RESUMO
Topochemical reactions have led to great progress in the discovery of new metastable compounds with novel chemical and physical properties. With these reactions, the overall crystal structure of the host material is generally maintained. Here we report a topochemical synthesis of a hexagonal nitride hydride, h-Ca3 CrN3 H, by heating an orthorhombic nitride, o-Ca3 CrN3 , under hydrogen at 673â K, accompanied by a rotational structural transformation. The hydrogen intercalation modifies the Ca-N rock-salt-like atomic packing in o-Ca3 CrN3 to a face-sharing octahedral chain in h-Ca3 CrN3 H, mimicking a "hinged tessellation" movement. In addition, the h-Ca3 CrN3 H exhibited stable ammonia synthesis activity when used as a catalyst.
RESUMO
Controlling oxygen deficiencies is essential for the development of novel chemical and physical properties such as high-Tc superconductivity and low-dimensional magnetic phenomena. Among reduction methods, topochemical reactions using metal hydrides (e.g., CaH2) are known as the most powerful method to obtain highly reduced oxides including Nd0.8Sr0.2NiO2 superconductor, though there are some limitations such as competition with oxyhydrides. Here we demonstrate that electrochemical protonation combined with thermal dehydration can yield highly reduced oxides: SrCoO2.5 thin films are converted to SrCoO2 by dehydration of HSrCoO2.5 at 350 °C. SrCoO2 forms square (or four-legged) spin tubes composed of tetrahedra, in contrast to the conventional infinite-layer structure. Detailed analyses suggest the importance of the destabilization of the SrCoO2.5 precursor by electrochemical protonation that can greatly alter reaction energy landscape and its gradual dehydration (H1-xSrCoO2.5-x/2) for the SrCoO2 formation. Given the applicability of electrochemical protonation to a variety of transition metal oxides, this simple process widens possibilities to explore novel functional oxides.
RESUMO
Making and breaking bonds in a solid-state compound greatly influences physical properties. A well-known playground for such bonding manipulation is the ThCr2Si2-type structure AT2X2, allowing a collapse transition where a X-X dimer forms by a chemical substitution or external stimuli. Here, we report a pressure-induced collapse transition in the structurally related BaTi2Pn2O (Pn = As, Sb) at a transition pressure Pc of â¼15 GPa. The Pn-Pn bond formation is related with Pn-p band filling, which is controlled by charge transfer from the Ti-3d band. At Pc, the Sb-Sb distance in BaTi2Sb2O shrinks due to bond formation, but interestingly, the Sb-Sb expands with increasing pressure above Pc. This expansion, which was not reported in ThCr2Si2-type compounds, may arise from heteroleptic coordination geometry around titanium, where a compression of the Ti-O bond plays a role. Electrical resistivity measurements of BaTi2Sb2O up to 55 GPa revealed an increasing trend of the superconducting transition temperature with pressure. This study presents structure motifs that allow flexible bonding manipulation and property control with heteroleptic coordination geometry.
RESUMO
While cation order-disorder transitions have been achieved in a wide range of materials and provide crucial effects in various physical and chemical properties, anion analogues are scarce. Here we have expanded the number of known lanthanide oxyhydrides, LnHO (Ln = La, Ce, Pr, Nd), to include Ln = Sm, Gd, Tb, Dy, Ho, and Er, which has allowed the observation of an anion order-disorder transition from the anion-ordered fluorite structure ( P4/ nmm) for larger Ln3+ ions (La-Nd) to a disordered arrangement ( Fm3Ì m) for smaller Ln3+ (Sm-Er). Structural analysis reveals that with the increase of Ln3+ radius (application of negative chemical pressure), the oxide anion in the disordered phase becomes too under-bonded, which drives a change to an anion-ordered structure, with smaller OLn4 and larger HLn4 tetrahedra, demonstrating that the size flexibility of hydride anions drives this transition. Such anion ordering control is crucial regarding applications that involve hydride diffusion such as catalysis and electrochemical solid devices.
RESUMO
BACKGROUND: Intraoperative oxygen management is poorly understood. It was hypothesized that potentially preventable hyperoxemia and substantial oxygen exposure would be common during general anesthesia. METHODS: A multicenter, cross-sectional study was conducted to describe current ventilator management, particularly oxygen management, during general anesthesia in Japan. All adult patients (16 yr old or older) who received general anesthesia over 5 consecutive days in 2015 at 43 participating hospitals were identified. Ventilator settings and vital signs were collected 1 h after the induction of general anesthesia. We determined the prevalence of potentially preventable hyperoxemia (oxygen saturation measured by pulse oximetry of more than 98%, despite fractional inspired oxygen tension of more than 0.21) and the risk factors for potentially substantial oxygen exposure (fractional inspired oxygen tension of more than 0.5, despite oxygen saturation measured by pulse oximetry of more than 92%). RESULTS: A total of 1,786 patients were found eligible, and 1,498 completed the study. Fractional inspired oxygen tension was between 0.31 and 0.6 in 1,385 patients (92%), whereas it was less than or equal to 0.3 in very few patients (1%). Most patients (83%) were exposed to potentially preventable hyperoxemia, and 32% had potentially substantial oxygen exposure. In multivariable analysis, old age, emergency surgery, and one-lung ventilation were independently associated with increased potentially substantial oxygen exposure, whereas use of volume control ventilation and high positive end-expiratory pressure levels were associated with decreased potentially substantial oxygen exposure. One-lung ventilation was particularly a strong risk factor for potentially substantial oxygen exposure (adjusted odds ratio, 13.35; 95% CI, 7.24 to 24.60). CONCLUSIONS: Potentially preventable hyperoxemia and substantial oxygen exposure are common during general anesthesia, especially during one-lung ventilation. Future research should explore the safety and feasibility of a more conservative approach for intraoperative oxygen therapy.
Assuntos
Anestesia Geral/métodos , Monitorização Intraoperatória/métodos , Oxigenoterapia/métodos , Respiração Artificial/métodos , Ventiladores Mecânicos , Idoso , Anestesia Geral/efeitos adversos , Anestesia Geral/normas , Estudos Transversais , Feminino , Humanos , Hiperóxia/induzido quimicamente , Hiperóxia/prevenção & controle , Masculino , Pessoa de Meia-Idade , Monitorização Intraoperatória/normas , Ventilação Monopulmonar/efeitos adversos , Ventilação Monopulmonar/métodos , Ventilação Monopulmonar/normas , Oxigenoterapia/efeitos adversos , Oxigenoterapia/normas , Estudos Prospectivos , Respiração Artificial/efeitos adversos , Respiração Artificial/normas , Ventiladores Mecânicos/normasRESUMO
Layered perovskite titanium oxyhydrides have been prepared by low-temperature topochemical CaH2 reduction from Ruddlesden-Popper Sr n+1Ti nO3 n+1 phases ( n = 1, 2) and structurally characterized by combined synchrotron X-ray and neutron diffraction data refinements. In the single-layered Sr2TiO3.91(2)D0.14(1) material, hydride anions are statistically disordered with oxides on the apical site only, as opposed to known transition-metal oxyhydrides exhibiting a preferred occupation of the equatorial site. This unprecedented site selectivity of H- has been reproduced by periodic DFT+ U calculations, emphasizing for the hydride defect a difference in formation energy of 0.24 eV between equatorial and apical sites. In terms of electronic structure, the model system Sr2TiO3.875H0.125 is found to be slightly metallic and the released electron remains mostly delocalized over several Ti atoms. On the other hand, hydride anions in the double-layered Sr3Ti2O6.20H0.12 material show a clear preference for the bridging apical site within the perovskite slabs, as confirmed by DFT calculations on the Sr3Ti2O6.875H0.125 model system. Finally, the influence of the B-site chemical nature on the hydride site selectivity for early 3d transition metals is theoretically explored in the single-layered system by substituting vanadium for titanium. The V3+ electronic polaron is suggested to play a role in stabilizing H- on the equatorial site in Sr2VO4- xH x for x = 0.125.
RESUMO
The problem of activating N2 and its subsequent hydrogenation to form NH3 has been approached from many directions. One of these approaches involves the use of transition metal hydride complexes. Recently, transition metal hydride complexes of Ti and Ta have been shown to activate N2, but without catalytic formation of NH3. Here, we show that at elevated temperatures (400 °C, 5 MPa), solid-state hydride-containing Ti compounds (TiH2 and BaTiO2.5H0.5) form a nitride-hydride surface similar to those observed with titanium clusters, but continuously (â¼7 days) form NH3 under H2/N2 flow conditions to achieve a catalytic cycle, with activity (up to 2.8 mmol·g·-1·h-1) almost comparable to conventional supported Ru catalysts such as Cs-Ru/MgO or Ru/BaTiO3 that we have tested. As with the homogeneous analogues, the initial presence of hydride within the catalyst is critical. A rare hydrogen-based Mars van Krevelen mechanism may be at play here. Conventional scaling rules of pure metals predict essentially no activity for Ti, making this a previously overlooked element, but our results show that by introducing hydride, the repertoire of heterogeneous catalysts can be expanded to include formerly unexamined compositions without resorting to precious metals.
RESUMO
We investigated topochemical anion exchange reactions for a ScIII-substituted SrTiIVO3 perovskite, Sr(Ti1-yScy)O3-y/2â¡y/2 (y ≤ 0.1), using CaH2. It was found that the initial introduction of a small amount of anion vacancies (y/2) is crucial to enhance the anion (H-/O2-) exchangeability. For example, hydride reduction of Sr(Ti0.95Sc0.05)O2.975 yielded the oxyhydride SrTi0.95Sc0.05O2.56H0.41 in which the hydride concentration is increased by 33% with respect to pristine SrTiO3 (leading to SrTiO2.76H0.24). This observation highlights the importance of anion vacancies to improve anion (H-/O2-) diffusion, which is a well-known strategy for improving oxide anion conductivity, and suggests that such a vacancy-assisted reaction could be applied to other anion exchange reactions (e.g., F-/O2- and N3-/O2-) to extend the solubility range.
RESUMO
We report a scandium oxyhydride BaScO2H prepared by solid state reaction under high pressure. Rietveld refinements against powder synchrotron X-ray and neutron diffraction data revealed that BaScO2H adopts the ideal cubic perovskite structure (Pm3Ì m), where oxide (O2-) and hydride (H-) anions are disordered. 1H nuclear magnetic resonance (NMR) spectroscopy provides a positive chemical shift of about +4.4 ppm, which can be understood by the distance to the nearest (and possibly the next nearest) cation from the H nucleus. A further analysis of the NMR data and calculations based on ab initio random structure searches suggest a partial cis preference in ScO4H2 octahedra. The present oxyhydride, if compositionally or structurally tuned, may become a candidate for H- conductors.
RESUMO
In this review we describe recent advances in transition metal oxyhydride chemistry obtained by topochemical routes, such as low temperature reduction with metal hydrides, or high-pressure solid-state reactions. Besides the crystal chemistry, magnetic and transport properties of the bulk powder and epitaxial thin film samples, the remarkable lability of the hydride anion is particularly highlighted as a new strategy to discover unprecedented mixed anion materials.
RESUMO
We present how the introduction of anion vacancies in oxyhydrides enables a route to access new oxynitrides, by conducting ammonolysis of perovskite oxyhydride EuTiO3-xHx (x â¼ 0.18). At 400 °C, similar to our studies on BaTiO3-xHx, hydride lability enables a low temperature direct ammonolysis of EuTi(3.82+)O2.82H0.18, leading to the N(3-)/H(-)-exchanged product EuTi(4+)O2.82N0.12â¡0.06. When the ammonolysis temperature was increased up to 800 °C, we observed a further nitridation involving N(3-)/O(2-) exchange, yielding a fully oxidized Eu(3+)Ti(4+)O2N with the GdFeO3-type distortion (Pnma) as a metastable phase, instead of pyrochlore structure. Interestingly, the same reactions using the oxide EuTiO3 proceeded through a 1:1 exchange of N(3-) with O(2-) only above 600 °C and resulted in incomplete nitridation to EuTiO2.25N0.75, indicating that anion vacancies created during the initial nitridation process of EuTiO2.82H0.18 play a crucial role in promoting anion (N(3-)/O(2-)) exchange at high temperatures. Hence, by using (hydride-induced) anion-deficient precursors, we should be able to expand the accessible anion composition of perovskite oxynitrides.
RESUMO
By using a high-pressure reaction, we prepared a new oxynitride ZnTaO2N that crystallizes in a centrosymmetric (R3Ì c) high-temperature LiNbO3-type structure (HTLN-type). The stabilization of the HTLN-type structure down to low temperatures (at least 20 K) makes it possible to investigate not only the stability of this phase, but also the phase transition to a noncentrosymmetric (R3c) LiNbO3-type structure (LN-type) which is yet to be clarified. Synchrotron and neutron diffraction studies in combination with transmission electron microscopy show that Zn is located at a disordered 12c site instead of 6a, implying an order-disorder mechanism of the phase transition. It is found that the closed d-shell of Zn2+, as well as the high-valent Ta5+ ion, is responsible for the stabilization of the HTLN-type structure, affording a novel quasitriangular ZnO2N coordination. Interestingly, only 3% Zn substitution for MnTaO2N induces a phase transition from LN- to HTLN-type structure, implying the proximity in energy between the two structural types, which is supported by the first-principles calculations.
RESUMO
The effect of lanthanoid (Ln = Nd, Sm, Ho) substitution on the structural and physical properties of the infinite-layer iron oxide SrFeO2 was investigated by X-ray diffraction (XRD) at ambient and high pressure, neutron diffraction, and 57Fe Mössbauer spectroscopy. Ln for Sr substituted samples up to â¼30% were synthesized by topochemical reduction using CaH2. While the introduction of the smaller Ln3+ ion reduces the a axis as expected, we found an unusual expansion of the c axis as well as the volume. Rietveld refinements along with pair distribution function analysis revealed the incorporation of oxygen atoms between FeO2 layers with a charge-compensated composition of (Sr1-xLnx)FeO2+x/2, which accounts for the failed electron doping to the FeO2 layer. The incorporated partial apical oxygen or the pyramidal coordination induces incoherent buckling of the FeO2 sheet, leading to a significant reduction of the Néel temperature. High-pressure XRD experiments for (Sr0.75Ho0.25)FeO2.125 suggest a possible stabilization of an intermediate spin state in comparison with SrFeO2, revealing a certain contribution of the in-plane Fe-O distance to the pressure-induced transition.
RESUMO
The high-pressure synthesis of a manganese oxyhydride LaSrMnO3.3 H0.7 is reported. Neutron and X-ray Rietveld analyses showed that this compound adopts the K2 NiF4 structure with hydride ions positioned exclusively at the equatorial site. This result makes a striking contrast to topochemical reductions of LaSrMnO4 that result in only oxygen-deficient phases down to LaSrMnO3.5 . This suggests that high H2 pressure plays a key role in stabilizing the oxyhydride phase, offering an opportunity to synthesize other transition-metal oxyhydrides. Magnetic susceptibility revealed a spin-glass transition at 24â K that is due to competing ferromagnetic (Mn(2+) -Mn(3+) ) and antiferromagnetic (Mn(2+) -Mn(2) , Mn(3+) -Mn(3+) ) interactions.
RESUMO
An ideal one-dimensional (1D) magnet is expected to show exotic quantum phenomena. For compounds with larger S (S = 3/2, 2, 5/2, ...), however, a small interchain interaction J' tends to drive a conventional long-range ordered (LRO) state. Here, a new layered structure of FeF3(4,4'-bpy) (4,4'-bpy = 4,4'-bipyridyl) with novel S = 5/2 (Fe(3+)) chains has been hydrothermally synthesized by using 4,4'-bpy to separate chains. The temperature-dependent susceptibility exhibits a broad maximum at high as 164 K, suggesting a fairly strong Fe-F-Fe intrachain interaction J. However, no anomaly associated with a LRO is seen in both magnetic susceptibility and specific heat even down to 2 K. This indicates an extremely small J' with J'/J < 3.2 × 10(-5), making this new material a nearly ideal 1D antiferromagnet. Mössbauer spectroscopy at 2.7 K reveals a critical slowing down of the 1D fluctuations toward a possible LRO at lower temperatures.
RESUMO
In synthesizing mixed anion oxides, direct syntheses have often been employed, usually involving high temperature and occasionally high pressure. Compared with these methods, here we show how the use of a titanium perovskite oxyhydride (BaTiO2.5H0.5) as a starting material enables new multistep low temperature topochemical routes to access mixed anion compounds. Similar to labile ligands in inorganic complexes, the lability of H(-) provides the necessary reactivity for syntheses, leading to reactions and products previously difficult to obtain. For example, BaTiO2.5N0.2 can be prepared with the otherwise inert N2 gas at 400-600 °C, in marked contrast with currently available oxynitride synthetic routes. F(-)/H(-) exchange can also be accomplished at 150 °C, yielding the oxyhydride-fluoride BaTi(O, H, F)3. For BaTiO2.4D0.3F0.3, we find evidence that further anionic exchange with OD(-) yields BaTiO2.4(D(-))0.26(OD(-))0.34, which implies stable coexistence of H(+) and H(-) at ambient conditions. Such an arrangement is thermodynamically unstable and would be difficult to realize otherwise. These results show that the labile nature of hydride imparts reactivity to oxide hosts, enabling it to participate in new multistep reactions and form new materials.
RESUMO
We have prepared the oxyhydride perovskite EuTiO(3-x)H(x) (x ≤ 0.3) by a low temperature CaH2 reduction of pyrochlore Eu2Ti2O7 and perovskite EuTiO3. The reduced EuTiO(3-x)H(x) crystallizes in the ideal cubic perovskite (Pm3Ì m), where O/H anions are randomly distributed. As a result of electron doping by the aliovalent anion exchange, the resistivity of EuTiO(3-x)H(x) shows metallic temperature dependence. Moreover, an antiferromagnetic-to-ferromagnetic transition is observed even when a small amount of hydride (x â¼ 0.07) is introduced. The Curie temperature TC of 12 K is higher than those of any other EuTiO3-derived ferromagnets. The ferromagnetism can be explained by the Ruderman-Kittel-Kasuya-Yosida (RKKY) interaction between the Eu(2+) spins mediated by the itinerant Ti 3d electrons. The present study shows that controlling the oxide/hydride ratio is a versatile method to tune magnetic and transport properties.