Influence of oil contamination on in vitro bond strength of bonding agents to dental substrates.

PURPOSE: To evaluate the influence of cleaning procedures (pumice, anionic detergent and both procedures together) on the tensile bond strength of etch-and-rinse and self-etch adhesive systems to bovine enamel and dentin in vitro. METHODS: Eighty non-carious, bovine incisors were extracted, embedded in acrylic resin to obtain enamel/dentin specimens. Flat bonding surfaces were obtained by grinding. Groups were divided according to substrate (enamel or dentin), adhesive system [etch-and-rinse, Adper Single Bond 2 (SB) or self-etch, Clearfil Protect Bond (PB)]; and cleaning substances (pumice, anionic detergent and their combination). The teeth were randomly divided into 20 groups (n=8): G1--Enamel (E) + SB; G2--E + oil (O) + SB; G3--E + O + Pumice (P) + SB; G4--E + O + Tergentol (T) + SB; G5--E + O + P + T + SB; G6--E + PB; G7--E + O + PB; G8--E + O + P + PB; G9--E + O + T + PB; G10--E + O + P + T + PB; G11--Dentin (D) + SB; G12 D + SB + O; G13--D + SB + O + P; G14--D + SB + O + T;G15--D + SB + O + P + T; G16--D + PB; G17--D + O + PB +; G18--D + O + P + PB; G19--D + O + T + PB; G20--D + O + P + T + PB. Specimens were contaminated with handpiece oil for 5 seconds before bonding. Adhesive systems and resin composite were applied according to manufacturers' instructions. Specimens were tested in tension after 24 hours of immersion using a universal testing machine at a crosshead speed of 0.5 mm/minute. Bond strengths were analyzed with ANOVA. Failure sites were observed and recorded. RESULTS: Tensile bond strength in MPa were: G1 (23.6 +/- 0.9); G2 (17.3 +/- 2.2); G3 (20.9 +/- 0.9); G4 (20.6 +/- 0.5); G5 (18.7 +/- 2.3); G6 (23.0 +/- 1.0); G7 (21.5 +/- 2.4); G8 (19.9 +/- 1.3); G9 (22.1 +/- 1.2); G10 (19.1 +/- 1.2); G11 (18.8 +/- 1.3); G12 (15.7 +/- 2.1); G13 (17.8 +/- 3.3); G14 (15.3 +/- 2.9); G15 (15.6 +/- 1.9); G16 (14.7 +/- 2.3); G17 (5.5 +/- 0.9); G18 (19.3 +/- 1.8); G19 (15.6 +/- 1.6); G20 (20.3 +/- 3.9). Statistical analysis showed that the main factors substrate and cleaning were statistically significant, as well as the triple interaction between factors of variance. However, the factor adhesive system did not show statistical difference. Oil contamination reduced bond strengths, being less detrimental to enamel than to dentin. Etch-and-rinse (SB) and two-step self-etch (PB) systems had similar bond strengths in the presence of oil contamination. For etch-and-rinse (SB), the cleaning procedures were able to clean enamel, but dentin was better cleaned by pumice. When self-etch (PB) system was used on enamel, anionic detergent was the best cleaning substance, while on dentin the tested procedures were similarly efficient.

Influence of Er:YAG laser surface treatment and primer application methods on microtensile bond strength self-etching systems.

OBJECTIVE: The aim of this in vitro study was to evaluate how surface preparation and primer application technique can influence the microtensile bond strength of self-etching system. BACKGROUND DATA: One of the possible applications of dental lasers includes increasing the quality of bond strength. MATERIALS AND METHODS: 12 extracted, sound human molars were ground flat to expose occlusal dentin and were then divided into six groups (G1-G6)(n = 30-36) according to surface preparation and primer application (active or passive): G1-diamond bur (DB) + active primer (AP); G2-DB + passive primer (PP); G3-Er:YAG laser (EL) + AP; G4-EL + PP; G5-#600-grit paper disc (PD) + AP; G6-PD + PP. After adhesive procedure, 5-mm high composite buildups were created with Z 250. After storage in water at 37 degrees C for 24 h, teeth were vertically sectioned into serial 1- mm2 sticks. Samples were tested for tension in an Instron machine at 0.5 mm/min. Nine additional molars were prepared to morphological analysis. Regular grit diamond bur, Er:YAG laser, or #600-grit SiC paper was used for SEM observations of dentin surfaces of each group before and after treatment with self-etching primers. Microtensile data were submitted to statistical analysis. RESULTS: G1-43.85 +/- 9.60 MPa; G2-24.28 +/- 8.90 MPa; G3-24.11 +/- 4.05 MPa; G4-23.30 +/- 4.21 MPa; G5-55.64 +/- 8.50 MPa; G6-56.45 +/- 12.05 MPa. CONCLUSIONS: (1) Er:YAG laser and diamond burs are able to create distinct smear layers; however the resistance of dentin/adhesive interface is similar. In this way, we can use both instruments clinically without diminishing bond strength; (2) the #600-grit sandpaper disc least affects resistance and is highly recommended for in vitro studies to achieve standard preparation of dentinal surface; (3) active primer application is the method most recommended, despite the type of dentin preparation instrument used.

Microtensile bond strength analysis of different adhesive systems and dentin prepared with high-speed and Er:YAG laser: a comparative study.

OBJECTIVE: The aim of this study was to evaluate the bond strength of two adhesive systems (Single Bond and Clearfil SE Bond) subjected or not to a thermocycling procedure and applied to cavities prepared either with high-speed diamond bur or Er:YAG laser. BACKGROUND DATA: One of the possible applications of dental lasers includes increasing the quality of bond strength. METHODS: This in vitro study was carried out using a microtensile test on 16 bovine teeth, divided into eight groups. Cavities were prepared on superficial dentin of the medium portion of the buccal surface. After application of adhesive systems, composite restorations were performed at 5-mm height. After 24 h, four groups of teeth were immersed in water, and the other four were thermocycled. Bonded specimens were sectioned into serial 1x1-mm beams, which were subjected to a microtensile test. Final values of bond strength were measured, expressed in MPa, and statistically analyzed. RESULTS: Results were as follows: G1 (26.281 +/- 5.454 MPa); G2 (10.965 +/- 3.714 MPa); G3 (18.549 +/- 6.113 MPa); G4 (14.295 +/- 3.806 MPa); G5 (18.225 +/- 5.701 MPa); G6 (5.588 +/- 2.211 MPa); G7 (18.256 +/- 3.819 MPa); and G8 (15.423 +/- 4.714 MPa). CONCLUSIONS: Self-etching adhesive system (SE) produced more stable bond strength results than the system that indicates total etching (SB). For dentin prepared at high speed, the total etching adhesive system was more indicated, whereas Er:YAG laser-preparation dentin was not influenced by the adhesive system. The thermocycling procedure could negatively affect microtensile bond strength of both adhesive systems, being more deleterious to SB than to SE.

Estudo comparativo in vitro da microinfiltração entre preparos Classe V realizados com alta rotação e Er:YAG laser, restaurados com materiais estéticos / Microleakage in vitro study comparative of Class V cavity preparations by high speed and Er:YAG laser restored with aesthetic materials

Introdução - O objetivo desta pesquisa experimental, in vitro, foi avaliar comparativamente a microinfiltração que ocorre entre preparos de Classe V realizados com alta rotação e com Er:YAG laser e restaurados com materiais estéticos. Métodos - Foram utilizados 40 dentes bovinos,e realizadas cavidades de Classe V nos terços cervicais vestibulares, utilizando cimento de ionômero de vidro fotopolimerizável (Vitremer - 3M) e resina composta fotoativada (Z250 ? 3M). A técnica restauradora de cada material foi como sugere o fabricante. Foram executados em 20 dentes, preparos com ponta diamantada em alta rotação refrigerado e nos outros 20 elementos dentários, preparos com Er:YAG laser. Em 10 dos 20 dentes preparados com alta rotação foi realizada a técnica restauradora, do cimento de ionômero de vidro fotopolimerizável, e nos outros 10, foram realizadas, restaurações com resina composta fotoativada. Nos 20 dentes, preparados com Er:YAG Laser, o procedimento restaurador foi similar aos grupos de alta rotação. Todos os corpos de prova foram submetidos à ciclagem térmica e técnica de infiltração com Nitrato de Prata a 50% por 8 horas. Após foi feito um corte no sentido longitudinal obtendo-se duas porções. As amostras foram examinadas com lupa estereomicroscópica e através de fotos foi feita a avaliação por três avaliadores. Resultados - Foi realizado o teste estatístico de Kruskal-Wallis com nível de significância de 5% e observamos que não houve diferença estatisticamente significante. Conclusões - Com base nos resultados, concluiu-se que todos os grupos apresentaram microinfiltração, não havendo diferenças entre os materiais selecionados.

Introduction - The purpose of this in vitro experimental study was to evaluate comparatively the microleakage of Class V cavity preparation by high speed and Er:YAG laser restored with aesthetic materials. Methods - Class V preparation were done on the cervical third of the facial surface in 40 extracted bovine teeth and restored with light cure glass ionomer (Vitremer - 3M) and light cure composite (Z250 - 3M). The restorative technique of each material followed the manufactorer's directions. Twenty teeth were prepared by high speed and diamond bur and the others twenty teeth were prepared by Er: YAG laser. Ten of twenty prepared teeth with high speed were restored by light cure glass ionomer and the another ten teeth were restored by light cure composite. In twenty teeth prepared by ER: YAG the restorations technique was similar to the high speed group. All specimens were termocycled and submitted to microleakage test with complete immersion in aqueous solution of 50 % Silver Nitrate for 8 hours. After this procedure the specimens were sectioned in two portions. The extend of microleakage was determined under stereomicroscopy and under pictures took from each specimen, following a criteria ranging from 0 to 3 by three examiners. Results - The results were submitted to Kruskal-Wallis statistic test with a significant level of 5% and we observed that there was no statistically significant difference between tested groups. Conclusions - It was concluded that all groups reveals microleakage and there were no differences between analysed materials.

Avaliaçäo morfológica da uniäo entre adesivo/resina composta e dentina irradiada com laser Er:YAG e laser Nd:YAG: estudo comparativo por microscopia de varredura / Morphological evaluation of the bonding between adhesive/composite resin and dentin irradiated with Er:YAG and Nd:YAG lasers: comparative study using scanning microscopy

Desde a introduçäo de sistemas adesivos nos procedimentos restauradores com materiais estéticos, tem-se estudado de forma abrangente o tipo de tratamento na superfície dentinária para se consagrar uma técnica ideal. A utilizaçäo do ácido fosfórico a 37 por cento sobre a dentina é atualmente ainda o método que mais se domina em termos de adesividade. Porém, métodos de tratamento alternativos, na dentina, têm sido discutidos na literatura, entre eles a aplicaçäo de alguns tipos de irradiaçäo a laser. O objetivo desta pesquisa foi avaliar morfologicamente a uniäo adesivo/resina composta e dentina irradiada com laser Er: YAG e laser Nd: YAG num estudo comparativo por microscopia de varredura, utilizados em substituiçäo ao condicionamento ácido ou associados ao mesmo. Foram utilizados dentes bovinos recém-extraídos, que receberam um preparo de cavidade de classe V, e restauraçäo com sistema adesivo e resina composta fotoativada. Com variantes alguns deles receberam o tratamento prévio de irradiaçäo com laser Er: YAG e outros de irradiaçäo com laser Nd: YAG, à aplicaçäo do agente adesivo e da resina composta. As amostras foram seccionadas, preparadas para microscopia de varredura e submetidas a uma análise morfológica, e foram feitos os registros por meio de fotomicrografias. Com base nessas observaçöes microscópicas, concluímos que somente no tratamento da superfície da dentina com laser Er: YAG e condicionamento ácido houve penetraçäo da resina na dentina. Nos tratamentos com laser Nd: YAG, houve apenas aparente superposiçäo da resina na superfície dentinária, sugerindo que houve oclusäo dos túbulos com características de fusäo na dentina superficial

Estudo comparativo in vitro da microinfiltração entre preparos de Classe V realizados com alta rotação e Er: YAG laser, restaurados com materiais estéticos / Microleakage in vitro study comparative of class V cavity preparations by high speed and Er: YAG laser restored with aesthetic materials

Introdução - O objetivo desta pesquisa experimental, in vitro, foi avaliar comparativamente a microinfiltração que ocorre entre preparos de Classe V, realizados com alta rotação e com Er: YAG laser e restaurados com materiais estéticos. Métodos - Foram utilizados 40 dentes bovinos, e realizadas cavidades de Classe V nos terços cervicais vestibulares, utilizando-se cimento de iônomero de vidro fotopolimerizável (Vitremer - 3M) e resina composta fotoativada (Z250 - 3M). A técnica restauradora de cada material foi como sugere o fabricante. Foram executados em 20 dentes, preparos com ponta diamantada em alta rotação refrigerado e nos outros 20 elementos dentários, preparos com o Er: YAG laser. Em 10 dos 20 dentes preparados com alta rotação foi realizada a técnica restauradora, do cimento de ionômero de vidro fotopolimerizável, e nos outros 10, foram realizadas restaurações com resina composta fotoativada. Nos 20 dentes, preparados com Er: YAG laser, o procedimento restaurador foi similar aos grupos de alta rotação. Todos os corpos de prova foram submetidos à ciclagem térmica e técnica de infiltração com Nitrato de Prata a 50% por 8 horas. Após foi feito um corte no sentido longitudinal obtendo-se duas porções. As amostras foram examinadas com lupa estereomicroscópica e através de fotos foi feita a avaliação por três avaliadores. Resultados - Foi realizado o teste estatístico de Kruskal-Wallis com nível de significância de 5% e observamos que não houve diferença estatisticamente significante. Conclusões - Com base nos resultados, concluiu-se que todos os grupos apresentaram microinfiltração, não havendo diferenças entre os materiais selecionados.

Efeito de pastas à base de hidróxido de cálcio sobre a polpa de molares de ratos, exposta experimentalmente: estudo histopatológico comparativo / The effect of calcium hydroxide pastes in pulpar capping of rat molars: comparative histologic study

Foram utilizados 120 primeiros molares superiores de 60 ratos, com o objetivo de avaliar a reaçäo da polpa sob a açäo de pastas à base de hidróxido de cálcio. Os animais foram distribuídos em 3 grupos de 10 ratos, divididos em 5 períodos de 4 animais de 3, 7, 15, 30 e 45 dias. Concluiu-se que: 1 - todas as pastas caracterizam-se como irritantes, persistindo no decorrer dos períodos evoluçäo por reparaçäo; 2 - houve melhor comportamento nos grupos 1 (hidróxido de cálcio + polietileno glicol 400) e iii (hidróxido de cálcio + polietileno glicol 400 + óxido de zinco) sobre o II (hidróxido de cálcio + polietileno glicol 400 + iodofórmio); 3 - todas as pastas, a partir do 7- dia, induziram à formaçäo de massas amorfas como mineralizadas, tendendo a barreira, apresentando variaçöes na qualidade e na quantidade, acompanhando o comportamento reacional

Avaliaçäo clínica da integridade marginal em restauraçöes de amálgama / Clinical evaluation of marginal integrity of amalgam dental fillings

A integridade marginal e restauraçöes a amálgama, confeccionadas a partir de três tipos de materiais, tratamentos superficiais e polimentos, foi analisada aos 6, 12 e 18 meses, através do exame clínico direto, proposto por Gunnar Ryge e com algumas modificaçöes por nós introduzidas, o qual revelou um aumento de falhas marginais nas restauraçöes analisadas ao longo do tempo, para quaisquer dos fatores, sendo que as restauraçöes polidas de imediato apresentaram maior tendência a falhas que as näo polidas ou polidas após 7 dias

Análise da resistência de uniäo entre diferentes sistemas adesivos e dentina preparada com alta rotaçäo e laser Er: YAG / Microtensile bond strength analysis of differents adhesive systems and dentin prepared with high speed and Er: YAG laser

Analisamos a resistência adesiva à dentina de dois adesivos (Single Bond e Clearfil SE Bond), submetidos ou näo à ciclagem térmica, aplicados em preparos cavitários convencionais e preparos com laser Er: YAG. O estudo in vitro realizado pela técnica de micro-traçäo utilizou 16 dentes bovinos, divididos em 8 grupos. Os preparos cavitários foram realizados no terço médio da face vestibular, em dentina superficial, onde após aplicaçäo dos sistemas adesivos, foi feita restauraçäo com 5 mm de altura. A seguir, 4 grupos passaram por ciclagem térmica e os outros 4 grupos foram armazenados em água por 24 horas. Os espécimes foram entäo seccionados serialmente (1 mm) nos sentidos mésio-distal e cérvico-incisal. Os corpos-de-prova obtidos, na forma de palitos, foram submetidos ao teste de micro-traçäo. Os valores finais de resistência adesiva foram expressos em MPa e analisados estatisticamente. Nossos resultados demonstraram que o sistema adesivo auto-condicionante (SE) apresenta resultados mais estáveis do que o sistema que necessita de condicionamento ácido como passo prévio/ para dentina preparada com alta rotaçäo, o sistema adesivo mais indicado é o que utiliza condicionamento ácido antes do sistema adesivo, enquanto para dentina preparada com laser Er: YAG, o sistema adesivo utilizado näo influencia na resistência de união/ a ciclagem térmica é capaz de afetar negativamente a resistência de união à dentina dos sistemas adesivos testados, sendo mais deletéria ao adesivo monocomponente com condicionamento ácido (SB) do que ao sistema auto-condicionante (SE)