Ba3Lu(BO3)3:Ce3+,Tb3+/Mn2+: Dual-Functional Material for WLEDs and Optical Pressure Sensing.
Inorg Chem
; 63(9): 4288-4298, 2024 Mar 04.
Article
en En
| MEDLINE
| ID: mdl-38369784
ABSTRACT
Ba3Lu(BO3)3(BLB)Ce3+,Tb3+/Mn2+ phosphors were designed to explore effective and multifunctional applications. Under the excitation of near-ultraviolet (n-UV) light, the BLBCe3+ phosphor showed broad-band blue emission. After codoping with Mn2+ ions, the single-phase white light phosphor is achieved through the energy transfer (ET) between Ce3+ and Mn2+. In addition, thermal stability is significantly enhanced by the addition of Tb3+ (BLB0.02Ce3+,0.20Tb3+) compared to that codoped with Mn2+ (BLB0.02Ce3+,0.10Mn2+). The light-emitting diode (LED) device with warm white light emission is fabricated with UV-chip-coated BLB0.02Ce3+,0.05Tb3+ and Sr2Si5N8Eu2+ phosphors, showing a good potential application value for LEDs. Additionally, the spectral properties of borate-based phosphors (BLB0.02Ce3+) under high pressure were studied for the first time. Surprisingly, the change of pressure enabled the emission peak of BLB0.02Ce3+ to be tuned from 485 to 552 nm, and dλ/dP is 3.51 nm GPa-1. The color changes from blue to yellow with an increase of pressure. Compared with the reported data, the pressure-sensing sensitivity based on the central peak shift in this work is the highest in all Ce3+ single-doped samples. In addition, the emitting color and intensity were gradually regained after decompression. The intensity can reach 80% of the initial intensity. All data demonstrate that the BLB0.02Ce3+ phosphor has the potential to be utilized as an optical pressure sensor due to the high-pressure sensitivity and visible color tuning.
Texto completo:
1
Bases de datos:
MEDLINE
Idioma:
En
Revista:
Inorg Chem
Año:
2024
Tipo del documento:
Article