RESUMO
This study determined the shear bond strength (SBS) between an indirect gingival composite resin and glazed gingival porcelain after various surface treatments. A total of 176 porcelain disks with natural glazing were used and assigned to one of four groups: no surface treatment, airborne-particle abrasion, hydrofluoric acid etching, or a combination of airborne-particle abrasion followed by hydrofluoric acid etching. Each group was divided into two subgroups: one subgroup was unprimed, and the other was silanized. An indirect composite resin was then bonded to the porcelain disks. Half of the specimens in each group (n = 11) were exposed to 5000 thermocycles. SBSs were measured, and data were analyzed with the Kruskal-Wallis and Steel-Dwass tests. Among silanized specimens, those treated with the combination of airborne-particle abrasion and hydrofluoric acid etching exhibited the highest bond strengths both before and after thermocycling. However, the SBS values of the silanized and unprimed hydrofluoric acid etched specimens did not differ significantly. Airborne-particle abrasion followed by hydrofluoric acid etching with silane application yielded stronger, more durable bonds between the indirect gingival composite resin and glazed gingival porcelain.
Assuntos
Colagem Dentária , Implantes Dentários , Condicionamento Ácido do Dente , Resinas Compostas , Porcelana Dentária , Análise do Estresse Dentário , Teste de Materiais , Cimentos de Resina , Resistência ao Cisalhamento , Propriedades de Superfície , ZircônioRESUMO
This study investigated the effect of preparation design on the marginal and internal adaptation of laminate veneers (LVs) fabricated from translucent zirconia. Thirty-three resin teeth were prepared for LVs of three designs: window preparation (WP); incisal shoulder preparation (ISP); and incisal palatal chamfer preparation (IPP). Marginal adaptation was evaluated by measuring the vertical discrepancy between the LV margin and the finish line at 60 points. The internal adaptation was assessed by measuring the internal space width as the distance between the LV and the tooth at cervical, central, and incisal sites after sectioning. At the incisal, mesial, and distal sites, mean marginal discrepancies were significantly lower in the WP group than in the other two groups; the IPP group had the highest marginal discrepancies. At incisal sites, the median internal space was significantly higher in the IPP group than in the WP and ISP groups and higher in the ISP group than in the WP group. At the incisal site, marginal and internal adaptations were better for the non-overlap translucent zirconia LV design (WP) than for the overlap designs (ISP and IPP). The characteristics of the translucent zirconia LVs used in the present study indicate acceptable clinical performance.
Assuntos
Adaptação Marginal Dentária , Planejamento de Prótese Dentária/métodos , Facetas Dentárias , Preparo Prostodôntico do Dente/métodos , Zircônio/química , Cerâmica , Desenho Assistido por Computador , Humanos , Processamento de Imagem Assistida por Computador/métodos , Incisivo , Cimentos de Resina , Propriedades de SuperfícieRESUMO
PURPOSE: This study evaluated the influence of firing procedures and layering thickness of porcelain on internal adaptation of maxillary anterior cantilever zirconia resin-bonded fixed dental prostheses (RBFDPs). METHODS: The maxillary right central incisor on a model was prepared for a single-retainer zirconia RBFDP. A total of 36 frameworks of cantilever zirconia RBFDPs were classified into three groups (CB0.5, CB1.0, and CB2.0 groups) based on the thickness of the cut-back on the facial surface (0.5 mm, 1.0 mm, and 2.0 mm, respectively). Feldspathic porcelain was layered onto the facial surface of the zirconia RBFDP frameworks. Internal space widths between the abutment tooth and the framework were measured before and after porcelain firing by a replica technique. The internal space values before and after porcelain firings were compared using the paired t-test within the same group (α = 0.05). Differences in internal space values (distortion) between before and after porcelain firing were compared using one-way analysis of variance and Tukey multiple comparison tests. RESULTS: For all framework designs, internal space values after porcelain firing were significantly higher than those before firing. Among all groups, the CB0.5 group showed the lowest internal distortion values for the whole measured area. The CB2.0 group showed higher distortion values than the CB1.0 group. CONCLUSION: Porcelain firing procedures negatively impacted the internal space in cantilever zirconia RBFDPs. In addition, the increased volume of layering porcelain had a negative effect on the internal distortion of maxillary anterior cantilever zirconia RBFDPs.
Assuntos
Colagem Dentária , Prótese Dentária , Porcelana Dentária , ZircônioRESUMO
PURPOSE: The objective of the present study was to evaluate fracture loads of screw-retained implant-supported zirconia prostheses after artificial aging. METHODS: Four types of screw-retained implant-supported prostheses were fabricated (n=11 each); porcelain-veneered zirconia prosthesis (PVZ), indirect composite-veneered zirconia prosthesis (IVZ), porcelain-fused-to-metal prosthesis (PFM), and monolithic zirconia prosthesis (ML). The specimens were subjected to 10,000 thermocycles and cyclic loading for 1.2 million cycles. Fracture loads were measured, and the data were analyzed with the Kruskal-Wallis and Steel-Dwass tests (α=0.05). RESULTS: All specimens survived the artificial aging procedures. The fracture loads for the PVZ (1.52kN), IVZ (1.62kN), and PFM groups (1.53kN) did not significantly differ; however, the fracture load for the ML group (6.61kN) was significantly higher than those for the other groups. The fracture load for the IVZ group was comparable to those for the PVZ and PFM groups. CONCLUSIONS: The monolithic zirconia prostheses exhibited significantly higher fracture loads than the bilayered prostheses. All the investigated types of screw-retained implant-supported zirconia prostheses appear sufficient to resist posterior masticatory forces during long-term clinical use.
Assuntos
Prótese Dentária Fixada por Implante , Zircônio , Parafusos Ósseos , Coroas , Porcelana Dentária , Falha de Restauração Dentária , Análise do Estresse Dentário , Teste de Materiais , Estresse MecânicoRESUMO
To investigate the effect of luting agent type on fracture loads of implant-supported ceramic prostheses in premolar region. Ninety-nine implant-abutment complexes were divided into three different implant-supported prostheses: monolithic yttria-partially stabilized zirconia (Y-PSZ) restorations (MPZ specimens), porcelain layered on yttria-stabilized tetragonal zirconia polycrystal (Y-TZP) restorations (PLZ specimens), and monolithic lithium disilicate ceramic restorations (MLD specimens). Implant-supported prostheses were luted with adhesive resin luting agent (RLA), glass ionomer cement (GIC), or zinc phosphate cement (ZPC). For MPZ and MLD specimens, fracture loads were significantly higher for RLA group than for GIC and ZPC groups. For PLZ specimens, fracture loads did not significantly differ in relation to luting agent. Fracture loads were significantly higher for MPZ specimens than for other test specimens, regardless of luting agent. Use of an adhesive resin luting agent is recommended for placement of premolar implant-supported monolithic Y-PSZ and lithium disilicate ceramic prostheses.
Assuntos
Cimentos Dentários , Implantes Dentários , Dente Pré-Molar , Cerâmica , Coroas , Porcelana Dentária , Análise do Estresse Dentário , Teste de Materiais , Cimentos de Resina , ZircônioRESUMO
Computer-aided design/computer-aided manufacturing (CAD/CAM) restorative materials have been widely used owing to a number of advantages, including stable quality of the materials, lower costs, and time-saving factors. Resin-based CAD/CAM materials for definitive restorations are classified into two groups: dispersed nanoparticle-filled composite resin and polymer-infiltrated-ceramic-network materials. Resin-based CAD/CAM materials have been applied to single crown restorations as a monolithic structure for the posterior region. In addition, resin-based CAD/CAM restorations have been applied recently for the anterior area. This literature review summarizes clinical outcomes, such as survival rates and clinical complications of single crown restorations fabricated with resin-based CAD/CAM materials.
Assuntos
Desenho Assistido por Computador , Coroas , Cerâmica , Resinas Compostas , Materiais Dentários , Porcelana Dentária , Planejamento de Prótese Dentária , Teste de MateriaisRESUMO
This study evaluated shear bond strengths of two gingiva-colored layering resin composites to zirconia frameworks coated with feldspathic porcelain. Airborne-particle abraded porcelain-coated zirconia disks were treated with one of the following primers: Clearfil Photo Bond, Clearfil Photo Bond with Clearfil Porcelain Bond Activator (CPB+Activator), Estenia Opaque Primer, Porcelain Liner M Liquid B (PLB), or no primer. A light-polymerizing (CER) or a photo/heat-polymerizing gingiva-colored indirect resin composite (EST) was bonded to the porcelain-coated zirconia disks in each group (n=11). Shear bond strength was measured. For both CER and EST specimens, bond strengths in CPB+Act group were significantly higher than those in the other groups. In all priming groups, bond strength was significantly higher for EST specimens than for CER specimens. Combined application of a phosphate monomer and silane enhanced initial bond strength of light-polymerized and photo/heat-polymerized gingiva-colored layering resin composites to porcelain-coated zirconia ceramics.