Characterization of Mn3 O4 -MnO2 nanocomposites biosynthesized by cell lysate of Haloferax alexandrinus GUSF-1.

Manganese oxide nanocomposites attract huge attention in various biotechnological fields due to their extensive catalytic properties. This study reports an easy, rapid, and cost-effective method of using the cell lysate of haloarchaeon, Haloferax alexandrinus GUSF-1 for the synthesis of manganese oxide nanoparticles. The reaction between the cell lysate and manganese sulfate resulted in the formation of a dark brown precipitate within 48 h at room temperature. The X-ray diffraction pattern showed the existence of Mn3 O4 and MnO2 phases consistent with the JCPDS card no. (01-075-1560 and 00-050-0866). The dark brown colloidal suspension of MnO3 -MnO2 in methanol showed maximum absorption between 220 and 260 nm. The EDX spectrum confirmed the presence of manganese and oxygen. The Transmission electron microscopy revealed the spherical morphology with an average particle size between 30 and 60 nm. The magnetic moment versus magnetic field (MH) curve, at room temperature (300 K) did not saturate even at a high magnetic field (±3T) indicating the paramagnetic nature of the prepared nanocomposite. The Atomic Emission Spectroscopic analysis showed a negligible amount of soluble manganese (0.03 ppm in 50 ppm) in the Mn3 O4 -MnO2 suspension suggesting the maximum stability of the material in the solvent over time. Interstingly, Mn3 O4 -MnO2 nanocomposites evidenced antimicrobial activity in the order of Pseudomonas aeruginosa > Salmonella typhi > Escherichia coli > Proteus vulgaris > Candida albicans > Staphylococcus aureus. Conclusively, this is the first report on the formation of Mn3 O4 -MnO2 nanocomposites using cell lysate of salt pan haloarcheon Haloferax alexandrinus GUSF-1 with antimicrobial potential.

Conversion of selenite by Haloferax alexandrinus GUSF-1 (KF796625) to pentagonal selenium nanoforms which in vitro modulates the formation of calcium oxalate crystals.

AIM: To investigate the ability of Haloferax alexandrinus GUSF-1 (KF796625) to biosynthesize non-toxic elemental selenium (Se0 ) and check their capacity in in vitro crystal structure modulation of calcium oxalate, which are implicated in the development of renal calculi. METHODS AND RESULTS: Haloferax alexandrinus GUSF-1 (KF796625) during growth in the presence of 5 mmol L-1 of selenite formed insoluble brick-red particles. Se0 formed was monitored spectrophotometrically using a combination of two assays; the ascorbic acid reduction and sodium sulphide solubilization assay. After 168 h of growth, 2.89 mmol L-1 of Se0 was formed from 4.9 mmol L-1 of selenite. Absorption bands at 1.5, 11.2 and 12.5 keV in EDX spectroscopy confirmed that the brick-red particulate matter was Se0 . Furthermore, these selenium nanoparticles (SeNPs) were pentagonal in shape in transmission electron microscopy imaging. The peak positions in X-ray diffractogram at 2θ values of 23.40°, 29.66°, 41.26°, 43.68°, 45.24°, 51.62°, 55.93° and 61.47° and the relative intensities further confirmed the formation of Se0 . In vitro addition of 50 and 100 µg ml-1 of these SeNPs to the mixture of sodium chloride, calcium chloride and sodium oxalate affected and modulated the shape and size of rectangular-shaped calcium oxalate crystals (average area of 1.23 ± 0.2 µm2 ) to smaller rectangular-shaped crystals (average area of 0.54 ± 0.2 µm2 ) and spherical-shaped crystals (average area 0.13 ± 0.005 µm2 ). CONCLUSION: Haloferax alexandrinus GUSF-1 (KF796625) transformed selenite to Se0 pentagonal nanoforms that modulated in vitro the formation of crystal shape and size of calcium oxalate. SIGNIFICANCE AND IMPACT OF STUDY: There are no reports on conversion of selenite to Se0 among the Haloferax genera, and this study involving the formation of pentagonal SeNPs with capacity to modulate the formation of calcium oxalate crystals in haloarchaea is recorded as the first report and of significance in pharmaceutical research related to formulations abetting urinary calculi.