Light-Sensing Properties of Amorphous Vanadium Oxide Films Prepared by RF Sputtering.

In this study we analyzed the structure and light-sensing properties of as-deposited vanadium oxide thin films, prepared by RF sputtering in different Ar:O2 flow rate conditions, at low temperature (e.g., 65 °C). X-ray diffraction (XRD), Scanning Electron Microscopy (SEM-EDX), Raman spectroscopy and X-ray photoelectron spectroscopy (XPS) were employed to analyze the film microstructure, composition and the oxidation states of vanadium ions. The SEM micrographs evidence VxOy films with smooth surfaces, whereas the XRD patterns show their amorphous structure. Raman spectra indicate an increased structural disorder in the films deposited in Ar:O2 flow comparatively with those deposited solely in Ar flow. The XPS data suggest the modification of the oxidation state from V4+ to V5+, thus proving the formation of the V2O5 phase when increasing the oxygen content, which further affects the films' optical properties. We observed a good stability of the photogenerated current in Si/SiO2/VxOy/TiN heterostructures upon excitation with pulses of UV (360 nm), VIS (white light) and NIR (860 nm) light. The responsivity, detectivity and linear dynamic range parameters increase with the O/V ratio in the VxOy films, reaching comparable values with photodetectors based on crystalline V2O5 or VO2.

Nd-Doped ZnO Nanostructures with Enhanced Photocatalytic Performance for Environmental Protection.

Neodymium (Nd)-doped ZnO nanostructures with different amounts of Nd were obtained by the electrospinning-calcination method. X-ray diffraction measurements indicated that the prepared nanostructures have a wurtzite structure without undesirable impurities. Nd doping changes the mean crystallite size as well the lattice strain, as proved by Williamson-Hall plots. The ZnO-based nanostructures were tested as photocatalysts for methylene blue (MB) dye and ciprofloxacin (CIP) drug pollutant degradations under visible light irradiation. Corroborating the obtained results, it was found that the reaction rate constant increased almost linearly with the mean crystallite size (from 2.235 × 10-2 to 3.482 × 10-2 min-1) with a variation in the mean crystallite size from 24.2 to 42.1 nm. Furthermore, the best catalyst sample (0.1% Nd-doped ZnO) was used to optimize the photodegradation process of ciprofloxacin, taking into account the pollutant concentration as well as the catalyst dose. The removal efficiency after 120 min was about 100%, with the rate constant of k = 5.291·10-2 min-1 (CIP) and k = 4.780·10-2 min-1 (MB) for the established optimal conditions. Considering the value of the rate constant, the half-life of the reaction (τ1/2 = ln2/k) was evaluated to be about τ1/2 =13 min for CIP and 14.5 min corresponding to MB. Several catalytic cycles were successfully performed without any loss of photocatalytic activity using these nanostructures, demonstrating that the obtained nanostructures have good stability in the leaching processes.

Antibacterial and Photocatalytic Activity of ZnO/Au and ZnO/Ag Nanocomposites.

The use of a combination of nanoparticles as antimicrobial agents can be one strategy to overcome the tendency of microbes to become resistant to antibiotic action. Also, the optimization of nano-photocatalysts to efficiently remove persistent pollutants from wastewater is a hot topic. In this study, two composites ZnO/Au (1% wt.) and ZnO/Ag (1% wt.) were synthesized by simple aqueous solution methods. The structure and morphology of the r nanocomposites were analyzed by structural and optical characterization methods. The formation of AuNPs and AgNPs in these experiments was also discussed. The antimicrobial properties of ZnO, ZnO/Au, and ZnO/Ag nanomaterials were investigated against Gram-negative bacteria (Pseudomonas aeruginosa) and Gram-positive bacteria (Staphylococcus aureus). The results showed an increase of 80% in the antimicrobial activity of ZnO/Au against Pseudomonas aeruginosa compared with 30% in the case of ZnO/Ag. Similarly, in the case of the S. aureus strain tests, ZnO/Au increased the antimicrobial activity by 55% and ZnO/Ag by 33%. The photocatalytic tests indicated an improvement in the photocatalytic degradation of methylene blue (MB) under UV irradiation using ZnO/Au and ZnO/Ag nanocomposites compared to bare ZnO. The photocatalytic degradation efficiency of ZnO after 60 min of UV irradiation was ∼83%, while the addition of AuNPs enhanced the degradation rate to ∼95% (ZP2), and AgNP presence enhanced the efficiency to ∼98%. The introduction of noble metallic nanoparticles into the ZnO matrix proved to be an effective strategy to increase their antimicrobial activity against P. aeruginosa and S. aureus, and their photocatalytic activity was evaluated through the degradation of MB dye. Comparing the enhancing effects of Au and Ag, it was found that ZnO/Au was a better antimicrobial agent while ZnO/Ag was a more effective photocatalyst under UV irradiation.

The microwave properties of tin sulfide thin films prepared by RF magnetron sputtering techniques.

In this paper we present the microwave properties of tin sulfide (SnS) thin films with the thickness of just 10 nm, grown by RF magnetron sputtering techniques on a 4 inch silicon dioxide/high-resistivity silicon wafer. In this respect, interdigitated capacitors in coplanar waveguide technology were fabricated directly on the SnS film to be used as both phase shifters and detectors, depending on the ferroelectric or semiconductor behaviour of the SnS material. The ferroelectricity of the semiconducting thin layer manifests itself in a strong dependence of the electrical permittivity on the applied DC bias voltage, which induces a phase shift of 30 degrees mm-1at 1 GHz and of 8 degrees mm-1at 10 GHz, whereas the transmission losses are less than 2 dB in the frequency range 2-20 GHz. We have also investigated the microwave detection properties of SnS, obtaining at 1 GHz a voltage responsivity of about 30 mV mW-1in the unbiased case and with an input power level of only 16µW.

Novel Antitumor Agents Based on Fluorescent Benzofurazan Derivatives and Mesoporous Silica.

Two novel fluorescent mesoporous silica-based hybrid materials were obtained through the covalent grafting of [4-hydrazinyl-7-nitrobenz-[2,1,3-d]-oxadiazole (NBDH) and N1-(7-nitrobenzo[c][1,2,5]-oxadiazol-4-yl) benzene-1,2-diamine (NBD-PD), respectively, inside the channels of mesoporous silica SBA-15. The presence of fluorescent organic compounds (nitrobenzofurazan derivatives) was confirmed by infrared spectroscopy (IR), X-ray photoelectron spectroscopy (XPS), thermal analysis (TG), and fluorescence spectroscopy. The nitrogen physisorption analysis showed that the nitrobenzofurazan derivatives were distributed uniformly on the internal surface of SBA-15, the immobilization process having a negligible effect on the structure of the support. Their antioxidant activity was studied by measuring the ability to reduce free radicals DPPH (free radical scavenging activity), in order to formulate potential applications of the materials obtained. Cytotoxicity of the newly synthesized materials, SBA-NBDH and SBA-NBD-PD, was evaluated on human B16 melanoma cells. The morphology of these cells, internalization and localization of the investigated materials in melanoma and fibroblast cells were examined through fluorescence imaging. The viability of B16 (3D) spheroids after treatment with SBA-NBDH and SBA-NBD-PD was evaluated using MTS assay. The results showed that both materials induced a selective antiproliferative effect, reducing to various degrees the viability of melanoma cells. The observed effect was enhanced with increasing concentration. SBA-NBD-PD exhibited a higher antitumor effect compared to SBA-NBDH starting with a concentration of 125 µg/mL. In both cases, a significantly more pronounced antiproliferative effect on tumor cells compared to normal cells was observed. The viability of B16 spheroids dropped by 40% after treatment with SBA-NBDH and SBA-NBD-PD at 500 µg/mL concentration, indicating a clear cytotoxic effect of the tested compounds. These results suggest that both newly synthesized biomaterials could be promising antitumor agents for applications in cancer therapy.

60-700 K CTAT and PTAT Temperature Sensors with 4H-SiC Schottky Diodes.

A SiC Schottky dual-diode temperature-sensing element, suitable for both complementary variation of VF with absolute temperature (CTAT) and differential proportional to absolute temperature (PTAT) sensors, is demonstrated over 60-700 K, currently the widest range reported. The structure's layout places the two identical diodes in close, symmetrical proximity. A stable and high-barrier Schottky contact based on Ni, annealed at 750 °C, is used. XRD analysis evinced the even distribution of Ni2Si over the entire Schottky contact area. Forward measurements in the 60-700 K range indicate nearly identical characteristics for the dual-diodes, with only minor inhomogeneity. Our parallel diode (p-diode) model is used to parameterize experimental curves and evaluate sensing performances over this far-reaching domain. High sensitivity, upwards of 2.32 mV/K, is obtained, with satisfactory linearity (R2 reaching 99.80%) for the CTAT sensor, even down to 60 K. The PTAT differential version boasts increased linearity, up to 99.95%. The lower sensitivity is, in this case, compensated by using a high-performing, low-cost readout circuit, leading to a peak 14.91 mV/K, without influencing linearity.

A New Hybrid Sensitive PANI/SWCNT/Ferrocene-Based Layer for a Wearable CO Sensor.

Developing a sensing layer with high electroactive properties is an important aspect for proper functionality of a wearable sensor. The polymeric nanocomposite material obtained by a simple electropolymerization on gold interdigitated electrodes (IDEs) can be optimized to have suitable conductive properties to be used with direct current (DC) measurements. A new layer based on polyaniline:poly(4-styrenesulfonate) (PANI:PSS)/single-walled carbon nanotubes (SWCNT)/ferrocene (Fc) was electrosynthesized and deposed on interdigital transducers (IDT) and was characterized in detail using electrochemical impedance spectroscopy (EIS), cyclic voltammetry (CV), scanning electron microscopy (SEM), Raman spectroscopy, X-ray photoemission spectroscopy (XPS), and X-ray diffraction (XRD). The sensor characteristics of the material towards carbon monoxide (CO) in the concentration range of 10-300 ppm were examined, showing a minimal relative humidity interference of only 1% and an increase of sensitivity with the increase of CO concentration. Humidity interference could be controlled by the number of CV cycles when a compact layer was formed and the addition of Fc played an important role in the decrease of humidity. The results for CO detection can be substantially improved by optimizing the number of deposition cycles and enhancing the Fc concentration. The material was developed for selective detection of CO in real environmental conditions and shows good potential for use in a wearable sensor.

Very large phase shift of microwave signals in a 6 nm Hf x Zr1-x O2 ferroelectric at ±3 V.

In this letter, we report for the first time very large phase shifts of microwaves in the 1-10 GHz range, in a 1 mm long gold coplanar interdigitated structure deposited over a 6 nm Hf x Zr1-x O2 ferroelectric grown directly on a high resistivity silicon substrate. The phase shift is larger than 60° at 1 GHz and 13° at 10 GHz at maximum applied DC voltages of ±3 V, which can be supplied by a simple commercial battery. In this way, we demonstrate experimentally that the new ferroelectrics based on HfO2 could play an important role in the future development of wireless communication systems for very low power applications.

Binary Mixtures of Meloxicam and L-Tartaric Acid for Oral Bioavailability Modulation of Pharmaceutical Dosage Forms.

Binary mixtures of active pharmaceutical ingredients (API) are researched to improve the oral bioavailability of pharmaceutical dosage forms. The purpose of this study was to obtain mixtures of meloxicam and L-tartaric acid because tartaric acid improves intestinal absorption and meloxicam is more soluble in a weakly basic environment. The mixtures in the 0-1 molar fraction range, obtained from solvent-assisted mechanosynthesis, were investigated by differential scanning calorimetry (DSC), Fourier Transform Infrared (FTIR) spectroscopy, Fourier Transform Raman spectroscopy (FT-Raman), X-ray powder diffraction (XRD) and solubility tests. The physicochemical characteristics of the compounds obtained from DSC data reveal, for the first time, the formation of a co-crystal at meloxicam molar fraction of 0.5. FTIR spectroscopy data show the existence of hydrogen bonds between the co-crystal components meloxicam and L-tartaric acid. FT-Raman spectroscopy was used complementary with FT-IR spectroscopy to analyze the pure APIs and their mixtures, to emphasize the appearance/disappearance and the shifts of the position/intensity of vibrational bands, following the formation of hydrogen-bonded structures or van der Waals interactions, and to especially monitor the crystal lattice vibrations below 400 cm-1. The experimental results obtained by X-ray powder diffraction confirmed the formation of the co-crystal by the loss and, respectively, the apparition of peaks from the single components in the co-crystal diffractogram. The solubility tests showed that the co-crystal product has a lower aqueous solubility due to the acidic character of the other component, tartaric acid. However, when the solubility tests were performed in buffer solution of pH 7.4, the solubility of meloxicam from the co-crystal mixture was increased by 57% compared to that of pure meloxicam. In conclusion, the studied API mixtures may be considered potential biomaterials for improved drug release molecular solids.

Thorough Wide-Temperature-Range Analysis of Pt/SiC and Cr/SiC Schottky Contact Non-Uniformity.

This paper evaluates the non-uniformity degree of platinum and chromium Schottky contacts on silicon carbide. The forward characteristics of experimental samples were acquired in a wide, 60-500 K, temperature range. Microstructural and conventional electrical characterizations were performed, revealing the presence of inhomogeneities on the contact surface. The main parameters were extracted using inhomogeneity models of varying complexity levels. Their relevance is discussed with respect to the models' applicable, limited, temperature ranges. Finally, complete forward curve fitting was achieved using p-diode modeling, evincing that each type of contact behaves as four parallel-connected ideal diodes. Since these parallel diodes have varying influences on the overall device current with temperature and bias, operable domains can be identified where the samples behave suitably.

Laser Processed Hybrid Lead-Free Thin Films for SAW Sensors.

In this study we report the specific interaction of various gases on the modified surface of acoustic wave devices for gas sensor applications, using the piezoelectric ceramic material BaSrTiO3 (BST), with different concentrations of Sr. For enhancing the sensitivity of the sensor, the conductive polymer polyethylenimine (PEI) was deposited on top of BST thin films. Thin films of BST were deposited by pulsed laser deposition (PLD) technique and integrated into a test heterostructure with PEI thin films deposited by matrix assisted pulsed laser evaporation (MAPLE) and interdigital Au electrodes (IDT). Further on, the layered heterostructures were incorporated into surface acoustic wave (SAW) devices, in order to measure the frequency response to various gases (N2, CO2 and O2). The frequency responses of the sensors based on thin films of the piezoelectric material deposited at different pressures were compared with layered structures of PEI/BST, in order to observe differences in the frequency shifts between sensors. The SAW tests performed at room temperature revealed different results based on deposition condition (pressure of oxygen and the percent of strontium in BatiO3 structure). Frequency shift responses were obtained for all the tested sensors in the case of a concentration of Sr x = 0.75, for all the analysed gases. The best frequency shifts among all sensors studied was obtained in the case of BST50 polymer sensor for CO2 detection.

Comparative Study of Graphene Nanoplatelets and Multiwall Carbon Nanotubes-Polypropylene Composite Materials for Electromagnetic Shielding.

Graphene nanoplatelets (GNPs) and multiwall carbon nanotubes (CNTs)-polypropylene (PP) composite materials for electromagnetic interference (EMI) shielding applications were fabricated as 1 mm thick panels and their properties were studied. Structural and morphologic characterization indicated that the obtained composite materials are not simple physical mixtures of these components but new materials with particular properties, the filler concentration and nature affecting the nanomaterials' structure and their conductivity. In the case of GNPs, their characteristics have a dramatic effect of their functionality, since they can lead to composites with lower conductivity and less effective EMI shielding. Regarding CNTs-PP composite panels, these were found to exhibit excellent EMI attenuation of more than 40 dB, for 10% CNTs concentration. The development of PP-based composite materials with added value and particular functionality (i.e., electrical conductivity and EMI shielding) is highly significant since PP is one of the most used polymers, the best for injection molding, and virtually infinitely recyclable.

Self-Sustained Three-Dimensional Macroporous TiO2-Graphene Photocatalyst for Sunlight Decolorization of Methyl Orange.

The development of highly efficient sunlight-driven photocatalysts has triggered increased attention due to their merit in effluent treatment through a chemically green approach. To this end, we present herein the synthesis and characterization of the TiO2/3D-GF/Ni hybrid emphasizing the main structural and morphological properties and the photodegradation process of a highly resistant aromatic azo dye, methyl orange, under both UV light and simulated sunlight. Three-dimensional (3D) graphene was grown by the thermal CVD method on the nickel foam and subsequently coated with thin films of anatase employing the sol-gel method. Thereafter, it was gratifyingly demonstrated that the hybrid nanomaterial, TiO2/3D-GF-Ni, was able to bring about more than 90% decolorization of methyl orange dye after 30 min under simulated sunlight irradiance. Moreover, the efficiency of the methyl orange decolorization was 99.5% after three successive cycles. This high-performance photocatalyst which can effectively decolorize methyl orange will most likely make a great contribution to reducing environmental pollution by employing renewable solar energy.

Carbon Allotropes-Based Paints and Their Composite Coatings for Electromagnetic Shielding Applications.

The present manuscript reports on optimized formulations of alcohol-based conductive paints for electromagnetic interference shielding (EMI), which can ensure compatibility and reduce the visibility of electronic equipment, as a continuation of our previous work in this field, which examined water-based formulations for other applications. Graphite, carbon black, graphene, Fe3O4, Fe ore, and PEDOT:PSS in various ratios and combinations were employed in an alcohol base for developing homogeneous paint-like fluid mixtures that could be easily applied to surfaces with a paintbrush, leading to homogeneous, uniform, opaque layers, drying fast in the air at room temperature; these layers had a reasonably good electrical conductivity and, subsequently, an efficient EMI-shielding performance. Uniform, homogeneous and conductive layers with a thickness of over 1 mm without exfoliations and cracking were prepared with the developed paints, offering an attenuation of up to 50 dB of incoming GHz electromagnetic radiation. The structural and morphological characteristics of the paints, which were studied in detail, indicated that these are not simple physical mixtures of the ingredients but new composite materials. Finally, mechano-climatic and environmental tests on the coatings demonstrated their quality, since temperature, humidity and vibration stressors did not affect them; this result proves that these coatings are suitable for commercial products.

Antimicrobial Activity and Degradation Ability Study on Nanoparticle-Enriched Formulations Specially Designed for the Neutralization of Real and Simulated Biological and Chemical Warfare Agents.

The present work reveals a comprehensive decontamination study on real and simulated biological and chemical warfare agents (BCWA). The emphasis was on evaluating the antimicrobial activity against real biological warfare agents, such as Bacillus anthracis, and also the capacity of neutralizing real chemical warfare agents, such as mustard gas or soman, by employing three different types of organic solutions enriched with ZnO, TiO2, and zeolite nanoparticles, specially designed for decontamination applications. The capacity of decontaminating BCWA was evaluated through specific investigation tools, including surface monitoring with the swabs method, minimum inhibitory (MIC) and minimum bactericidal concentration (MBC) evaluations, time-kill tests for microorganisms, and GC-MS for monitoring chemical agents on different types of surfaces (glass, painted metal, rubber, and cotton butyl rubber). These tests revealed high decontamination factors for BCWA even after only 10 min, accomplishing the requirements imposed by NATO standards. At the completion of the decontamination process, the formulations reached 100% efficacy for Bacillus anthracis after 10-15 min, for soman after 20-30 min, and for mustard gas in an interval comprised between 5 and 24 h depending on the type of surface analyzed.

Novel Water-Based Paints for Composite Materials Used in Electromagnetic Shielding Applications.

The development of materials offering electromagnetic interference (EMI) shielding is of significant consideration, since this can help in expanding the lifetime of devices, electromagnetic compatibility, as well as the protection of biological systems. Conductive paints used widely today in electromagnetic interference (EMI) shielding applications are often based on organic solvents that can create safety issues due to the subsequent environment problems. This paper concerned the development of eco-friendly conductive water-based paints for use in EMI-shielding applications. Graphene nanoplatelets, polyaniline emeraldine (PANI) doped with poly(styrene sulfonic acid) (PSS) or HCl or HBr and poly(3,4-ethylenedioxythiophene) poly(styrene sulfonic acid) (PEDOT:PSS) in various ratios were employed in a water base for developing the paints. The target was to develop homogeneous water-based paint-like fluid mixtures easily applied onto surfaces using a paint brush, leading in homogeneous, uniform, opaque layers, draying fast in air at room temperature, and having quite good electrical conductivity that can offer efficient EMI-shielding performance. The results of this parametric trial indicated the optimum compositions leading in paints with optimized properties that can result in uniform, homogeneous, and conductive layers up to a thickness of over 500 µm without deformation and cracking, offering attenuation of up to 60 dBs of incoming GHz electromagnetic radiation. In addition, the structural and morphological characteristics of these paints were studied in detail.

New Amorphous Hydrogels with Proliferative Properties as Potential Tools in Wound Healing.

The study and discovery of bioactive compounds and new formulations as potential tools for promoting the repair of dermoepidermal tissue in wound healing is of continuing interest. We have developed a new formulation of amorphous hydrogel based on sodium alginate (NaAlg); type I collagen, isolated by the authors from silver carp tails (COL); glycerol (Gli); Aloe vera gel powder (AV); and silver nanoparticles obtained by green synthesis with aqueous Cinnamomum verum extract (AgNPs@CIN) and vitamin C, respectively. The gel texture of the amorphous hydrogels was achieved by the addition of Aloe vera, demonstrated by a rheological analysis. The evaluations of the cytotoxicity and cell proliferation capacity of the experimental amorphous hydrogels were performed against human foreskin fibroblast Hs27 cells (CRL-1634-ATCC). The developed gel formulations did not show a cytotoxic effect. The hydrogel variant containing AgNPs@CIN in a concentration of 8 µg Ag/gel formulation and hydrogel variant with vitamin C had proliferative activity. In addition, the antibacterial activity of the hydrogels was evaluated against S. aureus ATCC 6538, Ps. aeruginosa ATCC 27853, and E. coli ATCC 25922. The results demonstrated that the gel variant based on AgNPs@CIN in a concentration of 95 µg Ag/gel formulation and the hydrogel based on vitamin C show antibacterial activity. Therefore, the developed hydrogels with AgNPs@CIN and vitamin C could be promising alternatives in wound healing.

3D Printed Metal Oxide-Polymer Composite Materials for Antifouling Applications.

Current technology to prevent biofouling usually relies on the use of toxic, biocide-containing materials, which can become a serious threat to marine ecosystems, affecting both targeted and nontargeted organisms. Therefore, the development of broad-spectrum, less toxic antifouling materials is a challenge for researchers; such materials would be quite important in applications like aquaculture. In this respect, surface chemistry, physical properties, durability and attachment scheme can play a vital role in the performance of the materials. In this work, acrylonitrile butadiene styrene (ABS)/micro ZnO or nano ZnO composite lattices with different metal oxide contents were developed using 3D printing. Their antifouling behavior was examined with respect to aquaculture applications by monitoring growth on them of the diatoms Navicula sp. and the monocellular algae Chlorella sp. with image analysis techniques. As shown, the presence of metal oxides in the composite materials can bring about antifouling ability at particular concentrations. The present study showed promising results, but further improvements are needed.

The Physicochemical and Antimicrobial Properties of Silver/Gold Nanoparticles Obtained by "Green Synthesis" from Willow Bark and Their Formulations as Potential Innovative Pharmaceutical Substances.

Green chemistry is a pharmaceutical industry tool, which, when implemented correctly, can lead to a minimization in resource consumption and waste. An aqueous extract of Salix alba L. was employed for the efficient and rapid synthesis of silver/gold particle nanostructures via an inexpensive, nontoxic and eco-friendly procedure. The nanoparticles were physicochemically characterized using ultraviolet-visible spectroscopy (UV-Vis), Fourier transform infrared spectroscopy (FT-IR), dynamic light scattering (DLS), X-ray diffraction (XRD) and scanning electron microscopy (SEM), with the best stability of up to one year in the solution obtained for silver nanoparticles without any chemical additives. A comparison of the antimicrobial effect of silver/gold nanoparticles and their formulations (hydrogels, ointments, aqueous solutions) showed that both metallic nanoparticles have antibacterial and antibiofilm effects, with silver-based hydrogels having particularly high antibiofilm efficiency. The highest antibacterial and antibiofilm efficacies were obtained against Pseudomonas aeruginosa when using silver nanoparticle hydrogels, with antibiofilm efficacies of over 75% registered. The hydrogels incorporating green nanoparticles displayed a 200% increased bacterial efficiency when compared to the controls and their components. All silver nanoparticle formulations were ecologically obtained by "green synthesis" and were shown to have an antimicrobial effect or potential as keratinocyte-acting pharmaceutical substances for ameliorating infectious psoriasis wounds.

Photocatalytic Properties of Eco-Friendly ZnO Nanostructures on 3D-Printed Polylactic Acid Scaffolds.

The present paper reports a novel approach for fabrication of eco-friendly ZnO nanoparticles onto three-dimensional (3D)-printed polylactic acid (PLA) scaffolds/structures. Several alcohol-based traditional Greek liquors were used to achieve the corrosion of metallic zinc collected from a typical galvanic anode to obtain photocatalytic active nanostructured ZnO, varying from water, to Greek "ouzo" and "raki", and pure ethanol, in combination with "Baker's ammonia" (ammonium bicarbonate), sold worldwide in every food store. The photocatalytic active ZnO nanostructures onto three-dimensional (3D)-printed PLA scaffolds were used to achieve the degradation of 50 ppm paracetamol in water, under UV irradiation. This study provides evidence that following the proposed low-cost, eco-friendly routes for the fabrication of large-scale photocatalysts, an almost 95% degradation of 50 ppm paracetamol in water can be achieved, making the obtained 3D ZnO/PLA structures excellent candidates for real life environmental applications. This is the first literature research report on a successful attempt of using this approach for the engineering of low-cost photocatalytic active elements for pharmaceutical contaminants in waters.