The COVID-19 pandemic has claimed millions of lives worldwide, sickened many more, and has resulted in severe socioeconomic consequences. As society returns to normal, understanding the spread and persistence of SARS CoV-2 on commonplace surfaces can help to mitigate future outbreaks of coronaviruses and other pathogens. We hypothesize that such an understanding can be aided by studying the binding and interaction of viral proteins with nonbiological surfaces. Here, we propose a methodology for investigating the adhesion of the SARS CoV-2 spike glycoprotein on common inorganic surfaces such as aluminum, copper, iron, silica, and ceria oxides as well as metallic gold. Quantitative adhesion was obtained from the analysis of measured forces at the nanoscale using an atomic force microscope operated under ambient conditions. Without imposing further constraints on the measurement conditions, our preliminary findings suggest that spike glycoproteins interact with similar adhesion forces across the majority of the metal oxides tested with the exception to gold, for which attraction forces â¼10 times stronger than all other materials studied were observed. Ferritin, which was used as a reference protein, was found to exhibit similar adhesion forces as SARS CoV-2 spike protein. This study results show that glycoprotein adhesion forces for similar ambient humidity, tip shape, and contact surface are nonspecific to the properties of metal oxide surfaces, which are expected to be covered by a thin water film. The findings suggest that under ambient conditions, glycoprotein adhesion to metal oxides is primarily controlled by the water capillary forces, and they depend on the surface tension of the liquid water. We discuss further strategies warranted to decipher the intricate nanoscale forces for improved quantification of the adhesion.
Assuntos
COVID-19 , Humanos , Microscopia de Força Atômica , Pandemias , SARS-CoV-2 , Glicoproteína da Espícula de Coronavírus , Propriedades de SuperfícieRESUMO
We combine nanoindentation, herein achieved using atomic force microscopy-based pulsed-force lithography, with tip-enhanced Raman spectroscopy (TERS) and imaging. Our approach entails indentation and multimodal characterization of otherwise flat Au substrates, followed by chemical functionalization and TERS spectral imaging of the indented nanostructures. We find that the resulting structures, which vary in shape and size depending on the tip used to produce them, may sustain nano-confined and significantly enhanced local fields. We take advantage of the latter and illustrate TERS-based ultrasensitive detection/chemical fingerprinting as well as chemical reaction imaging-all using a single platform for nano-lithography, topographic imaging, hyperspectral dark field optical microscopy, and TERS.
RESUMO
Imaging biological systems with simultaneous intrinsic chemical specificity and nanometer spatial resolution in their typical native liquid environment has remained a long-standing challenge. Here, we demonstrate a general approach of chemical nanoimaging in liquid based on infrared scattering scanning near-field optical microscopy (IR s-SNOM). It is enabled by combining AFM operation in a fluid cell with evanescent IR illumination via total internal reflection, which provides spatially confined excitation for minimized IR water absorption, reduced far-field background, and enhanced directional signal emission and sensitivity. We demonstrate in-liquid IR s-SNOM vibrational nanoimaging and conformational identification of catalase nanocrystals and spatio-spectral analysis of biomimetic peptoid sheets with monolayer sensitivity and chemical specificity at the few zeptomole level. This work establishes the principles of in-liquid and in situ IR s-SNOM spectroscopic chemical nanoimaging and its general applicability to biomolecular, cellular, catalytic, electrochemical, or other interfaces and nanosystems in liquids or solutions.
Assuntos
Microscopia de Força Atômica , Nanopartículas , Nanotecnologia , Espectrofotometria Infravermelho , VibraçãoRESUMO
Light-matter interaction in two-dimensional photonic or phononic materials allows for the confinement and manipulation of free-space radiation at sub-wavelength scales. Most notably, the van der Waals heterostructure composed of graphene (G) and hexagonal boron nitride (hBN) provides for gate-tunable hybrid hyperbolic plasmon phonon-polaritons (HP3). Here, we present the anisotropic flow control and gate-voltage modulation of HP3 modes in G-hBN on an air-Au microstructured substrate. Using broadband infrared synchrotron radiation coupled to a scattering-type near-field optical microscope, we launch HP3 waves in both hBN Reststrahlen bands and observe directional propagation across in-plane heterointerfaces created at the air-Au junction. The HP3 hybridization is modulated by varying the gate voltage between graphene and Au. This modifies the coupling of continuum graphene plasmons with the discrete hBN hyperbolic phonon polaritons, which is described by an extended Fano model. This work represents the first demonstration of the control of polariton propagation, introducing a theoretical approach to describe the breaking of the reflection and transmission symmetry for HP3 modes. Our findings augment the degree of control of polaritons in G-hBN and related hyperbolic metamaterial nanostructures, bringing new opportunities for on-chip nano-optics communication and computing.
RESUMO
Control of photoinduced forces allows nanoparticle manipulation, atom trapping, and fundamental studies of light-matter interactions. Scanning probe microscopy enables the local detection of photoinduced effects with nano-optical imaging and spectroscopy modalities being used for chemical analysis and the study of physical effects. Recently, the development of a novel scanning probe technique has been reported with local chemical sensitivity attributed to the localization and detection of the optical gradient force between a probe tip and sample surface via infrared vibrationally resonant coupling. However, the magnitude and spectral line shape of the observed signals disagree with theoretical predictions of optical gradient forces. Here, we clarify this controversy by resolving and analyzing the interplay of several photoinduced effects between scanning probe tips and infrared resonant materials through spectral and spatial force measurements. Force spectra obtained on IR-active vibrational modes of polymer thin films are symmetric and match the material absorption spectra in contrast to the dispersive spectral line shape expected for the optical gradient force response. Sample thickness dependence shows continuous increase in force signal beyond the thickness where the optical dipole force would saturate. Our results illustrate that photoinduced force interactions between scanning probe tips and infrared-resonant materials are dominated by short-range thermal expansion and possibly long-range thermally induced photoacoustic effects. At the same time, we provide a guideline to detect and discriminate optical gradient forces from other photoinduced effects, which opens a new perspective for the development of new scanning probe modalities exploiting ultrastrong opto-mechanical coupling effects in tip-sample cavities.
RESUMO
Many phase transitions in correlated matter exhibit spatial inhomogeneities with expected yet unexplored effects on the associated ultrafast dynamics. Here we demonstrate the combination of ultrafast nondegenerate pump-probe spectroscopy with far from equilibrium excitation, and scattering scanning near-field optical microscopy (s-SNOM) for ultrafast nanoimaging. In a femtosecond near-field near-IR (NIR) pump and mid-IR (MIR) probe study, we investigate the photoinduced insulator-to-metal (IMT) transition in nominally homogeneous VO2 microcrystals. With pump fluences as high as 5 mJ/cm(2), we can reach three distinct excitation regimes. We observe a spatial heterogeneity on â¼50-100 nm length scales in the fluence-dependent IMT dynamics ranging from <100 fs to â¼1 ps. These results suggest a high sensitivity of the IMT with respect to small local variations in strain, doping, or defects that are difficult to discern microscopically. We provide a perspective with the distinct requirements and considerations of ultrafast spatiotemporal nanoimaging of phase transitions in quantum materials.
RESUMO
Infrared vibrational nano-spectroscopy based on scattering scanning near-field optical microscopy (s-SNOM) provides intrinsic chemical specificity with nanometer spatial resolution. Here we use incoherent infrared radiation from a 1400 K thermal blackbody emitter for broadband infrared (IR) nano-spectroscopy. With optimized interferometric heterodyne signal amplification we achieve few-monolayer sensitivity in phonon polariton spectroscopy and attomolar molecular vibrational spectroscopy. Near-field localization and nanoscale spatial resolution is demonstrated in imaging flakes of hexagonal boron nitride (hBN) and determination of its phonon polariton dispersion relation. The signal-to-noise ratio calculations and analysis for different samples and illumination sources provide a reference for irradiance requirements and the attainable near-field signal levels in s-SNOM in general. The use of a thermal emitter as an IR source thus opens s-SNOM for routine chemical FTIR nano-spectroscopy.
RESUMO
The surface plasmon polaritons (SPPs) of graphene reflect the microscopic spatial variations of underlying electronic structure and dynamics. Here, we excite and image the graphene SPP response in phase and amplitude by near-field interferometry. We develop an analytic cavity model that can self-consistently describe the SPP response function for edge, grain boundary, and defect SPP reflection and scattering. The derived SPP wave vector, damping, and carrier mobility agree with the results from more complex models. Spatial variations in the Fermi level and associated variations in dopant concentration reveal a nanoscale spatial inhomogeneity in the reduced conductivity at internal boundaries. The additional SPP phase information thus opens a new degree of freedom for spatial and spectral graphene SPP tuning and modulation for optoelectronics applications.
RESUMO
Observation of interlayer, charge transfer (CT) excitons in van der Waals heterostructures (vdWHs) based on 2D-2D systems has been well investigated. While conceptually interesting, these charge transfer excitons are highly delocalized and spatially localizing them requires twisting layers at very specific angles. This issue of localizing the CT excitons can be overcome via making nanoplate-2D material heterostructures (N2DHs) where one of the components is a spatially quantum confined medium. Here, we demonstrate the formation of CT excitons in a mixed dimensional system comprising MoSe2 and WSe2 monolayers and CdSe/CdS-based core/shell nanoplates (NPLs). Spectral signatures of CT excitons in our N2DHs were resolved locally at the 2D/single-NPL heterointerface using tip-enhanced photoluminescence (TEPL) at room temperature. By varying both the 2D material and the shell thickness of the NPLs and applying an out-of-plane electric field, the exciton resonance energy was tuned by up to 100 meV. Our finding is a significant step toward the realization of highly tunable N2DH-based next-generation photonic devices.
RESUMO
Understanding biomineralization relies on imaging chemically heterogeneous organic-inorganic interfaces across a hierarchy of spatial scales. Further, organic minority phases are often responsible for emergent inorganic structures from the atomic arrangement of different polymorphs, to nano- and micrometer crystal dimensions, up to meter size mollusk shells. The desired simultaneous chemical and elemental imaging to identify sparse organic moieties across a large field-of-view with nanometer spatial resolution has not yet been achieved. Here, we combine nanoscale secondary ion mass spectroscopy (NanoSIMS) with spectroscopic IR s-SNOM imaging for simultaneous chemical, molecular, and elemental nanoimaging. At the example of Pinctada margaritifera mollusk shells we identify and resolve ~ 50 nm interlamellar protein sheets periodically arranged in regular ~ 600 nm intervals. The striations typically appear ~ 15 µm from the nacre-prism boundary at the interface between disordered neonacre to mature nacre. Using the polymorph distinctive IR-vibrational carbonate resonance, the nacre and prismatic regions are consistently identified as aragonite ([Formula: see text] cm-1) and calcite ([Formula: see text] cm-1), respectively. We observe previously unreported morphological features including aragonite subdomains encapsulated in extensions of the prism-covering organic membrane and regions of irregular nacre tablet formation coincident with dispersed organics. We also identify a ~ 200 nm region in the incipient nacre region with less well-defined crystal structure and integrated organics. These results show with the identification of the interlamellar protein layer how correlative nano-IR chemical and NanoSIMS elemental imaging can help distinguish different models proposed for shell growth in particular, and how organic function may relate to inorganic structure in other biomineralized systems in general.
RESUMO
Polyoxometalates (POMs) with localized radical or open-shell metal sites have the potential to be used as transformative electronic spin based molecular qubits (MQs) for quantum computing (QC). For practical applications, MQs have to be immobilized in electronically or optically addressable arrays which introduces interactions with supports as well as neighboring POMs. Herein, we synthesized Keggin POMs with both tungsten (W) and vanadium (V) addenda atoms. Ion soft landing, a highly-controlled surface modification technique, was used to deliver mass-selected V-doped POMs to different self-assembled monolayer surfaces on gold (SAMs) without the solvent, counterions, and contaminants that normally accompany deposition from solution. Alkylthiol, perfluorinated, and carboxylic-acid terminated monolayers were employed as representative model supports on which different POM-surface and POM-POM interactions were characterized. We obtained insights into the vibrational properties of supported V-doped POMs and how they are perturbed by interactions with specific surface functional groups using infrared reflection absorption and scattering-type scanning near-field optical microscopy, as well as tip enhanced Raman spectroscopy. Different functional groups on SAMs and nanoscale heterogeneity are both shown to modulate the observed spectroscopic signatures. Spectral shifts are also found to be dependent on POM-POM interactions. The electronic structure of the V-doped POMs was determined in the gas phase using negative ion photoelectron spectroscopy and on surfaces with scanning Kelvin probe microscopy. The chemical functionality and charge transfer properties of the SAMs are demonstrated to exert an influence on the charge state and electronic configuration of supported V-doped POMs. The geometric and electronic structure of the POMs were also calculated using density functional theory. Our joint experimental and theoretical findings provide insight into how V substitution as well as POM-surface and POM-POM interactions influence the vibrational properties of POMs.
RESUMO
Microplastic particles are of increasing environmental concern due to the widespread uncontrolled degradation of various commercial products made of plastic and their associated waste disposal. Recently, common technology used to repair sewer pipes was reported as one of the emission sources of airborne microplastics in urban areas. This research presents results of the multi-modal comprehensive chemical characterization of the microplastic particles related to waste discharged in the pipe repair process and compares particle composition with the components of uncured resin and cured plastic composite used in the process. Analysis of these materials employs complementary use of surface-enhanced Raman spectroscopy, scanning transmission X-ray spectro-microscopy, single particle mass spectrometry, and direct analysis in real-time high-resolution mass spectrometry. It is shown that the composition of the relatively large (100 µm) microplastic particles resembles components of plastic material used in the process. In contrast, the composition of the smaller (micrometer and sub-micrometer) particles is significantly different, suggesting their formation from unintended polymerization of water-soluble components occurring in drying droplets of the air-discharged waste. In addition, resin material type influences the composition of released microplastic particles. Results are further discussed to guide the detection and advanced characterization of airborne microplastics in future field and laboratory studies pertaining to sewer pipe repair technology.
Assuntos
Microplásticos , Poluentes Químicos da Água , Plásticos/análise , Água/análise , Espectrometria de Massas , Poluentes Químicos da Água/análise , Monitoramento Ambiental/métodosRESUMO
Tip-enhanced Raman spectroscopy (TERS) is a powerful technique that enables ultrahigh spatial resolution and ultrasensitive chemical imaging. This technique's ability to track plasmon-induced/enhanced chemical reactions in real space has gained increasing popularity in recent years. In this study, we expose inherent difficulties associated with assigning TERS signatures that accompany chemical transformations. Namely, distinct selection rules as well as the possibility of multiple physical processes/chemical reaction pathways complicate spectral assignments and necessitate caution in assigning the experimental observables. We illustrate the latter using 4,4'-dimercaptostilbene-functionalized plasmonic silver nanocubes, wherein we identify the TERS signatures of product formation, molecular charging, multipolar Raman scattering, and preferred molecular orientations that all lead to distinct and assignable spectral patterns.
Assuntos
Análise Espectral Raman , Análise Espectral Raman/métodosRESUMO
Nanoplastic particles are inadequately characterized environmental pollutants that have adverse effects on aquatic and atmospheric systems, causing detrimental effects to human health through inhalation, ingestion and skin penetration1-3. At present, it is explicitly assumed that environmental nanoplastics (EnvNPs) are weathering fragments of microplastic or larger plastic debris that have been discharged into terrestrial and aquatic environments, while atmospheric EnvNPs are attributed solely to aerosolization by wind and other mechanical forces. However, the sources and emissions of unintended EnvNPs are poorly understood and are therefore largely unaccounted for in various risk assessments4. Here we show that large quantities of EnvNPs may be directly emitted into the atmosphere as steam-laden waste components discharged from a technology commonly used to repair sewer pipes in urban areas. A comprehensive chemical analysis of the discharged waste condensate has revealed the abundant presence of insoluble colloids, which after drying form solid organic particles with a composition and viscosity consistent with EnvNPs. We suggest that airborne emissions of EnvNPs from these globally used sewer repair practices may be prevalent in highly populated urban areas5, and may have important implications for air quality and toxicological levels that need to be mitigated.
Assuntos
Poluentes Ambientais , Poluentes Químicos da Água , Humanos , Microplásticos , Plásticos/análise , Plásticos/química , Atmosfera , Monitoramento Ambiental , Poluentes Químicos da Água/análiseRESUMO
We interrogate para-mercaptobenzoic acid (MBA) molecules chemisorbed onto plasmonic silver nanocubes through tip-enhanced Raman (TER) spectral nanoimaging. Through a detailed examination of the spectra, aided by correlation analysis and density functional theory calculations, we find that MBA chemisorbs onto the plasmonic particles with at least two distinct configurations: S- and CO2-bound. High spatial resolution TER mapping allows us to distinguish between the distinct adsorption geometries with a pixel-limited (<5 nm) spatial resolution under ambient laboratory conditions.
RESUMO
Classical versus quantum plasmons are responsible for the recorded signals in non-contact-mode versus contact-mode tip-enhanced Raman spectroscopy (TERS) and lead to distinct observables. Under otherwise identical experimental conditions, we illustrate the concept through tapping- and contact-mode TERS mapping of chemically functionalized silver nanocubes. Whereas molecular charging, chemical transformations, and optical rectification are prominent observables in contact-mode TERS, the same effects are suppressed using tapping-mode feedback. In effect, this work demonstrates that nanoscale physical and chemical processes can be accessed and/or suppressed on demand in the TERS geometry. The advantages of tapping-mode TERS are otherwise highlighted with the latter in mind.
RESUMO
We record nanoscale chemical images of thiobenzonitrile (TBN)-functionalized plasmonic gold nanocubes via tip-enhanced Raman spectroscopy (TERS). The spatially averaged optical response is dominated by conventional (dipolar) TERS scattering from TBN but also contains weaker spectral signatures in the 1225-1500 cm-1 region. The weak optical signatures dominate several of the recorded single-pixel TERS spectra. We can uniquely assign these Raman-forbidden transitions to multipolar Raman scattering, which implicates spatially varying enhanced electric field gradients at plasmonic tip-sample nanojunctions. Specifically, we can assign observations of tip-enhanced electric dipole-magnetic dipole as well as electric dipole-electric quadrupole driven transitions. Multipolar Raman scattering and local optical field gradients both need to be understood and accounted for in the interpretation of TERS spectral images, particularly in ongoing quests aimed at chemical reaction mapping via TERS.
RESUMO
We revisit the reductive coupling of p-nitrothiophenol (NTP) to form dimercaptoazobenzene (DMAB), herein monitored through gap-mode tip-enhanced Raman spectroscopy (TERS) and nanoimaging. We employ a plasmonic Au probe (100 nm diameter at its apex) illuminated with a 633 nm laser source (50 µW/µm2 at the sample position) to image an NTP-coated faceted silver nanoparticle (â¼70 nm diameter). A detailed analysis of the recorded spectra reveals that anionic NTP species contribute to the recorded spectral images, in addition to the more thoroughly described DMAB product. Notably, the signatures of the anions are more pronounced than those of the DMAB product under our present experimental conditions. Our results thus demonstrate that anions and their spectral signatures must be considered in the analysis of plasmon-enhanced optical spectra and images.
RESUMO
Tip-enhanced Raman (TER) spectral images of 4-thiobenzonitrile-coated Au nanorods map the spatial profiles and trace the resonances of dipolar and multipolar plasmonic modes that are characteristic of the imaged particles. For any particular rod, we observe sequential transitions between high-order modes at low frequency shifts and lower-order modes at higher frequencies. We also notice that higher-order modes (up to m = 4) are generally observed for long rods as compared to their shorter analogues, where longitudinal dipolar resonances (m = 1) are observable. In effect, this work adds a new dimension to local optical field mapping via TERS, which we have previously explored. Not only can the magnitudes, vector components, local/nonlocal characters of local optical fields be imaged through molecular TERS, but spatially varying local optical resonances are also direct observables.