Bestrhodopsins constitute a class of light-regulated pentameric ion channels that consist of one or two rhodopsins in tandem fused with bestrophin ion channel domains. Here, we report on the isomerization dynamics in the rhodopsin tandem domains of Phaeocystis antarctica bestrhodopsin, which binds all-trans retinal Schiff-base (RSB) absorbing at 661 nm and, upon illumination, converts to the meta-stable P540 state with an unusual 11-cis RSB. The primary photoproduct P682 corresponds to a mixture of highly distorted 11-cis and 13-cis RSB directly formed from the excited state in 1.4 ps. P673 evolves from P682 in 500 ps and contains highly distorted 13-cis RSB, indicating that the 11-cis fraction in P682 converts to 13-cis. Next, P673 establishes an equilibrium with P595 in 1.2 µs, during which RSB converts to 11-cis and then further proceeds to P560 in 48 µs and P540 in 1.0 ms while remaining 11-cis. Hence, extensive isomeric switching occurs on the early ground state potential energy surface (PES) on the hundreds of ps to µs timescale before finally settling on a metastable 11-cis photoproduct. We propose that P682 and P673 are trapped high up on the ground-state PES after passing through either of two closely located conical intersections that result in 11-cis and 13-cis RSB. Co-rotation of C11=C12 and C13=C14 bonds results in a constricted conformational landscape that allows thermal switching between 11-cis and 13-cis species of highly strained RSB chromophores. Protein relaxation may release RSB strain, allowing it to evolve to a stable 11-cis isomeric configuration in microseconds.
Assuntos
Diterpenos , Retinaldeído , Rodopsina , Isomerismo , Conformação Proteica , Rodopsina/metabolismo , Retinaldeído/químicaRESUMO
Abstract This study evaluated physicochemical properties, cytotoxicity and bioactivity of MTA Angelus (MTA), calcium silicate-based cement (CSC) and CSC with 30% Ytterbium oxide (CSC/Yb2O3). Setting time was evaluated using Gilmore needles. Compressive strength was evaluated in a mechanical machine. Radiopacity was evaluated using radiographs of materials and an aluminum scale. Solubility was evaluated after immersion in water. Cell viability was evaluated by means of MTT assay and neutral red staining, and the mineralization activity by using alkaline phosphatase activity and Alizarin Red staining. The data were submitted to ANOVA, Tukey and Bonferroni tests (5% significance). The bioactive potential was evaluated by scanning electron microscopy. The materials presented similar setting time. MTA showed the lowest compressive strength. MTA and CSC/Yb2O3 presented similar radiopacity. CSC/Yb2O3 showed low solubility. Saos-2 cell viability tests showed no cytotoxic effect, except to 1:1 dilution in NR assay which had lower cell viability when compared to the control. ALP at 1 and 7 days was similar to the control. MTA and CSC had greater ALP activity at 3 days when compared to control. All the materials present higher mineralized nodules when compared with the control. SEM analysis showed structures suggesting the presence of calcium phosphate on the surface of materials demonstrating bioactivity. Ytterbium oxide proved to be a properly radiopacifying agent for calcium silicate-based cement since it did not affected the physicochemical and biological properties besides preserving the bioactive potential of this material.
Resumo Este estudo avaliou as propriedades físico-químicas, citotoxicidade e bioatividade do MTA Angelus (MTA), cimento à base de silicato de cálcio (CSC) e CSC com 30% de óxido de itérbio (CSC/Yb2O3). O tempo de presa foi avaliado usando agulhas Gilmore. A resistência à compressão foi avaliada em uma máquina mecânica. A radiopacidade foi avaliada utilizando radiografias dos materiais e uma escala de alumínio. A solubilidade foi avaliada após imersão em água. A viabilidade celular foi avaliada por meio do ensaio MTT e coloração de vermelho neutro (NR), e a atividade de mineralização por meio da atividade da fosfatase alcalina e a coloração com Vermelho de Alizarina. Os dados foram submetidos aos testes ANOVA, Tukey e Bonferroni (5% de significância). O potencial bioativo foi avaliado por microscopia eletrônica de varredura. Os materiais apresentaram tempo de presa semelhante. O MTA mostrou menor resistência à compressão. MTA e CSC/Yb2O3 apresentaram radiopacidade semelhante. CSC/Yb2O3 apresentou menores valores de solubilidade. A viabilidade celular realizada pelos ensaios de MTT e NR não revelaram efeitos ctotóxicos em todas as diluições, exceto na diluição 1:1 no NR, o qual mostrou baixa viabilidade celular (p<0.05) em todos materiais testados quando comparado ao controle. A atividade de ALP em 1 e 7 dias foi similar ao controle (p>0.05). MTA e CSC tiveram significante aumento na atividade de ALP aos 3 dias quando comarados ao controle (p>0.05). Todos os materiais apresentaram grande produção de nódulos mineralizados quando comparados ao controle (P<0.05). A análise da SEM mostrou estruturas que sugerem a presença de depósitos de fosfato de cálcio na superfície dos materiais demonstrando bioatividade. O Yb2O3 mostrou ser um agente radiopacificador adequado em cimentos à base de silicato de cálcio uma vez que não afetou as propriedades físico-químicas e biológicas e ainda preservou o potencial bioativo desse material.
Assuntos
Óxidos/química , Itérbio/química , Bismuto/química , Silicatos/química , Compostos de Cálcio/química , Cimentos Dentários/química , Solubilidade , Coloração e Rotulagem , Teste de Materiais , Microscopia Eletrônica de Varredura , Sobrevivência Celular , Compostos de Alumínio/química , Força Compressiva , Fenômenos QuímicosRESUMO
Abstract The aim of this study was to evaluate the bond strength of root-end filling materials. Forty 2-mm-thick slices were obtained from human single-rooted teeth. After root canal preparation using a 1.5 mm diameter cylindrical drill, the dentinal walls were prepared by diamond ultrasonic tip (CVD T0F-2). The specimens were divided according the material (n=10): MTA Angelus (MTAA), MTA Sealer (MTAS, experimental), Sealer 26 (S26) and zinc oxide and eugenol cement (ZOE). The push-out test was performed in a mechanical test machine (EMIC DL 2000) at 1 mm/min speed. The failure type was evaluated by stereomicroscopy. The results were subjected to ANOVA and Tukey test, at 5% significance level. MTAA (19.18 MPa), MTAS (19.13 MPa) and S26 (15.91 MPa) showed higher bond strength (p<0.05). ZOE (9.50 MPa) showed the least bond strength values (p<0.05). Adhesive failure was prevalent in all groups, except for ZOE, which showed mixed failures. It was concluded that root-end filling materials MTA Angelus, MTA Sealer and Sealer 26 showed higher bond strength to dentinal walls than zinc oxide and eugenol cement after retrograde preparation.
Resumo O objetivo deste estudo foi avaliar a resistência de união de materiais retrobturadores. Quarenta fatias de 2 mm de espessura foram obtidas a partir de dentes unirradiculares humanos. Após o preparo do canal radicular usando uma broca cilíndrica de 1,5 mm de diâmetro, as paredes de dentina foram preparadas usando uma ponta de ultra-som diamantada (CVD T0F-2). As amostras foram divididas de acordo com os materiais (n=10): MTA Angelus (MTAA), MTA Sealer (MTAS, experimental), Sealer 26 (S26) e óxido de zinco e eugenol (ZOE). O teste de push-out foi realizado utilizando uma máquina de ensaios mecânicos (EMIC DL 2000) com velocidade de 1 mm/min. O tipo de falha foi avaliado em estereomicroscópio. Os resultados foram submetidos a ANOVA e teste de Tukey, com níveis de variância de 5%. MTAA (19,18 MPa), MTAS (19,13 MPa) e S26 (15,91 MPa) apresentaram os maiores valores de resistência de união (p<0,05). ZOE (9,50 MPa) apresentou os menores valores de resistência de união (p<0,05). A falha adesiva foi prevalente em todos os grupos, com exceção do ZOE, que apresentou falhas mistas. Concluiu-se que os materiais retrobturadores MTA Angelus, MTA Sealer e Sealer 26 apresentam maior resistência de união às paredes dentinárias que o óxido de zinco e eugenol após o preparo retrógrado.
Assuntos
Humanos , Teste de Materiais , Materiais Restauradores do Canal Radicular/química , Preparo de Canal RadicularRESUMO
Introdução: O Mineral Trióxido Agregado (MTA) é composto por cimento Portland (CP) e um radiopacificador (óxido de bismuto). Objetivo: Avaliar tempo de presa, solubilidade, pH, liberação de íons Cálcio e radiopacidade do cimento Portland puro ou associado a quatro radiopacificadores (sulfato de bário, carbonato de bismuto, óxido de bismuto e iodofórmio), comparados ao MTA branco (Angelus, Londrina, Brasil). Material e Método: A proporção empregada CP/radiopacificador foi de 4:1 em peso, (80% de cimento Portland e 20% de radiopacificador). A especificação 57 da ADA foi usada para avaliação do tempo de presa. A solubilidade foi analisada segundo a especificação ISO 6876/2001. A avaliação do pH foi realizada com peagâmetro digital e a liberação de íons Ca++foi verificada por meio de espectrofotômetro de absorção atômica. A radiopacidade foi determinada em milímetros de alumínio (mm/Al). Os resultados foram submetidos aos testes de Análise de Variância e Tukey, nível de significância 5%. Resultado: O sulfato de bário não alterou o tempo de presa final do CP. Radiopacidade inferior ao mínimo recomendado pelas normas da ADA nº 57 e ISO 6876/2001 foi observada para CP e CP associado com sulfato de bário. O CP associado ao iodofórmio apresentou solubilidade acima dos 3% recomendados pela ISO 6876/2001. Todos os materiais proporcionaram alcalinização do meio e promoveram liberação de íons cálcio. Conclusão: Carbonato de bismuto ou óxido de bismuto proporcionaram tempo de presa inicial, solubilidade, pH, liberação de íons Cálcio e radiopacidade adequados quando associados ao CP. .
Introduction: Mineral Trioxide Aggregate (MTA) is composed of Portland cement (PC), and a radiopacifier (bismuth oxide). Objective: To evaluate the setting time, solubility, pH, calcium ion release and radiopacity of pure Portland cement and its association to four radiopacifiers, (Barium sulfate, bismuth carbonate, bismuth oxide and iodoform), and White MTA (Angelus, Londrina, Brazil). Material and Method: The ratio CP/radiopacifier used was 4:1 by weight (80% Portland cement and 20% radiopacifier). The setting time was evaluated according the specification ADA 57. The solubility was analyzed according to ISO 6876/2001 specification. The pH was evaluated using a digital pHmeter and the release of Ca++ ions by atomic absorption spectrophotometer. The radiopacity was measured in millimeters of aluminum (mm/Al). The results were submitted to ANOVA and Tukey tests using 5% of significance level. Result: Barium sulfate did not alter the final setting time of the PC. Observed radiopacity was less than the minimum recommended by ADA 57 and ISO 6876/2001 for CP and CP associated with barium sulfate. The PC associated with iodoform showed solubility above the 3% recommended by ISO 6876/2001. All materials provided alkalinization and promoted calcium ion release. Conclusion: Bismuth carbonate and bismuth oxide provided proper initial setting time, solubility, pH, calcium ion release and radiopacity when combined with CP. .