Preparation of 2D supramolecular material doping with TiO2 for degradation of tetracycline.

Anatase TiO2 photocatalyst supported on [BMPP]2[2D-Mo18O56] (BMPP = 1, 3-bis(4-methylpyridine) propane dibromide) was successfully prepared by hydrothermal method. The composites were characterized by field emission scanning electron microscopy (SEM), X-ray diffractometer (XRD), infrared spectroscopy (IR) and energy-dispersive X-ray spectrometer (EDS). The results show that the high content anatase nanoparticles are uniformly loaded on the polyacid supramolecules to form the composite material. The photocatalytic activity of TiO2/Mo9O28-BMPP towards the tetracyclines (TCs), a model pollutant, has been investigated. The results show that under a 500W high-pressure xenon lamp, 0.15 g TiO2/MoB can degrade 97% of 20 mL (25 mg/L) Tc after 115 min, showing high catalytic activity. In addition, 0.15-TiO2/MoB can be easily separated from the reaction system by centrifugation, and the catalyst still maintains high photocatalytic activity after 3 cycles of tests under the same conditions. This shows that it has the potential for recycling. This research provides a new way for the development of new supported catalysts.

Effect of Bainite to Ferrite Yield Strength Ratio on the Deformability of Mesostructures for Ferrite/Bainite Dual-Phase Steels.

The strength and plasticity balance of F/B dual-phase X80 pipeline steels strongly depends on deformation compatibility between the soft phase of ferrite and the hard phase of bainite; thus, the tensile strength of ferrite and bainite, as non-negligible factors affecting the deformation compatibility, should be considered first. In this purely theoretical paper, an abstract representative volume elements (RVE) model was developed, based on the mesostructure of an F/B dual-phase X80 pipeline steel. The effect of the yield strength difference between bainite and ferrite on tensile properties and the strain hardening behaviors of the mesostructure was studied. The results show that deformation first occurs in ferrite, and strain and stress localize in ferrite prior to bainite. In the modified Crussard-Jaoul (C-J) analysis, as the yield strength ratio of bainite to ferrite (σy,B/σy,F) increases, the transition strain associated with the deformation transformation from ferrite soft phase deformation to uniform deformation of ferrite and bainite increases. Meanwhile, as the uncoordinated deformation of ferrite and bainite is enhanced, the strain localization factor (SLF) increases, especially the local strain concentration. Consequently, the yield, tensile strength, and yield ratio (yield strength/tensile strength) increase with the increase in σy,B/σy,F. Inversely, the strain hardening exponent and uniform elongation decrease.