Preparation and magnetic properties of multiferroic CuMnO2 nanoparticles.

CuMnO2 nanoparticles with diameters of 64 nm were synthesized by a novel wet chemical method. An optimized two-step annealing method was developed through the analysis of thermogravimetric differential thermal analysis (TG-DTA) measurements in order to obtain single-phase CuMnO2. A sharp exothermic peak was observed in the DTA curve at approximately 500 K where structural changes of the copper oxides and manganese oxides in the precursor are expected to occur. It is believed that Cu+ ions were oxidized to Cu2+ ions and that Mn2+ ions were oxidized to Mn3+ ions in the Cu-Mn-O system. Deoxidization reactions were also found at approximately 1200 K. The optimized annealing temperature for the first step was determined to be 623 K in air. The optimized annealing temperature for the second step was 1173 K in an Ar atmosphere. Magnetization measurements suggested an antiferromagnetic spin ordering at approximately 50 K. It was expected that Mn3+ spin interactions induced magnetic phase transition affected by definite temperature.

Characterization of magnetic and dielectric properties of Bi(1-x)Gd(x)FeO3 nanoparticles by local structure analyses.

Bi(1-x)Gd(x)FeO3 (0 < or = x < or = 1.0) nanoparticles were synthesized by a wet chemical method. The annealing temperatures were controlled to obtain single-phase Bi(1-x)Gd(x)FeO3 nanoparticles. The crystal diameters decreased as the number of doped Gd ions increased. The crystal structure changed, as the number of Gd ions increased, from rhombohedral to orthorhombic perovskite, at x = 0.2. The behavior of the magnetization curves observed at various values of x (x = 0.05, 0.1, 0.15) of the rhombohedral structure suggested that the canted antiferromagnetism and remanent magnetization (M(r)) drastically increased, compared with those at x = 0 (BiFeO3). It is suggested that the spin-canting angle of the Fe ions increased with the increase in the number of Gd ions. The dielectric properties at x = 0.1 showed that the dielectric loss (tan delta) was improved, compared with that at x = 0 (BiFeO3), by approximately 90%, while the real part of the dielectric constant epsilon' was reduced by approximately 15%. The reason is that the doping impurities restrained the reduction in the leakage current. It was found, from the X-ray absorption fine structure (XAFS) spectra, that Gd ions were doped accurately and that the symmetry of the B site was improved. The Mössbauer analysis suggested the existence of magnetic cycloid spiral ordering.