In previous studies, we demonstrated the ability to linearly guide axonal regeneration using scaffolds comprised of precision microchannels 2 mm in length. In this work, we report our efforts to augment the manufacturing process to achieve clinically relevant scaffold dimensions in the centimeter-scale range. By selective etching of multi-component fiber bundles, agarose hydrogel scaffolds with highly ordered, close-packed arrays of microchannels, ranging from 172 to 320 µm, were fabricated with overall dimensions approaching clinically relevant length scales. Cross-sectional analyses determined that the maximum microchannel volume per unit volume of scaffold approached 80%, which is nearly twice that compared to our previously reported study. Statistical analyses at various points along the length of the microchannels also show a significant degree of linearity along the entire length of the scaffold. Two types of multi-component fiber bundle templates were evaluated; polystyrene and poly(methyl methacrylate). The scaffolds consisting of 2 cm long microchannels were fabricated with the poly(methyl methacrylate) fiber-cores exhibited a higher degree of linearity compared to those fabricated using polystyrene fibers. It is believed that the materials process developed in this study is useful for fabricating high aspect ratio microchannels in biocompatible materials with a wide range of geometries for guiding nerve regeneration.
Assuntos
Sistema Nervoso Central/fisiologia , Sistema Nervoso Periférico/fisiologia , Hidrogéis , Polimetil Metacrilato , Poliestirenos , SefaroseRESUMO
Axons of the adult central nervous system exhibit an extremely limited ability to regenerate after spinal cord injury. Experimentally generated patterns of axon growth are typically disorganized and randomly oriented. Support of linear axonal growth into spinal cord lesion sites has been demonstrated using arrays of uniaxial channels, templated with agarose hydrogel, and containing genetically engineered cells that secrete brain-derived neurotrophic factor (BDNF). However, immobilizing neurotrophic factors secreting cells within a scaffold is relatively cumbersome, and alternative strategies are needed to provide sustained release of BDNF from templated agarose scaffolds. Existing methods of loading the drug or protein into hydrogels cannot provide sustained release from templated agarose hydrogels. Alternatively, here it is shown that pH-responsive H-bonded poly(ethylene glycol)(PEG)/poly(acrylic acid)(PAA)/protein hybrid layer-by-layer (LbL) thin films, when prepared over agarose, provided sustained release of protein under physiological conditions for more than four weeks. Lysozyme, a protein similar in size and isoelectric point to BDNF, is released from the multilayers on the agarose and is biologically active during the earlier time points, with decreasing activity at later time points. This is the first demonstration of month-long sustained protein release from an agarose hydrogel, whereby the drug/protein is loaded separately from the agarose hydrogel fabrication process.
RESUMO
Nerve repair in several mm-long nerve gaps often requires an interventional technology. Microchannel scaffolds have proven effective for bridging nerve gaps and guiding axons in the peripheral nervous system (PNS). Nonetheless, fabricating microchannel scaffolds at this length scale remains a challenge and/or is time consuming and cumbersome. In this work, a simple computer-aided microdrilling technique was used to fabricate 10 mm-long agarose scaffolds consisting of 300 µm-microchannels and 85 µm-thick walls in less than an hour. The agarose scaffolds alone, however, did not exhibit adequate stiffness and integrity to withstand the mechanical stresses during implantation and suturing. To provide mechanical support and enable suturing, poly caprolactone (PCL) conduits were fabricated and agarose scaffolds were placed inside. A modified salt-leaching technique was developed to introduce interconnected porosity in PCL conduits to allow for tuning of the mechanical properties such as elastic modulus and strain to failure. It was shown that the PCL conduits were effective in stabilizing the agarose scaffolds in 10 mm-long sciatic nerve gaps of rats for at least 8 weeks. Robust axon ingress and Schwann cell penetration were observed within the microchannel scaffolds without using growth factors. © 2017 Wiley Periodicals, Inc. J Biomed Mater Res Part A: 105A: 3392-3399, 2017.
Assuntos
Regeneração Tecidual Guiada/métodos , Hidrogel de Polietilenoglicol-Dimetacrilato/química , Regeneração Nervosa , Poliésteres/química , Nervo Isquiático/fisiologia , Sefarose/química , Alicerces Teciduais/química , Animais , Módulo de Elasticidade , Masculino , Porosidade , Ratos Sprague-Dawley , Células de Schwann/citologia , Nervo Isquiático/citologia , Nervo Isquiático/lesõesRESUMO
Alginate was studied as a degradable nerve guidance scaffold material in vitro and in vivo. In vitro degradation rates were determined using rheology to measure the change in shear modulus vs time. The shear modulus decreased from 155 kPa to 5 kPa within 2 days; however, alginate samples maintained their superficial geometry for over 28 days. The degradation behavior was supported by materials characterization data showing alginate consisted of high internal surface area (400 m2 /g), which likely facilitated the release of cross-linking cations resulting in the rapid decrease in shear modulus. To assess the degradation rate in vivo, multilumen scaffolds were fabricated using a fiber templating technique. The scaffolds were implanted in a 2-mm-long T3 full transection rodent spinal cord lesion model for 14 days. Although there was some evidence of axon guidance, in general, alginate scaffolds degraded before axons could grow over the 2-mm-long lesion. Enabling alginate-based scaffolds for nerve repair will likely require approaches to slow its degradation. © 2015 Wiley Periodicals, Inc. J Biomed Mater Res Part A: 104A: 611-619, 2016.
Assuntos
Alginatos/química , Regeneração Tecidual Guiada/métodos , Hidrogel de Polietilenoglicol-Dimetacrilato/química , Traumatismos da Medula Espinal/terapia , Alicerces Teciduais/química , Animais , Feminino , Ácido Glucurônico/química , Ácidos Hexurônicos/química , Filamentos Intermediários/metabolismo , Nitrogênio/química , Polimetil Metacrilato/química , Porosidade , Ratos Endogâmicos F344 , Reologia , Medula Espinal/patologiaRESUMO
Agarose nerve guidance scaffolds (NGS) seeded with cells expressing brain derived neurotrophic factor (BDNF) have demonstrated robust nerve regeneration in the rat central nervous system. The purpose of this work was to explore whether agarose NGS coated with hydrogen-bonded layer-by-layer (HLbL) could provide an acellular method of delivering prolonged and consistent dosages of active BDNF. Our results show that HLbL-coated agarose NGS could release BDNF over 10days in consistent dosages averaging 80.5±12.5(SD)ng/mL. Moreover, the BDNF released from HLbL was confirmed active by in vitro cell proliferation assays. To our knowledge, this is the first report demonstrating that HLbL assembled onto a hydrogel can provide consistent, prolonged release of active BDNF in clinically relevant dosages.
Assuntos
Fator Neurotrófico Derivado do Encéfalo/metabolismo , Materiais Revestidos Biocompatíveis/farmacologia , Regeneração Tecidual Guiada , Regeneração Nervosa/efeitos dos fármacos , Sefarose/química , Alicerces Teciduais/química , Animais , Camundongos , Células NIH 3T3 , Ratos , Receptor trkB/metabolismoRESUMO
Recent work demonstrated the efficacy of combining layer-by-layer assembly with hydrogels to provide the controlled delivery of proteins for use in nerve repair scaffolds. In this work, we augmented the protein dose response by controlling and increasing the hydrogel internal surface area. Sucrose was added to agarose during gelation to homogenize the nanopore morphology, resulting in increased surface area per unit volume of hydrogel. The surface area of a range of compositions (1.5-5.0 wt% agarose and 0, 50 and 65 wt% sucrose) was measured. Gels were supercritically dried to preserve porosity enabling detailed pore morphology measurements using nitrogen adsorption and high resolution scanning electron microscopy. The resulting surface area, normalized by superficial gel volume, ranged between 6m(2)/cm(3)gel and 56 m(2)/cm(3)gel. Using the layer-by-layer process to load lysozyme, a neurotrophic factor analog, a relationship was observed between surface area and cumulative dose response ranging from 176 to 2556 µg/mL, which is in the range of clinical relevance for the delivery of growth factors. In this work, we demonstrated that the ability to control porosity is key in tuning drug delivery dose response from layer-by-layer modified hydrogels.
Assuntos
Hidrogéis/química , Proteínas/química , Sefarose/química , Tamanho da Partícula , Propriedades de SuperfícieRESUMO
Experimentally induced axonal regeneration is compromised by glial scar formation arising from leptomeningeal fibroblasts cells in and around the hydrogel scaffold implanted for nerve repair. Strategies are needed to prevent such fibroblastic reactive cell layer formation for enhanced axonal regeneration. Here, we implement the technique of layer-by-layer assembled degradable, hydrogen bonded multilayers on agarose hydrogels to incorporate an anti-mitotic drug (1-ß-D-arabinofuranosylcytosine (Ara-C)) within the agarose hydrogels. We show controlled release of Ara-C under physiological conditions over a period of days. The concentrations of Ara-C released from agarose at the different time points were sufficient to inhibit fibroblast growth in vitro, while not adversely affecting the viability of the neuronal cells.