Morphology and properties of neutralized chitosan-cellulose nanocrystals biocomposite films.

Chitosan/cellulose nanocrystals (CH-CN) films were obtained by casting of dispersions, and treated with NaOH for neutralization proposes. The composition of films was varied from 1 to 10wt.% of CN. Changes in the morphology of the systems were correlated with the different properties studied. FTIR revealed the presence of a weak interaction between the polymer matrix and nanofiller, confirmed by a slightly increase in thermal stability. SEM images suggested that incorporating CN amounts higher than 3wt.% generates phase-segregated systems, and SAXS showed that CH avoid the typical organization of CN at concentrations below 5wt.%. Improved performance against water was obtained in composite materials comparing to the pure polymer matrix, as well as CH and CH-CN films did not show antibacterial activity demonstrating that remnant acetic acid, when no neutralization step is done, plays an important role in this property.

Nanomolar cationic dendrimeric sulfadiazine as potential antitoxoplasmic agent.

The high doses of sulfadiazine (SDZ), used in synergistic combination with pyrimethamine, are mainly responsible for severe side effects and discontinuation of toxoplasmosis treatments. In the search for new strategies that improve the efficacy of treatments with reduced doses of SDZ, we have determined the performance of cationic G4 (DG4) and anionic G4.5 (DG4.5) poly(amidoamine) (PAMAM) dendrimers to act as SDZ nanocarriers. Both dendrimers could efficiently load SDZ (SDZ-DG4 and SDZ-DG4.5) up to a ratio of 30 molecules SDZ per dendrimer molecule. The MTT assay on Vero and J774 cells showed no cytotoxicity for DG4.5 and its SDZ complex incubated between 0.03 and 33 microM of dendrimer concentration. On the other hand, DG4 and its SDZ complex resulted cytotoxic when incubated at dendrimer concentrations higher than 3.3 microM. Finally, complexes and empty dendrimers were in vitro tested against Vero cells infected with RH strain of Toxoplasma gondii along 4h of treatment. For SDZ-DG4.5 and DG4.5 to cause an infection decrease between 25 and 40%, respectively, a dendrimer concentration of 33 microM was required; however, SDZ-DG4 produced the highest infection decrease of 60% at 0.03 microM. These preliminary results, achieved with nanomolar doses of SDZ-DG4 as unique active principle, point to this complex as a suitable potential candidate for antitoxoplasmic therapy.

Use of sterically-stabilised polystyrene latex particles as a pH-responsive particulate emulsifier to prepare surfactant-free oil-in-water emulsions.

A pH-responsive, sterically-stabilised polystyrene latex is used as a particulate emulsifier for oil-in-water emulsions; demulsification occurs rapidly on lowering the solution pH and the original emulsion can be reformed on pH cycling.

Characterization of the nanomorphology of polymer-silica colloidal nanocomposites using electron spectroscopy imaging.

The internal nanomorphologies of two types of vinyl polymer-silica colloidal nanocomposites were assessed using electron spectroscopy imaging (ESI). This technique enables the spatial location and concentration of the ultrafine silica sol within the nanocomposite particles to be determined. The ESI data confirmed that the ultrafine silica sol was distributed uniformly throughout the poly(4-vinylpyridine)/silica nanocomposite particles, which is consistent with the "currant bun" morphology previously used to describe this system. In contrast, the polystyrene/silica particles had a pronounced "core-shell" morphology, with the silica sol forming a well-defined monolayer surrounding the nanocomposite cores. Thus these ESI results provide direct verification of the two types of nanocomposite morphologies that were previously only inferred on the basis of X-ray photoelectron spectroscopy and aqueous electrophoresis studies. Moreover, ESI also allows the unambiguous identification of a minor population of polystyrene/silica nanocomposite particles that are not encapsulated by silica shells. The existence of this second morphology was hitherto unsuspected, but it is understandable given the conditions employed to synthesize these nanocomposites. It appears that ESI is a powerful technique for the characterization of colloidal nanocomposite particles.

Effect of varying the oil phase on the behavior of pH-responsive latex-based emulsifiers: demulsification versus transitional phase inversion.

Sterically stabilized polystyrene latexes (previously described by Amalvy, J. I.; et al. Chem. Commun. 2003, 1826) were evaluated as pH-responsive particulate emulsifiers for the preparation of both oil-in-water and water-in-oil emulsions. The steric stabilizer was a well-defined AB diblock copolymer where A is poly(2-(dimethylamino)ethyl methacrylate) and B is poly(methyl methacrylate). Several parameters were varied during the emulsion preparation, including the polarity of the oil phase, the latex concentration, surface concentration of copolymer stabilizer, and solution pH. Nonpolar oils such as n-dodecane gave oil-in-water emulsions, and polar oils such as 1-undecanol produced water-in-oil emulsions. In both cases, these emulsions proved to be stimulus-responsive: demulsification occurred rapidly on adjusting the solution pH. Oils of intermediate polarity such as methyl myristate or cineole led to emulsions that underwent transitional inversion on adjusting the solution pH. All emulsions were polydisperse and typically ranged from 40 to 400 microm diameter, as judged by optical microscopy and Malvern Mastersizer measurements. Critical point drying of the emulsion droplets, followed by scanning electron microscopy studies, confirmed that the latex particles were adsorbed as a single monolayer at the oil/water interface, as anticipated.

Synthesis and characterization of novel pH-responsive microgels based on tertiary amine methacrylates.

Emulsion polymerization of 2-(diethylamino)ethyl methacrylate (DEA) in the presence of a bifunctional cross-linker at pH 8-9 afforded novel pH-responsive microgels of 250-700 nm diameter. Both batch and semicontinuous syntheses were explored using thermal and redox initiators. Various strategies were evaluated for achieving colloidal stability, including charge stabilization, surfactant stabilization, and steric stabilization. The latter proved to be the most convenient and effective, and three types of well-defined reactive macromonomers were examined, namely, monomethoxy-capped poly(ethylene glycol) methacrylate (PEGMA), styrene-capped poly[2-(dimethylamino)ethyl methacrylate] (PDMA50-St), and partially quaternized styrene-capped poly[2-(dimethylamino)ethyl methacrylate] (10qPDMA50-St). The resulting microgels were pH-responsive, as expected. Dynamic light scattering and 1H NMR studies confirmed that reversible swelling occurred at low pH due to protonation of the tertiary amine groups on the DEA residues. The critical pH for this latex-to-microgel transition was around pH 6.5-7.0, which corresponds approximately to the known pKa of 7.0-7.3 for linear PDEA homopolymer. The microgel particles were further characterized by electron microscopy and aqueous electrophoresis studies. Their swelling and deswelling kinetics were investigated by turbidimetry. The PDEA-based microgels were compared to poly[2-(diisopropylamino)ethyl methacrylate] (PDPA) microgels prepared with identical macromonomer stabilizers. These PDPA-based microgels had a lower critical swelling pH of around pH 5.0-5.5, which correlates with the lower pKa of PDPA homopolymer. In addition, the kinetics of swelling for the PDPA microgels was somewhat slower than that observed for PDEA microgels; presumably this is related to the greater hydrophobic character of the former particles.

Synthesis of vinyl polymer-silica colloidal nanocomposites prepared using commercial alcoholic silica sols.

The surfactant-free synthesis of vinyl polymer-silica nanocomposite particles has been achieved in aqueous alcoholic media at ambient temperature in the absence of auxiliary comonomers. Styrene, methyl methacrylate, methyl acrylate, n-butyl acrylate, and 2-hydroxypropyl methacrylate were homopolymerized in turn in the presence of three commercially available ultrafine alcoholic silica sols. Stable colloidal dispersions with reasonably narrow size distributions were obtained, with silica contents of up to 58% by mass indicated by thermogravimetric analysis. Particle size distributions were assessed using both dynamic light scattering and disk centrifuge photosedimentometry. The former technique indicated that the particle size increased for the first 1-2 h at 25 degrees C and thereafter remained constant. Particle morphologies were studied using electron microscopy. Most of the colloidal nanocomposites comprised approximately spherical particles with relatively narrow size distributions, but in some cases more polydisperse or nonspherical particles were obtained. Selected acrylate-based nanocomposites were examined in terms of their film formation behavior. Scanning electron microscopy studies indicated relatively smooth films were obtained on drying at 20 degrees C, with complete loss of the original particle morphology. The optical clarity of solution-cast 10 microm nanocomposite films was assessed using visible absorption spectrophotometry, with 93-98% transmission being obtained from 400 to 800 nm; the effect of long-term immersion of such films in aqueous solutions was also examined. X-ray photoelectron spectroscopy studies indicated that the surface compositions of these nanocomposite particles are invariably silica-rich, which is consistent with their long-term colloidal stability and also with aqueous electrophoresis measurements. FT-IR studies suggested that in the case of the poly(methyl methacrylate)-silica nanocomposite particles, the carbonyl ester groups in the polymer are hydrogen-bonded to the surface silanol groups. According to differential scanning calorimetry studies, the glass transition temperatures of several poly(methyl methacrylate)-silica and polystyrene-silica nanocomposites can be either higher or lower than those of the corresponding homopolymers, depending on the nature of the silica sol.

Synthesis of sterically stabilized polystyrene latex particles using cationic block copolymers and macromonomers and their application as stimulus-responsive particulate emulsifiers for oil-in-water emulsions.

2-(Dimethylamino)ethyl methacrylate (DMA) was block copolymerized with methyl methacrylate (MMA) using group transfer polymerization to give four AB diblock, ABA triblock, and BAB triblock copolymers of low polydispersity (Mw/Mn < 1.20). In addition, a near-monodisperse styrene-functionalized DMA-based macromonomer was synthesized via oxyanionic polymerization using a potassium 4-vinylbenzyl alcoholate initiator. These five well-defined, tertiary amine methacrylate-based copolymers were evaluated as steric stabilizers for the synthesis of polystyrene latexes via emulsion and dispersion polymerization. The most efficient steric stabilizers proved to be the DMA-MMA diblock copolymer and the DMA-based macromonomer. The polystyrene latexes were characterized in terms of their particle size and morphology, stabilizer content, surface charge, and surface activity using dynamic light scattering, scanning electron microscopy, 1H NMR spectroscopy, aqueous electrophoresis measurements, and surface tensiometry, respectively. The pH-dependent surface activity exhibited by selected latexes suggests potential applications as stimulus-responsive particulate emulsifiers for oil-in-water emulsions.