Electrospun PVA/CuONPs/Bitter Gourd Nanofibers with Improved Cytocompatibility and Antibacterial Properties: Application as Antibacterial Wound Dressing.

Antibacterial and cyto-compatible tricomponent composite electrospun nanofibers comprised of polyvinyl alcohol (PVA), copper II oxide nanoparticles (CuONPs), and Momordica charantia (bitter gourd, MC) extract were examined for their potential application as an effective wound dressing. Metallic nanoparticles have a wide range of applications in biomedical engineering because of their excellent antibacterial properties; however, metallic NPs have some toxic effects as well. The green synthesis of nanoparticles is undergoing development with the goal of avoiding toxicity. The aim of adding Momordica charantia extract was to reduce the toxic effects of copper oxide nanoparticles as well as to impart antioxidant properties to electrospun nanofibers. Weight ratios of PVA and MC extract were kept constant while the concentration of copper oxide was optimized to obtain good antibacterial properties with reduced toxicity. Samples were characterized for their morphological properties, chemical interactions, crystalline structures, elemental analyses, antibacterial activity, cell adhesion, and toxicity. All samples were found to have uniform morphology without any bead formation, while an increase in diameters was observed as the CuO concentration was increased in nanofibers. All samples exhibited antibacterial properties; however, the sample with CuO concentration of 0.6% exhibited better antibacterial activity. It was also observed that nanofibrous mats exhibited excellent cytocompatibility with fibroblast (NIH3T3) cells. The mechanical properties of nanofibers were slightly improved due to the addition of nanoparticles. By considering the excellent results of nanofibrous mats, they can therefore be recommended for wound dressing applications.

Sabina chinensis leaf extracted and in situ incorporated polycaprolactone/polyvinylpyrrolidone electrospun microfibers for antibacterial application.

Sabina chinensis is a valuable reforestation conifer and traditional medicinal plant. In order to retain the physiological and pharmacological activities of the plant and obtain a fibrous material with better antibacterial properties, a mixed solvent of dichloromethane and N,N'-dimethylformamide was used to obtain the leaf extracts, and Sabina chinensis leaf extract (ScLE)-loaded PCL/PVP microfibers were successfully fabricated by electrospinning. The whole preparation process was carried out at room temperature to avoid deterioration of active ingredients. From the antibacterial activity test, it was observed that ScLE-loaded polycaprolactone/polyvinylpyrrolidone (PCL/PVP) microfibers had potential antibacterial activity against both Gram-positive and Gram-negative bacteria stains. The morphological properties of the prepared microfibers were observed by SEM. As the proportion of ScLE increased, the fiber diameter gradually increased and the surface was smooth. The excess ScLE addition caused the formation of beads during electrospinning. Considering different characterization results, 33% (v/v) addition of ScLE to the spinning solution was the optimum ratio. The winding structure obtained by the interaction of components in ScLE with PCL and PVP was confirmed by FTIR, XRD and WCA tests, which indicated that ScLE-loaded microfibers possessed excellent thermal stability, tear resistance and degradation resistance. It is expected that the prepared composite microfibers have potential applications as robust antibacterial meshes and films in the fields of biomedicine and air purification.

Lignin-mediated in-situ synthesis of CuO nanoparticles on cellulose nanofibers: A potential wound dressing material.

Herein we present our research on the synthesis of CuO nanoparticles on the surface of electrospun cellulose (CE) nanofibers using alkali lignin as a reducing agent. Fascinatingly, CA nanofibers were deacetalized during alkali lignin treatment, which was verified by FTIR-ATR spectra. The morphology of the produced nanofibers was observed with SEM and TEM. The presence of CuO nanoparticles was verified by EDX, XRD, and XPS. The Cu/CE nanofibers showed low thermal stability. MVTR values of 2100-1900 g/m2/day are adequate for the transport of air and moisture from the wound surface. The Cu/CE showed faster release (80%) of copper ions to aqueous environment within 24 h and seemed to advance towards plateau for the next five days. The Cu/CE nanofibrous mats exhibited excellent antibacterial efficacy against both gram-negative Escherichia coli (E. coli) and gram-positive Staphylococcus aureus (S. aureus) bacteria. NIH3T3 fibroblast cells have excellent migrating and proliferating ability on our prepared nanofibrous mats. The presence of bound alkali lignin on the surface of nanofibers added a benefit of antioxidant activity. These findings revealed that such type of nanofibrous mats could be used as a potential wound dressing material.

Evaluating Antibacterial Efficacy and Biocompatibility of PAN Nanofibers Loaded with Diclofenac Sodium Salt.

Side effects of the drugs' oral administration led us to examine the possibility of using diclofenac sodium (DLF) in a polymeric drug delivery system based on electrospun polyacrylonitrile (PAN) nanofibers, which can be produced cost-effectively and with good applicability for transdermal treatments. The inclusion of DLF in PAN nanofibers increased the nanofiber diameter from ~200 nm to ~500 nm. This increase can be attributed to the increase in the spinning solution viscosity. FTIR spectra confirm the entrapment of the DLF into the PAN nanofibers. X-ray diffraction pattern showed that the inclusion of the DLF in the PAN nanofibers had caused the misalignment in the polymeric chains of the PAN, thus resulting in a decrease of the peak intensity at 2θ = 17o. The DLF loaded PAN nanofibers were efficient against the gram-positive Staphylococcus aureus (S. aureus) and gram-negative Escherichia coli (E. coli), with maximum inhibition zone of 16 ± 0.46 mm for E. coli and 15.5 ± 0.28 mm for S. aureus. Good cell viability ~95% for L929 cells in more extended incubation periods was reported. A gradual release of DLF from the PAN nanofiber was observed and can be attributed to the stability of Pan in PBS medium. Cell adhesion micrographs show that cell-cell interaction is stronger than the cell-material interaction. This type of weak cell interaction with the wound dressing is particularly advantageous, as this will not disturb the wound surface during the nursing of the wound.

Fabricating Antibacterial and Antioxidant Electrospun Hydrophilic Polyacrylonitrile Nanofibers Loaded with AgNPs by Lignin-Induced In-Situ Method.

Concerning the environmental hazards owing to the chemical-based synthesis of silver nanoparticles (AgNPs), this study aimed to investigate the possibility of synthesizing AgNPs on the surface polyacrylonitrile (PAN) nanofibers utilizing biomacromolecule lignin. SEM observations revealed that the average diameters of the produced nanofibers were slightly increased from ~512 nm to ~673 nm due to several factors like-swellings that happened during the salt treatment process, surface-bound lignin, and the presence of AgNPs. The presence of AgNPs was validated by transmission electron microscope (TEM) and X-ray photoelectron spectroscopy (XPS) analysis. The amount of synthesized AgNPs on PAN nanofibers was found to be dependent on both precursor silver salt and reductant lignin concentration. Fourier transform infrared-attenuated total reflectance (FTIR-ATR) spectra confirm the presence of lignin on PAN nanofibers. Although the X-ray diffraction pattern did not show any AgNPs band, the reduced intensity of the stabilized PAN characteristics bands at 2θ = 17.28° and 29.38° demonstrated some misalignment of PAN polymeric chains. The water contact angle (WCA) of hydrophobic PAN nanofibers was reduced from 112.6 ± 4.16° to 21.4 ± 5.03° for the maximum AgNPs coated specimen. The prepared membranes exhibited low thermal stability and good swelling capacity up to 20.1 ± 0.92 g/g and 18.05 ± 0.68 g/g in distilled water and 0.9 wt% NaCl solution, respectively. Coated lignin imparts antioxidant activity up to 78.37 ± 0.12% at 12 h of incubation. The resultant nanofibrous membranes showed a proportional increase in antibacterial efficacy with the rise in AgNPs loading against both Gram-positive S. aureus and Gram-negative E. coli bacterial strains by disc diffusion test (AATCC 147-1998). Halos for maximum AgNPs loading was calculated to 18.89 ± 0.15 mm for S. aureus and 21.38 ± 0.17 mm for E. coli. An initial burst release of silver elements within 24 h was observed in the inductively coupled plasma-atomic emission spectrometry (ICP-AES) test, and the release amounts were proportionally expansive with the increase in Ag contents. Our results demonstrated that such types of composite nanofibers have a strong potential to be used in biomedicine.