Stabilizing catalytically active nanoparticles by ligand linking: toward three-dimensional networks with high catalytic surface area.

A general approach for the linking of Pt nanoparticles (NPs) with bifunctional amine ligands (organic molecules with two amine groups) is presented that allows for the preparation of NP catalysts without inorganic supports and high densities of the catalytically active metal. Advantage was taken of the use of "unprotected" NPs, which enables us to prepare different ligand-functionalized NPs from the same particle batch and thus to relate changes of the resulting material properties exclusively to the influence of the ligand. Three bifunctional ligands with similar functional groups (amines) but different hydrocarbon skeletons were used and compared to monofunctional ligands of similar molecular structures (alkyl and aryl amines) showing significantly different material properties. Monofunctional molecules with minor steric demand cover almost completely the NP surface and lead to two-dimensional assembling of the NPs. In contrast, the use of bifunctional amine ligands leads to the formation of porous, three-dimensional NP networks (ligand-linked NPs) with a high density of ligand free surface atoms, thus enabling for the application as catalytic materials. The stabilizing effect of bifunctional ligands serves as an alternative to the use of inorganic support materials and enables for catalytic applications of ligand-linked NP networks.

Pt based PEMFC catalysts prepared from colloidal particle suspensions--a toolbox for model studies.

A colloidal synthesis approach is presented that allows systematic studies of the properties of supported proton exchange membrane fuel cell (PEMFC) catalysts. The applied synthesis route is based on the preparation of monodisperse nanoparticles in the absence of strong binding organic stabilizing agents. No temperature post-treatment of the catalyst is required rendering the synthesis route ideally suitable for comparative studies. We report work concerning a series of catalysts based on the same colloidal Pt nanoparticle (NP) suspension, but with different high surface area (HSA) carbon supports. It is shown that for the prepared catalysts the carbon support has no catalytic co-function, but carbon pre-treatment leads to enhanced sticking of the Pt NPs on the support. An unwanted side effect, however, is NP agglomeration during synthesis. By contrast, enhanced NP sticking without agglomeration can be accomplished by the addition of an ionomer to the NP suspension. The catalytic activity of the prepared catalysts for the oxygen reduction reaction is comparable to industrial catalysts and no influence of the particle size is found in the range of 2-5 nm.

Electrochemical stability and postmortem studies of Pt/SiC catalysts for polymer electrolyte membrane fuel cells.

In the presented work, the electrochemical stability of platinized silicon carbide is studied. Postmortem transmission electron microscopy and X-ray photoelectron spectroscopy were used to document the change in the morphology and structure upon potential cycling of Pt/SiC catalysts. Two different potential cycle aging tests were used in order to accelerate the support corrosion, simulating start-up/shutdown and load cycling. On the basis of the results, we draw two main conclusions. First, platinized silicon carbide exhibits improved electrochemical stability over platinized active carbons. Second, silicon carbide undergoes at least mild oxidation if not even silicon leaching.

Gold nanoparticles assembled with dithiocarbamate-anchored molecular wires.

A protocol for the bottom-up self-assembly of nanogaps is developed through molecular linking of gold nanoparticles (AuNPs). Two π-conjugated oligo(phenylene ethynylene) molecules (OPE) with dithiocarbamate anchoring groups are used as ligands for the AuNPs. OPE-4S with a dithiocarbamate in each end of the molecule and a reference molecule OPE-2S with only a single dithiocarbamate end group. The linking mechanism of OPE-4S is investigated by using a combination of TEM, UV-Vis absorption and surface enhanced Raman spectroscopy (SERS) as well as studying the effect of varying the OPE-4S to AuNP concentration ratio. UV-Vis absorption confirms the formation of AuNP aggregates by the appearance of an extended plasmon band (EPB) for which the red shift and intensity depend on the OPE-4S:AuNP ratio. SERS confirms the presence of OPE-4S and shows a gradual increase of the signal intensity with increasing OPE-4S:AuNP ratios up to a ratio of about 4000, after which the SERS intensity does not increase significantly. For OPE-2S, no linking is observed below full coverage of the AuNPs indicating that the observed aggregate formation at high OPE-2S:AuNP ratios, above full AuNP coverage, is most likely of a physical nature (van der Waals forces or π-π interactions).