Design of TiO2-Surfactin Hybrid Systems with Multifunctional Properties.

In recent years, multifunctional inorganic-organic hybrid materials have been widely investigated in order to determine their potential synergetic, antagonist, or independent effects in terms of reactivity. The aim of this study was to design and characterize a new hybrid material by coupling well-known photocatalytic TiO2 nanoparticles with sodium surfactin (SS), a biosurfactant showing high binding affinity for metal cations as well as the ability to interact with and disrupt microorganisms' cell membranes. We used both chemical and colloidal synthesis methodologies and investigated how different TiO2:SS weight ratios affected colloidal, physicochemical, and functional properties. We discovered a clear breaking point between TiO2 and SS single-component trends and identified different ranges of applicability by considering different functional properties such as photocatalytic, heavy metal sorption capacity, and antibacterial properties. At low SS contents, the photocatalytic properties of TiO2 are preserved (conversion of organic dye = 99% after 40 min), and the hybrid system can be used in advanced oxidation processes, taking advantage of the additional antimicrobial SS properties. At high SS contents, the TiO2 photoactivity is inhibited, and the hybrid can be usefully exploited as a UV blocker in cosmetics, avoiding undesired oxidative effects (UV adsorption in the range between 300-400 nm). Around the breaking point (TiO2:SS 1:1), the hybrid material preserves the high surface area of TiO2 (specific surface area around 180 m2/g) and demonstrates NOx depletion of up to 100% in 80 min, together with improved adhesion of hybrid antibacterial coating. The last design demonstrated the best results for the concurrent removal of inorganic, organic, and biological pollutants in water/soil remediation applications.

Mussel Shell-Derived Macroporous 3D Scaffold: Characterization and Optimization Study of a Bioceramic from the Circular Economy.

Fish industry by-products constitute an interesting platform for the extraction and recovery of valuable compounds in a circular economy approach. Among them, mussel shells could provide a calcium-rich source for the synthesis of hydroxyapatite (HA) bioceramics. In this work, HA nanoparticles have been successfully synthesized starting from mussel shells (Mytilus edulis) with a two steps process based on thermal treatment to convert CaCO3 in CaO and subsequent wet precipitation with a phosphorus source. Several parameters were studied, such as the temperature and gaseous atmosphere of the thermal treatment as well as the use of two different phosphorus-containing reagents in the wet precipitation. Data have revealed that the characteristics of the powders can be tailored, changing the conditions of the process. In particular, the use of (NH4)2HPO4 as the phosphorus source led to HA nanoparticles with a high crystallinity degree, while smaller nanoparticles with a higher surface area were obtained when H3PO4 was employed. Further, a selected HA sample was synthesized at the pilot scale; then, it was employed to fabricate porous 3D scaffolds using the direct foaming method. A highly porous scaffold with open and interconnected porosity associated with good mechanical properties (i.e., porosity in the range 87-89%, pore size in the range 50-300 µm, and a compressive strength σ = 0.51 ± 0.14 MPa) suitable for bone replacement was achieved. These results suggest that mussel shell by-products are effectively usable for the development of compounds of high added value in the biomedical field.