RESUMO
Currently, the desired research focus in energy storage technique innovation has been gradually shifted to next-generation aqueous batteries holding both high performance and sustainability. However, aqueous Zn-I2 batteries have been deemed to have great sustainable potential, owing to the merits of cost-effective and eco-friendly nature. However, their commercial application is hindered by the serious shuttle effect of polyiodides during reversible operations. In this work, a Janus functional binder based on chitosan (CTS) molecules was designed and prepared; the polar terminational groups impart excellent mechanical robustness to hybrid binders; meanwhile, it can also deliver isochronous enhancement on physical adsorption and redox kinetics toward I2 species. By feat of highly effective remission to shuttle effect, the CTS cell exhibits superb electrochemical storage capacities with long-term robustness, specifically, 144.1 mAh g-1, at a current density of 0.2 mA g-1 after 1500 cycles. Simultaneously, the undesired self-discharging issue could be also well-addressed; the Coulombic efficiency could remain at 98.8 % after resting for 24 h. More importantly, CTS molecules endow good biodegradability and reusable properties; after iodine species were reloaded, the recycled devices could also deliver specific capacities of 73.3 mAh g-1, over 1000 cycles. This Janus binder provides a potential synchronous solution to realize high comprehensive performance with high iodine utilization and further make it possible for sustainable Zn-I2 batteries.
RESUMO
Since sodium-ion batteries (SIBs) have become increasingly commercialized in recent years, Na3V2(PO4)2O2F (NVPOF) offers promising economic potential as a cathode for SIBs because of its high operating voltage and energy density. According to reports, NVPOF performs poorly in normal commercial poly(vinylidene fluoride) (PVDF) binder systems and performs best in combination with aqueous binder. Although in line with the concept of green and sustainable development for future electrode preparation, aqueous binders are challenging to achieve high active material loadings at the electrode level, and their relatively high surface tension tends to cause the active material on the electrode sheet to crack or even peel off from the collector. Herein, a cross-linkable and easily commercial hybrid binder constructed by intermolecular hydrogen bonding (named HPP) has been developed and utilized in an NVPOF system, which enables the generation of a stable cathode electrolyte interphase on the surface of active materials. According to theoretical simulations, the HPP binder enhances electronic/ionic conductivity, which greatly lowers the energy barrier for Na+ migration. Additionally, the strong hydrogen-bond interactions between the HPP binder and NVPOF effectively prevent electrolyte corrosion and transition-metal dissolution, lessen the lattice volume effect, and ensure structural stability during cycling. The HPP-based NVPOF offers considerably improved rate capability and cycling performance, benefiting from these benefits. This comprehensive binder can be extended to the development of next-generation energy storage technologies with superior performance.
RESUMO
All-weather operation is considered an ultimate pursuit of the practical development of sodium-ion batteries (SIBs), however, blocked by a lack of suitable electrolytes at present. Herein, by introducing synergistic manipulation mechanisms driven by phosphorus/silicon involvement, the compact electrode/electrolyte interphases are endowed with improved interfacial Na-ion transport kinetics and desirable structural/thermal stability. Therefore, the modified carbonate-based electrolyte successfully enables all-weather adaptability for long-term operation over a wide temperature range. As a verification, the half-cells using the designed electrolyte operate stably over a temperature range of -25 to 75 °C, accompanied by a capacity retention rate exceeding 70% even after 1700 cycles at 60 °C. More importantly, the full cells assembled with Na3V2(PO4)2O2F cathode and hard carbon anode also have excellent cycling stability, exceeding 500 and 1000 cycles at -25 to 50 °C and superb temperature adaptability during all-weather dynamic testing with continuous temperature change. In short, this work proposes an advanced interfacial regulation strategy targeted at the all-climate SIB operation, which is of good practicability and reference significance.
RESUMO
Sodium-ion batteries (SIBs) have gradually become one of the most promising energy storage techniques in the current era of post-lithium-ion batteries. For anodes, transitional metal selenides (TMSe) based materials are welcomed choices , owing to relatively higher specific capacities and enriched redox active sites. Nevertheless, current bottlenecks are blamed for their poor intrinsic electronic conductivities, and uncontrollable volume expansion during redox reactions. Given that, an interfacial-confined isochronous conversion strategy is proposed, to prepare orthorhombic/cubic biphasic TMSe heterostructure, namely CuSe/Cu3 VSe4 , through using MXene as the precursor, followed by Cu/Se dual anchorage. As-designed biphasic TMSe heterostructure endows unique hierarchical structure, which contains adequate insertion sites and diffusion spacing for Na ions, besides, the surficial pseudocapacitive storage behaviors can be also proceeded like 2D MXene. By further investigation on electronic structure, the theoretical calculations indicate that biphasic CuSe/Cu3 VSe4 anode exhibits well-enhanced properties, with smaller bandgap and thus greatly improves intrinsic poor conductivities. In addition, the dual redox centers can enhance the electrochemical Na ions storage abilities. As a result, the as-designed biphasic TMSe anode can deliver a reversible specific capacity of 576.8 mAh g-1 at 0.1 A g-1 , favorable Na affinity, and reduced diffusion barriers. This work discloses a synchronous solution toward demerits in conductivities and lifespan, which is inspiring for TMSe-based anode development in SIBs systems.
RESUMO
2D compounds exfoliated from weakly bonded bulk materials with van der Waals (vdW) interaction are easily accessible. However, the strong internal ionic/covalent bonding of most inorganic crystal frameworks greatly hinders 2D material exfoliation. Herein, we first proposed a radical/strain-synergistic strategy to exfoliate non-vdW interacting pseudo-layered phosphate framework. Specifically, hydroxyl radicals (â OH) distort the covalent bond irreversibly, meanwhile, H2O molecules as solvents, further accelerating interlayered ionic bond breakage but mechanical expansion. The innovative 2D laminar NASICON-type Na3V2(PO4)2O2F crystal, exfoliated by â OH/H2O synergistic strategy, exhibits enhanced sodium-ion storage capacity, high-rate performance (85.7â mAh g-1 at 20â C), cyclic life (2300 cycles), and ion migration rates, compared with the bulk framework. Importantly, this chemical/physical dual driving technique realized the effective exfoliation for strongly coupled pseudo-layered frameworks, which accelerates 2D functional material development.
RESUMO
During multivalent ions insertion processes, intense electrostatic interaction between charge carriers and host makes the high-performance reversible Al3+ storage remains an elusive target. On account of the strong electrostatic repulsion and poor robustness, Prussian Blue analogues (PBAs) suffer severely from the inevitable and large strain and phase change during reversible Al3+ insertion. Herein, we demonstrate an entropy-driven strategy to realize ultralong life aqueous Al-ion batteries (AIBs) based on medium entropy PBAs (ME-PBAs) host. By multiple redox active centers introduction, the intrinsic poor conductivity can be enhanced simultaneously, resulting in outstanding capabilities of electrochemical Al3+ storage. Meanwhile, the co-occupation at metal sites in PBA frameworks can also increase the M-N bond intensity, which is beneficial for constraining the phase change during consecutive Al3+ reversible insertion, to realize an extended lifespan over 10,000 cycles. Based on the calculation at different operation states, the fluctuation of ME-PBA lattice parameters is only 1.2 %. Assembled with MoO3 anodes, the full cells can also deliver outstanding electrochemical properties. The findings highlight that, the entropy regulation strategy could uncover the isochronous constraint on both strain and phase transition for long-term reversible Al3+ storage, providing a promising design for advanced electrode materials for aqueous multivalent ions batteries.
RESUMO
With the rapid development of sodium-ion batteries (SIBs), it is urgent to exploit the cathode materials with good rate capability, attractive high energy density and considerable long cycle performance. Na3V2(PO4)3(NVP), as a NASICON-type electrode material, is one of the cathode materials with great potential for application because of its good thermal stability and stable. However, NVP has the inherent problem of low electronic conductivity, and various strategies are proposed to improve it, moreover, nanotechnology or nanostructure are involved in these strategies, the construction of nanostructured active particles and nanocomposites with conductive carbon networks have been shown to be effective in improving the electrical conductivity of NVP. Herein, we review the research progress of NVP performance improvement strategies from the perspective of nanostructures and classifies the prepared nanomaterials according to their different nano-dimension. In addition, NVP nanocomposites are reviewed in terms of both preparation methods and promotion effects, and examples of NVP nanocomposites at different nano-dimension are given. Finally, some personal views are presented to provide reasonable guidance for the research and design of high-performance polyanionic cathode materials of SIBs.
RESUMO
In recent years, with the vigorous development and gradual deployment of new energy vehicles, more attention has been paid to the research on lithium-ion batteries (LIBs). Compared with the booming LIBs, lithium primary batteries (LPBs) own superiority in specific energy and self-discharge rate and are usually applied in special fields such as medical implantation, aerospace, and military. Widespread application in special fields also means more stringent requirements for LPBs in terms of energy density, working temperature range and shelf life. Therefore, how to obtain LPBs with high energy density, wide operational temperature range and long storage life is of great importance in future development. In view of the above, this paper reviews the latest research on LPBs in cathode, anode and electrolyte over the years, and puts forward relevant insights for LPBs, along with the intention to explore avenues for the design of LPBs components in the coming decades and promote further development in this field.
RESUMO
There are still many problems that hinder the development of sodium-ion batteries (SIBs), including poor rate performance, short-term cycle lifespan, and inferior low-temperature property. Herein, excellent Na-storage performance in fluorophosphate (Na3 V2 (PO4 )2 F3 ) cathode is achieved by lattice regulation based on charge balance theory. Lattice regulation of aliovalent Mn2+ for V3+ increases both electronic conductivity and Na+ -migration kinetics. Because of the maintaining of electrical neutrality in the material, aliovalent Mn2+ -introduced leads to the coexistence of V3+ and V4+ from charge balance theory. It decreases the particle size and improves the structural stability, suppressing the large lattice distortion during cathode reaction processes. These multiple effects enhance the specific capacity (123.8 mAh g-1 ), outstanding high-rate (68% capacity retention at 20 C), ultralong cycle (only 0.018% capacity attenuation per cycle over 1000 cycles at 1 C) and low-temperature (96.5% capacity retention after 400 cycles at -25 °C) performances of Mn2+ -induced Na3 V1.98 Mn0.02 (PO4 )2 F3 when used as cathode in SIBs. Importantly, a feasible sodium-ion full battery is assembled, achieving outstanding rate capability and cycle stability. The strategy of aliovalent ion-induced lattice regulation constructs cathode materials with superior performances, which is available to improve other electrode materials for energy storage systems.
RESUMO
Although ether-based electrolytes have been extensively applied in anode evaluation of batteries, anodic instability arising from solvent oxidability is always a tremendous obstacle to matching with high-voltage cathodes. Herein, by rational design for solvation configuration, the fully coordinated ether-based electrolyte with strong resistance against oxidation is reported, which remains anodically stable with high-voltage Na3 V2 (PO4 )2 O2 F (NVPF) cathode under 4.5â V (versus Na+ /Na) protected by an effective interphase. The assembled graphite//NVPF full cells display superior rate performance and unprecedented cycling stability. Beyond that, the constructed full cells coupling the high-voltage NVPF cathode with hard carbon anode exhibit outstanding electrochemical performances in terms of high average output voltage up to 3.72â V, long-term cycle life (such as 95 % capacity retention after 700 cycles) and high energy density (247â Wh kg-1 ). In short, the optimized ether-based electrolyte enriches systematic options, the ability to maintain oxidative stability and compatibility with various anodes, exhibiting attractive prospects for application.
RESUMO
Polyanion-type phosphate materials are highly promising cathode candidates for next-generation batteries due to their excellent structural stability during cycling; however, their poor conductivity has impeded their development. Isostructural and multivalent anion substitution combined with carbon coating is proposed to greatly improve the electrochemical properties of phosphate cathode in sodium-ion batteries (SIBs). Specifically, multivalent tetrahedral SiO4 4- substitute for PO4 3- in Na3 V2 (PO4 )3 (NVP) lattice, preparing the optimal Na3.1 V2 (PO4 )2.9 (SiO4 )0.1 with high-rate capability (delivering a high capacity of 82.5 mAh g-1 even at 20 C) and outstanding cyclic stability (≈98% capacity retention after 500 cycles at 1 C). Theoretical calculation and experimental analyses reveal that the anion-substituted Na3.1 V2 (PO4 )2.9 (SiO4 )0.1 reduces the bandgap of NVP lattice and enhanced its structural stability, Na+ -diffusion kinetics and electronic conductivity. This strategy of multivalent and isostructural anion substitution chemistry provides a new insight to develop advanced phosphate cathodes.
RESUMO
Phosphate cathode materials are practical for use in sodium-ion batteries (SIBs) owing to their high stability and long-term cycle life. In this work, the temperature-dependent properties of the phosphate cathode Na3 V2 (PO4 )2 O2 F (NVPOF) are studied in a wide temperature range from -25 to 55 °C. Upon cycling at general temperature (above 0 °C), the NVPOF cathode retains an excellent charge/discharge performance, and the rate capability is noteworthy, indicating that NVPOF is a competitive candidate as a temperature-adaptive cathode for SIBs. Upon decreasing the temperature below 0 °C, the cell performance deteriorates, which may be caused by the electrolyte and Na electrode, based on the study of ionic conductivity and electrode kinetics. This work proposes a new breakthrough point for the development of SIBs with high performance over a wide temperature range for advanced power systems.
RESUMO
Na3MnTi(PO4)3 (NMTP) emerges as a promising cathode material with high-performance for sodium-ion batteries (SIBs). Nevertheless, its development has been limited by several challenges, including poor electronic conductivity, the Mn3+ Jahn-Teller effect, and the presence of a Na+/Mn2+ cation mixture. To address these issues, we have developed a cation/anion-dual regulation strategy to activate the redox reactions involving manganese, thereby significantly enhancing the performance of NMTP. This strategy simultaneously enhances the structural dynamics and facilitates rapid ion transport at high rates by inducing the formation of sodium vacancy. The combined effects of these modifications lead to a substantial improvement in specific capacity (79.1 mAh/g), outstanding high-rate capabilities (35.9 mAh/g at 10C), and an ultralong cycle life (only 0.040 % capacity attenuation per cycle over 250 cycles at 1C for Na3.34Mn1.2Ti0.8(PO3.98F0.02)3) when used as a cathode material in SIBs. Furthermore, its performance in full cell demonstrates impressive rate capability (44.4 mAh/g at 5C) and exceptional cycling stability (with only 0.116 % capacity decay per cycle after 150 cycles at 1C), suggesting its potential for practical applications. This work presents a dual regulation strategy targeting different sites, offering a significant advancement in the development of NASICON phosphate cathodes for SIBs.
RESUMO
Flexible quasi-solid-state sodium ion batteries featuring their low-cost, high safety and excellent mechanical strength have attracted widespread interest in the field of wearable electronic devices. However, the development of such batteries faces great challenges including the construction of interfacial compatible flexible electrode materials and addressing the high safety demands of electrolyte. Here selenium-vacancies regulated bimetallic selenide heterojunctions anchored on waste cotton cloth-derived flexible carbon cloth (FCC) with robust interfacial C-Se-Co/Fe chemical bonds as a flexible anode material (CCFSF) is proposed by ultrafast microwave pyrolysis method. Rich selenium vacancies and CoSe2 /FeSe2-x heterostructures are synchronously formed that can significantly improve ionic and electronic diffusion kinetics. Additionally, a uniform carbon layer coating on the surface of Se-deficient heterostructures endows it with outstanding structural stability. The flexible cathode (PB@FCC) is also fabricated by directly growing Prussian blue nanoparticles on the FCC. Furthermore, an advanced flexible quasi-solid-state Na-ion pouch cell is assembled by coupling CCFSF anode, PB@FCC cathode with P(VDF-HFP)-based gel polymer electrolyte. The full cell not only demonstrates excellent energy storage performance but also robust mechanical flexibility and safety. The present work offers an effective avenue to achieve high safety flexible energy storage device, promoting the development of flexible wearable electronic devices.
RESUMO
The unique electronic and crystal structures of rare earth metals (RE) offer promising opportunities for enhancing the hydrogen evolution reaction (HER) properties of materials. In this work, a series of RE (Sm, Nd, Pr and Ho)-doped Rh@NSPC (NSPC stands for N, S co-doped porous carbon nanosheets) with sizes less than 2 nm are prepared, utilizing a simple, rapid and solvent-free joule-heat pyrolysis method for the first time. The optimized Sm-Rh@NSPC achieves HER performance. The high-catalytic performance and stability of Sm-Rh@NSPC are attributed to the synergistic electronic interactions between Sm and Rh clusters, leading to an increase in the electron cloud density of Rh, which promotes the adsorption of H+, the dissociation of Rh-H bonds and the release of H2. Notably, the overpotential of the Sm-Rh@NSPC catalyst is a mere 18.1 mV at current density of 10 mAcm-2, with a Tafel slope of only 15.2 mV dec-1. Furthermore, it exhibits stable operation in a 1.0 M KOH electrolyte at 10 mA cm-2 for more than 100 h. This study provides new insights into the synthesis of composite RE hybrid cluster nanocatalysts and their RE-enhanced electrocatalytic performance. It also introduces fresh perspectives for the development of efficient electrocatalysts.
RESUMO
Due to the rapid increase in the number of spent lithium-ion batteries, there has been a growing interest in the recovery of degraded graphite. In this work, a rapid thermal shock (RTS) strategy is proposed to regenerate spent graphite for use in lithium-ion batteries. The results of structural and morphological characterization demonstrate that the graphite is well regenerated by the RTS process. Additionally, an amorphous carbon layer forms and coats onto the surface of the graphite, contributing to excellent rate performance. The regenerated graphite (RG-1000) displays excellent rate performance, with capacities of 413 mAh g-1 at 50 mA g-1 and 102.1 mAh g-1 at 1000 mA g-1, respectively. Furthermore, it demonstrates long-term cycle stability, maintaining a capacity of 80 mAh g-1 at 1000 mA g-1 with a capacity retention of 78.4 % after 600 cycles. This RTS method enables rapid and efficient regeneration of spent graphite anodes for lithium-ion batteries, providing a facile and environmentally friendly strategy for their direct regeneration.
RESUMO
The stable phase transformation during electrochemical progress drives extensive research on vanadium-based polyanions in sodium-ion batteries (SIBs), especially Na3V2(PO4)3 (NVP). And the electron transfer between V3+/4+ redox couple in NVP could be generally achieved, owing to the confined crystal variation during battery service. However, the more favorable V4+/5+ redox couple is still in hard-to-access situation due to the high barrier and further brings about the corresponding inefficiency in energy densities. In this work, the multilevel redox in NVP frame (MLNP) alters reaction pathway to undergo homeostatic solid solution process and breaks the high barrier of V4+/5+ at high voltage, taking by progressive transition metal (V, Fe, Ti, and Cr) redox couple. The diversified reaction paths across diffusion barriers could be realized by distinctive release/uptake of inactive Na1 site, confirmed by the calculations of density functional theory. Thereby its volume change is merely 1.73% during the multielectron-transfer process (≈2.77 electrons). MLNP cathode could achieve an impressive energy density of 440 Wh kg-1, driving the leading development of MLNP among other NASICON structure SIBs. The integration of multiple redox couples with low strain modulates the reaction pathway effectively and will open a new avenue for fabricating high-performance cathodes in SIBs.
RESUMO
Expanded graphite (EG) stands out as a promising material for the negative electrode in potassium-ion batteries. However, its full potential is hindered by the limited diffusion pathway and storage sites for potassium ions, restricting the improvement of its electrochemical performance. To overcome this challenge, defect engineering emerges as a highly effective strategy to enhance the adsorption and reaction kinetics of potassium ions on electrode materials. This study delves into the specific effectiveness of defects in facilitating potassium storage, exploring the impact of defect-rich structures on dynamic processes. Employing ball milling, we introduce surface defects in EG, uncovering unique effects on its electrochemical behavior. These defects exhibit a remarkable ability to adsorb a significant quantity of potassium ions, facilitating the subsequent intercalation of potassium ions into the graphite structure. Consequently, this process leads to a higher potassium voltage. Furthermore, the generation of a diluted stage compound is more pronounced under high voltage conditions, promoting the progression of multiple stage reactions. Consequently, the EG sample post-ball milling demonstrates a notable capacity of 286.2 mAh g-1 at a current density of 25 mA g-1, showcasing an outstanding rate capability that surpasses that of pristine EG. This research not only highlights the efficacy of defect engineering in carbon materials but also provides unique insights into the specific manifestations of defects on dynamic processes, contributing to the advancement of potassium-ion battery technology.
RESUMO
After application in electric vehicles, spent LiFePO4 (LFP) batteries are typically decommissioned. Traditional recycling methods face economic and environmental constraints. Therefore, direct regeneration has emerged as a promising alternative. However, irreversible phase changes can significantly hinder the efficiency of the regeneration process owing to structural degradation. Moreover, improper storage and treatment practices can lead to metamorphism, further complicating the regeneration process. In this study, a sustainable recovery method is proposed for the electrochemical repair of LFP batteries. A ligand-chain Zn-complex (ZnDEA) is utilized as a structural regulator, with its âNHâ group alternatingly facilitating the binding of preferential transition metal ions (Fe3+ during charging and Zn2+ during discharging). This dynamic coordination ability helps to modulate volume changes within the recovered LFP framework. Consequently, the recovered LFP framework can store more Li-ions, enhance phase transition reversibility between LFP and FePO4 (FP), modify the initial Coulombic efficiency, and reduce polarization voltage differences. The recovered LFP cells exhibit excellent capacity retention of 96.30% after 1500 cycles at 2 C. The ligand chain repair mechanism promotes structural evolution to facilitate ion migration, providing valuable insights into the targeted ion compensation for environmentally friendly recycling in practical applications.