AIM: We conducted a cross-sectional study to investigate risk factors for births of light-for-gestational-age (LGA) infants. METHODS: A survey was conducted at the Department of Obstetrics and Gynecology at Sapporo Medical University Hospital in Sapporo, Japan from 2013 to 2014. LGA and appropriate for gestational age (AGA) are defined as having a birthweight below the 10th percentile and between the 10th percentile and 90th percentile for gestational age at birth in the population standard of gestational age, sex, and parity, respectively. An odds ratio (OR) and its 95% confidence interval (95%CI) for LGA were calculated by analysis using the logistic regression model. RESULTS: In total, 307 inpatients (94.2%) participated in the study out of 326 consecutive post-partum inpatients. Among them, 37 infants and 237 infants were classified into the LGA and AGA groups, respectively. As a result of multivariable analysis, prevalence of gestational hypertension (OR = 8.96, 95%CI 1.81-44.35) and the presence of placental infarction (OR = 9.65, 95%CI 1.76-53.01) were significantly associated with an increased risk of LGA. Placentas weighing 510-603 g and ≥604 g were significantly associated with reduced risk of LGA (OR = 0.04, 95%CI 0.01-0.29 and OR = 0.03, 95%CI 0.01-0.32, respectively), and higher placental weights were significantly observed in the trend for reduced LGA risk (P for trend < 0.001). CONCLUSION: We found that the prevalence of gestational hypertension, lower placental weight, and the presence of placental infarctions were all independently associated with the risk of LGA. Placental abnormalities may be etiologically important for LGA risk, though further research is necessary.

Direct Writing of Copper Micropatterns Using Near-Infrared Femtosecond Laser-Pulse-Induced Reduction of Glyoxylic Acid Copper Complex.

We have fabricated Cu-based micropatterns in an ambient environment using femtosecond laser direct writing to reduce a glyoxylic acid Cu complex spin-coated onto a glass substrate. To do this, we scanned a train of focused femtosecond laser pulses over the complex film in air, following which the non-irradiated complex was removed by rinsing the substrates with ethanol. A minimum line width of 6.1 µm was obtained at a laser-pulse energy of 0.156 nJ and scanning speeds of 500 and 1000 µm/s. This line width is significantly smaller than that obtained in previous work using a CO2 laser. In addition, the lines are electrically conducting. However, the minimum resistivity of the line pattern was 2.43 × 10-6 Ω·m, which is ~10 times greater than that of the pattern formed using the CO2 laser. An X-ray diffraction analysis suggests that the balance between reduction and re-oxidation of the glyoxylic acid Cu complex determines the nature of the highly reduced Cu patterns in the ambient air.