RESUMO
Nanocellulose from sugarcane bagasse was isolated by high pressure homogenization in a homogeneous media. Pretreatment with an ionic liquid (1-butyl-3-methylimidazolium chloride ([Bmim]Cl)) was initially involved to dissolve the bagasse cellulose. Subsequently, the homogeneous solution was passed through a high pressure homogenizer without any clogging. The nanocellulose was obtained at 80 MPa for 30 cycles with recovery of 90% under the optimum refining condition. Nanocellulose had been characterized by Fourier transformed infrared spectra, X-ray diffraction, thermogravimetric analysis, rheological measurements and transmission electron microscopy. The results showed that nanocellulose was 10-20 nm in diameter, and presented lower thermal stability and crystallinity than the original cellulose. The developed nanocellulose would be a very versatile renewable material.