Electrocaloric materials are promising working bodies for caloric-based technologies, suggested as an efficient alternative to the vapor compression systems. However, their materials efficiency defined as the ratio of the exchangeable electrocaloric heat to the work needed to trigger this heat remains unknown. Here, we show by direct measurements of heat and electrical work that a highly ordered bulk lead scandium tantalate can exchange more than a hundred times more electrocaloric heat than the work needed to trigger it. Besides, our material exhibits a maximum adiabatic temperature change of 3.7 K at an electric field of 40 kV cm-1. These features are strong assets in favor of electrocaloric materials for future cooling devices.
RESUMO
The electrocaloric effect (ECE) in ferroelectric materials is a promising candidate for small, effective, low cost, and environmentally friendly solid state cooling applications. Instead of the commonly used indirect estimates based on Maxwell's relations, direct measurements of the ECE are required to obtain reliable values. In this work, we report on a custom-made quasi-adiabatic calorimeter for direct ECE measurements. The ECE is measured for two promising lead-free materials: Ba(Zr0.12Ti0.88)O3 and Ba(Zr0.2Ti0.8)O3 bulk ceramics. Adiabatic temperature changes of ΔTEC = 0.5 K at 355 K and ΔTEC = 0.3 K at 314 K were achieved under the application of an electric field of 2 kV/mm for the Ba(Zr0.12Ti0.88)O3 and Ba(Zr0.2Ti0.8)O3 samples, respectively. The quasi-adiabatic ECE measurements reliably match other direct EC measurements using a differential scanning calorimeter or an infrared camera. The data are compared to indirect EC estimations based on Maxwell's relations and show that the indirect measurements typically underestimate the effect to a certain degree.