Analysis of the residual monomer content in milled and 3D-printed removable CAD-CAM complete dentures: an in vitro study.
J Dent
; 120: 104094, 2022 05.
Article
en En
| MEDLINE
| ID: mdl-35301079
ABSTRACT
OBJECTIVE:
The study aimed to quantitatively evaluate the elution of methylmethacrylate from CAD-CAM manufactured removable complete dentures (RCDs) using high performance liquid chromatography (HPLC).METHODS:
Thirty-two RCDs were manufactured following either the CNC-milling (Milled n=8) or the 3D-printing (n=24) protocols. The 3D-printed dentures were further categorized into three groups based on their post-production rinsing cycles [Extended wash cycle (EWC), Standard wash cycle (SWC), and SWC with an additional Durécon coating (SWC2)]. HPLC was used to evaluate the methylmethacrylate concentrations (MMCs) eluted from the dentures in each group for different time periods (1, 2, 4, 8, and 24 hours). Mean and standard deviations were calculated for the MMCs; data was verified for normal distribution, ANOVA and post hoc tests were applied for statistical analyses (âº=0.05).RESULTS:
The HPLC revealed that all the denture groups recorded some amounts of MMCs, with significant differences [F (3, 31) = 23.646, p<0.0001]. The milled denture group had the highest MMCs at 24 hours when compared to the EWC (p<0.0001), SWC (p=0.001), and SWC2 (p<0.0001) denture groups. SWC had a higher MMC than EWC (p=0.032) and SWC2 (p=0.015). No differences were found in MMCs when comparing EWC and SWC2 (p=0.989).CONCLUSION:
Methylmethacrylate concentrations were significantly lower in 3D-printed RCDs than in milled RCDs when using the resins employed in this study. Furthermore, the MMCs can be further decreased in 3D-printed RCDs when coated with an additional thin protective layer (Durécon) by following the manufacturer-recommended rinsing protocol or when an extended isopropanol wash cycle is adopted.Palabras clave
Texto completo:
1
Bases de datos:
MEDLINE
Asunto principal:
Diseño Asistido por Computadora
/
Dentadura Completa
Idioma:
En
Revista:
J Dent
Año:
2022
Tipo del documento:
Article