A Recipe for a Great Meal: A Benchtop Route from Elemental Se to Superior Thermoelectric ß-Ag2Se.

The low-temperature modification of ß-Ag2Se has proven to be useful as a near-room-temperature thermoelectric material. Over the past years, research has been devoted to interstitial, vacancy, and substitutional doping into the parent ß-Ag2Se structure, aiming at tuning the material's charge and heat transport properties to enhance thermoelectric performance. The transformation of ß-Ag2Se into α-Ag2Se at ∼134 °C and the low solubility of dopants are the main obstacles for the doping approach. Herein, we report a facile, safe, scalable, and cost-effective benchtop approach to successfully produce metal-doped ß-Ag2Se. The doped materials display a remarkable enhancement of thermoelectric performance with a record-high peak zT of 1.30 at 120 °C and an average zT of ∼1.15 in the 25-120 °C range for 0.2 at. % Zn-doped Ag2Se. The enhancement in zT is attributed to point defects created by Zn doping into Ag vacancies/interstitials, which enhances the scattering of phonons and tunes the charge carrier properties, leading to the significant suppression of thermal conductivity. The simplicity of the synthetic method developed herein and the high performance of the final products provide an avenue to produce high-quality Ag2Se-based thermoelectric materials.

Inducing Ferrimagnetic Exchange in 1D-FeSe2 Chains Using Heteroleptic Amine Complexes: [Fe(en)(tren)][FeSe2]2.

[Fe(en)(tren)][FeSe2]2 (en = ethylenediamine, C2H8N2, tren = tris(2-aminoethyl)amine, C6H18N4) has been synthesized by a mixed-ligand solvothermal method. Its crystal structure contains heteroleptic [Fe(en)(tren)]2+ complexes with distorted octahedral coordination, incorporated between 1D-FeSe2 chains composed of edge-sharing FeSe4 tetrahedra. The twisted octahedral coordination environment of the Fe-amine complex leads to partial dimerization of Fe-Fe distances in the FeSe2 chains so that the FeSe4 polyhedra deviate strongly from the regular tetrahedral geometry. 57Fe Mössbauer spectroscopy reveals oxidation states of +3 for the Fechain atoms and +2 for the Fecomplex atoms. The close proximity of Fe atoms in the chains promotes ferromagnetic nearest neighbor interactions, as indicated by a positive Weiss constant, θ = +53.8(6) K, derived from the Curie-Weiss fitting. Magnetometry and heat capacity reveal two consecutive magnetic transitions below 10 K. DFT calculations suggest that the ordering observed at 4 K is due to antiferromagnetic intrachain interactions in the 1D-FeSe2 chains. The combination of two different ligands creates an asymmetric coordination environment that induces changes in the structure of the Fe-Se fragments. This synthetic strategy opens new ways to explore the effects of ligand field strength on the structure of both Fe-amine complexes and surrounding Fe-Se chains.

Make Selenium Reactive Again: Activating Elemental Selenium for Synthesis of Metal Selenides Ranging from Nanocrystals to Large Single Crystals.

The inertness of elemental selenium is a significant obstacle in the synthesis of selenium-containing materials at low reaction temperatures. Over the years, several recipes have been developed to overcome this hurdle; however, most of the methods are associated with the use of highly toxic, expensive, and environmentally harmful reagents. As such, there is an increasing demand for the design of cheap, stable, and nontoxic reactive selenium precursors usable in the low-temperature synthesis of transition metal selenides with vast applications in nanotechnology, thermoelectrics, and superconductors. Herein, a novel synthetic route has been developed for activating elemental selenium by using a solvothermal approach. By comprehensive 77Se NMR, Raman, and infrared spectroscopies and gas chromatography-mass spectrometry, we show that the activated Se solution contained HSe-, [Se-Se]2-, and Se2- ions, as well as dialkyl selenide (R2Se) and dialkyl diselenide (R-Se-Se-R) species in dynamic equilibrium. This also corresponded to the first observation of naked Se22- in solution. The versatility of the developed Se precursor was demonstrated by the successful synthesis of (i) the polycrystalline room-temperature modification of the ß-Ag2Se thermoelectric material; (ii) large single crystals of superconducting ß-FeSe; (iii) CdSe nanocrystals with different particle sizes (3-10 nm); (iv) nanosheets of PtSe2; and (v) mono- and dibenzyl selenides and diselenides at room temperature. The simplicity and diversity of the developed Se activation method holds promise for applied and fundamental research.