Surface modification of polyether ether ketone implant with a novel nanocomposite coating containing poly (vinylidene fluoride) toward improving piezoelectric and bioactivity performance.

Polyether ether ketone (PEEK) is an appropriate biomaterial for orthopedic implant applications due to its superior mechanical properties, chemical resistance, nontoxicity, and Magnetic resonance imaging (MRI) compatibility. Unfortunately, the inherent bio-inertness of PEEK restricted its application and required some modification to provide better bioactivity. Besides it, the generated electrical signals in the bone due to its piezoelectricity features have a vital role in regulating bone repair and regeneration. We aimed to modify the surface of PEEK with a dual-functionality nanocomposite that provides surface bioactivity and simulates the piezoelectricity of bone. So, we introduced a novel piezoelectric-bioactive nanocomposite of dispersed poly (vinylidene fluoride) (PVDF) in a sulfonated PEEK (SPEEK) matrix containing Nanohydroxyapatite (nHA) and Carbon nanofiber (CNF) fillers for coating on PEEK substrate to improve its biological activity and simulate the electrical microenvironment for bone tissue. Furthermore, sulfonation of the PEEK surface was conducted as an intermediate layer to prepare better adhesion between the coating nanocomposite and the PEEK sublayer. Surface and cross-section morphology, apatite formation, and cell attachment were investigated on the different treated PEEK surfaces using field-emission scanning electron microscopy (FESEM) and energy dispersive X-ray analysis (EDX). Also, piezoelectric performance, electrical conductivity, contact angle, and mechanical properties were examined on the prepared samples. Moreover, cell viability and cell morphology were investigated for biological evaluation with human osteoblast-like MG-63 cells. Collectively, the hydrophilicity of modified PEEK (mPEEK) coated with nanocomposite was improved due to the synergistic effects of SPEEK functional groups and nHA. Also, comprehensive investigation on the mPEEK treated with nanocomposite indicated a noticeably better bone-like apatite formation, cell proliferation, and cell attachments in the presence of nHA. The transfer of induced piezoelectric charges from dispersed PVDF in the matrix to the surface of nanocomposite containing 2 wt% of CNF increased output voltage to 1893 mV. On the other hand, the presence of CNF in nanocomposites enhanced tensile strength and Young's modulus by 92% and 117%, respectively.

Falcaria vulgaris leaves extract as an eco-friendly corrosion inhibitor for mild steel in hydrochloric acid media.

Undoubtedly, metal corrosion is one of the most challenging problems faced by industries. Introducing corrosion inhibitors is a reasonable approach to protecting the metal surface. Due to environmental concerns and the toxicity of industrial organic corrosion inhibitors, researchers are continually exploring acceptable replacements. The current study focused on the application of Falcaria Vulgaris (FV) leaves extract to mitigate mild steel (MS) corrosion in a 1 M HCl environment. The polarization findings demonstrated that the corrosion current density decreased from 264.0 µA/cm2 (for the sample submerged in the blank solution) to 20.4 µA/cm2 when the optimal concentration of 800 ppm of FV leaves extract was added to the acid solution. Electrochemical impedance spectroscopy (EIS) analysis revealed an inhibition efficiency of 91.3% at this concentration after 6 h of immersion. It was determined by analyzing several adsorption isotherms that this corrosion inhibitor obeys the Frumkin isotherm. AFM, FE-SEM, and GIXRD surface analyses also supported the findings that adding FV leaves extract can reduce metal damage by adsorption on the metal surface.