively. Experiment 1: Transverse microradiography (TMR) analysis - Immediately after respective culture treatments, integrated mineral loss (IML) and lesion depth (LD) in the dentin specimens were analyzed by TMR. Experiment 2: Microbiome analysis - Sequence data of the 16S rRNA gene of each sample was obtained using MiSeq, and partial base sequences were determined. Next-generation sequencing was performed to determine the taxonomic groups of fungi present in the biofilm samples. RESULTS: Experiment 1: In the control group, formation of dentin demineralization lesions by polymicrobial species biofilms was confirmed. The S(-) group showed significantly decreased IML and shallower LD compared to the control group. The S(-)de group showed a significant increase in IML and LD compared to the S(-) group. Experiment 2: There were statistically significant differences in microbiome between the control group and each of the three experimental groups, both at the genus and species levels. A significant difference in genus was observed between the S(-) group and the S(-)de group. CLINICAL SIGNIFICANCE: The confirmation of the possibility of microbial shift occurring during the remineralization process of root caries will lead to the development of new remineralization therapies.

Enamel remineralisation prospect of Moringa Oleifera hydrogel, eggshell hydrogel versus sodium fluoride varnish on artificially demineralised primary teeth: in vitro study.

PURPOSE: The purpose of the present in vitro study is to investigate and compare the remineralising potential of Moringa Oleifera extract, eggshell, and sodium fluoride varnish on microhardness of artificially demineralised enamel of primary teeth with biomimetic minimally invasive approach following the world paradigm shift towards natural products in paediatric dentistry. MATERIAL AND METHODS: Sample size included 44 primary molars. The mineral content and surface microhardness of all specimens were initially assessed using energy dispersive x-ray examination (EDX) and Vickers microhardness. The specimens were artificially demineralised for 96 h at a temperature of 37°C and then reassessed directly after demineralisation. The demineralised enamel specimens were randomly divided into four groups according to the remineralisation regimen utilised. Group 1: Artificial saliva (control); Group 2: Sodium fluoride varnish; Group 3: Eggshell hydrogel; and Group 4: Moringa Oleifera hydrogel. The specimens were stored for 8 days and then subsequently evaluated using EDX and microhardness assessment by Vickers microhardness test and scanning electron microscope (SEM).  Results: Regarding the microhardness test, there was a significant difference between the Moringa Oleifera group and Eggshell group compared to fluoride varnish (p < 0.05). Regarding EDX analysis, there was a statistically significant difference (p < 0.05) between Moringa Oleifera group and Eggshell group compared to fluoride varnish as the highest values were for Moringa Oleifera and Eggshell. On the other hand, there was no statistically significant difference (p > 0.05) between Moringa Oleifera and Eggshell in both the measurements. CONCLUSION: Moringa Oleifera and Eggshell might be considered as a biomimetic natural material capable of guiding enamel tissue remineralisation in early carious lesion of primary teeth. CLINICAL RELEVANCE: This research demonstrated the capability for early enamel caries to be remineralised using novel materials with a naturally counterpart implicated in biomineralisation as proved to be more effective than traditionally used fluoride varnish in primary teeth.

New Generation of Orthodontic Elastomeric Ligature to Prevent Enamel Demineralization In Vivo.

This study aimed to synthesize a novel elastomeric ligature with dimethylaminohexadecyl methacrylate (DMAHDM) grafted, providing a new strategy for improving the issue of enamel demineralization during fixed orthodontics. DMAHDM was incorporated into elastomeric ligatures at different mass fractions using ultraviolet photochemical grafting. The antibacterial properties were evaluated and the optimal DMAHDM amount was determined based on cytotoxicity assays. Moreover, tests were conducted to evaluate the in vivo changes in the mechanical properties of the elastomeric ligatures. To assess the actual in vivo effectiveness in preventing enamel demineralization, a rat demineralization model was established, with analyses focusing on changes in surface microstructure, elemental composition, and nanomechanical properties. Elastomeric ligatures with 2% DMAHDM showed excellent biocompatibility and the best antibacterial properties, reducing lactic acid production by 65.3% and biofilm bacteria by 50.0% within 24 h, without significant mechanical property differences from the control group (p > 0.05). Most importantly, they effectively prevented enamel demineralization in vivo, enhancing elastic modulus by 73.2% and hardness by 204.8%. Elastomeric ligatures incorporating DMAHDM have shown great potential for application in preventing enamel demineralization, providing a new strategy to solve this issue during fixed orthodontics.

Ultrastructural investigation of the effect of toothpastes containing different remineralizing agents on demineralized enamel.

OBJECTIVE: The present study aimed to evaluate the effect of remineralizing agents on demineralized enamel intended for use as fluoride substitutes or supplements for oral hygiene applications. METHODOLOGY: Enamel samples were obtained from 30 bovine teeth. The enamel blocks were stored in 20 mL of demineralization solution for 72 h. They were then brushed with the following toothpaste for the remineralization protocol: NaF, NaF/SnF2 combination, NovaMin, or nano-hydroxyapatite. SEM/EDX examinations and microhardness measurements of the samples were performed to investigate the remineralization efficacy of the studied toothpaste. One-way analysis of variance (ANOVA) with post hoc Tukey's HSD test was used to analyze the change in microhardness values in different remineralization protocols (p < 0.05). RESULTS: Differences in the mean remineralization (%RP) and hardness recovery (%HR) were determined between the groups (p < 0.05). Groups 1 and 4 showed significant differences in %RP (p < 0.05). In the SEM/EDX examinations, the samples treated with n-HAp showed an accumulation of crystal deposits on the enamel surface, although at a lower density than those treated with NaF and NaF/SnF2 combination. CONCLUSION: The remineralization strategy in toothpaste plays an important role in enamel remineralization. NovaMin-containing toothpaste showed positive effects on the enamel surface with better Ca/P ratio. Toothpastes containing n-HAp triggered less change in the increase of microhardness values compared to other toothpastes. The use of SnF2 in toothpaste in combination with NaF significantly increased the binding of fluoride to demineralized enamel compared to toothpaste containing NaF alone.

Effect of phosphoric acid containing polyvinylpyrrolidone as protective etchant for dentin bonding.

STATEMENT OF PROBLEM: Phosphoric acid is commonly used in dentistry as an etchant but can result in excessive demineralization of dentin, a major contributor to the instability of dentin-bonded restorations. Nevertheless, research on the development of etchants that can reduce acid damage is sparse. PURPOSE: The purpose of this in vitro study was to investigate the effects of polyvinylpyrrolidone-modified phosphoric acid on the dentin bonding of an etch-and-rinse adhesive. MATERIAL AND METHODS: Protective etchants were prepared by adding polyvinylpyrrolidone to 35% phosphoric acid aqueous solutions: the 3 concentrations were 0.5% (P0.5% group), 1% (P1% group), and 2% (P2% group) w/v. The treatment agent of the control group (C) was 35% phosphoric acid gel. Scanning electron microscopy (SEM), Fourier transform infrared spectroscopy (FTIR), microhardness, microtensile bonding strength (µTBS), nanoleakage, and in situ zymography were used to evaluate the appearance of the protective etchant on dentin bonding. The results were analyzed with a 1-way ANOVA test (α=.05). RESULTS: SEM showed no obviously exposed collagen fiber in the P1% and P2% groups. FTIR showed less demineralization of the dentin surface, and microhardness was higher after treatment with the protective etchant (P<.05). The µTBS of P1% (70 ±9.2 MPa) was the highest, and group C (44 ±5.8 MPa) was the lowest in all groups (P<.05). Moreover, there was weaker MMP activity in the P1% and P2% groups (P<.05). CONCLUSIONS: This study demonstrated that the protective etchant effectively reduced demineralization, enhanced bond strength, and reduced nanoleakage and enzyme activity within the hybrid layer.

Efficacy of peptide-based enamel coatings in the prevention of demineralization using fixed orthodontic brackets in a rat model.

INTRODUCTION: White spot lesions (WSLs) represent a prominent pathology encountered during orthodontic treatment, originating from enamel demineralization induced by the accumulation of bacterial biofilms. The previously developed bioinspired enamel coating form of self-assembling antimicrobial peptide D-GL13K exhibited antimicrobial activity and enhanced acid impermeability, offering a potential solution to prevent demineralization. The primary aim of this investigation is to assess the in vivo anti-demineralization properties and biocompatibility of the D-GL13K coating. METHODS: A rat model was developed to assess the antimicrobial enamel coating during fixed orthodontic treatment. The anti-demineralization efficacy attributed to the D-GL13K coating was evaluated by employing optical coherence tomography, Vickers microhardness testing, and scanning electron microscopy. The biocompatibility of the D-GL13K coating was investigated through histologic observations of vital organs and tissues using hematoxylin and eosin. RESULTS: The D-GL13K coating demonstrated significant anti-demineralization effects, evidenced by reduced demineralization depth analyzed through optical coherence tomography and enhanced Vickers hardness than in the noncoated control group, showcasing the coating's potential to protect teeth from WSLs. Scanning electron microscopy analysis further elucidated the diminished enamel damage observed in the group treated with D-GL13K. Importantly, histologic examination of vital organs and tissues using hematoxylin and eosin staining revealed no overt disparities between the D-GL13K coated group and the noncoated control group. CONCLUSIONS: The D-GL13K enamel coating demonstrated promising anti-demineralization and biocompatibility properties in a rat model, thereby suggesting its potential for averting WSLs after orthodontic interventions. Further research in human clinical settings is needed to evaluate the coating's long-term efficacy.

Effect of the use of remineralization agents before resin infiltration on the treatment of initial enamel lesions: an in-vitro study.

AIM: This study aimed to evaluate the effect of the use of remineralization agents before the application of resin infiltration on the treatment of initial enamel lesions. MATERIALS AND METHODS: Eighty buccal enamel samples were prepared from human molars, and artificial initial lesions were formed after 96 h of incubation with a demineralizing solution. The samples were randomly divided into 8 groups (n = 10) including a remineralizing agent (Tooth Mousse, Medical Mineral Gel, Remin Pro), resin infiltration (ICON), and a combined treatment of both. Remineralizing agents were applied in pH cycle for 7 days. Baseline, demineralization, and after-treatment fluorescence (FluoreCam and DIAGNOdent Pen), surface microhardness (HMV-2T), surface roughness (M300C), OCT (Maestro-2) and ultrasonic system (Novascope 4500) data were obtained for all groups. The sample surfaces were examined under SEM/EDX (SU3500) at x1000. Data were statistically analyzed using the Two-Way Robust ANOVA and Bonferroni tests (p < 0.05). RESULTS: There was no statistically significant difference between the groups for microhardness, roughness, OCT, DIAGNOdent Pen, ultrasound, and FluoreCam size/intensity values (p = 0.582; p = 0.963; p = 0.884; p = 0.923; p = 0.051; p = 0.268; p = 0.793 respectively). The effect of the treatment procedure showed a significant difference (p < 0.001), except for the roughness values (p = 0.984). The lowest Calcium (Ca) ratio (%atomic) was observed in the RI group in the EDX analysis. CONCLUSION: Remineralizing agents and resin infiltration methods may be used in combination or alone in the treatment of initial enamel lesions. Combining remineralizing agents with resin infiltration does not alter the efficacy of the treatment.

Impact of acidic beverages on composition and surface characteristics of human teeth: scanning electron microscopic, stereomicroscopic and energy dispersive x-ray analyses.

OBJECTIVES: The objective of this study was to evaluate the effect of acidic beverages on the surface topography and elemental composition of human teeth. METHODS: A total of five highly acidic beverages (Red Bull, Pepsi, Apple Cidra, Tang Mosambi, and Tang Orange) were investigated. The tooth specimens of experimental groups were submerged in each beverage and incubated at 37 °C for 7 days, whereas, the tooth specimens of control groups were placed in distilled water. Afterwards, tooth specimens were analyzed using scanning electron microscopic (SEM), stereomicroscopic, and energy dispersive x-ray (EDX) techniques. RESULTS: All experimental groups revealed a decline in the tooth elements compared to controls, however, such decline was not statistically significant. Nevertheless, comparing the experimental groups, the Red Bull beverage caused a marked reduction in the percentage of both calcium and phosphorus elements compared to the Pepsi, Apple Cidra, Tang Mosambi, and Tang Orange beverages but it was insignificant as well in contrast to its control counterpart. All five acidic beverages demonstrated erosive potential under SEM analysis; however, each group of specimens showed a diverse amount of demineralization. In addition, all experimental groups exhibited significant discoloration of tooth specimens compared to their respective control counterparts. CONCLUSIONS: Within the limitations of study, all five acidic beverages demonstrated erosive potential in the simulated in vitro conditions under SEM analysis; however, each group of specimens exhibited a different extent of demineralization. In addition, the overall effect of all beverages was insignificant under EDX analysis as no substantial difference was revealed between the elemental composition of experimental and control group specimens.

Comparing the remineralization potential of undemineralized dentin powder versus chicken eggshell powder on artificially induced initial enamel carious lesions: an in-vitro investigation.

BACKGROUND: White spot lesions are a widespread undesirable effect, especially prevalent during fixed orthodontic treatments. The study compared the in vitro enamel remineralization potential of undemineralized dentin matrix (UDD) versus chicken eggshell powder (CESP) for artificially induced enamel lesions. METHODS: 100 caries-free and sound maxillary premolars were randomly divided into four groups each contain 25 teeth: Group I (Baseline): No treatment was done to the enamel surface. Group II (Negative control ): The enamel surface of the teeth underwent demineralization using demineralizing solution to create artificial carious lesions then kept in artificial saliva. Group III (CESP treated): After demineralizing the tooth surface, the teeth have been suspended in the CESP remineralizing solution. Group IV (UDD treated): After enamel demineralization, the teeth were suspended in UDD remineralizing solution. The remineralization potential was assessed by Vickers microhardness testing, scanning electron microscopic examination (SEM), and energy dispersive X-ray (EDX). RESULTS: The current study demonstrated an increase in the mean microhardness of CESP and UDD-treated groups; however, It was nearer to the baseline level in the UDD group. SEM imaging revealed greater enamel remineralization in the UDD group compared to the remaining groups. The UDD group disclosed complete coverage for the prismatic enamel compared to the CESP group, which revealed a partially remineralized enamel surface. Interestingly, the Ca/P ratio increased significantly in the CESP group compared to the negative control group. In contrast, a higher significant increase in the mean Ca/P ratios was recorded in the UDD group compared to the test groups. CONCLUSION: biomimetic UDD and CESP powder should be utilized to treat enamel early carious lesions. However, UDD demonstrated the most significant remineralization potential.

Effect of Biomin F toothpaste and Diode laser on remineralization of white spot lesions (in vitro study).

BACKGROUND: White-spot lesions are considered an initial carious stage characterized by an outer enamel layer with significantly reduced mineralization. This study was conducted to assess the combined effect of Biomin F toothpaste and Diode laser on remineralization of white spot lesions. MATERIALS AND METHODS: An invitro study conducted on a total of 30 premolars divided into three groups; Group A (Biomin F Tooth paste), Group B (Biomin F with laser application for 30 sec), Group C (Negative control). The three groups were submitted to three stages; stage 1:Baseline,stage 2:After demineralization ,and stage 3:After remineralization. In each stage, elemental analysis(calcium, phosphorus, and fluoride)was measured quantitatively using Energy Dispersive X-ray (EDX) analysis and qualitatively by micrographs using scanning electron microscope. The data were tested to find significant difference between mineral changes during stages by using (ANOVA) test and Bonferroni test. RESULTS: Calcium, phosphorus and fluoride ions decreased in all groups after demineralization. In stage 3, after application of remineralizing agents, Calcium ions increased significantly in groups A and B where p<.05. As regards to the phosphorus ions, a significant increase was observed in all groups with group A showed the highest gain as phosphorus level percentage change (%mass) was 56.52±18.02 . Fluoride ions increased significantly in groups A and B (p<0.05) but decreased significantly in group C. There was no statistical significant difference between group A and B (p ≥.05) in calcium, phosphorus, and fluoride level after remineralization. CONCLUSION: Within the limitation of the present study, we concluded that Biomin F toothpaste is promising in the repairing of white spot lesions on the surface of the demineralized enamel. Diode laser did not affect the remineralizing ability of Biomin F toothpaste.

The damage and remineralization strategies of dental hard tissues following radiotherapy.

OBJECTIVES: This study pursued two main purposes. The first aim was to expound on the microscopic factors of radiation-related caries (RRC). Further, it aimed to compare the remineralization effect of different remineralizing agents on demineralized teeth after radiotherapy. METHODS: The enamel and dentin samples of bovine teeth were irradiated with different doses of radiation. After analysis of scanning electron microscope (SEM), X-Ray diffraction (XRD), and energy dispersive spectrometer (EDS), the samples irradiated with 50 Gy radiation were selected and divided into the demineralization group, the double distilled water (DDW) group, the Sodium fluoride (NaF) group, the Casein phosphopeptide-amorphous calcium phosphate (CPP-ACP) group, the NaF + CPP-ACP group, and the Titanium tetrafluoride (TiF4) group. After demineralization, remineralizing agents treatment, and remineralization, the samples were evaluated using SEM, atomic force microscope (AFM), EDS, and transverse microradiography (TMR). RESULTS: A radiation dose of 30 Gy was sufficient to cause damage to the dentinal tubules, but 70 Gy radiation had little effect on the microstructure of enamel. Additionally, the NaF + CPP-ACP group and the TiF4 group significantly promoted deposit formation, decreased surface roughness, and reduced mineral loss and lesion depth of demineralized enamel and dentin samples after radiation. CONCLUSIONS: Radiation causes more significant damage to dentin compared to enamel. NaF + CPP-ACP and TiF4 had a promising ability to promote remineralization of irradiated dental hard tissues. ADVANCES IN KNOWLEDGE: This in vitro study contributes to determining a safer radiation dose range for teeth and identifying the most effective remineralization approach for RRC.

Remineralizing effect of NSF on artificial enamel caries.

INTRODUCTION: Nanotechnology offers new approaches and endless opportunities for remineralizing tooth decay without being toxic or causing allergies. This study aimed to determine the effect of nanosilver fluoride (NSF) on the remineralization potential of enamel caries-like lesions compared to 5% sodium fluoride varnish in permanent teeth. METHODS: Fifteen teeth (molars and premolars) were gathered, cleaned, and polished using a scaler. After sectioning the teeth mesiodistally and removing the roots, the thirty specimens were subjected to a demineralized solution to induce early enamel lesions and then assigned randomly into two equal groups. The test materials were applied, and then all the specimens were subjected to a pH cycling model for 30 days. DIAGNOdent and surface roughness were investigated, and an evaluation of the enamel Ca and P weight% for Ca/P ratio calculation was done using SEM-EDX to analyze the specimens at the end of the study. The data were analyzed using an independent t-test. RESULTS: The mean values for the DIAGNOdent measurements for NSF and NaF at baseline and after demineralization were not significantly different (p > 0.05). After treatment, NaF varnish showed a significantly higher mean DIAGNOdent measurement (11.8 ± 5.80) than NSF (4.7 ± 1.6). The mean surface roughness of the NaF group (1.64 ± 0.39) was much higher than NSF's mean surface roughness (1.07 ± 0.21). Specimens treated with NSF had statistically significant smoother surfaces (p < 0.001). The NSF group had a higher mean Ca/P ratio (2.9 ± 0.35) than NaF (2.2 ± 0.11). This difference was statistically significant (p = 0.012). CONCLUSION: The study reveals that nano silver fluoride is a more effective treatment than sodium fluoride varnish in enhancing teeth's clinical characteristics, particularly in terms of mineral content and surface roughness, suggesting it could be an improved strategy to prevent dental caries and maintain enamel integrity.