RESUMO
We report on the microstructure, morphology, and growth of 5,5'-bis(naphth-2-yl)-2,2'-bithiophene (NaT2) thin films deposited on graphene, characterized by grazing incidence X-ray diffraction (GIXRD) and complemented by atomic force microscopy (AFM) measurements. NaT2 is deposited on two types of graphene surfaces: custom-made samples where chemical vapor deposition (CVD)-grown graphene layers are transferred onto a Si/SiO2 substrate by us and common commercially transferred CVD graphene on Si/SiO2. Pristine Si/SiO2 substrates are used as a reference. The NaT2 crystal structure and orientation depend strongly on the underlying surface, with the molecules predominantly lying down on the graphene surface (face-on orientation) and standing nearly out-of-plane (edge-on orientation) on the Si/SiO2 reference surface. Post growth GIXRD and AFM measurements reveal that the crystalline structure and grain morphology differ depending on whether there is polymer residue left on the graphene surface. In situ GIXRD measurements show that the thickness dependence of the intensity of the (111) reflection from the crystalline edge-on phase does not intersect zero at the beginning of the deposition process, suggesting that an initial wetting layer, corresponding to 1-2 molecular layers, is formed at the surface-film interface. By contrast, the (111) reflection intensity from the crystalline face-on phase grows at a constant rate as a function of film thickness during the entire deposition.
RESUMO
Small π-conjugated organic molecules have attracted substantial attention in the past decade as they are considered as candidates for future organic-based (opto-)electronic applications. The molecular arrangement in the organic layer is one of the crucial parameters that determine the efficiency of a given device. The desired orientation of the molecules is achieved by a proper choice of the underlying substrate and growth conditions. Typically, one underlying material supports only one inherent molecular orientation at its interface. Here, we report on two different orientations of diindenoperylene (DIP) molecules on the same underlayer, i.e. on a few-layer MoS2 substrate. We show that DIP molecules adopt a lying-down orientation when deposited on few-layer MoS2 with horizontally oriented layers. In contrast, for vertically aligned MoS2 layers, DIP molecules are arranged in a standing-up manner. Employing in situ and real-time grazing-incidence wide-angle X-ray scattering (GIWAXS), we monitored the stress evolution within the thin DIP layer from the early stages of the growth, revealing different substrate-induced phases for the two molecular orientations. Our study opens up new possibilities for the next-generation of flexible electronics, which might benefit from the combination of MoS2 layers with unique optical and electronic properties and an extensive reservoir of small organic molecules.
RESUMO
At present, the power conversion efficiency of single-junction perovskite-based solar cells reaches over 26%. The further efficiency increase of perovskite-based optoelectronic devices is limited mainly by defects, causing the nonradiative recombination of charge carriers. To improve efficiency and ensure reproducible fabrication of high-quality layers, it is crucial to understand the perovskite nucleation and growth mechanism along with associated process control to reduce the defect density. In this study, we investigate the growth kinetics of a promising narrow bandgap perovskite, formamidinium methylammonium lead iodide (FAMAPbI3), for high-performance single-junction solar cells. The temporal evolution of structural and optoelectronic properties during FAMAPbI3 vacuum codeposition was inspected in real time by grazing-incidence wide-angle X-ray scattering and photoluminescence. Such a combination of analytical techniques unravels the evolution of intrinsic defect density and layer morphology correlated with lattice strain from the early stages of the perovskite deposition.
RESUMO
The efficiency of perovskite-based solar cells has increased dramatically over the past decade to as high as 25%, making them very attractive for commercial use. Vapor deposition is a promising technique that potentially enables fabrication of perovskite solar cells on large areas. However, to implement a large-scale deposition method, understanding and controlling the specific growth mechanisms are essential for the reproducible fabrication of high-quality layers. Here, we study the structural and optoelectronic kinetics of MAPbI3, employing in-situ photoluminescence (PL) spectroscopy and grazing-incidence small/wide-angle X-ray scattering (GI-SAXS/WAXS) simultaneously during perovskite vapor deposition. Such a unique combination of techniques reveals MAPbI3 formation from the early stages and uncovers the morphology, crystallographic structure, and defect density evolution. Furthermore, we show that the nonmonotonous character of PL intensity contrasts with the increasing volume of the perovskite phase during the growth, although bringing valuable information about the presence of defect states.
RESUMO
Lead-halide perovskites have established a firm foothold in photovoltaics and optoelectronics due to their steadily increasing power conversion efficiencies approaching conventional inorganic single-crystal semiconductors. However, further performance improvement requires reducing defect-assisted, nonradiative recombination of charge carriers in the perovskite layers. A deeper understanding of perovskite formation and associated process control is a prerequisite for effective defect reduction. In this study, we analyze the crystallization kinetics of the lead-halide perovskite MAPbI3-xClx during thermal annealing, employing in situ photoluminescence (PL) spectroscopy complemented by lab-based grazing-incidence wide-angle X-ray scattering (GIWAXS). In situ GIWAXS measurements are used to quantify the transition from a crystalline precursor to the perovskite structure. We show that the nonmonotonous character of PL intensity development reflects the perovskite phase volume, as well as the occurrence of the defects states at the perovskite layer surface and grain boundaries. The combined characterization approach enables easy determination of defect kinetics during perovskite formation in real-time.
RESUMO
The last few decades faced on the fabrication of advanced engineering materials involving also different composites. Here, we report on the fabrication of few-layer molybdenum disulfide on top of thin polycrystalline diamond substrates with a high specific surface area. In the method, pre-deposited molybdenum coatings were sulfurized in a one-zone furnace at ambient pressure. As-prepared MoS2 layers were characterized by several techniques including grazing-incidence wide-angle X-ray scattering, atomic force microscopy, scanning electron microscopy, Raman spectroscopy and X-ray photoelectron spectroscopy. We found out that the initial thickness of Mo films determined the final c-axis crystallographic orientation of MoS2 layer as previously observed on other substrates. Even though it is well-known that Mo diffuses into diamond at elevated temperatures, the competing sulfurization applied effectively suppressed the diffusion and a chemical reaction between molybdenum and diamond. In particular, a Mo2C layer does not form at the interface between the Mo film and diamond substrate. The combination of diamond high specific surface area along with a controllable layer orientation might be attractive for applications, such as water splitting or water disinfection.
RESUMO
Few-layer MoS2 films are promising candidates for applications in numerous areas, such as photovoltaics, photocatalysis, nanotribology, lithium batteries, hydro-desulfurization catalysis and dry lubricants, especially due to their distinctive electronic, optical, and catalytic properties. In general, two alignments of MoS2 layers are possible - the horizontal and the vertical one, having different physicochemical properties. Layers of both orientations are conventionally fabricated by a sulfurization of pre-deposited Mo films. So far, the Mo thickness was considered as a critical parameter influencing the final orientation of MoS2 layers with horizontally and vertically aligned MoS2 grown from thin (1 nm) and thick (3 nm) Mo films, respectively. Here, we present a fabrication protocol enabling the growth of horizontally or vertically aligned few-layer MoS2 films utilizing the same Mo thickness of 3 nm. We show that the sulfur vapor is another parameter influencing the growth mechanism, where a sulfurization with higher sulfur vapor pressure leads to vertical MoS2 layers and slow sulfur evaporation results in horizontally aligned layers for a thicker Mo starting layer.