Emissions of DEHP-free PVC flooring.

Degrading 2-ethylhexyl-containing PVC floorings (eg DEHP-PVC floorings) and adhesives emit 2-ethylhexanol (2-EH) in the indoor air. The danger of flooring degradation comes from exposing occupants to harmful phthalates plasticisers (eg DEHP), but not from 2-EH as such. Since the EU banned the use of phthalates in sensitive applications, the market is shifting to use DEHP-free and alternative types of plasticisers in PVC products. However, data on emissions from DEHP-free PVC floorings are scarce. This study aimed at assessing the surface and bulk emissions of two DEHP-free PVC floorings over three years. The floorings were glued on the screed layer of concrete casts at 75%, 85%, and 95% RH. The volatile organic compounds (VOCs) were actively sampled using FLEC (surface emissions) and micro-chamber/thermal extractor (µ-CTE, bulk emissions) onto Tenax TA adsorbents and analyzed with TD-GC-MS. 2-EH, C9-alcohols, and total volatile organic compound (TVOC) emissions are reported. Emissions at 75% and 85% RH were similar. As expected, the highest emissions occurred at 95% RH. 2-EH emissions originated from the adhesive. Because the two DEHP-free floorings tested emitted C9-alcohols at all tested RH, it makes the detection of flooring degradation harder, particularly if the adhesive used does not emit 2-EH.

Impact of Glass Composition on Hydrolytic Degradation of Polylactide/Bioactive Glass Composites.

Understanding the degradation of a composite material is crucial for tailoring its properties based on the foreseen application. In this study, poly-L,DL-lactide 70/30 (PLA70) was compounded with silicate or phosphate bioactive glass (Si-BaG and P-BaG, respectively). The composite processing was carried out without excessive thermal degradation of the polymer and resulted in porous composites with lower mechanical properties than PLA70. The loss in mechanical properties was associated with glass content rather than the glass composition. The degradation of the composites was studied for 40 weeks in Tris buffer solution Adding Si-BaG to PLA70 accelerated the polymer degradation in vitro more than adding P-BaG, despite the higher reactivity of the P-BaG. All the composites exhibited a decrease in mechanical properties and increased hydrophilicity during hydrolysis compared to the PLA70. Both glasses dissolved through the polymer matrix with a linear, predictable release rate of ions. Most of the P-BaG had dissolved before 20 weeks in vitro, while there was still Si-BaG left after 40 weeks. This study introduces new polymer/bioactive glass composites with tailorable mechanical properties and ion release for bone regeneration and fixation applications.