RESUMO
Crystalline silicon films on an inexpensive glass substrate are currently prepared by depositing an amorphous silicon film and then crystallizing it by excimer laser annealing, rapid thermal annealing, or metal-induced crystallization because crystalline silicon films cannot be directly deposited on glass at a low temperature. It was recently shown that by adding HCI gas in the hot-wire chemical vapor deposition (HWCVD) process, the crystalline silicon film can be directly deposited on a glass substrate without additional annealing. The electrical properties of silicon films prepared using a gas mixture of SiH4 and HCl in the HWCVD process could be further improved by controlling the initial structure, which was achieved by adjusting the delay time in deposition. The size of the silicon particles in the initial structure increased with increasing delay time, which increased the mobility and decreased the resistivity of the deposited films. The 0 and 5 min delay times produced the silicon particle sizes of approximately 10 and approximately 28 nm, respectively, in the initial microstructure, which produced the final films, after deposition for 300 sec, of resistivities of 0.32 and 0.13 Omega-cm, mobilities of 1.06 and 1.48 cm2 V(-1) S(-1), and relative densities of 0.87 and 0.92, respectively.
RESUMO
Since n-type crystalline silicon films have the electric property much better than those of hydrogenated amorphous and microcrystalline silicon films, they can enhance the performance of advanced electronic devices such as solar cells and thin film transistors (TFTs). Since the formation of amorphous silicon is unavoidable in the low temperature deposition of microcrystalline silicon on a glass substrate at temperatures less than 550 degrees C in the plasma-enhanced chemical vapour deposition and hot wire chemical vapour deposition (HWCVD), crystalline silicon films have not been deposited directly on a glass substrate but fabricated by the post treatment of amorphous silicon films. In this work, by adding the HCl gas, amorphous silicon-free n-type crystalline silicon films could be deposited directly on a glass substrate by HWCVD. The resistivity of the n-type crystalline silicon film for the flow rate ratio of [HCl]/[SiH4] = 7.5 and [PH3]/[SiH4] = 0.042 was 5.31 x 10(-4) ohms cm, which is comparable to the resistivity 1.23 x 10(-3) ohms cm of films prepared by thermal annealing of amorphous silicon films. The absence of amorphous silicon in the film could be confirmed by high resolution transmission electron microscopy.