Effects of a Dielectric Barrier Discharge (DBD) on Characteristics of Polyaniline Nanoparticles Synthesized by a Solution Plasma Process with an Ar Gas Bubble Channel.

The quality of polyaniline nanoparticles (PANI NPs) synthesized in plasma polymerization depends on the discharge characteristics of a solution plasma process (SPP). In this paper, the low temperature dielectric barrier discharge (DBD) is introduced to minimize the destruction of aniline molecules induced by the direct current (DC) spark discharge. By adopting the new electrode structure coupled with a gas channel, a low temperature DBD is successfully implemented in a SPP, for the first time, thus inducing an effective interaction between the Ar plasma and aniline monomer. We examine the effects of a low temperature DBD on characteristics of polyaniline nanoparticles synthesized by a SPP with an Ar gas bubble channel. As a result, both carbonization of aniline monomer and erosion of the electrode are significantly reduced, which is confirmed by analyses of the synthesized PANI NPs.

Synthesis of a Polyaniline Nanoparticle Using a Solution Plasma Process with an Ar Gas Bubble Channel.

This work researched polymerization of liquid aniline monomer by solution plasma with a gas bubble channel and investigated characteristics of solution plasma and polyaniline (PANI). The injected gas bubble channel in the proposed solution plasma process (SPP) played a significant role in producing a stable discharge in liquid aniline monomer at a low voltage and furthermore enhancing the contact surface area between liquid aniline monomer and plasma, thereby achieving polymerization on the boundary of the liquid aniline monomer and plasma. Solution plasma properties were analyzed with voltage⁻current, optical emission spectroscopy, and high-speed camera. Conductivity, percentage yield, and firing voltage of PANI nanoparticle dispersed solution were measured. To investigate the characteristics of synthesized PANI nanoparticles, field emission scanning electron microscopy, dynamic light scattering, transmission electron microscopy, selective area electron diffraction (SAED) pattern, Fourier transform infrared spectroscopy (FTIR), gel permeation chromatography, ¹H-nuclear magnetic resonance (¹H-NMR), and X-ray photo spectroscopy (XPS) were examined. The FTIR, ¹H-NMR, and XPS analysis showed the PANI characteristic peaks with evidence that some quinoid and benzene rings were broken by the solution plasma process with a gas bubble channel. The results indicate that PANI nanoparticles have a spherical shape with a size between 25 and 35 nm. The SAED pattern shows the amorphous pattern.

In-Liquid Plasma Process for Size- and Shape-Controlled Synthesis of Silver Nanoparticles by Controlling Gas Bubbles in Water.

Most methods controlling size and shape of metal nanoparticles are chemical methods, and little work has been done using only plasma methods. Size- and shape-controlled synthesis of silver nanoparticles (Ag NPs) is proposed based on adjusting the gas bubble formation produced between two silver electrodes. The application of a voltage waveform with three different pulse widths during a plasma process in water can generate different gas bubble formations. Transmission electron microscopy (TEM) and scanning electron microscopy (SEM) images of Ag NPs synthesized using three different bubble formations reveal that spherical Ag NPs are synthesized when very tiny bubbles are generated between two electrodes or when only the grounded electrode is enveloped with large gas bubbles, but Ag nanoplates are synthesized when both electrodes are completely enveloped with large gas bubbles.