Despite a recent shift toward methylammonium (MA)-free lead-halide perovskites for perovskite solar cells, high-efficiency formamidinium lead iodide (FAPbI3) devices still often require methylammonium chloride (MACl) as an additive, which evaporates away during the annealing process. In this article, it is shown that the residual MA+, however, triggers thermal instability. To investigate the possibility of an optimal concentration of MA+ that may improve thermal stability, the intrinsic thermal stability of pure FA, FA-rich, MA-rich, and pure MA perovskite films (FA1-xMAxPbI3, FAMA) is studied. The results show that the thermal stability of FAMA perovskites decreases with more MA+, under degradation conditions that isolate the intrinsic thermal stability of the material (i.e., without moisture and oxygen effects). X-ray diffraction (XRD), proton-transfer-reaction time-of-flight mass spectrometry (PTR-ToF-MS), photoluminescence (PL) and UV-visible spectroscopy, and depth-profiling X-ray Photoelectron Spectroscopy (XPS) are employed to show that the observed trend is mainly due to the decomposition of the MA+ cation, as opposed to other effects such as the precursor solvent and film morphologies. It is also found that the surfaces of these FAMA films are MA+ rich, although this phenomenon does not appear to affect thermal stability. Finally, it is demonstrated that this trend is unaffected by the presence of Spiro-OMeTAD atop the film, and thus solar cell devices should preserve this trend.
RESUMO
Formation of charged trions is detrimental to the luminescence quantum efficiency of colloidal quantum dot (QD) thin films as they predominantly undergo nonradiative recombination. In this regard, control of charged trion formation is of interest for both fundamental characterization of the quasi-particles and performance optimization. Using CdSe/CdS QDs as a prototypical material system, here we demonstrate a metal-oxide-semiconductor capacitor based on QD thin films for studying the background charge effect on the luminescence efficiency and lifetime. The concentration ratio of the charged and neutral quasiparticles in the QDs is reversibly controlled by applying a gate voltage, while simultaneous steady-state and time-resolved photoluminescence measurements are performed. Notably, the photoluminescence intensity is modulated by up to 2 orders of magnitude with a corresponding change in the effective lifetime. In addition, chip-scale modulation of brightness is demonstrated, where the photoluminescence is effectively turned on and off by the gate, highlighting potential applications in voltage-controlled electrochromics.
RESUMO
The local confinement effect, which can generate a high concentration of hydroxide ions and reaction intermediates near the catalyst surface, is an important strategy for converting CO2 into multi-carbon products in electrocatalytic CO2 reduction. Therefore, understanding how the shape and dimension of the confinement geometry affect the product selectivity is crucial. In this study, we report for the first time the effect of the shape (degree of confinement) and dimension of the confined space on the product selectivity without changing the intrinsic property of Cu. We demonstrate that geometry influences the outcomes of products, such as CH4 , C2 H4 , and EtOH, in different ways: the selectivity of CH4 and EtOH is affected by shape, while the selectivity of C2 H4 is influenced by dimension of geometry predominantly. These phenomena are demonstrated, both experimentally and through simulation, to be induced by the local confinement effect within the confined structure. Our geometry model could serve as basis for designing the confined structures tailored for the production of specific products.
RESUMO
The CO2 electroreduction to fuels is a feasible approach to provide renewable energy sources. Therefore, it is necessary to conduct experimental and theoretical investigations on various catalyst design strategies, such as electronic metal-support interaction, to improve the catalytic selectivity. Here a solvent-free synthesis method is reported to prepare a copper (Cu)-based metal-organic framework (MOF) as the precursor. Upon electrochemical CO2 reduction in aqueous electrolyte, it undergoes in situ decomposition/redeposition processes to form abundant interfaces between Cu nanoparticles and amorphous carbon supports. This Cu/C catalyst favors the selective and stable production of CH4 with a Faradaic efficiency of ≈55% at -1.4 V versus reversible hydrogen electrode (RHE) for 12.5 h. The density functional theory calculation reveals the crucial role of interfacial sites between Cu and amorphous carbon support in stabilizing the key intermediates for CO2 reduction to CH4 . The adsorption of COOH* and CHO* at the Cu/C interface is up to 0.86 eV stronger than that on Cu(111), thus promoting the formation of CH4 . Therefore, it is envisioned that the strategy of regulating electronic metal-support interaction can improve the selectivity and stability of catalyst toward a specific product upon electrochemical CO2 reduction.
RESUMO
Optical reflectance imaging is a popular technique for characterizing 2D materials, thanks to its simplicity and speed of data acquisition. The use of this method for studying interlayer phenomena in stacked 2D layers has, however, remained limited. Here we demonstrate that optical imaging can reveal the nature of interlayer coupling in stacked MoS2 and WS2 bilayers through their observed reflectance contrast versus the substrate. Successful determination of interlayer coupling requires co-optimization of the illumination wavelength and the thickness of an underlying SiO2 film. Our observations are supported by multilayer optical calculations together with an analysis of the effect of any interlayer gap. This approach promises quick characterization of constructed 2D material systems.
RESUMO
Isotopically purified semiconductors potentially dissipate heat better than their natural, isotopically mixed counterparts as they have higher thermal conductivity (κ). But the benefit is low for Si at room temperature, amounting to only â¼10% higher κ for bulk ^{28}Si than for bulk natural Si (^{nat}Si). We show that in stark contrast to this bulk behavior, ^{28}Si (99.92% enriched) nanowires have up to 150% higher κ than ^{nat}Si nanowires with similar diameters and surface morphology. Using a first-principles phonon dispersion model, this giant isotope effect is attributed to a mutual enhancement of isotope scattering and surface scattering of phonons in ^{nat}Si nanowires, correlated via transmission of phonons to the native amorphous SiO_{2} shell. The Letter discovers the strongest isotope effect of κ at room temperature among all materials reported to date and inspires potential applications of isotopically enriched semiconductors in microelectronics.
RESUMO
(Photo)electrolysis of water or gases with water to species serving as industrial feedstocks and energy carriers, such as hydrogen, ammonia, ethylene, propanol, etc., has drawn tremendous attention. Moreover, these processes can often be driven by renewable energy under ambient conditions as a sustainable alternative to traditional high-temperature and high-pressure synthesis methods. In addition to the extensive studies on catalyst development, increasing attention has been paid to the regulation of gas transport/diffusion behaviors during gas-involving (photo)electrocatalytic reactions towards the goal of creating industrially viable catalytic systems with high reaction rates, excellent long-term stabilities and near-unity selectivities. Biomimetic surfaces and systems with special wetting capabilities and structural advantages can shed light on the future design of (photo)electrodes and address long-standing challenges. This article is dedicated to bridging the fields of wetting and catalysis by reviewing the cutting-edge design methodologies of both gas-evolving and gas-consuming (photo)electrocatalytic systems. We first introduce the fundamentals of various in-air/underwater wetting states and their corresponding bioinspired structural properties. The relationship amongst the bubble transport behavior, wettability, and porosity/tortuosity is also discussed. Next, the latest implementations of wetting-related design principles for gas-evolving reactions (i.e. the hydrogen evolution reaction and oxygen evolution reaction) and gas-consuming reactions (i.e. the oxygen reduction reaction and CO2 reduction reaction) are summarized. For photoelectrode designs, additional factors are taken into account, such as light absorption and the separation, transport and recombination of photoinduced electrons and holes. The influences of wettability and 3D structuring of (photo)electrodes on the catalytic activity, stability and selectivity are analyzed to reveal the underlying mechanisms. Finally, remaining questions and related future perspectives are outlined.
RESUMO
Kinetic Monte Carlo (KMC) methods are frequently used for mechanistic studies of thermally driven heterogeneous catalysis systems but are underused for electrocatalysis. Here, we develop a lattice KMC approach for electrocatalytic CO2 reduction. The work is motivated by a prior experimental report that performed electroreduction of a mixed feed of 12CO2 and 13CO on Cu; differences in the 13C content of C2 products ethylene and ethanol (Δ13C) were interpreted as evidence of site selectivity. The lattice KMC model considers the effect of surface diffusion on this system. In the limit of infinitely fast diffusion (mean-field approximation), the key intermediates 12CO* and 13CO* would be well mixed on the surface and no evidence of site selectivity could have been observed. Using a simple two-site model and adapting a previously reported microkinetic model, we assess the effects of diffusion on the relative isotope fractions in the products using the estimated surface diffusion rate of CO* from literature reports. We find that the size of the active sites and the total surface adsorbate coverage can have a large influence on the values of Δ13C that can be observed. Δ13C is less sensitive to the CO* diffusion rate as long as it is within the estimated range. We further offer possible methods to estimate surface distribution of intermediates and to predict intrinsic selectivity of active sites based on experimental observations. This work illustrates the importance of considering surface diffusion in the study of electrochemical CO2 reduction to multi-carbon products. Our approach is entirely based on a freely available open-source code, so will be readily adaptable to other electrocatalytic systems.
RESUMO
Exploring efficient and low-cost electrocatalysts for hydrogen evolution reaction (HER) in alkaline media is critical for developing anion exchange membrane electrolyzers. The key to a rational catalyst design is understanding the descriptors that govern the alkaline HER activity. Unfortunately, the principles that govern the alkaline HER performance remain unclear and are still under debate. By studying the alkaline HER at a series of NiCu bimetallic surfaces, where the electronic structure is modulated by the ligand effect, we demonstrate that alkaline HER activity can be correlated with either the calculated or the experimental-measured d band center (an indicator of hydrogen binding energy) via a volcano-type relationship. Such correlation indicates the descriptor role of the d band center, and this hypothesis is further supported by the evidence that combining Ni and Cu produces a variety of adsorption sites, which possess near-optimal hydrogen binding energy. Our finding broadens the applicability of d band theory to activity prediction of metal electrocatalysts and may offer an insightful understanding of alkaline HER mechanism.
RESUMO
Numerous studies have examined the electrochemical reduction of CO (COR) to oxygenates (e.g., ethanol). None have considered the possibility that oxygen in the product might arise from water rather than from CO. To test this assumption, C16O reduction was performed in H218O electrolyte. Surprisingly, we found that 60-70% of the ethanol contained 18O, which must have originated from the solvent. We extended our previous all-solvent density functional theory metadynamics calculations to consider the possibility of incorporating water, and indeed, we found a new mechanism involving a Grotthuss chain of six water molecules in a concerted reaction with the *C-CH intermediate to form *CH-CH(18OH), subsequently leading to (18O)ethanol. This competes with the formation of ethylene that also arises from *C-CH. These unforeseen results suggest that all previous studies of COR under aqueous conditions must be reexamined.
RESUMO
BACKGROUND: The standard therapy for women with unexplained infertility is gonadotropin or clomiphene citrate. Ovarian stimulation with letrozole has been proposed to reduce multiple gestations while maintaining live birth rates. METHODS: We enrolled couples with unexplained infertility in a multicenter, randomized trial. Ovulatory women 18 to 40 years of age with at least one patent fallopian tube were randomly assigned to ovarian stimulation (up to four cycles) with gonadotropin (301 women), clomiphene (300), or letrozole (299). The primary outcome was the rate of multiple gestations among women with clinical pregnancies. RESULTS: After treatment with gonadotropin, clomiphene, or letrozole, clinical pregnancies occurred in 35.5%, 28.3%, and 22.4% of cycles, and live birth in 32.2%, 23.3%, and 18.7%, respectively; pregnancy rates with letrozole were significantly lower than the rates with standard therapy (gonadotropin or clomiphene) (P=0.003) or gonadotropin alone (P<0.001) but not with clomiphene alone (P=0.10). Among ongoing pregnancies with fetal heart activity, the multiple gestation rate with letrozole (9 of 67 pregnancies, 13%) did not differ significantly from the rate with gonadotropin or clomiphene (42 of 192, 22%; P=0.15) or clomiphene alone (8 of 85, 9%; P=0.44) but was lower than the rate with gonadotropin alone (34 of 107, 32%; P=0.006). All multiple gestations in the clomiphene and letrozole groups were twins, whereas gonadotropin treatment resulted in 24 twin and 10 triplet gestations. There were no significant differences among groups in the frequencies of congenital anomalies or major fetal and neonatal complications. CONCLUSIONS: In women with unexplained infertility, ovarian stimulation with letrozole resulted in a significantly lower frequency of multiple gestation but also a lower frequency of live birth, as compared with gonadotropin but not as compared with clomiphene. (Funded by the National Institutes of Health and others; ClinicalTrials.gov number, NCT01044862.).
Assuntos
Clomifeno/uso terapêutico , Fármacos para a Fertilidade Feminina/uso terapêutico , Gonadotropinas/uso terapêutico , Infertilidade Feminina/tratamento farmacológico , Nitrilas/uso terapêutico , Indução da Ovulação/métodos , Gravidez Múltipla/estatística & dados numéricos , Triazóis/uso terapêutico , Adolescente , Adulto , Feminino , Humanos , Letrozol , Nascido Vivo/epidemiologia , Gravidez , Taxa de Gravidez , Adulto JovemRESUMO
Hydrostatic pressure applied using diamond anvil cells (DAC) has been widely explored to modulate physical properties of materials by tuning their lattice degree of freedom. Independently, electrical field is able to tune the electronic degree of freedom of functional materials via, for example, the field-effect transistor (FET) configuration. Combining these two orthogonal approaches would allow discovery of new physical properties and phases going beyond the known phase space. Such experiments are, however, technically challenging and have not been demonstrated. Herein, we report a feasible strategy to prepare and measure FETs in a DAC by lithographically patterning the nanodevices onto the diamond culet. Multiple-terminal FETs were fabricated in the DAC using few-layer MoS2 and BN as the channel semiconductor and dielectric layer, respectively. It is found that the mobility, conductance, carrier concentration, and contact conductance of MoS2 can all be significantly enhanced with pressure. We expect that the approach could enable unprecedented ways to explore new phases and properties of materials under coupled mechano-electrostatic modulation.
RESUMO
Understanding edge effects and quantifying their impact on the carrier properties of two-dimensional (2D) semiconductors is an essential step toward utilizing this material for high performance electronic and optoelectronic devices. WS2 monolayers patterned into disks of varying diameters are used to experimentally explore the influence of edges on the material's optical properties. Carrier lifetime measurements show a decrease in the effective lifetime, τeffective, as a function of decreasing diameter, suggesting that the edges are active sites for carrier recombination. Accordingly, we introduce a metric called edge recombination velocity (ERV) to characterize the impact of 2D material edges on nonradiative carrier recombination. The unpassivated WS2 monolayer disks yield an ERV â¼ 4 × 104 cm/s. This work quantifies the nonradiative recombination edge effects in monolayer semiconductors, while simultaneously establishing a practical characterization approach that can be used to experimentally explore edge passivation methods for 2D materials.
RESUMO
The complexity of strongly correlated electron physics in vanadium dioxide is exemplified as its rich phase diagrams of all kinds, which in turn shed light on the mechanisms behind its various phase transitions. In this work, we map out the hydrostatic pressure-temperature phase diagram of vanadium dioxide nanobeams by independently varying pressure and temperature with a diamond anvil cell. In addition to the well-known insulating M1 (monoclinic) and metallic R (tetragonal) phases, the diagram identifies the existence at high pressures of the insulating M1' (monoclinic, more conductive than M1) phase and two metallic phases of X (monoclinic) and O (orthorhombic, at high temperature only). Systematic optical and electrical measurements combined with density functional calculations allow us to delineate their phase boundaries as well as reveal some basic features of the transitions.
RESUMO
van der Waals (vdW) forces, despite being relatively weak, hold the layers together in transition metal dichalcogenides (TMDs) and play a key role in their band structure evolution, hence profoundly affecting their physical properties. In this work, we experimentally probe the vdW interactions in MoS2 and other TMDs by measuring the valence band maximum (VBM) splitting (Δ) at K point as a function of pressure in a diamond anvil cell. As high pressure increases interlayer wave function coupling, the VBM splitting is enhanced in 2H-stacked MoS2 multilayers but, due to its specific geometry, not in 3R-stacked multilayers, hence allowing the interlayer contribution to be separated out of the total VBM splitting, as well as predicting a negative pressure (2.4 GPa) where the interlayer contribution vanishes. This negative pressure represents the threshold vdW interaction beyond which neighboring layers are electronically decoupled. This approach is compared to first-principles calculations and found to be widely applicable to other group-VI TMDs.
RESUMO
Oxide-derived (OD) Cu catalysts have high selectivity towards the formation of multi-carbon products (C2 /C3 ) for aqueous electrochemical CO2 reduction (CO2 R). It has been proposed that a large fraction of the initial oxide can be surprisingly resistant to reduction, and these residual oxides play a crucial catalytic role. The stability of residual oxides was investigated by synthesizing 18 O-enriched OD Cu catalysts and testing them for CO2 R. These catalysts maintain a high selectivity towards C2 /C3 products (ca. 60 %) for up to 5â h in 0.1 m KHCO3 at -1.0â V vs. RHE. However, secondary-ion mass spectrometry measurements show that only a small fraction (<1 %) of the original 18 O content remains, showing that residual oxides are not present in significant amounts during CO2 R. Furthermore, we show that OD Cu can reoxidize rapidly, which could compromise the accuracy of exâ situ methods for determining the true oxygen content.
RESUMO
The use of sunlight to drive organic reactions constitutes a green and sustainable strategy for organic synthesis. Herein, we discovered that the earth-abundant aluminum oxide (Al2O3) though paradigmatically known to be an insulator could induce an immense increase in the selective photo-oxidation of different benzyl alcohols in the presence of a large variety of dyes and O2. This unique phenomenon is based on the surface complexation of benzyl alcohol (BnOH) with the Brønsted base sites on Al2O3, which reduces its oxidation potential and causes an upshift in its HOMO for electron abstraction by the dye. The surface complexation of O2 with Al2O3 also activates the adsorbed O2 for receiving electrons from the photoexcited dyes. This discovery brings forth a new understanding on utilizing surface complexation mechanisms between the reactants and earth abundant materials to effectively achieve a wider range of photoredox reactions.
RESUMO
Optoelectronic devices based on two-dimensional (2D) materials have shown tremendous promise over the past few years; however, there are still numerous challenges that need to be overcome to enable their application in devices. These include improving their poor photoluminescence (PL) quantum yield (QY) as well as better understanding of exciton-based recombination kinetics. Recently, we developed a chemical treatment technique using an organic superacid, bis(trifluoromethane)sulfonimide (TFSI), which was shown to improve the quantum yield in MoS2 from less than 1% to over 95%. Here, we perform detailed steady-state and transient optical characterization on some of the most heavily studied direct bandgap 2D materials, specifically WS2, MoS2, WSe2, and MoSe2, over a large pump dynamic range to study the recombination mechanisms present in these materials. We then explore the effects of TFSI treatment on the PL QY and recombination kinetics for each case. Our results suggest that sulfur-based 2D materials are amenable to repair/passivation by TFSI, while the mechanism is thus far ineffective on selenium based systems. We also show that biexcitonic recombination is the dominant nonradiative pathway in these materials and that the kinetics for TFSI treated MoS2 and WS2 can be described using a simple two parameter model.
Assuntos
Compostos de Selênio/química , Sulfetos/química , CinéticaRESUMO
Hybrid organic-inorganic halide perovskite based semiconductor materials are attractive for use in a wide range of optoelectronic devices because they combine the advantages of suitable optoelectronic attributes and simultaneously low-cost solution processability. Here, we present a two-step low-pressure vapor-assisted solution process to grow high quality homogeneous CH3NH3PbI3-xBrx perovskite films over the full band gap range of 1.6-2.3 eV. Photoluminescence light-in versus light-out characterization techniques are used to provide new insights into the optoelectronic properties of Br-containing hybrid organic-inorganic perovskites as a function of optical carrier injection by employing pump-powers over a 6 orders of magnitude dynamic range. The internal luminescence quantum yield of wide band gap perovskites reaches impressive values up to 30%. This high quantum yield translates into substantial quasi-Fermi level splitting and high "luminescence or optically implied" open-circuit voltage. Most importantly, both attributes, high internal quantum yield and high optically implied open-circuit voltage, are demonstrated over the entire band gap range (1.6 eV ≤ Eg ≤ 2.3 eV). These results establish the versatility of Br-containing perovskite semiconductors for a variety of applications and especially for the use as high-quality top cell in tandem photovoltaic devices in combination with industry dominant Si bottom cells.
RESUMO
P-type transparent conducting films of nanocrystalline (CuS)x:(ZnS)1-x were synthesized by facile and low-cost chemical bath deposition. Wide angle X-ray scattering (WAXS) and high resolution transmission electron microscopy (HRTEM) were used to evaluate the nanocomposite structure, which consists of sub-5 nm crystallites of sphalerite ZnS and covellite CuS. Film transparency can be controlled by tuning the size of the nanocrystallites, which is achieved by adjusting the concentration of the complexing agent during growth; optimal films have optical transmission above 70% in the visible range of the spectrum. The hole conductivity increases with the fraction of the covellite phase and can be as high as 1000 S cm(-1), which is higher than most reported p-type transparent materials and approaches that of n-type transparent materials such as indium tin oxide (ITO) and aluminum doped zinc oxide (AZO) synthesized at a similar temperature. Heterojunction p-(CuS)x:(ZnS)1-x/n-Si solar cells were fabricated with the nanocomposite film serving as a hole-selective contact. Under 1 sun illumination, an open circuit voltage of 535 mV was observed. This value compares favorably to other emerging heterojunction Si solar cells which use a low temperature process to fabricate the contact, such as single-walled carbon nanotube/Si (370-530 mV) and graphene/Si (360-552 mV).