Solid Electrolyte Interphase Formation in Tellurium Iodide Perovskites during Electrochemistry and Photoelectrochemistry.

ABSTRACT

Halide perovskites are promising photoelectrocatalytic materials. Their further development requires understanding of surface processes during electrochemistry. Thin films of tellurium-based vacancy-ordered perovskites with formula A2TeI6, A = Cs, methylammonium (MA), were deposited onto transparent conducting substrates using aerosol-assisted chemical vapor deposition. Thin film stability as electrodes and photoelectrodes was tested in dichloromethane containing tetrabutylammonium PF6 (TBAPF6). Using photoemission spectroscopy, we show that the formation of a solid electrolyte interphase on the surface of the Cs2TeI6, consisting of CsPF6, enhances the stability of the electrode and allows extended chopped-light chronoamperometry measurements at up to 1.1 V with a photocurrent density of 16 µA/cm2. In contrast, (CH3NH3)2TeI6 does not form a passivating layer and rapidly degrades upon identical electrochemical treatment. This demonstrates the importance of surface chemistry in halide perovskite electrochemistry and photoelectrocatalysis.